WO1995026758A1 - Flexible, porous, absorbent, polymeric macrostructures and methods of making the same - Google Patents
Flexible, porous, absorbent, polymeric macrostructures and methods of making the same Download PDFInfo
- Publication number
- WO1995026758A1 WO1995026758A1 PCT/US1994/011136 US9411136W WO9526758A1 WO 1995026758 A1 WO1995026758 A1 WO 1995026758A1 US 9411136 W US9411136 W US 9411136W WO 9526758 A1 WO9526758 A1 WO 9526758A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- precursor particles
- plasticizer
- interparticle
- weight
- aggregate
- Prior art date
Abstract
Description
Claims