WO1997022553A1 - Method and apparatus for forming fused silica by combustion of liquid reactants - Google Patents
Method and apparatus for forming fused silica by combustion of liquid reactants Download PDFInfo
- Publication number
- WO1997022553A1 WO1997022553A1 PCT/US1996/020756 US9620756W WO9722553A1 WO 1997022553 A1 WO1997022553 A1 WO 1997022553A1 US 9620756 W US9620756 W US 9620756W WO 9722553 A1 WO9722553 A1 WO 9722553A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- feedstock
- siloxane
- liquid
- silica
- conversion site
- Prior art date
Abstract
Description
Claims