WO1993023793A1

WO1993023793A1 - Addenda for an aqueous photographic stabilizing solution

Info

Publication number: WO1993023793A1
Application number: PCT/US1993/004106
Authority: WO
Inventors: Hugh Gerald Mcguckin; John Stuart Badger; Michael William Orem
Original assignee: Eastman Kodak Company
Priority date: 1992-05-12
Filing date: 1993-05-03
Publication date: 1993-11-25
Also published as: JPH06509667A; DE69315534T2; DE69315534D1; EP0593734B1; US5529890A; EP0593734A1; US5578432A

Abstract

A stabilizing bath that provides image stability and uniform drainage of excess fluid to prevent drying spots and that reduces or eliminates the formation of residue on the base side of color negative films is comprised of hexamethylenetetramine, a nonionic polyethoxylated surfactant, and an anionic sulfate of sulfonate surfactant. The stabilizing bath is used as the final processing bath prior to drying. The nonionic surfactant provides uniform drainage of excess fluid and the anionic sulfate or sulfonate surfactant functions to reduce or eliminate the formation of residue on the base side of color negative films.

Description

ADDENDA FOR AN AQUEOUS PHOTOGRAPHIC STABILIZING SOLUTION

This application is a continuation-in-part application of a co- pending application, U.S.S.N. 07/881,916 filed May 12, 1992, and entitled "Addenda for an Aqueous Photographic Stabilizing Solution" by McGuckin et at., herein incorporated by reference.

Field of the Invention This invention relates to the field of silver halide photographic processing, and in particular to compositions of a stabilizing solution which improve the image stability and appearance of processed color negative films.

Background of the Invention The processing of silver halide color film generally involves the steps of color evolution, bleaching, fixing, stabilizing and drying. The stabilizing bath is used as the final step in the processing of color films in order to reduce stain and/or to enhance dye stability. The stability of the dye image is believed to be affected by the presence of unreacted coupler in the emulsion layers, because the coupler and the dye can react slowly with one another to degrade a color image. Dye stability is also believed to be influenced by temperature, humidity, air quality, and exposure to fight. In particular the image from magenta dye tends to fade much more rapidly than either the cyan or the yellow dye image. The addition of a compound that releases a methylene group to a stabilizing formulation can prevent the redox degradation of the magenta coupler that would otherwise cause magenta dye fade. Stabilizing solutions are aqueous formulations that contain a compound that produces a methylene group as the key component for dye stabilization. Typical stabilizing solutions often contain an aldehyde, in particular formaldehyde, as the methylene-releasing agent. Formaldehyde possesses the added benefit of high volatility, so that any residual formaldehyde on the base side of the film is readily removed in a drying step- However in recent years concerns over the hazardous effects of formaldehyde have stimulated the development of stabilizing solutions that do not contain hazardous components, and alternative stabilizing compositions have been formulated.

Hexamethylenetetramine (HMTA) is an acceptable substitute for some or all of the formaldehyde in the stabilizing bath. HMTA is a water-soluble, nonvolatile crystalline compound with superior methylene- releasing properties. HMTA does not release significant levels of formaldehyde into solution or as vapor at the pH of the stabilizer solution (~pH 7 to 9). However, color negative films processed in machines that provide minimal or no squeegeeing of the film after stabilization in a HMTA-containing stabilizing bath will exhibit an objectionable residue on the base side of the film upon drying. This residue contains significant amounts of HMTA.

A laid open Japanese patent application from Konica Corporation (63/244,036) has described the use of a stabilizing solution consisting of a sulfite-ion releasing compound, and at least one of the following surfactants: anionic surfactant of the alkyl polyalklyeneoxides or alkyl arylpolyalkyleneoxides containing sulfate or phosphate groups, nonionic hydrocarbon polyalklyeneoxide surfactants, or a water-soluble organic siloxane type compound. The application suggests that such a formulation can be useful in preventing the adherence of crystals which form on the surface of the stabilizing bath. A second laid open Japanese application from Konica (40/25,835) has disclosed the use of an HMTA-containing stabilizing solution containing at least one of the following surfactants: anionic polyalkyleneoxide sulfates or phosphates, nonionic polyalkyleneoxide alcohols or water soluble organic siloxane compounds. It is the object of the present invention to provide a stabilizer solution containing HMTA that significantly reduces or completely eliminates observable residue on the base side of the color negative film, and which can be dried without forming drying marks or spots.

