WO2001087528A2 - Welding superalloy articles - Google Patents
Welding superalloy articles Download PDFInfo
- Publication number
- WO2001087528A2 WO2001087528A2 PCT/US2001/040155 US0140155W WO0187528A2 WO 2001087528 A2 WO2001087528 A2 WO 2001087528A2 US 0140155 W US0140155 W US 0140155W WO 0187528 A2 WO0187528 A2 WO 0187528A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- article
- temperature
- superalloy
- welding
- weld
- Prior art date
Abstract
Description
Claims