WO2001058981A1 - Continuous process for producing poly(trimethylene terephthalate) - Google Patents
Continuous process for producing poly(trimethylene terephthalate) Download PDFInfo
- Publication number
- WO2001058981A1 WO2001058981A1 PCT/US2000/021779 US0021779W WO0158981A1 WO 2001058981 A1 WO2001058981 A1 WO 2001058981A1 US 0021779 W US0021779 W US 0021779W WO 0158981 A1 WO0158981 A1 WO 0158981A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- poly
- flasher
- trimethylene terephthalate
- continuously
- terephthalate
- Prior art date
Abstract
Description
Claims