WO1994026847A1 - Process for hydrocracking hydrocarbons - Google Patents
Process for hydrocracking hydrocarbons Download PDFInfo
- Publication number
- WO1994026847A1 WO1994026847A1 PCT/EP1994/001563 EP9401563W WO9426847A1 WO 1994026847 A1 WO1994026847 A1 WO 1994026847A1 EP 9401563 W EP9401563 W EP 9401563W WO 9426847 A1 WO9426847 A1 WO 9426847A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- catalyst
- alumina
- range
- silica
- hydrocracking
- Prior art date
Abstract
Description
Claims