WO2001093279A2 - Insulated electric cable - Google Patents
Insulated electric cable Download PDFInfo
- Publication number
- WO2001093279A2 WO2001093279A2 PCT/SE2001/001232 SE0101232W WO0193279A2 WO 2001093279 A2 WO2001093279 A2 WO 2001093279A2 SE 0101232 W SE0101232 W SE 0101232W WO 0193279 A2 WO0193279 A2 WO 0193279A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- viscosity
- temperatures
- cable
- range
- dielectric
- Prior art date
Abstract
Description
Claims