WO1997016487A1 - Miscible polymers - Google Patents

Miscible polymers Download PDF

Info

Publication number
WO1997016487A1
WO1997016487A1 PCT/US1995/014743 US9514743W WO9716487A1 WO 1997016487 A1 WO1997016487 A1 WO 1997016487A1 US 9514743 W US9514743 W US 9514743W WO 9716487 A1 WO9716487 A1 WO 9716487A1
Authority
WO
WIPO (PCT)
Prior art keywords
polymer
styrene
polymers
weight percent
monomer
Prior art date
Application number
PCT/US1995/014743
Other languages
French (fr)
Inventor
Allen Robert Padwa
Original Assignee
Bayer Antwerpen S.A./N.V.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bayer Antwerpen S.A./N.V. filed Critical Bayer Antwerpen S.A./N.V.
Priority to ES95941383T priority Critical patent/ES2145939T3/en
Priority to CA002235934A priority patent/CA2235934A1/en
Priority to DE69516912T priority patent/DE69516912T2/en
Priority to EP95941383A priority patent/EP0858482B1/en
Priority to US09/051,741 priority patent/US5905118A/en
Priority to PCT/US1995/014743 priority patent/WO1997016487A1/en
Publication of WO1997016487A1 publication Critical patent/WO1997016487A1/en

Abstract

Disclosed herein are terpolymers of styrene, acrylonitrile and dimethyl styrene phosphonate and blends thereof with poly(styrene acrylonitrile) polymers and polymers and copolymers of methylmethacrylate.

