WO1996024632A1 - Thermoplastic elastomer - Google Patents
Thermoplastic elastomer Download PDFInfo
- Publication number
- WO1996024632A1 WO1996024632A1 PCT/NL1996/000040 NL9600040W WO9624632A1 WO 1996024632 A1 WO1996024632 A1 WO 1996024632A1 NL 9600040 W NL9600040 W NL 9600040W WO 9624632 A1 WO9624632 A1 WO 9624632A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- thermoplastic elastomer
- compound
- hals
- rubber
- thermoplastic
- Prior art date
Abstract
Description
Claims