WO2003042271A1 - Composition de resine d'urethanne thermofusible exempte de solvant, durcissant a l'humidite, produit mousse et structure de feuille utilisant ceux-ci - Google Patents

Composition de resine d'urethanne thermofusible exempte de solvant, durcissant a l'humidite, produit mousse et structure de feuille utilisant ceux-ci Download PDF

Info

Publication number
WO2003042271A1
WO2003042271A1 PCT/JP2002/006009 JP0206009W WO03042271A1 WO 2003042271 A1 WO2003042271 A1 WO 2003042271A1 JP 0206009 W JP0206009 W JP 0206009W WO 03042271 A1 WO03042271 A1 WO 03042271A1
Authority
WO
WIPO (PCT)
Prior art keywords
resin composition
prepolymer
moisture
water
solvent
Prior art date
Application number
PCT/JP2002/006009
Other languages
English (en)
Japanese (ja)
Inventor
Yoshinori Kanagawa
Toshio Niwa
Masahiko Takahashi
Original Assignee
Dainippon Ink And Chemicals, Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dainippon Ink And Chemicals, Inc. filed Critical Dainippon Ink And Chemicals, Inc.
Publication of WO2003042271A1 publication Critical patent/WO2003042271A1/fr

Abstract

L'invention concerne une composition de résine d'uréthanne thermofusible exempte de solvant, durcissant à l'humidité, caractérisée en ce qu'elle comprend un prépolymère d'uréthanne thermofusible contenant un groupe isocyanate (A), un composé (B) comprenant au moins deux atomes d'hydrogène actif et de l'eau (C) ; le rapport entre équivalents du groupe isocyanate du prépolymère (A) et équivalents totaux des groupes réactifs du composé (B) et de l'eau (C) [équivalents du groupe NCO/équivalents totaux des groupes réactifs de (B+C)] se situe entre 1,5 et 20.
PCT/JP2002/006009 2001-11-09 2002-06-17 Composition de resine d'urethanne thermofusible exempte de solvant, durcissant a l'humidite, produit mousse et structure de feuille utilisant ceux-ci WO2003042271A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2001-344706 2001-11-09
JP2001344706 2001-11-09

Publications (1)

Publication Number Publication Date
WO2003042271A1 true WO2003042271A1 (fr) 2003-05-22

Family

ID=19158186

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2002/006009 WO2003042271A1 (fr) 2001-11-09 2002-06-17 Composition de resine d'urethanne thermofusible exempte de solvant, durcissant a l'humidite, produit mousse et structure de feuille utilisant ceux-ci

Country Status (2)

Country Link
TW (1) TWI316064B (fr)
WO (1) WO2003042271A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2004060655A1 (fr) 2002-12-27 2004-07-22 Kahei Co., Ltd. Feuille en mousse de polyurethanne et procede de production d'une plaque stratifiee au moyen de cette derniere
US7670517B2 (en) 2002-12-27 2010-03-02 Kahei Co., Ltd. Method of producing polyurethane foam sheet and laminated sheet using same

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN107922562B (zh) * 2015-09-02 2021-05-07 Dic株式会社 湿固化型热熔聚氨酯组合物、其发泡固化物的制造方法、合成皮革及其制造方法

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0297317A2 (fr) * 1987-06-08 1989-01-04 Bridgestone Corporation Procédé de fabrication d'un matériau en mousse rigide ou semi rigide et d'un panneau composite obtenu à partir de cette mousse
JPH07278320A (ja) * 1994-04-13 1995-10-24 Nitta Gelatin Inc ガス非透過性素材の貼合方法およびそれに使用される反応型ホットメルト接着剤

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0297317A2 (fr) * 1987-06-08 1989-01-04 Bridgestone Corporation Procédé de fabrication d'un matériau en mousse rigide ou semi rigide et d'un panneau composite obtenu à partir de cette mousse
JPH07278320A (ja) * 1994-04-13 1995-10-24 Nitta Gelatin Inc ガス非透過性素材の貼合方法およびそれに使用される反応型ホットメルト接着剤

