WO1985002838A1 - Water reducing agent utilized in mortar and concrete

Info

Publication number: WO1985002838A1
Application number: PCT/US1984/002074
Authority: WO
Inventors: Kiyoto Imai; Masanobu Sugawara; Yasuhiko Ohtaki; Kazuo Uno
Original assignee: Sandoz Ltd
Priority date: 1983-12-27
Filing date: 1984-12-19
Publication date: 1985-07-04
Also published as: AU3831285A; EP0166774A1; DE3470027D1; JPS60141660A; EP0166774B1; JPS6235985B2; CA1228607A; BR8407247A; AU578925B2

Abstract

Water-reducing additives for mortar and concrete are prepared by the formaldehyde condensation of isocyanuric acid and naphthalene sulfonic acid, or salts thereof.

Description

WATER REDUCING AGENT UTILIZED IN MORTAR AND CONCRETE

BACKGROUND OF THE INVENTION

This invention relates to a non-air entraining water-reducing agent for use with mortar and/or concrete. This water-reducing agent comprises a high molecular weight condensate of formaldehyde with naphthalene sulfonic acid and socyanuric acid, or the respective neutralized salts thereof.

In the industry, util zation s made of condensates of formaldehyde and naphthalene sulfonic acid, and formaldehyde and melamine sulfonic acid, or their respective salts, as water-reducing agents. The resultant condensation products, particularly those of a high molecular weight, are often referred to as high-range or high performance water-reducing agents.

. Generally, high-range water-reducing agents are used with high cement content mixes, and if added at the time the concrete is being mixed, increase the workability of the concrete, increase the efficiency of the cement, and reduce the amount of water required in the concrete, as well as increase the strength of the concrete at all ages measured. Such agents also increase the quality of the concrete by reducing the tendency of the concrete to form cracks or fissures. Therefore, high-range water-reducing agents are extremely beneficial in the dispersion of crushed rock, mortar, and cement in manufactured concrete.

For all practical purposes, water-reducing agents are utilized to stop slump loss associated with transporting of ready mix concrete, to improve the water reducing character stics, to improve concrete flowability, and to improve ultimate quality. High-range water-reducing agents are used to produce high strength concrete, particularly with concrete used in secondary products such as prestressed members, and as agents to improve concrete flowability for ease of placement.

Japanese Patent announcement SHO 54-1331 reports that water reduction in concrete is obtained from the use of tris (hydroxyal yl) isocyanurate by itself, or in combination with other known commercial high-range water-reducing agents. However, the use of tr s (hydroxyalkyl) isocyanurate alone shows little water reduction in concrete, and water reducing characteristics are in fact diminished as the quantity of tris (hydroxyalkyl) isocyanurate increases in commercial compounds.

SUMMARY OF THE PRESENT INVENTION

The present invention, as a result of an earnest study of water-reducing agents utilized with mortar or concrete, is able to offer a water-reducing agent with performance that greatly reduces the amount of slump loss of concrete when a combination of naphthalene sulfonic acid and isocyanuric acid compounds is used as a product of a co-reaction and/or condensation with formaldehyde.

Thus, this invention relates to a water-reducing agent utilized with mortar and concrete, of which the primary components are condensates of formaldehyde, naphthalene sulfonic acid, and at least one type of isocyanuric acid composition selected from a group which includes isocyanuric acid, tris (hydroxyalk l) isocyanurate, tris (carboxy) isocyanurate, and tris (alkyl) isocyanurate. The neutralized salts of the. two acids may be used in place of the acids themselves.

DESCRIPTION OF PREFERRED EMBODIMENTS

In manufacturing the water-reducing agent of the invention, for each mol of naphthalene sulfonic acid, 0.01-0.5 mol of sulfuric acid is used as a catalyst, preferably within the range of 0.04-0.4 mol, and 0.01-0.5 mol of isocyanuric acid composition, preferably the range of 0.02-0.3 mol is added. When the quantity of isocyanuric acid composition in the mixture is less than 0.01 mol, the resulting product is not an effective water-reducing agent, and when above 0.5 mol, the water reducing effectiveness is diminished. Also, 0.08-2.0 mol of formaldehyde (ordinarily as a solution of 37 percent formalin in water), preferably within the range of 0.9-1.5 mol, is added to the reaction mixture. Following the introduction of an amount of inert gas in a quantity greater than 0.2 kg/cm G,

3 preferably 0.5-10 kg/cm G, the temperature of the reaction mixture is held between 100-140° C, preferably 110-130" C, from 1-10 hours, preferably 3-8 hours, until the reaction is completed.