Description

MISCIBLE POLYMERS BACKGROUND OF THE INVENTION The present invention relates to terpolymers of a vinyl aromatic monomer such as styrene, α-methylstyrene, chlorostyrene and the like; an unsaturated nitrile monomer such as acrylonitrile, methacrylonitrile and the like and a dialkylvinyl aromatic phosphonate and to miscible blends thereof with certain polymers such as poly(styrene acrylonitrile) polymers (SAN) and polymers and copolymers of methylmethacrylate.
FIELD OF THE INVENTION Terpolymers of styrene (S) , acrylonitrile (AN) and dimethylstyrene phosphonate (DMSP) and blends thereof with other polymers such as SAN and polymethylmethacrylate (PMMA) .
DESCRIPTION OF RELATED ART Polymers containing phosphonic acid groups are known in the art. Examples include styrene/1-phenylvinylphosphonic acid copolymers (Plast. Massy, No. 8 (1966)24) , crosslinked vinyl phosphonate copolymers (U.S. Pat. No. 3,726,839) , and styrenic polymers that contain pendent phosphonate ester groups [J. Polym. Sci. Polym. Chem. Ed. A 28 (1990) 227;27 (1989) 3985] .
U.S.P. 5,237,028, 5,274,050 and 5,340,883 to S. H. Guo and R. A. Grey teach copolymers of a styrene monomer and 1-phenylvinyl phosphinic acid. These copolymers are reacted with a diamine or polyamine to form absorbents for organic liquids. Phosphorus compounds have been used to impart flame retardance to a number of polymer systems (see Huggard, M.T. 1993, New Intumescent Phosphorus-Based Fire Retardants, Plastics Engineering, 49, 28) . In mixtures of polymers such as ABS with main-chain aromatic polymer such as polycarbonate, phosphorous based compounds can impart flame retardance (see itgosky, V. Flame Retardants, Plast. Eng. 49,10,21) .
The incorporation of organophosphorus compounds, while minimizing some of the environmental concerns of halogens, can still result in performance changes due to plasticization and migration. Incorporation of bound phosphorous functional groups into the polymer structure opens up the possibility of new performance regimes.
SUMMARY OF THE INVENTION Disclosed herein are novel styrenic compositions which contain phosphorous and which are miscible with polymers such as styrene acrylonitrile polymers (SAN) and polymers and copolymers of methylmethacrylate. The novel styrenic compositions comprise at least one vinyl aromatic monomer, at least one unsaturated nitrile monomer and a dialkylvinylaromatic phosphonate. The preferred vinylaromatic monomers are styrene, alphamethyl styrene, vinyl toluene, halostyrenes, e.g. bromo- or chloro-styrene, paramethyl styrene and the like. Most preferred are styrene and alphamethylstyrene. The preferred unsaturated nitrile monomers are acrylonitrile and methacrylonitrile with acrylonitrile being more preferred. The foregoing monomers may also be used to prepare variations of the SAN used in the miscible blends with the phosphorous containing polymer. The preferred alkyls used in the dialkyl phosphonates are Cx to C10 alkyls with methyl, ethyl and propyl being preferred. The resulting miscible compositions of the S/AN/DMSP and the SAN components may further contain rubbery polymers such as methylacrylate-butadiene-styrene polymers (MBS) , acrylonitrile-butadiene-styrene polymers (ABS) , acrylonitrile-styrene-acrylate rubber polymers (ASA) , acrylonitrile-styrene-ethylene propylene diene monomer polymers (EPDM-g-SAN) and the like. The phosphorous component contributes to flame retardance while the rubber components impart toughness.
BRIEF DESCRIPTION OF THE DRAWING The sole drawing is a diagram showing the glass transition temperature (Tg) of 50/50 blends of SAN with a S/AN/DMSP polymer as a function of the weight percent of AN in the SAN.
DESCRIPTION OF THE PREFERRED EMBODIMENTS The S/AN/DMSP polymers of the present invention contain from 40 to 84 weight percent of styrene (S) , from 15 to 35 weight percent of acrylonitrile (AN) and from 1 to 25 weight percent of dimethylstyrene phosphonate. Preferably the amount of styrene is in the range of from 50 to 70 weight percent, the amount of acrylonitrile is in the range of from 20 to 30 weight percents and the DMSP is in the range of from 10 to 20 weight percent. All weight percents being based on the total weight of the S/AN/DMSP polymer.
The S/AN/DMSP polymer is prepared by conventional polymerization methods such as emulsion, suspension, solution, bulk or mass techniques. One method of such a preparation is shown in Example 1 below. Examples 1 to 11 PREPARATION OF S/AN/DMSP POLYMERS The DMSP was copolymerized with styrene (S) and/or acrylonitrile (AN) . The S and AN used were commercial grade monomers which were purified to remove inhibitor using catechol and quinone removal aluminas, respectively, which aluminas were obtained from Scientific Polymer Products, Ontario, New York. The polymerization initiator used was azobisisobutyronitrile (AIBN) , reagent grade from Aldrich Chemical.
Monomer and initiator mixtures were sealed under nitrogen in 5 mm glass tubes after freezing the mixtures with dry ice. The initiator concentration was 0.066 wt% except where noted. All polymerizations were carried out without solvent. The contents of the tubes were polymerized at 70°C for the required time. The subsequent solution of polymer in monomers (about 5 gm) were poured into a tared 50 ml glass centrifuge tube and weighed. The polymer was precipitated with 30 ml of methanol and spun at 5000 rpm. After decanting and drying, in vacuo, at 80°C overnight, the dry polymer was weighed and used for subsequent analysis. For composition and molecular weight determination, samples of near 1% conversion were chosen.
The composition of the polymer was determined by automated Carlo-Erba C-H-N analysis. Phosphorus content was determined by Galbraith Labs (Knoxville, TN) . Molecular weight was estimated by automated size exclusion chromatography in tetrahydrofuran using four columns containing a mixed pore-size bed of 5 μm beads (Polymer Laboratories, Amherst, MA.) The flow rate was 1 ml min'1 at 35°C with a refractive index detector. Molecular weights were estimated using the universal calibration method and are reported in polystyrene equivalents.
The compositions of the polymers prepared in Examples 1 to 11 are summarized in Table I below.
TABLE I
Teφolvmerization of DMSP with Styrene and Acrylonitrile
Effect of Mo nomer Composition on the Rate of Polymerization. Molecular weieht. and T„
Example DMSP(l) AN(1) DMSP(2) AN(2) AIBN (3) Mn — T g
1 0 25.0 0 18.2 0.066 190.6 108.2
2 0 0 0 0 0.066 147.3 95.5
3 2 0 <5 0 0.066 73.8 108.9
4 5 0 13.1 0 0.066 35.3 108.0
5 10 0 32.3 0 0.066 25.8 110.8
6 20 0 33.4 0 0.066 24.2 114.4
7 30 0 45.1 0 0.066 22.4 109.3 Cf,
8 2 24.5 4.9 20.3 0.066 101.6 111.4
9 5 23.8 6.2 18.1 0.066 73.6 110.6
10 10 22.5 14.2 19.9 0.0066 56.2 116.1
11 17 20.8 19.7 18.8 0.0066 41.5 117.5
KEY TO EXAMPLES
(1) - weight % of DMSP and AN in monomer charge
(2) - weight % of DMSP and AN in polymer; wt% of styrene in polymer is by difference (
(3) - weight % AIBN in monomer charge Mn - is number average molecular weight in grams/mole Example 1 - (control) a copolymer of styrene (81.8% by wt) and acrylonitrile (18.2% by wt) Example 2 - (control) a polystyrene homopolymer Examples 3 to 7 - (controls) styrene/DMSP copolymers Examples 8 to 11 - terpolymers of S/AN/DMSP
Examples 8 to 11 show the S/AN/DMSP terpolymers of the present invention. In these examples the amount of DMSP in the terpolymer varies from 4.9 to 19.7% by weight based on the total weight of the terpolymer. The amount of AN in the terpolymer varies from 18.1 to 20.3. The amount of styrene is by difference. The Tg of the terpolymers in Examples 8 to 11 generally increases with increasing amounts of DMSP.
EXAMPLES 12 TO 18 These examples illustrate blends of the S/AN/DMSP terpolymer with SAN and with PMMA. The SAN and PMMA polymers used for blending with the S/AN/DMSP copolymers were made by well known polymerization methods.
Polymer blends were prepared by casting a 1:1 (weight/weight) mixture of the S/AN/DMSP and SAN or PMMA polymer as a 5 wt% solution in 2- butanone into warmed (about 75°C) Petri dishes. After evaporation of the solvent, the film was removed from the glass and dried, in vacuo, at 120°C overnight. The resulting film was scanned at 20°C/min. in a Perkin-Elmer DSC-2 scanning calorimeter under nitrogen from 30 to 200°C. To minimize the effect of thermal stresses on the Tg measurement, the reported data is the result of the scan obtained after quenching from 200°C.
The S/AN/DMSP terpolymer of Example 10 containing 19.9 wt% of acrylonitrile and 14.2 wt% of DMSP was solution blended with a series of SAN copolymers of varying AN contents and similar molecular weights (Mw/Mn about 100,000/50,000) , solvent cast, dried, annealed and tested. Similarly, the S/AN/DMSP terpolymer of Example 12 was blended with V-811, a polymethylmethacrylate (PMMA) obtained from Rohm and Haas Company (Philadelphia, PA) , solvent cast, dried, annealed and tested.
The properties of the blends are summarized in Table II below. In all cases studied, the 5 wt% casting solution in 2-butanone was clear and showed no signs of phase separation. The dried films were observed visually and the phase behavior determined by DSC. The films which exhibited turbidity or cloudiness had two glass transition temperatures (Tgs) , while the clear films exhibited a single Tg.
TABLE II
Examples 9 to 16
Blends of SAN and S/AN/DMSP
Example % An* Film Tcr°C Miscible
9** 0 cloudy 105/116 No
10 5 cloudy 107/117 No
11 10 cloudy 107/117 No
12 18 clear 107/113 No
13 25 clear 108 Yes
14 28 clear 107 Yes
15 32 clear 107 Yes
16*** 0 clear 108 Yes
* Weight % of AN in the SAN ** Polystyrene was used as a control *** PMMA used instead of SAN in Example 16
The data in Table II is presented graphically in the drawing. Referring to the drawing, when the amount of AN in the SAN copolymer is in the range of from 0 to 18 weight percent, based on the total weight of the SAN, the blends of SAN and S/AN/DMSP are not miscible as is evidenced by the cloudy film appearance and the two (2) Tg values. However, in the examples shown, at about 20 weight percent of AN, a clear film and a single Tg is obtained indicating that the blends are miscible.
These miscible blends may be used as is or added to conventional ABS, MBS, ASA, ASEPDM polymers.

