WO1981002236A1 - Process for making discs - Google Patents

Process for making discs Download PDF

Info

Publication number
WO1981002236A1
WO1981002236A1 PCT/US1980/001728 US8001728W WO8102236A1 WO 1981002236 A1 WO1981002236 A1 WO 1981002236A1 US 8001728 W US8001728 W US 8001728W WO 8102236 A1 WO8102236 A1 WO 8102236A1
Authority
WO
WIPO (PCT)
Prior art keywords
group
photopolymerizable liquid
flexible layer
bead
formula
Prior art date
Application number
PCT/US1980/001728
Other languages
French (fr)
Inventor
D Kerfeld
Original Assignee
Minnesota Mining & Mfg
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Minnesota Mining & Mfg filed Critical Minnesota Mining & Mfg
Priority to DE8181900699T priority Critical patent/DE3071280D1/en
Priority to AU67830/81A priority patent/AU536709B2/en
Publication of WO1981002236A1 publication Critical patent/WO1981002236A1/en

Abstract

The manufacture of information carrying discs (2) has required relatively slow processing because of the need to conform materials to exact mold shapes and to remove entrapped gases. The use of either preformed films or liquids provides different degrees of this problem. The use of a process whereby a bead of photopolymerizable liquid (14) is moved across the mold surface has been found to accurately fill the mold, remove air bubbles, and enable rapid replication of information carrying discs.

Description

PROCESS FOR MAKING DISCS
Field of the Invention The present invention relates to information carrying systems and more particularly to discs which carry light readable or stylus readable information.
These discs may be useful in carrying information which is convertible to electronic signals for such varied uses as sound recordings, audio/visual recordings, or even computer type information retrieval.
Background of the Invention
Information retrieval in the form of discs having information distributed in a circular, arc-like, or spiral pattern has been available in various forms for many years. Early forms of musical reproduction equipment, for example, used discs with either holes or protuberances to pluck an array of strings or vibrating posts to produce music. Early displays of moving pictures operated by rotation of a disc bearing consecutive images on the periphery. The most common form of storing reproductions of musical performances, which has been in use for about one hundred years, is the phonograph record which uses a spiral pattern of grooves having vertical and horizontal modulations to generate signals which can be converted to sound. With the introduction of the laser to industry, a new information storage system was developed which comprised a disc having a circular or spiral pattern of depressions or protuberances which would disturb, reflect, or refract incident light patterns. These information storing discs, often used for storage of audio/visual information and generally referred to as video discs, are well known in the art. Such U.S. Patents as 3,658,954; 3,795,534; 3,798,134; 3,855,426; 3,901,994; 4,124,672; 4,126,716; and 4,130,620 show various constructions, compositions, and processes for forming video discs. In addition to the laser readable video disc, another commercial construction is used which is more similar to the classic phonograph recording. This type of construction, as described in RCA Review, Vol. 39, No. 1 March, 1978, comprises a spiral array of grooves which is tracked by a stylus. The grooves are impressed with coded information in the form of vertical and/or radial modulations.
Even though these systems are read by totally different techniques, they are affected by similar, if not identical, problems. Imperfections in the depressions, protuberances, or modulations cause undesirable or spurious signals to be generated. The imperfections can be produced during manufacture of the disc or can develop from wear during use or manipulation of the disc.
The present invention relates to information storage discs for use with laser or stylus readout systems which have good fidelity and resistance to wear.
More particularly, the present invention relates to a process for forming information storage discs or disc blanks for use with laser or stylus readout systems.
Summary of the Invention It has been found according to the present invention that high density information storage discs or disc blanks comprising discs having a circular, arc-like, or spiral pattern of depressions, protuberances, and/or grooves with or without (in the case of blanks) modulations, can be made by photopolymerization of a liquid mass properly deposited between a stamper and a substrate to which the polymerized mass is to adhere. The photopolymerizable mass is deposited by moving a bead or wave of the photopolymerizable liquid between a flexible substrate or flexible stamper and the corresponding optical disc stamper or substrate so as to fill the pattern in the stamper and then irradiating the photopolymerizable mass, through either the stamper or the substrate. The process of the present invention generally comprises the use of at least one flexible sheet, either the substrate, which would carry the information layer, or the stamper, (which may be a video disc or video disc blank stamper) to spread a bead of photopolymerizable liquid over a surface (corresponding to a video disc stamper or substrate) and the polymerization of the liquid by exposure to radiation through the substrate or disc stamper. The use of liquid photopolymerizable materials to form replicated information carrying discs is known in the art, such as for example Belgian Patent 859,711. The process of the present invention provides a number of advantages over prior art methods, including those using photopolymerizable liquids.
