WO1998058000A1 - A curable, water-borne one-component coating system using thermally labile hydrophilic groups - Google Patents
A curable, water-borne one-component coating system using thermally labile hydrophilic groups Download PDFInfo
- Publication number
- WO1998058000A1 WO1998058000A1 PCT/US1998/011306 US9811306W WO9858000A1 WO 1998058000 A1 WO1998058000 A1 WO 1998058000A1 US 9811306 W US9811306 W US 9811306W WO 9858000 A1 WO9858000 A1 WO 9858000A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- composition
- resin
- group
- coating
- oligomer
- Prior art date
Abstract
Description
Claims