US20170044679A1

US20170044679A1 - High performance earth-abundant electrocatalysts for hydrogen evolution reaction and other reactions

Info

Publication number: US20170044679A1
Application number: US15/233,498
Authority: US
Inventors: Song Jin; Miguel Cabán-Acevedo; Michael L. Stone
Original assignee: Wisconsin Alumni Research Foundation
Current assignee: Wisconsin Alumni Research Foundation
Priority date: 2015-08-11
Filing date: 2016-08-10
Publication date: 2017-02-16
Also published as: US11421333B2; US20190309426A1

Abstract

Electrodes for catalyzing electrochemical reactions (e.g., the hydrogen evolution reaction) are provided. The electrode may comprise a ternary pyrite-phase transition metal phosphochalcogenide (e.g., CoPS) disposed on a substrate, wherein the ternary pyrite-phase transition metal phosphochalcogenide is a solid material of a ternary compound of a transition metal, phosphorous (P), and a chalcogen, the solid material characterized by a substantially single, ternary alloy phase having a pyrite crystal structure. Methods of using and making the electrodes are also provided.

Description

CROSS-REFERENCE TO RELATED APPLICATIONS

The present application claims priority to U.S. Provisional Patent Application No. 62/203,811 that was filed Aug. 11, 2015, the entire content of which is hereby incorporated by reference.

REFERENCE TO GOVERNMENT RIGHTS

This invention was made with government support under DE-SC0002162 awarded by the US Department of Energy. The government has certain rights in the invention.

BACKGROUND

Hydrogen is a sustainable energy carrier that promises an environmentally friendly alternative to meet the future global terawatt energy demand^1,2. The production of hydrogen by means of water splitting, preferably solar-driven, requires highly efficient and robust catalyst materials². Noble metals such as platinum are currently the most active catalysts for the hydrogen evolution reaction (HER). Unfortunately, their application in large scale hydrogen production is limited by high cost and low elemental abundance^3,4. Thus, the search for cost-effective, earth-abundant materials with both high HER activity at low overpotentials and excellent stability has attracted significant research interest and become an important pursuit toward enabling a hydrogen economy. Various classes of earth-abundant transition metal compounds⁴, such as MoS₂ ^5,6, WS₂ ^7,8, amorphous MoS_x ⁹, CoS₂ ¹⁰, CoSe₂ ¹¹, CoP^12,13, Ni₂P¹⁴, FeP¹⁵, MoP^16,17, MoP|S¹⁸, and Ni—Mo alloys¹⁹, have been identified as promising HER electrocatalysts. Ultimately, it would be useful to integrate catalyst materials in solar-driven photoelectrochemical cells (PECs)²⁰.
Among the various earth-abundant HER catalysts recently discovered⁴, the pyrite structure-type transition metal dichalcogenides (MX₂, where M=Fe, Co, or Ni and X=S or Se) have emerged as an interesting family of low cost materials with high catalytic activity toward the HER^10,11,21-23. The family of metal pyrites includes semiconducting and metallic compounds that are very abundant as minerals or in sedimentary deposits within the earth's crust, which makes them appealing for a variety of energy conversion-related applications. For example, iron pyrite (cubic FeS₂; fool's gold) is a semiconductor that has been extensively studied as a promising cost-effective solar absorber^24,25, and has been studied as an HER catalyst^22,23. Moreover, metallic cobalt pyrite (CoS₂; cattierite; FIG. 1a ) has been found to display high catalytic activity toward HER¹⁹, polysulfide and triiodide reduction reactions^22,23.

SUMMARY

Ternary pyrite-phase transition metal phosphochalcogenide electrocatalysts, methods of making the electrocatalysts, and methods of using the electrocatalysts to catalyze electrochemical reactions (e.g., the hydrogen evolution reaction) are provided.
In one aspect, electrodes for catalyzing electrochemical reactions are provided. In one embodiment, an electrode comprises a ternary pyrite-phase transition metal phosphochalcogenide disposed on a substrate, wherein the ternary pyrite-phase transition metal phosphochalcogenide is a solid material of a ternary compound of a transition metal, phosphorous (P), and a chalcogen, the solid material characterized by a substantially single, ternary alloy phase having a pyrite crystal structure.
In another aspect, methods for catalyzing electrochemical reactions are provided. In one embodiment, a method for catalyzing an electrochemical reaction comprises exposing an electrode to a fluid comprising an oxidant to be reduced in the presence of free electrons, wherein the electrode comprises a ternary pyrite-phase transition metal phosphochalcogenide disposed on a substrate, wherein the ternary pyrite-phase transition metal phosphochalcogenide is a solid material of a ternary compound of a transition metal, phosphorous (P), and a chalcogen, the solid material characterized by a substantially single, ternary alloy phase having a pyrite crystal structure, whereby the free electrons induce the reduction of the oxidant at the ternary pyrite-phase transition metal phosphochalcogenide-fluid interface to form a reduction product.
In another aspect, methods for making electrodes are provided. In one embodiment, a method comprises exposing a transition metal-containing precursor disposed on a substrate to a chalcogen-phosphorous atmosphere at an elevated temperature and for a period of time sufficient to convert the transition metal-containing precursor to a ternary pyrite-phase transition metal phosphochalcogenide, wherein the ternary pyrite-phase transition metal phosphochalcogenide is a solid material of a ternary compound of a transition metal, phosphorous (P), and a chalcogen, the solid material characterized by a substantially single, ternary alloy phase having a pyrite crystal structure.
Other principal features and advantages of the invention will become apparent to those skilled in the art upon review of the following drawings, the detailed description, and the appended claims.