The prior art processes, involving the deposition of the liquid on the stamper or substrate (by knife coating or spin coating) and subsequent application of the substrate, are two step processes. The substrate is usually laid over the liquid coated master and the amounts of liquid material and its general displacement over the master is difficult to control. Excess liquid is usually applied to insure minimum thickness in the information carrying layer. The advancement of a bead of liquid acording to the present invention as by the substrate being rolled out over the master has been found to remove substantially all of the air in the mold. The leading edge of the bead tends to pick up and carry the air without redepositing it in progressive features of the master because the air bubbles rupture, releasing the gas. This eliminates beading and wicking of the thin liquid film both of which creates voids. The need for levelling agents, which can deleteriously affect the physical properties of the coating or raise the cost of materials used is avoided.
The process of the present invention also offers advantages over the thermal molding or embossing processes of the prior art. Photopolymerization can, with reasonable selection of photocatalysts or photoinitiators, be performed at faster rates and with simpler equipment with no loss of quality as compared to thermal molding and embossing processes. Little pressure is used and no heat curing is required, so little stress is applied to or built into the discs. Because little stress and softer materials are used, the life of the stamper is believed to also be extended. In fact, with the process of the present invention, a non-metallic master may be used to provide numerous replications. Such organic resin stampers (usually with a thin metal coating) are far less expensive than metal stampers used in conventional processes.
As long as the substrate or master is able to bend sufficiently to enable the formation of a bead and propagation of that bead as the bend-point is moved forward, the substrate or master is sufficiently flexible. Materials that would otherwise be considered semi-flexible are therefore useful in the practice of the present invention.
These and other features can be seen with a review of the drawings.
Description of the Drawings FIGURE 1 shows a cross-section view of an information carrying disc.
FIGURE 2 shows a view of apparatus which could typically be used to practice the present invention.
FIGURE 3 shows a side view of apparatus which could typically be used to practice the present invention.
Detailed Description of the Invention
Information carrying elements are made according to the process of the present invention. A cross-section of an information carrying disc 2 is shown in Figure 1. A substrate 4 carries an information carrying layer 6 which has depressions or grooves 7 or protuberances 5 thereon. As hereinafter described, substrate 4 may be opaque or transparent. If the substrate is opaque to the radiation used for curing the photopolymerizable liquid, a stamper substantially transparent to this radiation must be used. A reflective layer or primer layer or both may be present between the substrate 4 and the information carrying layer 6.
The process itself can be more readily understood from Figure 2. The substrate 4 is moved by an element 12 over the stamper carrying surface 10. On this surface, facing upwards towards the advancing substrate 4 is a negative mold 8 of the information carrying disc or disc blank to be replicated. The pattern 9 on the mold 8 is the specific pattern to be duplicated. As element 12 advances substrate 4 so that it flattens out over the surface 10, a mass of photopolymerizable liquid 14 is also advanced over the surface 10 and the pattern 9 on the mold 8. If the stamper is both transparent and flexible, the relative positions of the substrate and stamper may be reversed.
The dynamics of the process can be readily seen in Figure 3. As element 12 advances the substrate 4 over the stamper 10, a bead of photopolymerizable liquid 14 is advanced in front of the substrate 4. The. liquid 14 fills the depressions 16 in the mold 8. The photopolymerizable liquid 14, after it has been spread over the mold 8 and when the substrate 4 is laying over it can be cured by irradiation transmitted through either the mold 8 from the backside 18 of the stamper 10 or through the substrate 4. After curing of the photopolymerizable liquid 14, the substrate 4 is lifted off of the mold 8 carrying the polymerized resin with it. This produces the article of Figure 1.
