WO1987002396A1 - Papermaking process - Google Patents
Papermaking process Download PDFInfo
- Publication number
- WO1987002396A1 WO1987002396A1 PCT/US1986/002178 US8602178W WO8702396A1 WO 1987002396 A1 WO1987002396 A1 WO 1987002396A1 US 8602178 W US8602178 W US 8602178W WO 8702396 A1 WO8702396 A1 WO 8702396A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- slurry
- papermaking
- toc
- cationic
- charge
- Prior art date
Abstract
A method for controlling the addition (33) of cationic additive materials (28) to a paper mill slurry (22) used to neutralize the anionic contaminants in a papermaking process which utilizes total organic carbon measurements (32, 34) of samples of the slurry as an indicator of the cationic demand of the paper mill slurry. The method of the present invention discloses the discovery that measurements of the total organic carbon (32, 34) taken form filtered samples of the papermaking slurry correlate very well to cationic demand measurements of the papermaking slurry (22). Therefore, measurements of the total dissolved organic carbon content may be used to determine the desired addition rate of cationic additives (28) in a very convenient and reliable manner.
Description
TITLE: PAPERMAKING PROCESS
Technical Field
The present invention relates generally to the field of papermaking processes and particularly to improving the capability of monitoring the cationic demand of the system to better control the rate of addition of chemical additives to provide enhanced production and quality and reduce costs.
Background Art
The state of flocculation of a papermaking slurry is very important to the runability of that slurry on a paper machine. The state of flocculation is affected by both mechanical factors and chemical factors. The mechanical factors are usually optimized as best they can be and then chemical additives are utilized to control the state of flocculation. The state of flocculation influences the machine drainage, response to vacuum, retention, pressing
and drying conditions. These factors in turn influence the strength and optical properties of the sheet. Two major non-mechanical factors affecting additive performance are the state of the electrokinetic charge in the system and the quantity of fine solids present. The materials which affect these factors have often been referred to as "anionic trash". Zeta potential has been used to monitor the state of charge present in the system. This measurement, although conceptually correct, is difficult to obtain on an on-line basis in a paper mill. Sensors have been developed for on-line usage but have not been widely applied. The Zeta potential measurement only gives magnitude of charge and not the total quantity of charge in the system. To speak to this need the colloid titration technique has been developed and instrumented. The technique is proposed as a means to control additive addition rates in the papermaking system. A current study has shown this technique to have limited value. A better technique is to monitor the cationic demand of the papermaking slurry. This approach is used in an off-line mode of operation by many chemical supplier companies. This approach conceptually is correct but suffers the same problems of measurement difficulties as the Zeta potential since it uses Zeta potential to determine its end point and is relatively 'cumbersome and time-consuming to employ in an effective on-line mode.
Stricter governmental requirements for controlling the
contaminants from papermaking effluents in addition to attractive cost saving potential has led the paper industry toward increasing degrees of closure of the papermaking process and white water re-use via recycling. However, such a practice leads to an increase in the build-up of organic and inorganic contaminants and fines in the recycle white water.
The anionic organic moieties in the papermaking slurry complete with the filler and fiber constituents of the papermaking stock for adsorption of the costly cationic chemicals used to influence the retention, drainage and other important factors in the papermaking process.
Under present practice, the use of costly chemical additives has proceeded on a trial and error basis to attempt to improve retention and drainage in papermaking processes. This practice has proven only minimally satisfactory because a reliable monitoring and control strategy has not been devised which offers a convenient and reliable indication of the parameters which influence cationic demand of the papermaking slurry and hence the control of the addition rate of cationic materials used to neutralize anionic contaminants for more effective use of cationic and anionic additives.
Since system upsets can easily occur in paper mill operations, lack of a relatively convenient and sufficiently
reliable control parameter often leads to errors in the necessary chemical addition rate and failure to achieve the desired quality of product or a significant increase in costs or both. This is true irrespective of the degree of recycling of the white water, although it becomes more significant as the system is closed and the degree of recycling increases above 80% or so.
