WO2003086756A1 - Fuel filler hose - Google Patents
Fuel filler hose Download PDFInfo
- Publication number
- WO2003086756A1 WO2003086756A1 PCT/US2003/011130 US0311130W WO03086756A1 WO 2003086756 A1 WO2003086756 A1 WO 2003086756A1 US 0311130 W US0311130 W US 0311130W WO 03086756 A1 WO03086756 A1 WO 03086756A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- thv
- fkm
- layers
- article
- Prior art date
Abstract
Description
Claims