WO1996038504A1 - Polyesters of 2,6-naphthalenedicarboxylic acid having improved hydrolytic stability - Google Patents
Polyesters of 2,6-naphthalenedicarboxylic acid having improved hydrolytic stability Download PDFInfo
- Publication number
- WO1996038504A1 WO1996038504A1 PCT/US1996/008001 US9608001W WO9638504A1 WO 1996038504 A1 WO1996038504 A1 WO 1996038504A1 US 9608001 W US9608001 W US 9608001W WO 9638504 A1 WO9638504 A1 WO 9638504A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- mole
- polyester composition
- polyester
- glycol
- poly
- Prior art date
Abstract
Description
Claims