WO1997020662A1 - Abrasive article back up pad with foam layer - Google Patents
Abrasive article back up pad with foam layer Download PDFInfo
- Publication number
- WO1997020662A1 WO1997020662A1 PCT/US1996/017292 US9617292W WO9720662A1 WO 1997020662 A1 WO1997020662 A1 WO 1997020662A1 US 9617292 W US9617292 W US 9617292W WO 9720662 A1 WO9720662 A1 WO 9720662A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- pad
- foam
- ofthe
- abrasive article
- abrasive
- Prior art date
Abstract
Description
Claims