WO2002102909A1 - Reactive oligomers - Google Patents
Reactive oligomers Download PDFInfo
- Publication number
- WO2002102909A1 WO2002102909A1 PCT/US2002/010447 US0210447W WO02102909A1 WO 2002102909 A1 WO2002102909 A1 WO 2002102909A1 US 0210447 W US0210447 W US 0210447W WO 02102909 A1 WO02102909 A1 WO 02102909A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- oligomer
- reactive
- composition
- component
- weight
- Prior art date
Abstract
Description
Claims