Another manner of propagating the advancing bead of liquid within the practice of the present invention is with an essentially flat or rigid layer. By placing the mass of liquid on one side of an upright or angled rigid substrate or master, the rigid layer may be rotated about the lower edge so as to squeeze a bead of liquid forward until the rigid layer and the other substrate enclosing the liquid are essentially parallel. This operates substantially better than would simple hand spreading of liquid and pressing with a stamper because of reduced air entrapment. This method can be described as 1) moving a first layer relative to a second layer from a non-paralle to a parallel position so as to spread in the form of a bead, a photopolymerizable liquid mass between the two layers, one of said layers having a patterned surface facing the other layer with a circular, arc-like, or spiral pattern of depressions, protubernances, grooves with or without modulations or combinations of depressions, protubernances and grooves with or without modulations, the other of said layers having a surface to which the photopolymerizable liquid will bond upon polymerizing, 2) then irradiating said photopolymerizable liquid to polymerize said liquid and bond the polymer formed to the other of said layers, and then 3) removing said polymeric resin and the layer to which it is bonded from said patterned surface.
The composition of the photopolymerizable material may be any material which polymerizes into a polymeric resin which has satisfactory properties for use in an information carrying disc or disc blank. The polymeric resin usually is at least transparent for the radiation used to read information off the disc. Ordinarily a fairly narrow band of radiation is used for these purposes so that the photopolymerizable liquid and the polymeric resin only preferably should be transmissive of at least 50% of the radiation in a 100 nm, 50 nm, or 30 nm band. Preferably the layer is transmissive of at least 75 to 90% of the radiation within such a band. Many different types of photopolymerizable systems are useful. Acrylates (including methacrylates), epoxy resins, silanes, vinyl resins, and others are useful photopolymerizable systems. The preferred polymerizable systems of the present invention are ambifunctional silanes and polyacryloyl polymerizable systems. Ambifunctional silanes are materials (monomers and/or hydrolyzates and precondensates thereof) having a di- or trialkoxy silane on one end and a different polymerizable group, such as an epoxy, acryloyl (including methacryloyl), or vinyl group on the other end. A formula for these materials would be:
Figure imgf000009_0001
wherein A is an epoxy, acryloyloxy, or vinyl containing group,
R is a divalent organic radical, R1 is a monovalent organic radical such that OR1 is hydrolyzable,.
R2 is a monovalent organic radical, and n is 0 or 1, and most preferably 0.
A is preferably selected from the groups
CH2=CH-,
Figure imgf000009_0002
Figure imgf000009_0003
wherein a and b are selected from H, or, when fused together, represent the atoms necessary to form a 5- or 6-membered cycloaliphatic ring, and R3 is H or CH3.
R is preferably an alkylene group which may be interrupted with an oxygen atom. Preferably the group has from 1 to 16 total carbon atoms and more preferably may be represented by the formula
-(CH2)p-(O)m-(CH2)q wherein p is 1 to 6, m is 0 or 1, and q is 1 to 6. R1 is preferably alkyl or acyl of 1 to 10 carbon atoms and most preferably alkyl of 1 to 3 carbon atoms. R2 may be H or alkyl of 1 to 10 carbon atoms. As noted above, these compounds are most preferably trialkoxy silanes.