Claims

Claims
1. A polymer composition comprising from 1 to 99 weight percent of a first polymer which comprises: a) from about 40 to 84 weight percent of a vinyl aromatic monomer; b) from about 15 to 35 weight percent of an unsaturated nitrile monomer; and c) from about 1 to 25 weight percent of a dialkylvinyl aromatic phosphonate; and from 99 to 1 weight percent of a second polymer selected from the group consisting of (i) polymers of a vinyl aromatic monomer and an unsaturated nitrile monomer; (ii) polymers and copolymers of methylmethacrylate; and (iii) mixtures thereof.
Wherein the polymer composition is characterized by having a single glass transition temperature (Tg) .
2. A polymer composition as in Claim 1 wherein the second polymer is a styrene acrylonitrile polymer and the phosphonate polymer is based on DMSP.
3. A polymer composition as in Claim 1 wherein the second polymer is polymethylmeth- acrylate and the phosphonate polymer is based on DMSP.
4. A polymer composition as in Claim 1 wherein the second polymer is a copolymer of methylmethacrylate.
5. A polymer composition as in Claim 1 which further contains a rubber modified polymer.
6. A polymer composition as in Claim 5 wherein the rubber modified polymer is selected from the group consisting of methylacrylate- butadiene-styrene polymers (MBS) , acrylonitrile- butadiene-styrene polymers (ABS) , acrylonitrile- styrene-acrylate rubber polymers (ASA) , acrylonitrile-styrene-ethylene propylene diene monomer polymers (EPDM-g-SAN) and mixtures thereof
7. A polymer of a vinyl aromatic monomer, an unsaturated nitrile monomer and dimethylstyrene phosphonate.
8. A polymer as in Claim 7 which comprises: a) from about 40 to 84 weight percent of a vinyl aromatic monomer; b) from about 15 to 35 weight percent of an unsaturated nitrile monomer; and c) from about 1 to 25 weight percent of a dimethylstyrene phosphonate.
9. A polymer as in Claim 8 wherein the aromatic monomer is a styrene monomer.
10. A polymer as in Claim 8 wherein the unsaturated nitrile monomer is acrylonitrile or methacrylonitrile.
PCT/US1995/014743 1995-11-03 1995-11-03 Miscible polymers WO1997016487A1 (en)