WO2003006515A1 - Functional fluorine-containing polymers and ionomers derived therefrom - Google Patents
Functional fluorine-containing polymers and ionomers derived therefrom Download PDFInfo
- Publication number
- WO2003006515A1 WO2003006515A1 PCT/US2002/021526 US0221526W WO03006515A1 WO 2003006515 A1 WO2003006515 A1 WO 2003006515A1 US 0221526 W US0221526 W US 0221526W WO 03006515 A1 WO03006515 A1 WO 03006515A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polymer
- copolymer
- monomer
- psepve
- reactor
- Prior art date
Abstract
Description
Claims