The current procedure of utilizing Zeta potential measurements, colloidal titration techniques or direct off-line cationic demand monitoring has not provided a satisfactory solution to the problem of achieving satisfactory control techniques necessary to maximize the desirable economic and environmental results in papermaking processes.
Brief Disclosure Of Invention
The present invention relates generally to paper board and papermaking processes and particularly to an improved process which utilizes total organic carbon measurements of the papermaking slurry to control the addition rates of cationic chemicals necessary to obtain the desired level of charge neutralization of the slurry prior to introduction into the head box of papermaking machines.
Total organic carbon, hereinafter referred to as TOC,
as used herein is defined as measurements or the analysis of the dissolved, oxidizeable carbonaceous compounds found in the filtrate of a filtered sample of a papermaking slurry and any of the same type of materials in colloidal form which may pass through the filter and are present in the filtrate.
At present, cationic demand measurements appear to be the most reliable indicator of the total quantity of electrokinetic charge of the papermaking slurry as compared to other prior measurements such as Zeta potential and the like and therefore a very important parameter to use to control polymer addition rates.
The invention revolves around the surprising discovery that TOC measurements based upon filtered samples of the papermaking slurry correlate very well with cationic demand measurements of the slurry and therefore may be used as a control parameter for the rate of addition of conventional cationic polymers used to neutralize the anionic contaminants in the slurry.
In view of this unexpected and surprising discovery, TOC measurements may be advantageously employed in a more reliable and more convenient manner to monitor and control the very important addition rates of cationic materials in a papermaking process to achieve greater efficiency and aid in maintaining the desired level of quality of the resulting
paper product as compared to prior methods and means.
Additionally, the nature of measuring the TOC content of a given papermaking slurry lends itself more conveniently to the development of on-line instrumentation within a paper mill as compared to cationic demand measurements which are a reliable indicator but more cumbersome and difficult to employ in a highly useful manner.
Implementation of the discovery of the present invention provides a base to develop an essentially fully automatic control system wherein other desired measurements of system variables can be exploited to bring the evolving increase of recycled white water in the papermaking industry to its fullest and most efficient development.
In accordance with the present invention, TOC measurements would be selectively monitored in the incoming papermaking slurry coming from the thick stock system at a point prior to the stock preparation and blending system. A baseline value of the incoming slurry would first be established to check the correlation with cationic demand measurements of the same slurry such that the correlation could be used throughout continuation of the processing.
Then the addition of conventionally used cationic polymer materials would be controlled in response to the measurements of TOC. In addition to measurements of TOC, it would be preferred to also monitor the specific conductance
of the incoming slurry as an indication of th.e inorganic content of the slurry. Recent studies at Miami University (Ohio) have shown that a rise in the inorganic content of the slurry tend to lower the cationic demand and are reflected by a decrease in TOC.
Further, in any such process, a conventional retention meter, fine solids sensor and ash sensor could be advantageously employed to monitor these variables in the system to provide fuller control of the chemical additives necessary to obtain desired retention and drainage levels.
It is therefore a primary object to provide an improved papermaking process which incorporates monitoring the charge of a papermaking slurry by a novel and more convenient control parameter to adjust the addition of cationic materials to the paper stock and to improve control of such important factors of machine drainage, response to vacuum and retention, for example.
It is another object of the present invention to provide a method for indirectly, but reliably, determining the rate of polymer addition to a papermaking slurry by employing TOC measurements which are more reliable indicators of the total quantity of the charge in the slurry than measurements of either Zeta potential or those obtained by colloidal titration methods.
It is a further object of the present invention to
provide, an improved papermaking process wherein TOC analysis of a slurry sample is used to control polymer addition to the slurry in a manner which reduces loss of costly raw materials, increases the economic benefits of water recycle/reuse, and provides the potential for increased production rates to be achieved while lowering energy consumption.
Further objects and advantages of the present invention will be apparent from the following description, reference being had to the accompanying drawings wherein a preferred form of embodiment of the invention is clearly shown.
Brief Description Of Drawings
Fig. 1 is a diagrammatic view of a simplified papermaking process employing the teachings of the present invention.
Fig. 2 is a diagrammatic view of a typical papermaking process including proposed monitoring and control features in addition to the TOC measurements used in accordance with the present invention.