A preferred class of polyacryloyl compounds for use in the process of the present invention is described below. The class herein defined as "polyacryloyl heterocyclics" are represented by the formulae:
1) A1-Z-A2 wherein A1 and A2 independently are alkoxyalkyl groups having terminal ethylenic unsaturation and having the formula
Figure imgf000010_0001
wherein R9-O- is a monovalent residue of an aliphatic terminally unsaturated primary alcohol, R9OH, formed by the removal of the active hydrogen from the primary -OH group, R9 having the formula:
[E(CH2)d]tR13(CH2)c
Figure imgf000010_0002
c is an integer of from 1 to 6, d is zero or an integer of from 1 to 6, R10 and R14 are independently selected from hydrogen and methyl,
R13 is an aliphatic group having from 1 to 15 carbon atoms, and no more than two catenary oxygen or carboxy groups, a valence of m + 1, t is an integer of from 1 to 5,
R11 is selected from hydrogen and groups of the formula
or
Figure imgf000011_0001
wherein R15 is selected from alkyl and alkenyl groups
R16 is an aliphatic or aromatic group of up to eight carbon atoms,
R12 is an alkylene group of from 1 to 6 carbon atoms with up to one catenary oxygen atom, and
Z is a heterocyclic group of the formula
Figure imgf000011_0002
wherein X is a divalent group which is required to complete a 5- or 6-membered heterocyclic ring, or
(2)
Figure imgf000011_0003
wherein R17 and R18 independently represent hydrogen or methyl,
R19 represents hydrogen, an alkyl group, or a phenyl group,
R18 and R19 together may represent a trimethylene or tetramethylene group, r represents a number of from 1 to 30, s is 2 or 3, and
A represents a group of the formula
Figure imgf000012_0002
wherein X1 represents the divalent radical necessary to complete a 5- or 6-membered heterocyclic ring group
The more preferred compounds of. this class are selected from those where m is 1 to 4 in formula 1) and in formulae 1) or 2) X1 and X are selected from
Figure imgf000012_0001
wherein R4, R5, R6 and R7 independently represent hydrogen, and alkyl group, an alkylene group, a cycloalkyl group, or a phenyl group, and
R8 represents hydrogen, an aliphatic group, or an aromatic group, except, that with regard to X, R8 is an alkyoxyalkyl group as defined for A1 and A2. Most preferably X and X1 are selected from
Figure imgf000013_0001
wherein R4 and R5 are hydrogen or alkyl of 1 to 4 carbon atoms.
It is also preferred that t is 2 to 5, R9 is
[E(CH2-)d]mR13 (CH2)c
E is
Figure imgf000013_0002
and R13 is alkylene of 1 to 13 carbon atoms. These compounds, as noted above, may be pure monomers, or, particularly in the case of the epoxy-silanes, hydrolyzates or precondensates. In addition, copolymerizable materials may be combined therewith. In fact, in some instances, copolymers are preferably combined with the compounds. Either aliphatic or cycloaliphatic epoxy comonomers are useful in the epoxy-terminated silanes, as are other copolymerizable silanes. Acrylates, preferably diacryloyloxy and dimethacryloyloxy (as well as tri-, tetra-, and penta-functional acryloyloxy materials) are useful comonomers with both the acryloyloxy-terminated silanes and the polyfunctional acryloyloxy-substituted heterocyclics described above. The use of the copolymerizable materials in conjunction with the preferred compounds of the invention is well described in the prior art, as for examples U.S. Patent No.s. 4,049,861, 4,101,513, 4,084,021 and U.S. Patent Application Serial Nos. 51,876, 51,877 and 51,888 filed on 25 June 1979.
In each of these systems, it is desirable to add materials that will render them sufficiently photo sensitive, for the preferred compounds and compositions made therefrom are not inherently photosensitive to a useful degree. With the silane containing compounds, at least a cationic photoinitiator is desirable, and when using the acryloyloxy- terminated silane, or the polyaryloyloxy-containing heterocyclics a free radical photoinitiator should also be present. These materials are well known in the art and are thoroughly described in U.S. Patent Nos. 4,049,861, 4,101,513, 4,058,400, 4,058,401 and U.S. Patent Application Serial No. 51,876, 51,877 and 51,888, and the literature. Preferred cationic photoinitiators are the SbF6-, PF6", BF4-, and AsF6" salt of polyaryl iodonium and sulfonium salts. Preferred free radical photoinitiators are polyaryl iodonium and sulfonium salts and the phenones. The compounds discussed above are generally preferred because they may be used without solvents. The absence of solvents prevents trapping of the solvents in the coating during cure. The preferred compounds, as noted in the prior art described above, also produce highly abrasion resistant and solvent resistant articles which are particularly desirable. In the case of the ambifunctional silanes, and particularly the epoxy- and acryloyloxy-terminated silanes, highly abrasion resistant materials are produced when the ambifunctional silanes comprise at least 30% by weight of the reactive ingredients. With the described heterocyclic acrylates, at least 15% by weight and preferably 25% by weight of the composition should be the heterocyclic acryloyloxy materials for abrasion resistance and/or oxygen insensitivity.