Summary of the Invention In one aspect of this invention an aqueous photographic stabilizing solution containing the dye stabilizing agent hexamethylenetetramine for use in the color processing of photographic elements is provided with chemical addenda for the purpose of avoiding the formation of drying marks or spots, and reducing or eliminating formation of a residue on the base side surface of color negative film, wherein said chemical addenda are a nonionic polyethoxylated surfactant and an anionic sulfate or suifonate surfactant.

In preferred embodiments the nonionic polyethoxylated surfactants have the general formula R,-(B)_x-(E)_m-D, wherein R_λ is an alkyl group with 8-20 carbons, B is a phenyl group and x is 0 or 1, E is -(OCH₂CH₂)- and m is 6-20, and D is -OH or -OCH₃. Most preferably the nonionic surfactant is tridecylpolyethyleneoxide(12)alcohol (trade name "Renex 30", available from ICI). Another most preferred nonionic surfactant is octylphenoxypolyethyleneoxide(ll-12)ethanol (trade name "Triton X-102"). In preferred embodiments the nonionic polyethoxylated surfactant is present at a working concentration of approximately 0.1 to 0.5 g/L. In some embodiments the nonionic polyethoxylated surfactant is present at a working concentration of 0.2 g/L.

In one preferred embodiment the anionic sulfate or suifonate surfactants have the general formula

wherein Rg is an alkyl group with 8-20 carbons and more preferably 10-16 carbons, A is an aryl or a hydroxy ethylene group, and C is SO₃"M⁺ or S0₄ ^"M⁺ wherein M⁺ is ammonium or an alkali metal such as K⁺, Na⁺, Li⁺. Most preferably the anionic surfactant is sodium dodecylbenzenesulfonate (trade name "Siponate DS-10", available from Rhone-Poulenc) or sodium 2-hydroxy-tetra-, and hexa, -decane-1-sulfonate (trade name "Witconate AOS", available from Witco). In another preferred embodiment the anionic sulfate or suifonate surfactants have the general formula (R₃)_n-(B)_x-(E)_y-C, wherein R₃ is an alkyl group with 4-20 carbons and more preferably 4-16 carbons, n is 1 when x is 0, and n is 1, 2, or 3 when x is 1, B is a phenyl group and x is 0 or 1, E is -(OCH₂CH₂)- and y is an integer from 1 to 8, and C is SO₃ ^"M⁺ or SO₄ ^*M⁺ wherein M⁺ is ammonium or an alkali metal such as K⁺, Na^*", and Li\ Examples of suitable anionic sulfate or suifonate surfactant are sodium tributylphenoxypolyethyleneoxidesulfate (trade name Ηostapal BV, available from Hoechst Celanese), or sodium alkyl(C₁₂-C₁₅)polyethyleneoxide(5)sulfate (trade name "Witcolate SE-5" available from Witco), or sodium alkyl(C₉-C₁₂)polyethyleneoxide(7)- ethanesulfonate (trade name "Avanel S-70", available from PPG). In preferred embodiments the anionic sulfate or suifonate surfactant is present at a working concentration of approximately 0.05 to 1.0 g L. More preferably, the anionic sulfate or suifonate surfactant is present at a working concentration of approximately 0.1 to 0.5 g/L. Most preferably, the anionic sulfate or suifonate surfactant is present at a working concentration of 0.2 g/L.

Description of the Preferred Embodiments The invention provides an aqueous photographic stabilizing solution containing the dye stabilizing agent HMTA that has the desirable properties of providing superior image stability, while avoiding the formation of drying marks or spots, and reducing or eliminating the formation of residue on the film that is associated with HMTA. The invention has identified chemical addenda for use in an aqueous photographic stabilizing solution that are commercially available and environmentally safe. An HMTA-containing stabilizing solution that further includes a nonionic hydrocarbon polyethoxylated surfactant and an anionic sulfate or suifonate surfactant has the advantage that it can be utilized in any processing method and is especially useful in avoiding the formation of drying marks or spots and in reducing or eliminating residue from color negative film , particularly when the film has been processed in a rack and tank machine that does not rinse or squeegee the film prior to drying. A stabilizing solution containing a nonionic hydrocarbon polyethoxylated surfactant has the desired uniform draining behavior so that drying marks are not formed. A stabilizing solution also containing an anionic sulfate or suifonate surfactant has the additional desired property of reducing or eliminating the formation of residue on the base side of the film.

An aqueous stabilizing solution utilized in rack and tank and in other types of processing machines contains a dye stabilizing agent (formaldehyde) and a wetting agent. The use of a stabilizer solution which substitutes HMTA for formaldehyde can result in the formation of a residue on the base side of the processed film. Several general types of chemical addenda were tested for their ability to reduce or eliminate residue formation on color negative film in a HMTA containing formula. These addenda included polymers, dispersεmts, and cationic, anionic and non-ionic surfactants. Over 100 chemicals were tested for their usefulness in reducing residue formation.

