WO2000075205A1 - Waterborne thickeners and dispersants having improved chemical resistance - Google Patents
Waterborne thickeners and dispersants having improved chemical resistance Download PDFInfo
- Publication number
- WO2000075205A1 WO2000075205A1 PCT/US2000/015754 US0015754W WO0075205A1 WO 2000075205 A1 WO2000075205 A1 WO 2000075205A1 US 0015754 W US0015754 W US 0015754W WO 0075205 A1 WO0075205 A1 WO 0075205A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polymer
- monomer
- monomers
- macromonomer
- stage
- Prior art date
Abstract
Description
Claims