Other additives such as antioxidants, lubricants, surfactants, flow control factants, flow control aids, fillers, dyes, etc. may be present in the composition of the present invention. These and other aspects of the invention may be understood from the following examples.
Example 1
A highly hydrolyzed precondensate of γ-glycidoxypropyl- trimethoxy silane (about 80-90% of methoxy groups removed) (70gm) was mixed with 30 gm of 1,4-diglycidoxybutane and 2 gm of triarylsulfonium hexafluoroantimonate photocatalyst described in assignee's
U.S. Patent No. 4,173,476 by shaking for 3 hours. Bubbles were then removed from the mixture by placing it in an evacuated chamber for 15 minutes. The resulting photopolymerizable material was used to make a video disc replica according to the following roll coating process. A nickel video disc stamper was utilized. Approximately 2.0 cm3 of the material prepared as described above is spread by a cylindrical coating roller between a video disc stamper and a primed 0.18 mm polyester film. The sheet of 0.18 mm thick polyester film was positioned between the stamper and the roller to serve as a base element. This rolling process spread out a bubble free coating of resin composition over the surface of the stamper and simultaneously covered it with the polyester sheet. The stamper covered in this manner was then passed at 3 cm/sec under a 200 watt/inch high intensity medium pressure Hg vapor lamp. The UV exposure cured and hardened the resin composition. After this exposure, the laminated structure containing the replicated information was easily peeled from the nickel stamper. The sheet was then cut to produce a circular center hole and a circular outside edge, both concentric with the replicated information grooves.
The resulting video disc replica had an information bearing layer which was approximately 10 ± 5 μm thick which did not curl when laid on a flat surface. It retained this flatness after more than one year under ambient conditions and produced a good television picture when played on a commercial video disc player.
Example 2 A resin composition was prepared by mixing 60 gm of 1,3-bis 3-[2,2,2-(triacryloyloxymethyl)ethoxy] 2-hydroxyproρyl -5 ,5-dimethyl-2,4-imidizolidinedione (containing approximately 25% pentaerythritol tetraacrylate), referred to as Compound A in the remaining examples, with 40 gm 1,6-hexanediol diacrylate and 2 gm 2,2-dimethoxy-2phenyl-acetophenone. This composition was mixed by shaking and then filtered through a 5 μm filter. The resulting photopolymerizable material was used to make a video disc replica according to the roll coating process of Example 1 using polyvinylidenechloride primed polyester as the substrate.
The resulting video disc replica had an information bearing layer 10 ± 5 μm thick. This disc lay flat when placed on a level surface. It provided. a good television picture when played on a video disc player.
Example 3 A resin composition was prepared by mixing 70 gm of Compound A with 30 gm of hexanediol diacrylate and 2 gm of the photoinitiator of Example 1. The resulting material was used to make a video disc according to the procedure of Example 1. The video disc replica made in this way had a cured information bearing layer 6 ± 2 μm thick. This disc lay flat when placed on a level surface. It provided a good television picture when played on a video disc player.
Example 4 A resin composition was prepared by mixing 30 gm of Compound A with 70 gm of hexanediol diacrylate and 2 gm of the photoinitiator of Example 1. The resulting material was used to make a video disc according to the procedure of Example 1. The video disc replica made in this way had a cured information bearing layer 5 ± 2.5 μm thick. This disc lay flat when placed on a level surface. It provided a good television picture when played on a video disc player.
Example 5 A sample of commercially available poly vinylchloride film 14 inches square was prepared for use as a video disc substrate in the following way. The sheet was placed between two flat, smooth, chrome-steel plates. The plates were in turn sandwiched between four layers of cardboard and the resulting stack pressed for ten minutes in a hydraulic press. The press was operated with a force of 11 metric tons, and the press platens were heated to 160°C. This pressing operation reduced the surface roughness of the manufactured film and provided a substrate of suitable flatness.
The substrate thus prepared was used to make a video disc replica according to the procedure of Example 2, except that the surface of the polyvinylchloride opposite the information bearing layer was also coated with the resin composition. The cured polymer showed good adhesion to the otherwise untreated surface of the polyvinylchloride substrate. The disc lay flat when placed on a level surface and provided a good television picture when played on a video disc player. Information could be read from this disc with the laser beam incident from either side of the disc.