The efficacy of potential chemical addenda in reducing or eliminating the formation of residue on color negative film was initially analyzed by adding 0.1-3.0 g/L of each chemical addenda separately to an aliquot of a standard aqueous stabilizing composition and drying a portion of the mixture on a glass microscope slide to simulate the conditions of a standard rack and tank machine that dries film immediately after the stabilizing step. Briefly, the mixture was coated onto the glass slide, allowed to drain, and then the adherent mixture was dried with a warm air blower. The slide was then viewed under a microscope (~50x magnification) and the extent of residue formation was determined.

Test 1 Promising chemical addenda were further tested in a PAKO, model

HTC rack and tank processing machine for efficacy in eUminating the formation of residue on the base side surface of color negative films The processing steps were as follows: 1) color development (~100°F), 2) bleach, 3) wash, 4) fix, 5) wash, 6) stabilize and dry (~110°F to 120°F)- The recommended KODAK color developer, bleach and fix for the C-41 process were utilized. The stabilizing bath (our standard solution) contained 5.0 g/L HMTA, 0.20 g/L tridecylpolyethyleneoxide(12)alcohol (RENEX 30), a biocide, and a hydrolyzed polymaleic anhydride polymer for calcium ion control. Each anionic surfactant to be tested was added to this solution at a concentration of 0.2 g/L, respectively. Three strips of color negative film (Kodacolor Gold 100), 35 mm x 13", were processed for each stabOizer with addenda. As a control, three strips of film were also processed using the above stabilizer solution without the added anionic surfactant.

After processing, each film strip was evaluated for residue by viewing the base side of each strip under a specular light (a Cambridge halogen microscope source) that was held approximately 8 inches from the film. The amount of residue observed was rated on a scale of 1 to 4; wherein a rating of 1 signifies no residue observed; a rating of 2 signifies noticeable residue easily observed under specular fight; a rating of 3 signifies noticeable residue easily observed under normal room fighting; a rating of 4 signifies a very noticeable, heavy deposit of residue observed under normal room lighting. The control film strips were given the rating 2, as they had noticeable residue under specular light. Several anionic surfactants were found to be very effective for reducing or eliminating the residue on the base side of the color negative film. Anionic surfactants that were given the rating 1 for no visible residue included sodium dodecylbenzenesulfonate (available from Rhone-Poulenc, trade name "Siponate DS-10), sodium 2-hydroxy-tetra-, and -hexa, -decane-1-sulfonate (available from Witco, trade name "Witconate AOS"), sodium tributylphenoxypolyethyleneoxidesulfate (trade name "Hostapal BV, available from Hoechst Celanese), sodium al-kyl(C.₂-C_I5)polyethyleneo-ride(5)sulfate (trade name "Witcolate SE-5", available from Witco), sodium alkyl(C₉-C_I2)polyethyleneoxide(7)- ethanesulfonate (trade name "Avanel S-70", available from PPG).

Test 2 Stabilizing solutions containing an anionic surfactant were evaluated for efficacy in reducing film base residue and water spotting, both with and without a nonionic surfactant.

Film processing was carried out using a PAKO (Model HTC) rack and tank processing machine as described above in Test 1. The processing steps were as follows: 1) color development (ca. 100°F); 2) bleach; 3) wash; 4) fix; 5) wash; 6) stabiHze; and dry (ca. 110°F to 120°F). The recommended KODAK C-41 color developer, bleach, fix and processing conditions for Kodacolor films were utilized. Three strips of exposed Kodacolor Gold film 100 film, 35 mm x 13" (33 cm), were processed with each solution. The stabilizing bath was formulated as follows:

Stabilizing bath: hexamethylenetetramine (HMTA) 5.0 g/L hydrolyzed polymaleic anhydride polymer 0.05 g/L

(Irgaform 3000)

l,2-benzisothiazoline-3-one (Proxel GXL) 60 ppm anionic surfactant (if present) 0.2-0.6 g/L nonionic surfactant (if present) 0.0-0.2 g/L

After processing, the samples were evaluated for residue as described in Test 1. The amount of residue on each strip was judged by two observers using the scale (1-4) employed in Test 1. Table 1 lists the results for a variety of anionic and nonionic surfactants used alone and in combination. The rating listed for each solution is an average based on the results from three film strips. Table 1. Comparative results for single and mixed surfactant stabilizing solutions.

i co a e x = ammonium nony p enoxypo ye y eneoxi esu a e

Referring to Table 1, water spotting was observed on those film samples treated in the stabilizing bath which contained only an anionic surfactant, such as Witcolate 1075x, Witcolate SE-5 and Siponate DS-10 (see, nos. 1-3, 7-9, and 11-14). These spots appeared as a crystalline residue on the base side of the film. When these same anionic surfactants were combined in solution with the polyethoxylated nonionic surfactants, such as Renex 30 and Triton X-102, both uniform drying (no water spots) and no observable residue were noted (see, nos. 5, 6, 10 and 11). Nonionic surfactants alone, such as no. 4, were sufficient to eliminate water spotting, but received an inferior rating because of observable residue.

