WO1997008242A1 - Polymer blends - Google Patents
Polymer blends Download PDFInfo
- Publication number
- WO1997008242A1 WO1997008242A1 PCT/US1996/013682 US9613682W WO9708242A1 WO 1997008242 A1 WO1997008242 A1 WO 1997008242A1 US 9613682 W US9613682 W US 9613682W WO 9708242 A1 WO9708242 A1 WO 9708242A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polymer
- polyamide
- composition
- ofthe
- halide
- Prior art date
Abstract
Description
Claims