Fig. 3 is a graphical representation of the data collected to establish a typical baseline value for the correlation of cationic demand versus TOC illustrating a
reliable linear relationship between these parameters of a papermaking slurry.
Fig. 4 is a graphical representation of experimental data gathered during the development of the present invention wherein cationic demand is plotted against total organic carbon measurements of the various slurries investigated.
In describing the preferred embodiment of the invention which is illustrated in the drawings, specific terminology will be resorted to for the sake of clarity. However, it is not intended that the invention be limited to the specific terms so selected and it is to be understood that each specific term includes all technical equivalents which operate in a similar manner to accomplish a similar purpose.
Detailed Description Of A Preferred Embodiment
Fig. 1 is a diagrammatic view representing a relatively simplified papermaking process which incorporates the novel concept of TOC monitoring for control of the addition of cationic chemical employed in a typical papermaking process.
In such systems, although equipment and techniques may
vary, typically the pulp materials which are to be used in making of the paper mill slurry are first processed in what is referred to as a "thick stock area" prior to further dilution with water to "thin" the stock. This water may be 5 "fresh" (previously unused), or may include a given proportion, up to 100 percent, of recycled "white water". "White water" refers to the effluent liquid which leaves the papermaking machine at the so-called "wet end" of the process. Such a process is well-known in the art and 10 therefore a detailed description is not necessary for purposes of understanding the present invention.
Environmental regulations require that this white water be treated to reduce or eliminate undesirable contamination
15 prior to release into the environment. Such regulations have also encouraged the trend to develop increased use of recycled white water in the process along with certain economic incentives, including recovery and re-use of raw materials used in the process and reduction of costly
20. waste-water treatment.
The desired level of control of such processes has been relatively difficult in view of the variables inherent therein which are introduced by both mechanical and chemical factors. The mechanical factors may be improved to an optimum by appropriate design within the limits of the high initial cost of equipment, however, this would not be sufficient to account for the changing chemical environment
during the process to maintain the desired level of efficient operation. This is particularly true with regard to control of the important factos of first pass retention and machine drainage. Other important parameters include response to vacuum and pressing dryness as well as strength and optical qualities of the final product in certain applications. However, the first pass retention level and machine drainage are two of the common parameters which determine the effectiveness and efficiency of any medium to high speed papermaking process.
For some time the industry has known that electrokinetic charge is a very important parameter to consider in the chemistry of papermaking. Prior attempts to utilize Zeta potential measurements have not proven to be sufficient to offer a satisfactory solution to the wet-end chemistry phenomena which occur.
While cationic demand measurements, which are determined by titration of the papermaking slurry to zero mobility by addition of a cationic polymer, represent reliable and useful indications of the total quantity of the charge in the system, it is so cumbersome and time-consuming as to be inconvenient for use under the dynamic conditions of commercial papermaking.
In accordance with the present invention, it has been discovered that TOC measurements can serve as a very
reliable measure of the cationic demand of a papermaking process and therefore can serve as a reliable monitor for controlling the addition level of the cationic polymers used to neutralize the slurry prior to delivery to the papermaking machine.
As shown in Fig. 1, pulp formed into thick stock at 20 is delivered to a stock preparation and blending area 22. Water, fresh or recycled, not shown, would be used to thin the stock prior to addition of typical filler and sizing materials, such as clay at 24 and titanium oxide at 26. Depending upon the nature of the raw materials initially used and the specifications of the final paper product, other materials may be conventionally used without departing from the spirit of the present invention.
In the stock preparation area of the process, a charge neutralization chemical is conventionally added to reduce the" toal anionic charge in the papermaking slurry to a given level as indicated at 27.
It is well known that cationic additives are useful and necessary to provide improved - retention and machine drainage. The anionic contaminants in a papermaking slurry include the dissolved carbonaceous compounds derived from the wood components used and tend to block the bonding sites on the fibers and fillers to the detriment of the flocculation desired in the process. These anionic
contaminants are referred to in the industry as "anionic trash".
