WO2001064323A1 - Air management in cementitious mixtures having plasticizer and a clay-activity modifying agent - Google Patents
Air management in cementitious mixtures having plasticizer and a clay-activity modifying agent Download PDFInfo
- Publication number
- WO2001064323A1 WO2001064323A1 PCT/US2001/004860 US0104860W WO0164323A1 WO 2001064323 A1 WO2001064323 A1 WO 2001064323A1 US 0104860 W US0104860 W US 0104860W WO 0164323 A1 WO0164323 A1 WO 0164323A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- air
- admixture
- composition
- surface active
- admixture composition
- Prior art date
Abstract
Description
Claims