What is claimed is:

Claims

1. An aqueous photographic stabilizing solution containing hexamethylenetetramine for use in the color processing of photographic elements, further comprising: a nonionic polyethoxylated surfactant; and an anionic surfactant selected from the group consisting of sulfate and suifonate anionic surfactants.

2. The stabilizing solution of claim 1 wherein said nonionic polyethoxylated surfactant has the chemical formula R,-(B)_x-(E)_m-D, wherein said Rj is an alkyl group having 8 to 20 carbon atoms, said B is a phenyl group and x is 0 or 1, said E is a -(OCH₂CH₂)- and m is an integer from 6 to 20, and D is selected from the group containing -OH and -OCH₃.

3. The stabilizing solution of claim 2 wherein said nonionic surfactant comprises tridecylpolyethyleneoxide(12)alcohol.

4. The stabilizing solution of claim 2, wherein said nonionic surfactant comprises octylphenoxypolyetheneoxide(ll-12)ethanol.

5. The stabilizing solution of claim 1 wherein said anionic surfactant has the chemical formula R-^AVC, wherein said R₂ is an alkyl group having 8 to 20 carbon atoms, said A is selected from the group including a phenyl group and an hydroxy ethylene group, and said C is selected from the group including S0₃ ^"M⁺ and S0₄ ^*M\ wherein said M⁺ is selected from the group including NH4⁺, and the alkali metals Na⁺, K⁺, and Li^*.

6. The stabilizing solution of claim 5 wherein said R^ contains 10-16 carbon atoms.

7. The stabilizing solution of claim 5 wherein said anionic surfactant is present at a working concentration of approximately 0.05 to 1.0 g/L.

8. The stabilizing solution of claim 5 wherein said anionic surfactant is present at a working concentration of approximately 0.1 to 0.5 g L.

9. The stabilizing solution of claim 5 wherein said anionic surfactant is present at a working concentration of 0.2 g/L.

10. The stabilizing solution of claim 3, 4 or 5 wherein said anionic surfactant comprises sodium dodecylbenzenesulfonate.

11. The stabilizing solution of claim 3, 4 or 5 wherein said anionic surfactant comprises a mixture of sodium 2-hydroxy-tetra-decane- 1-sulfonate and 2-hydroxy-hexa-decane-l-sulfonate.

12. The stabilizing solution of claim 1 wherein said anionic surfactant has the chemical formula (R₃)_n-(B)._c-(E)_}r-C, wherein said Rg is an alkyl group having 4 to 20 carbon atoms and n is 1 when x is 0, and n is 1, 2, or 3 when x is 1, said B is a phenyl group and x is 0 or 1, said E is a -(OCH₂CH₂)- group and y is an integer from 1 to 8, and said C is selected from the group including S0₃ ^"M⁺ and S0₄ ^"M⁺, wherein said M⁺ is selected from the group including NH4⁺, and the alkali metals Na⁺, K⁺, and Li⁺.

13. The stabilizing solution of claim 3, 4 or 12 wherein said anionic surfactant comprises sodium tributylphenoxy- polyethyleneoxidesulfate.

14. The stabilizing solution of claim 3, 4 or 12 wherein said anionic surfactant comprises sodium alkyl(C₁₂-Cι₅)polyethyleneoxide(5)- sulfate.

15. The stabilizing solution of claim 3, 4 or 12 wherein said anionic surfactant comprises sodium alkyl(C₉-Cι₂)polyethyleneoxide(7)- ethanesulfonate.

16. The stabilizing solution of claim 12 wherein said Ra contains 4-16 carbon atoms.

17. The stabilizing solution of claim 12 wherein said anionic surfactant is present at a working concentration of approximately 0.05 to 1.0 g/L-

18. The stabilizing solution of claim 12 wherein said anionic surfactant is present at a working concentration of approximately 0.1 to 0.5 g/L.

19. The stabilizing solution of claim 12 wherein said anionic surfactant is present at a working concentration of 0.2 g/L.