WO2000032330A1 - Process of making brake rotors - Google Patents
Process of making brake rotors Download PDFInfo
- Publication number
- WO2000032330A1 WO2000032330A1 PCT/US1999/027802 US9927802W WO0032330A1 WO 2000032330 A1 WO2000032330 A1 WO 2000032330A1 US 9927802 W US9927802 W US 9927802W WO 0032330 A1 WO0032330 A1 WO 0032330A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- mold
- fin core
- brake rotor
- sand
- cooling fins
- Prior art date
Abstract
Description
Claims