The reaction is completed when the non-reacted naphthalene sulfonic acid and the non-reacted isocyanuric acid composition are analyzed by means of HLC, and 90 percent or more of the naphthalene sulfonic acid and the isocyanuric acid composition have reacted. Following the completion of the reaction, neutralization is accomplished through ordinary means with caustic soda or calcium hydroxide. The reaction fluid is adjusted to a pH of 8-10. Following the removal, if necessary, of the undissolved components, the water-reducing agent s ready for use.

As sources of naphthalene sulfonic acid, utilization may be made of such mono sulfonic acid types as beta-naphthalene sulfonic acid, alpha-naphthalene sulfonic acid, etc., poly sulfonic acids such as di -sulfonic acid, or tri -sulfonic acid, as well as compounds or mixtures of these. Naphthalene sulfonic acids can also be obtained from naphthalene sulfate salts. However, in these instances, if the acid sulfate reacting liquor is used directly in the joint condensation reaction of this invention, a catalyst of sulfuric acid is obtained without the need for duplication as an added benefit.

The isocyanuric acid compositions may be used independently as reactants or as mixtures. In addition, a by-product of producing an isocyanuric acid compound may be utilized which waste fluids have an isocyanuric acid composition of 10 percent or more.

Conventional sources of formaldehyde may, of course, be utilized. For example, gaseous formaldehyde may be dissolved directly in water to produce formalin for the condensation reaction described. The water-reducing agents of this invention may be used in concrete or mortars the ratio of 0.01-10 percent, with respect to the hydraulic cement. When compared with other commercial water-reducing agents, there is an improvement in the water reducing capabil ty, and there is a reduction in the degree of slump loss with extended mixing time.

In addition to the indicated preferred mode of the invention, the formal ehyde, condensate of the naphthalene sulfonic acid and the isocyanuric acid compounds, various organic functions of these adducts, and the number of molecules, can be changed to generate various types of molecular formulae. In addition, the water-reduc ng agent of this invention, as indicated earlier, can utilize isocyanuric acid waste fluids, a characteristic which makes it possible to produce a product at a cost which normally is less than that of presently marketed commercial water-reducing agents. Hereafter, we will provide a detailed explanation of this invention by means of various examples. However, the invention is not technologically limited to these examples, since variations within the scope of the invention would be clearly evident.

Example 1 115 grams of naphthalene is heated to melting, and, while maintaining the temperature between 120-130° C, 115 grams of 98 percent sulfuric acid is added over a 1 hour time period. The temperature is slowly increased to 160° C over a 1 hour period, and the reaction is maintained at between 155-160° C for 4 hours or more. Following this, the reaction is allowed to cool to ^•approximately 100° C. To this sulfonate reaction liquor, 46 grams of tris (2-hydroxyethyl ) isocyanurate is added, and the temperature is maintained at 80-90° C, while 73 grams of 37 percent formalin are added over a 2 hour time period. Next, 3-5 atmospheres of nitrogen gas are added to the reaction container, followed by a temperature increase to 115-120° C, after which the temperature of the reaction is maintained for about 7 hours. As the viscosity of the reaction liquor increases, water may be added and blended into the mix. During the reaction, the reduction in the quantity of beta-naphthalene sulfonic acid and (2-hydroxyethyl ) isocyanurate is determined by means of HLC. After completion of the reaction, approximately 100 grams of water is added, and while cooling, the pressure within the reaction chamber s reduced. Subsequently, the reaction liquor is neutralized by normal means, and following the separation of the sulfuric acid salt, adjustment is made to obtain a solution of 42 percent by weight solids. After tests in concrete, it was evident that concrete containing the product of this invention has better flow characteristics, strength, and less slump loss during mixing when compared with other commercial high-range water-reducing agents. Test results are shown in Table 1.

Example 2 In a similar manner as was described in example 1, naphthalene is sulfonated by means of concentrated sulfuric acid. An approximately 30% by weight solution of tris (2-hydroxyethyl ) isocyanurate, remaining after precipitation of the isocyanurate from the mother liquor, s added in an amount of 23 grams of solids for each 115 grams of naphthalene. Subsequently, 73 grams of 37% formalin are added, and the temperature is held at between 80-90° C for 2 hours, followed by an increase to 115-120° C where it is held for approximately 5 hours, in an atmosphere of nitrogen (3-5 atmospheres), until completion of the reaction. The resulting reactant fluid is treated in the same manner as described in example 1. The results of the concrete tests using the above described product demonstrate improved performance even when the additions are made of residues including tris (hydroxyethyl ) isocyanate.

