WO2000006817A1 - Nonwoven webs having zoned migration of internal additives - Google Patents
Nonwoven webs having zoned migration of internal additives Download PDFInfo
- Publication number
- WO2000006817A1 WO2000006817A1 PCT/US1999/015535 US9915535W WO0006817A1 WO 2000006817 A1 WO2000006817 A1 WO 2000006817A1 US 9915535 W US9915535 W US 9915535W WO 0006817 A1 WO0006817 A1 WO 0006817A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- nonwoven fabric
- nonwoven
- additive
- fabric
- web
- Prior art date
Abstract
Description
Claims