WO1998021032A2 - Multi-layer flexible container for flowable materials - Google Patents
Multi-layer flexible container for flowable materials Download PDFInfo
- Publication number
- WO1998021032A2 WO1998021032A2 PCT/US1997/020834 US9720834W WO9821032A2 WO 1998021032 A2 WO1998021032 A2 WO 1998021032A2 US 9720834 W US9720834 W US 9720834W WO 9821032 A2 WO9821032 A2 WO 9821032A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- ethylene
- flexible container
- alpha
- approximately
- parts
- Prior art date
Abstract
Description
Claims