Generally, the charge-neutralizing polymers preferred in the papermaking industry are those having a relatively low molecular weight, a high charge density and are cationically charged. Their main function is to control the dissolved and fine solid anionic components in the papermaking slurry to effectively neutralize the system to a desired level. Examples of such polymers include quaternay polyamines, polyethylenimines, and aluminum sulfate or alum.
Some papermaking systems employ dual polymer additive strategy. After addition of the cationic charge-neutralizer to the slurry, a retention aid is added, such as indicated at 28 in Fig. 1. The most prevalent commercial anionic polymers which aid retention can be classified into two main categories. The first includes those which are co-polymerized with a given quantity of acrylic acid. The second includes those whose anionic character is derived from the hydrolysis of a specific number of amide groups in a polyacrylamide backbone. These anionic polymers are characterized by having a relatively very high molecular weight and a low charge density.
After addition of the anionic polymer retention aid, the treated papermaking slurry enters the conventional
papermaking machine 36 wherein it is formed on a moving screen into the desired paper product. Typically, the percent of solids in this slurry is low and the fibers, fillers and fines are matted on the screen to form a continuous sheet. Solid concentrations typically may be approximately 1% or so with the remainder being liquid. Much of the water in the slurry is drawn through the screen. This effluent, referred to as white water, is either treated for release into the environment as waste water or recycled depending upon the design of the system. The retained solids matted on the screen to form the paper product are then pressed and dried prior to being wound upon rollers or the like.
A conventional retention measuring means 30 may be used to monitor the percentage of solids in the slurry entering the head box or inlet end of the papermaking machine versus the solids in the outlet water to control the rate of anionic polymer additions such as indicated at 28 in response to maintaining a desired level of retention of solids.
The prior description generally applies to most papermaking pocesses, except these prior processes have employed a more or less trial and error method to determine the given level of the anionic polymer required to provide the desired neutralization of the anionic charge in the slurry. Frequently, this has led to many problems due to
system upsets from several sources in the dynamic changing chemical requirements in the process.
In accordance with the present invention, TOC measurements, indicated at 32, are selectively taken of the incoming slurry from the thick stock area to the stock preparation and blending system. These measurements may be used to control the release of the charge neutralization chemical to the blending system. In accordance with the TOC measurement, any change in the TOC measurement would dictate a corresponding change in the addition rate of the cationic polymer used to obtain the desired level of neutralization which is illustrated by line 33.
Preferably, a second TOC measurement 34 would be taken at the outlet of the stock preparation and blending system to be assured the proper state of neutralization was accomplished and to adjust that level with further additive if required. After this adjustment any anionic retention aid agent may be added prior to introduction to the paper machine.
For each particular papermaking system, a baseline value of TOC versus cationic demand may need to be established for the particular papermaking slurry. This may be accomplished by plotting corresponding measurements to TOC versus cationic demand, such as illustrated in Fig. 3, from samples of the thick stock. In this example, cationic
demand in pounds per ton is plotted against TOC in parts per million of carbon as determined from a representative papermaking slurry.
The slope of the linear relationship may prove to be relatively constant for many typical commercial slurries, however, further testing and evaluation would be needed on a wider range of basis of samples to confirm such a conclusion. However, in this instance, the baseline value for zero cationic demand corresponds to a TOC measurement of 0.85ppm.
These tests were conducted using several different papermaking variables. Initial investigation revealed that the TOC measurements varied with changes in pH, dissolved inorganics, and with different levels of beating of the pulp fibers. In all these instances, a direct linear correlation was established for cationic demand measurements versus TOC measurements. In the slurries examined an addition rate of one pound of cationic polymer (polyamine) per ton of slurry for each 5mg increase in organic carbon was established as shown in Fig. 4.
While TOC analysis is a well known technique, its previous use has been limited to merely determine the level of dissolved organic carbon in a solution. It has also been recognized that increased levels of dissolved organics, which are anionic in character, would cause an increase in
cationic demand of a slurry. However, it has never been recognized or expected by those skilled in the art that in a papermaking slurry, that other variables in the slurry heretofore having an unknown relationship to TOC would effect TOC measurements in a linear correlation to the cationic demand of the slurry.
For example, increases in the dissolved inorganics typically present., in papermaking slurries were found to lower both the cationic demand and the TOC measurement.
