WO2003087252A1 - Cleanly removable tapes and methods for the manufacture thereof - Google Patents
Cleanly removable tapes and methods for the manufacture thereof Download PDFInfo
- Publication number
- WO2003087252A1 WO2003087252A1 PCT/US2003/004398 US0304398W WO03087252A1 WO 2003087252 A1 WO2003087252 A1 WO 2003087252A1 US 0304398 W US0304398 W US 0304398W WO 03087252 A1 WO03087252 A1 WO 03087252A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- tape
- adhesive layer
- adhesive
- layer
- fire retardant
- Prior art date
Abstract
Description
Claims