WO1998000456A1 - Process for curing a polymerizable composition - Google Patents
Process for curing a polymerizable composition Download PDFInfo
- Publication number
- WO1998000456A1 WO1998000456A1 PCT/EP1997/003219 EP9703219W WO9800456A1 WO 1998000456 A1 WO1998000456 A1 WO 1998000456A1 EP 9703219 W EP9703219 W EP 9703219W WO 9800456 A1 WO9800456 A1 WO 9800456A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- alkyl
- phenyl
- alkoxy
- group
- hydroxy
- Prior art date
Abstract
Description
Claims