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2004060655A1 (fr) 2002-12-27 2004-07-22 Kahei Co., Ltd. Feuille en mousse de polyurethanne et procede de production d'une plaque stratifiee au moyen de cette derniere
EP1586442A1 (fr) * 2002-12-27 2005-10-19 Kahei Co. Ltd. Feuille en mousse de polyurethanne et procede de production d'une plaque stratifiee au moyen de cette derniere
EP1586442A4 (fr) * 2002-12-27 2006-01-25 Kahei Co Ltd Feuille en mousse de polyurethanne et procede de production d'une plaque stratifiee au moyen de cette derniere
US7670517B2 (en) 2002-12-27 2010-03-02 Kahei Co., Ltd. Method of producing polyurethane foam sheet and laminated sheet using same

Also Published As

Publication number Publication date
TWI316064B (fr) 2009-10-21

Similar Documents

Publication Publication Date Title
US7670517B2 (en) Method of producing polyurethane foam sheet and laminated sheet using same
EP1586442B1 (fr) Feuille en mousse de polyurethanne et procede de production d'une plaque stratifiee au moyen de cette derniere
KR101123262B1 (ko) 알코올 가용형 우레탄 수지 조성물의 제조 방법, 폴리우레탄 다공체 및 투습성 필름
EA000075B1 (ru) Способ получения водных дисперсий полиуретанов с повышенной теплостойкостью и стойкостью к действию растворителей, осуществляемый с уменьшенным количеством растворителя
JP5353559B2 (ja) アルコール可溶型ポリウレタンコーティング剤、接着剤及びそれを用いて得られる皮革様シート
JP5532224B2 (ja) ウレタンプレポリマー
JP4029667B2 (ja) 無溶剤型湿気硬化性ホットメルトウレタン樹脂組成物、発泡体及びそれを用いたシート構造体
KR20090028832A (ko) 첨가제로서 실란 화합물을 포함하는 폴리우레탄 접착제
JP2001207111A (ja) ポリオレフィン系樹脂成形品用コーティング剤およびそれを被覆した成形品
JP4051609B2 (ja) 人工皮革または合成皮革
JP4038608B2 (ja) 耐久性に優れた無溶剤型湿気硬化性ホットメルトウレタン樹脂組成物、発泡体、及びそれを用いたシート構造体
JP4107032B2 (ja) 無溶剤型湿気硬化性ホットメルトウレタン樹脂組成物、発泡体、及びそれを用いたシート構造体
JPH03190981A (ja) 熱硬化性塗料
JP4040895B2 (ja) ポリウレタンウレア発泡体シートおよび該シートを用いた合成皮革
JP4258135B2 (ja) 発泡体、及びそれを用いた発泡シート構造体
JP2003049147A (ja) 合成皮革用無溶剤型湿気硬化性ホットメルトウレタン樹脂接着剤及びそれを用いた合成皮革構成体
WO2003042271A1 (fr) Composition de resine d'urethanne thermofusible exempte de solvant, durcissant a l'humidite, produit mousse et structure de feuille utilisant ceux-ci
JP5142309B2 (ja) 湿気硬化性ポリウレタンホットメルト樹脂組成物
JP2001106896A (ja) 敷物裏打ち用水性樹脂組成物
JPH08253545A (ja) 架橋性ウレタン樹脂の製造方法および架橋性ウレタン樹脂組成物
JP2024020871A (ja) 湿気硬化型ポリウレタンホットメルト接着剤
WO2024122084A1 (fr) Procédé de fabrication de feuille de mousse de polyuréthane, et procédé de fabrication de cuir synthétique
JPH05239175A (ja) 多孔質シート材料

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): CN KR US

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE TR

121 Ep: the epo has been informed by wipo that ep was designated in this application
DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
122 Ep: pct application non-entry in european phase