Example 6
A sheet of cast acrylic material (polymethylmethacrylate) 1000 m thick was sputter etched according to the following procedure to promote adhesion of the polymer. The acrylic substrate was placed in a Vecco Model 776 radio frequency diode sputtering apparatus operating at a frequency of 13.56 MHz. The substrate was then subjected to a radio frequency sputter etch as described in assignee's copending application S.N. 80,530 (filed 10 October 1974). The resin composition of Example 2 and the roll coating technique of Example 2 was used to prepare a vide disc replica with the above described substrate. The semiflexible substrate was allowed to bend slightly when it was lowered slowly onto the stamper as the roller moved along. The resin composition was cured with a bank of low intensity UV lamps, and the replica removed from the stamper. An aluminum coating 30 nm thick was vapor coated onto the surface of the information bearing layer. A circular hole was cut in the center of the disc, and a circular outer edge was cut. The resulting disc was then played on a video disc player; a good television picture was obtained. The laser beam of the player was incident through the uncoated acrylic surface and reflected by the aluminum coating on the information bearing surface.
Example 7
A resin composition was made by mixing 70 gm of a precondensate of γ-methacryloxypropyltrimethoxy silane (made according to U.S. Patent Application Serial No. 911,892, filed 2 June, 1978) with 30 gm of hexanedioldiacrylate and 2 gm of 2,2-dimethoxy-2-phenylacetophenone. The resulting material was used to make a video disc according to the procedure of Example 1 except that the resin was cured under a bank of low intensity "black lights" for 15 minutes. The video disc replica made in this way had a cured information bearing layer 6 ± 3.5 μm thick. This disc lay flat when placed on a level surface. It provided a good television picture when played on a video disc player. Example 8 A resin composition was made by mixing 90 gm γ-glycidoxypropyltrimethoxy silane with 10 gm limonene oxide and 2 gm of the photocatalyst of Example 1. The resulting material was used to make a video disc according to the procedure of Example 1 except that the resin was cured under a bank of low intensity "black lights" for 30 minutes. The video disc replica made in this way had a cured information bearing layer 5 i 3 μm thick. This disc lay flat when placed on a level surface. It provided a television picture when played on a video disc player but gave a slightly low signal level.
Example 9 A video recording was made in a commercially available polymeric photoresist layer and the layer developed by standard wash-development techniques after exposure. The recording was then vapor coated with 10 m of chrome. The resulting photoresist stamper was used in place of a nickel stamper to make a video disc replica according to the procedures of example 1. This replica was playable. When vapor coated with lOnm of chrome and used in place of a nickel stamper, repeated playable replications were made.
Example 10 A photoresist stamper was made according to the procedure of example 9. This stamper was used in place of a nickel stamper to produce a video disc replica according to the procedure of example 2. This replica provided a good television picture when played on a video disc player and again there was no significant wear on the stamper.
Example 11 An audio record replica was prepared using commercially available 1 mm polyvinylchloride as the base element. The resin composition of Example 1 was used with the roll-coating technique of Example 1. The semiflexible base element was allowed to bend slightly as it was lowered slowly onto the audio record stamper as the roller moved along. The resin composition was cured with a bank of low intensity UV lamps, and the replica stripped from the stamper. A circular hole was cut in the center of the record and a circular outer edge was cut. The resulting replica had an information bearing layer approximately 50 m thick. The audio record replica was successfully played on a conventional stereo audio system

Claims

Claims :
1. A method for making an information carrying disc or disc blank which comprises 1) moving a first layer relative to a second layer from a non-parallel to a parallel position so as to spread in the form of a bead, a photopolymerizable liquid mass between the two layers, one of said layers having a patterned surface facing the other layer with a circular, arc-like, or spiral pattern of depressions, protubernances, grooves with or without modulations or combinations of depressions, protubernances and grooves with or without modulations, the other of said layers having a surface to which the photopolymerizable liquid will bond upon polymerizing, 2) then irradiating said photopolymerizable liquid to polymerize said liquid and bond the polymer formed to the other of said layers, and then 3) removing said polymeric resin and the layer to which it is bonded from said patterned surface.
