WO2002070615A1 - Bimodal aqueous polymer dispersions - Google Patents
Bimodal aqueous polymer dispersions Download PDFInfo
- Publication number
- WO2002070615A1 WO2002070615A1 PCT/US2002/001085 US0201085W WO02070615A1 WO 2002070615 A1 WO2002070615 A1 WO 2002070615A1 US 0201085 W US0201085 W US 0201085W WO 02070615 A1 WO02070615 A1 WO 02070615A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- particles
- formulation
- coating
- latex
- dispersion
- Prior art date
Abstract
Description
Claims