WO1998049206A1 - Introducing functional groups to a polymer - Google Patents
Introducing functional groups to a polymer Download PDFInfo
- Publication number
- WO1998049206A1 WO1998049206A1 PCT/GB1998/001213 GB9801213W WO9849206A1 WO 1998049206 A1 WO1998049206 A1 WO 1998049206A1 GB 9801213 W GB9801213 W GB 9801213W WO 9849206 A1 WO9849206 A1 WO 9849206A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polymer
- polymers
- azo compound
- produce
- radicals
- Prior art date
Abstract
Description
Claims