In the same manner, it was discovered that an increase in the concentration level of kaolin clay filler to a slurry containing unbleached softwood kraft pulp at constant consistency and pH showed that a strong linear correlation between cationic demand and TOC existed. In this instance, however, the relationship was inverse. When the filler concentration increased, the TOC ir.-asurement was lowered as cationic demand increased.
The very thrust of the present invention resides in this discovery which clearly indicates that the analysis of the dissolved organic carbon content in the papermaking slurry or in the white water recycle provides much more information than merely the level of the oxidizable carbonaceous components present. It provides a more convenient and readily obtainable parameter to use to control the polymer addition rates to the papermaking
process which in turn strongly affect the retention of solids and machine drainage rates obtained in the papermaking process.
Further, improved control of the necessary level of cationic polymer also leads to more effective and efficient use of anionic polymer additives for improved retention and drainage results.
As described in detail in the appendix section attached hereto, a conventional TOC analyzer, known by the trade name, DOHRMAN DC-80, was used to determine TOC levels. This instrument is based upon a chemical oxidation determination using an ultra-violet promoted persulfate oxidation system followed by infrared detection to determine organic carbon levels. Samples were first filtered to remove solids and the filtrate was analyzed for organic carbon values. The pH was adjusted prior to the organic analysis to remove any inorganic carbon compounds from the measurement.
It should be readily apparent that use of the TOC measurement in accordance with the teachings herein become increasingly valuable in processes having a high level of closure and recycle a greater percentage of the white water effluent. Previous studies have shown that dissolved contaminants in such recycle systems increase greatly as the percentage of recycling increases.
As the dissolved organics and inorganics, as well as
the non-soluble fines increase, the degree of control of the process variables becomes increasingly important to maintain desired production rates and product quality. In view of the past difficulties in obtaining reliable control information based upon Zeta potential analysis and colloid titration, and the inherent difficulty of automating direct on-line cationic demand measurements, the discovery of the unexpected relationship between TOC analysis and cationic demand is a truly dramatic step' forward in the art toward achieving a reliable control parameter for adjusting the chemical retention aid addition rates in papermaking processes.
Fig. 2 illustrates, by way of example, a proposed retention and drainage control strategy for a papermaking process which utilizes TOC analysis to control the addition of cationic neutralization agents as well as utilizing other process variable measuring means.
In accordance with this strategy, on-line instrumentation would be developed to essentially automate the control of the process variables. Previously published studies based upon work done at Miami University of Ohio have developed background data which leads to the conclusions forming the basis for this control strategy. The continuous monitoring of the level of contaminants and key process responses and the automatic adjustments of addition control agents in response to the monitored
variables would produce many benefits such as:
1. Reduced loss of high cost materials such as titanium dioxide, synthetic size, etc. 2. Increased dewatering on the paper machine leading to a lower water content sheet to the press section (lesser energy requirement in the dryer section). 3. Potential increased machine speeds due to increased drainage rates.
4. Improved paper machine runnability and product properties.
5. Increased water reuse potential which can result in energy and raw material savings.
Three major generalizations can be drawn from the extensive amount of research aimed at elucidating wet-end chemistry mechanisms and fundamental knowledge. These serve as the major basis of a first-pass retention control strategy:
1. The wet-end chemistry performance of most additives and components is highly dependent on the level of first-pass retention achieved. 2. On medium to high speed paper machines.
retention aid addition is necessary to achieve acceptable first-pass retention levels. 3. The effectiveness of cationic additives is greatly impaired due to interference by dissolved and colloidal anionic substances in the wet-end.
The proposed retention and drainage control strategy consists of three main control loops. The first loop measures and neutralizes the organic derived contaminants on the thick stock side of the stock preparation area. Total organic carbon measurements serve as a measure of the cationic demand of the system. Based on the levels detected, a cationic charge neutralizing additive of low molecular weight and high charge density is added to counteract the detrimental organic effects. This amount will be slightly affected by the level of dissolved inorganic material present since these cationic species will react with the negatively charged organics. Specific conductance measurements serve to quantify the level of dissolved inorganic. In theory, as the furnish exists the stock preparation area, the total charge of the system is checked to determine if the organics are sufficiently neutralized to the desired level.