2. A method for making an information carrying disc or disc blank which comprises moving a bead of photopolymerizable liquid composition over a first surface by advancing said bead in front of a flexible layer having a facing surface in contact with said liquid so that said flexible layer lies substantially parallel to said first surface with said liquid between the flexible layer and the first surface in the direction from which the bead advances, and the flexible layer is angled away from the first surface in the direction towards which the bead advances, and there is a supporting surface located on the side of the flexible layer away from said facing surface along the length of the flexible layer at least in part between the area of the flexible layer that changes from angling away from the first surface to lying parallel to said first surface, wherein one of said first surface and said facing surface has a patterned surface in contact with said photopolymerizable liquid which is selected from the group consisting of circular patterns, arc-like patterns, and spiral patterns of depressions, grooves, protuberances and combinations of depressions, grooves and protuberances, advancing the bead until it covers the area of the patterned surface, irradiating said polymerizable liquid to convert it to a polymeric resin and bond it to whichever of said first surface and facing surface which is not said patterned surface, and then removing said polymeric resin and the surface to which it is bonded from said patterned surface.
3. The method of claims 1 and 2 wherein said photopolymerizable liquid comprises at least 30% by weight of radiation polymerizable components having the formula: 1) A1- Z-A2 wherein A 1 and A2 independently are alkoxyalkyl groups having terminal ethylenic unsaturation and having the formula
Figure imgf000022_0001
wherein R-O- is a monovalent residue of an aliphatic terminally unsaturated primary alcohol, ROH, formed by the removal of the active hydrogen from the primary -OH group, R having the formula:
[E(CH2)b]mR5(CH2)c
Figure imgf000022_0002
c is an integer of from 1 to 6, b is zero or an integer of from 1 to 6, R1 and R4 are independently selected from hydrogen and methyl, R5 is an aliphatic group having from 1 to 15 carbon atoms, and no more than two catenary oxygen or carboxy groups, a valence of m + 1, m is an integer of from 1 to 5, R2 is selected from hydrogen and groups of the formula
or
Figure imgf000023_0003
wherein R6 is selected from alkyl and alkenyl groups
R7 is an aliphatic or aromatic group of up to eight carbon atoms, R3 is an alkylene group of from 1 to 6 carbon atoms with up to one catenary oxygen atom, and
Z is a heterocyclic group of the formula
Figure imgf000023_0002
wherein X is a divalent group which is required to complete a 5- or 6-membered heterocyclic ring, or
2)
Figure imgf000023_0001
wherein R12 and R13 independently represent hydrogen or methyl, R 14 represents hydrogen, an alkyl group, or a phenyl group, R13 and R14 together may represent a trimethylene or tetramethylene group, m represents a number of from 1 to 30, n is 2 or 3, and
A represents a group of the formula
4. The method of claims 1 and 2 wherein said photopolymerizable liquid comprises at least 30% by weight of radiation polymerizable components selected from epoxyterminated silanes.
5. The method of claim 4 wherein said epoxyterminated silane is represented by one of the formulae:
Figure imgf000024_0001
wherein R is a divalent organic radical of the formula
-(CH2)p - (O)m - (CH2)q wherein p is 1 to 6, m is 0 or 1, and q is 1 to 6 and R1 is alkyl of 1 to 3 carbon atoms.
6. The method of claim 5 wherein said photopolymerizable liquid comprises from 10 to 70% by weight of an epoxy monomer copolymerizable with said epoxy-terminated silane.
7. The method of claim 3 wherein said photopolymerizable liquid comprises 10 to 70% by weight of an acrylate copolymerizable with said radiation polymerizable components.
8. The method of claim 2 wherein said photopolymerizable liquid comprises at least 30% by weight of an epoxy-terminated silane and said flexible layer is a transparent polymeric film.
9. The method of claim 2 wherein said photopolymerizable liquid comprises at least 15% by weight of polyacryloyl heterocyclics and said flexible layer is a transparent polymeric film.
PCT/US1980/001728 1980-02-01 1980-12-23 Process for making discs WO1981002236A1 (en)