WO1996003469A1 - Automotive protectant for use with cleaning compositions - Google Patents
Automotive protectant for use with cleaning compositions Download PDFInfo
- Publication number
- WO1996003469A1 WO1996003469A1 PCT/US1995/008662 US9508662W WO9603469A1 WO 1996003469 A1 WO1996003469 A1 WO 1996003469A1 US 9508662 W US9508662 W US 9508662W WO 9603469 A1 WO9603469 A1 WO 9603469A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- silicone
- protective composition
- detergent
- composition
- dispersant
- Prior art date
Abstract
Description
Claims