In the second loop, the first-pass retention performance is measured, and the high molecular weight retention aid addition rate is adjusted if a change in retention is necessary. This is to achieve a targeted
uniform retention level. A retention value that correlates with first-pass retention can be derived with the M/K retention meter. The adjustment of drainage rates and couch dryness levels would be controlled by this additive, also. Information about the mass of incoming fine solids (filler, pulp, and broke fines) from the stock preparation area is also known and fed forward to this loop.
The third loop illustrated in the diagram monitors the level of filler retention in both the final sheet and in the recycled broke recovery system. This information is fed back so as to adjust the flow rates of mineral fillers, such as clay and TiO , accordingly in the stock preparation
2 area.
Not illustrated in the diagram, but quite desirable, is a feedback loop which relays information concerning such properties as the optical and strength characteristics of the paper to some type of process control computer. This information would include measurements of opacity, brightness, strength, etc., so that product specifications would remain acceptable.
In short, a first-pass retention and drainage control strategy could be implemented with relatively few on-line sensors. However, sensors which are currently commercially unavailable are those which measure total charge of the system, process stream fines levels, and wet ash levels in
the system. Given the future demands required in the paper machine wet end from alkaline papermaking and the increased filler loading levels, higher machine speeds, lower basis weights, white water recycle, etc., the industry needs to take a stronger approach toward this type of additional on-line process control strategy.
It should be noted that the charge sensor indicated is a Zeta potential measurement, however, this could also be preferably replaced with a TOC measurement.
Current work at Miami Univesity of Ohio to automate an on-line TOC monitoring system is showing significant progress. However, based upon the current practices, off-line TOC determinations still offer " significant improvement to provide control data for cationic addition rates to improve papermaking processing compared to prior and current control means.
At this time, and for all pactical purposes, it appears that cationic demand is the best parameter of the total quantity of charge in a papermaking system.
In view of the foregoing description, it should be readily apparent that the surprising and unexpected correlation between TOC measurements and cationic demand measurements of papermaking slurries in response to variables heretofore having unknown relationship to these two parameters represents a very dramatic step forward to
improving the process of papermaking.
Also included herein are portions of the experimental studies which formed the basis of the present invention and are identified as Appendix A. These excerpts include certain details of testing procedure, equipment and methods used to generate data which led to confirmation of the correlation between TOC measurements and cationic demand of a papermaking slurry.
Appendix A
Total Organic Carbon/Cationic Demand Correlation Study
Total organic carbon (TOC) measurements via chemical oxidation are known to determine the soluble organic concentration of a sample. This study demonstrated that TOC increases linearly with proportional increases in dissolved, oxidizeable, carbonaceous compounds. Further work with this same system revealed a strong correlation between total organic carbon and cationic demand measurements. In addition, it was determined that the total organic carbon measurements are non-specific toward the detection of individual carbon-based contaminants.
Even with its non-selectivity, TOC measurement could prove to be an important parameter of the detection of system upsets resulting from areas such as the pulp mill.
Based on this reasoning, the measurement was incorporated
into the thick stock loop of the Springer retention control strategy.
Springer and Noe first indicated that the total organic carbon measurement may indirectly yield more information than strictly soluble organic carbon levels present in a sample. They found that with increasing levels of dissolved inorganics, the corresponding TOC values decreased. From this trend, it wad decided that a series of correlation studies would be performed using several different papermaking variables in order to better investigate the relationship between cationic demand and TOC. Table 12 shows the factors and their levels used in separate fiber and clay systems. All possible combinations of the factors were utilized in both a 0.5% unbleached kraft pulp furnish and a 1,000 mg clay/liter sample. It is important to remember that the samples were filtered through Fisher brand Q5 medium porosity filter paper prior to each test. It is possible that the TOC signal is an indication of the colloidal as well as dissolved materials in the filtrate since the pore size distribution of the paper is not known.
