WO1993014928A1 - Laminated films - Google Patents
Laminated films Download PDFInfo
- Publication number
- WO1993014928A1 WO1993014928A1 PCT/GB1993/000177 GB9300177W WO9314928A1 WO 1993014928 A1 WO1993014928 A1 WO 1993014928A1 GB 9300177 W GB9300177 W GB 9300177W WO 9314928 A1 WO9314928 A1 WO 9314928A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- cross
- rollers
- laminate
- stretching
- grooved rollers
- Prior art date
Abstract
Description
Claims