WO2000052106A1 - Pigment printing compositions - Google Patents
Pigment printing compositions Download PDFInfo
- Publication number
- WO2000052106A1 WO2000052106A1 PCT/GB2000/000703 GB0000703W WO0052106A1 WO 2000052106 A1 WO2000052106 A1 WO 2000052106A1 GB 0000703 W GB0000703 W GB 0000703W WO 0052106 A1 WO0052106 A1 WO 0052106A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- component
- composition according
- composition
- polymer
- groups
- Prior art date
Abstract
Description
Claims