TABLE 12
Factors and Their Levels for the Simple
Fiber and Clay Systems
(-) (+)
Calcium (mg/1 ) 0 140
Lignin (mg/1 ) 0 130 pH 3 . 0 4.5 2
The combined correlation was found to be (R =.884). A closer look at the effects of the individual variables on
TOC response • reveals that the organic lignin causes the expected increase while the addition of calcium causes a corresponding decrease. A possible explanation for this phenomena in regards to TOC comes from the technique by which the total organic carbon is determined. It is possible that the calcium precipitates the soluble organics, and consequently, decreases the TOC. Also, an adsorption mechanism may be operating between the negative lignin and the similarly charged fiber or clay surfaces through the presence of the cationic calcium ion which acts to promote a more favorable electrostatic interaction.
An increase in the level of the third variable, pH, was accompanied by an increase in TOC response. As was previously stated, it is believed that the kaolin clay crystal structure contains hydroxyl groups along its faces.
Raising the pH promotes the dissociation of hydroxyl groups, and consequently, creates a greater negative surface charge. Therefore, the increased repulsive forces allow the lignin and other anionic organic materials a greater chance to be present in the final filtrate by remaining in solution. Ionization also occurs in the fiber system. It has been priorly found that fibers swell with increases in pH due to the greater dissociation of acidic groups. With a more open fiber structure, it is possible that organic materials escape. Also, it is likely that the relative solubility of various organic components increases with pH, and, therefore, the TOC value of the filtrate should increase.
Identical trends in cationic demand response were noticed with the same changes in variable levels, thus, yielding a strong correlation. Explanations for the cationic demand measurement with respect to the variables used in this particular study were given in the first part of this chapter.
The effect of fine solids on the measurement parameters were explored in two separate manners. First, varying concentrations of kaolin clay were added to a 0.5% consistency unbleached softwood kraft pulp at 4.5 pH. Filler levels in this study were 5, 15 and 25% clay on dry fiber weight. Linear regression of the data indicates that
2 a strong correlation exists (R =.953). However, in this case, an inverse relationship was discovered. From this data, it is evident that the cationic demand value increased while TOC response decreased when filler concentration was raised. It is believed that the greater surface area in the sample was responsible for this phenomena. Since the cationic demand is due in part to the hydrodynamic surface area, its value increased when the concentration of clay was increased. Likewise, the greater surface area imparted by the clay caused a decrease in the total organic carbon due to the enhanced probability of adsorption of the soluble organic materials present in the sample. When one considers the range of clay concentrations used in this study, it seems that a greater difference in response value would have resulted. Although the changes were found to be statistically significant, the effect is minor by observation of the TOC and cationic demand values.
The second study investigating fines was an experiment using a 0.5% unbleached kraft pulp beaten to different degrees in a Waring Blendor. Times ranging from 0 to 40 minutes were used with 10 minute increments for each sample level. Analysis of the results revealed a direct
2 correlation (R =.946). Intense shear action such as this on fiber surface probably causes fibrillation of the external fiber wall thereby exposing more sites onto which the cationic demand polymer can adsorb. Thus, the cationic
demand value is increased. With the agitation induced by the blender apparatus coupled with any fiber fibrillation that is likely to occur, it is possible that soluble organic materials trapped within the fiber structure are released which then act to increase the TOC. Cationic demand may be increased for this reason as well because the organic material released contains a higher proportion of anionic groups than does the cellulose. From the data of the study it appears that the effects observed in this small range could be due to error. Again, analysis of the data indicated that the changes were significant.
In order to appropriately test the relationship in a highly contaminated system, a filler-ply sample was obtained from Jefferson Smurfit Corporation. The 1.2% consistency stock was composed of 68% recycled newsprint and ledger and 32% draft softwood. Two variables were used to allow differences in the levels of TOC and cationic demand. Lignin concentrations of 0, 130, and 260 mg/liter were combined in all combinations with pH levels of 3.0, 4.5, and 6.0. The results of this difficult test showed more scatter than any of the other correlation studies performed between
2 these measurements (R =.705). This could be due to the variety of fiber components and recycle contaminants present causing the samples to be somewhat non-uniform in nature.