Example 3 Tris (2-carboxyethyl ) isocyanurate is added to the completely reacted sulfonate liquor, as was the tris (2- ydroxyethyl ) isocyanurate of example 1. Condensation with formalin is accomplished under the same conditions, resulting in a substance having good performance in concrete, as shown in Table 1.

Example 4 The 46 grams of tris (2-hydroxyethyl ) isocyanurate of example 1 is increased to 69 grams, and condensation s achieved in the same manner by the addition of 73 grams of 37% formalin under pressure in the reaction flask. Following the neutral zation of the condensate liquor, concrete tests were performed.

Example 5

The 23 grams of 30% by weight of tris (2-h droxyethyl ) isocyanurate utilized in example 2 is increased to 34 grams, and condensation and neutralization were performed in the same manner. The resultant product was then tested in concrete.

Comparative Example 1 A commercial high performance water-reducing agent, the sodium salt of a beta-naphthalene sulfonic acid - formaldehyde condensation, was tested in concrete.

Comparative Example 2 A commercial high performance water-reducing agent, the sodium salt of formaldehyde condensed melamine sulfonate, was tested in concrete.

Comparative Example 3 Tris (2-h droxyethyl) isocyanurate produced by standard methods (a white powder having a melting point of 134-6° C) was tested in concrete.

Comparative Example 4

During manufacture of the tris (2-hydroxyethyl ) isocyanurate utilized in example 2, the concentrated residue of the fluid containing 30% tris (2-hydroxyethyl) isocyanurate by weight was dried for 5 hours at 107° C, and tested in concrete.

Comparative Examples 5 and 6

The commercial high performance water-reducing agent shown in comparative example 1, and tris (2-hydroxyethyl ) isocyanurate were mixed in ratios of 9 to 1 and 7.5 to 2.5, respectively, and then ^: tested in concrete.

Comparative Examples 7 and 8

The commercial high performance water-reducing agent shown in comparative example 1, and the residue obtained in preparing comparative example 3 are mixed in ratios of 9 to 1 and 7.5 to 2.5, respectively, and then tested n concrete. RESULTS

Material Used O 1. Cement - Ordinary Portland 3 type mix O O 2. Fine Bonemeal - Oikawawa Sangawa Sand, Chiba Sangawa Sand (mix ratio 9:1) n 3. Coarse Bonemeal - Aoume Crushed Rock (M.S. = 20 mm) o

Claims

We claim:

1. A water-reducing admixture for mortar and concrete, said admixture compr sing a high molecu ar weight condensate of a formaldehyde condensation reaction with isocyanuric acid, and naphthalene sulfonic acid.

2. An admixture as set forth in claim 1, wherein said isocyanuric acid is provided as a neutralized salt.

3. An admixture as set forth in claim 1, wherein said isocyanuric acid is provided as a compound selected from the group consisting of isocyanuric acid, tris (hydroxyalkyl) isocyanurate, tris carboxy isocyanurate, and trialky! isocyanurate.

4. An admixture as set forth in claim 1, wherein said naphthalene sulfonic acid is provided as a neutralized salt.

5. An admixture as set forth in claim 1, wherein said naphthalene sulfonic acid is provided as a compound selected from the group consisting of naphthalene sulfonic acid, beta-naphthalene sulfonic acid, di-sulfonic acid, tri-sulfonic acid, naphthalene sulfate salts, and mixtures thereof.

6. An admixture as set forth in claim 1, wherein the isocyanuric acid and the naphthalene sulfonic acid are present in a molar ratio of from about 0.01:1 to about 0.5:1.

7. An admixture as set forth in claim 6, wherein the molar ratio of isocyanuric acid to naphthalene sulfonic acid is from about 0.02:1 to about 0.3:1.

8. An admixture as set forth in claim 6, wherein the molar ratio of formaldehyde to naphthalene sulfonic acid is from about 0.08:1 to about 2.0:1. 9. An admixture as set forth in claim 6, wherein the molar ratio of formaldehyde to naphthalene sulfonic acid is from about 0.

9:1 to about 1.5:1.

10. An admixture as set forth in claim 1, wherein said isocyanuric acid is provided as an isocyanuric acid waste fluid.