WO1997022423A1 - Tole metallique a revetement organique antirouille, son procede de production et liquide de traitement necessite par ce procede - Google Patents
Tole metallique a revetement organique antirouille, son procede de production et liquide de traitement necessite par ce procede Download PDFInfo
- Publication number
- WO1997022423A1 WO1997022423A1 PCT/JP1996/003676 JP9603676W WO9722423A1 WO 1997022423 A1 WO1997022423 A1 WO 1997022423A1 JP 9603676 W JP9603676 W JP 9603676W WO 9722423 A1 WO9722423 A1 WO 9722423A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- water
- resin
- organic
- acid
- metal plate
- Prior art date
Description
Claims