Based on the results of these correlation studies, it
30
appears that in a given system the total organic carbon measurement could prove to be a replacement for the usually time consuming cationic demand measurement. As long as a baseline value of each measurement was determined for varying systems within a mill, it would be possible to extrapolate a cationic demand value from the respective TOC
2 response. For example. Fig. 4 (R =.905) gives a summary of all points generated in the investigation of these two important measurements except for the filler-ply experiment. From the slope of the graph, one can tell that the rise in cationic demand value is approximately 1 lb. polyamine/ton for every 5 mg carbon/liter increase in TOC.
An important point derived from this series of experiments is that the cationic demand measurement is highly dependent on the soluble organic materials present in a given sample in addition to that sample's hydrodynamic surface area.
Conclusion
This study further supports the belief that Zeta potential via microelectrophoresis is a capable measure of the magnitude of surface charge of a particle in colloidal suspension.
Cationic demand can be used as a reliable means of measuring the total quantity of charge and gives an indication of the charge density of a sample. The soluble organic material of a sample was found to be a dominant factor in the cationic demand determination through the TOC correlation study.
The total organic carbon (TOC) value of a filtered sample is not only an effective measure of the amount of "anionic trash" present but also indirectly gives an indication of the total charge of the sample.
Colloid titration as performed is not a viable measure of either charge density or total quantity of charge. The current procedure requires modification if it is to delineate more than merely a sample's net sign of charge.
While certain preferred embodiments of the present invention have been disclosed in detail, it is to be understood that various modifications may be adopted without departing from the spirit of the invention or scope of the following claims.
Claims
5 1. In an improved papermaking process of the type employing cationic polymer addition to the papermaking slurry to adjust electrokinetic charge of the slurry prior to introduction of th slurry to the paper machine, the steps of:
(1) taking samples of thick stock of a
10 paper slurry at preselected internals during a process run prior to introduction of said thick stock to a blending zone in which filler and water are added;
(2) measuring the TOC value of filtered 15. samples of said thick stock; and
(3) adjusting the addition rate of cationic polyer to said blending zone directly proportional to the measured TOC values obtained in step (2). 0 33
2. The process defined in claim 1 including the step of establishing a baseline correlation between cationic demand and TOC values of preselected samples of said thick stock; employin said baseline correlation to further monitor the electrokinetic charge of said thick stock and adjust the addition rate of cationic polymer to the blending zone in conjunction with the T values obtained in step (2) as defined in claim 1.
3. The process defined in claim 2 including the steps of taki further samples from the papermaking slurry leaving said blendi zone but prior to introduction of the slurry to a papermaking machine; making TOC determinations of each of said•samples; and adjusting the rate of said cationic polymer additions to said papermaking slurry in the blending zone directly proportional t the TOC values obtained from the further samples taken from the slurry as needed to adjust the level of neutralization of the slurry to a preselected value.
4. In a papermaking process of the type having a thick stock preparation zone communicated to a stock preparation and filler blending zone for preparing a papermaking slurry to be delivere to the inlet of the paper machine for making a finished paper sheet product, the combination of the steps of:
(a) sampling the papermaking slurry communicated from the thick stock preparation zone to the stock preparation and filler blending zone; 34
.(b) filtering the solids from the sample obtained in step (a) and collecting the filtrate; (c) measuring the TOC content of said filtrate obtained in step (b); (d) adding an electrokinetic charge neutralization agent to the paper mill slurry prepared in the stock preparation and filler blending zone at a rate directly proportional to the TOC value obtained in step (c) corresponding to obtaining a predetermined level of electrokinetic charge of the slurry introduced to the paper machine for making a final paper product;
(e) communicating the papermaking slurry neutralized in accordance to step (d) to a conventional papermaking machine; and
(f) repeating steps (a)-(d) as required to maintain a given level of neutralization of the charge of the paper slurry communicated to the paper machine.
'. A process as described in claim 4 including the step of:
(g) sampling the papermaking slurry exiting the stock preparation and filler blending zone prior to delivery to the paper machine and repeating steps (b) and (c); and (h) adjusting the level of charge of the papermaking slurry by adjusting the addition rate of the charge neutralization agent to the slurry directly proportional to the TOC measurement obtained in step (g).