BRIEF DESCRIPTION OF THE DRAWINGS

Illustrative embodiments of the invention will hereafter be described with reference to the accompanying drawings.

FIGS. 1a-1c demonstrate the design of the ternary pyrite CoPS catalyst and the results from DFT calculations. The crystal structure of cobalt pyrite (CoS₂) (FIG. 1a ), intrinsic {100} pyrite surface coordination environment (FIG. 1b ), and crystal structure of pyrite-type cobalt phosphosulfide (CoPS) (FIG. 1c ) are shown. The free energy diagram is shown in FIG. 1d for hydrogen (H*) adsorption at the Co site on the {100} surface of CoS₂, and at the Co site, P site, and Co site after H* at P site on the {100} surface of CoPS. Note that density function theory (DFT) calculations for CoPS were performed for ordered P-S dumbbells for simplicity.

FIGS. 2a-2g illustrate the structural characterization of the CoPS nanostructures. Included are SEM images of as-synthesized (FIG. 2a ) CoPS film and (FIG. 2b ) CoPS NWs on graphite, and CHCH NPIs on carbon fiber paper (FIG. 2c ) before and (FIG. 2d ) after thermal conversion into CoPS NPIs. FIG. 2e shows EDS spectra and FIG. 2f shows confocal micro-Raman spectra for CoPS film and CoPS NWs on graphite, and CoPS NPIs on carbon fiber paper. The peak positions for the E_gand A_gRaman modes for CoS₂were included as vertical dash lines for comparison. FIG. 2g shows the PXRD patterns for various CoPS products with different morphologies in comparison to simulated pattern for cubic CoPS (ICSD collection code #62414) and standard pattern for CoS₂(JCPDS #41-1471). Note that the CoPS film measured by PXRD was grown on borosilicate glass. A minor marcasite-type CoPS polymorph phase (Pmnn, orthorhombic CoPS) was observed in this sample (labeled as “m”). All peaks corresponding to graphite and carbon paper were labeled as “*”.

FIGS. 3a-3f illustrate the electrochemical characterization of CoPS film on graphite, CoPS nanowires (NWs) on graphite and CoPS nanoplates (NPIs) on carbon fiber paper electrodes for HER catalysis. FIG. 3a includes J-V curves after iR correction, showing the catalytic performance of the CoPS electrodes (film, open squares; NWs, open triangles; NPIs, open diamonds) in comparison to a Pt wire (open circles). FIG. 3b shows a long-term stability test for CoPS electrodes at a current density of 10 mA/cm². FIG. 3c shows a Tafel plot for the data presented in panel FIG. 3a . FIG. 3d includes a plot showing the extraction of the double-layer capacitance (C_dl) for each type of CoPS electrode. FIGS. 3e, 3f show electrochemical impedance spectroscopy (EIS) Nyquist plots for CoPS electrodes. The data were fitted using modified Randles circuits shown in insets.

FIGS. 4a-4c demonstrate photoelectrochemical hydrogen generation using integrated CoPS/Si photocathodes. FIG. 4a includes J-V curves under dark and 1 Sun (100 mW/cm², AM 1.5) illumination in 0.5 M H₂SO₄, obtained for thermally converted 3 nm (down triangles), 5 nm (up triangles), 7.5 nm (diamonds), 10 nm (squares) and 15 nm (circles) cobalt films in comparison with 5 nm Pt film (solid trace), on n⁺-p-p⁺ micropyramid silicon. A planar CoPS/p-silicon electrode obtained by thermal conversion of 10 nm Co on p-Si is shown in comparison. FIGS. 4b, 4c show SEM images of CoPS/n⁺-p-p⁺ micropyramid silicon photoelectrode obtained by conversion of 10 nm Co film, showing (FIG. 4b ) top-down and (FIG. 4c ) cross-section views of the surface.

FIGS. 5a-5b show the PXRD patterns of NiP₂and NiP_2-xSe_xprepared at n(P):n(Se)=3:2 and 3:1 (FIG. 5a ) and NiSe₂and NiP_xSe_2-xprepared at n(P):n(Se)=2:3 and 3:3 (FIG. 5b ). The stars mark the diffraction peaks from the graphite disk substrate.

FIGS. 6a-6h show SEM and TEM images of the NiP₂(FIGS. 6a, 6b ) NiP_1.93Se_0.07(FIGS. 6c, 6d ), NiP_0.09Se_1.91(FIGS. 6e, 6f ) and NiSe₂(FIGS. 6g, 6h ) nanostructures.

FIGS. 7a-7b show EDS spectra of NiP₂, NiP_1.93Se_0.07, NiP_0.09Se_1.91, and NiSe₂samples (FIG. 7a ) and Raman spectra of NiP₂. NiP_1.93Se_0.07, NiP_0.09Se_1.91, and NiSe₂samples (FIG. 7b ).

FIGS. 8a-8d show the electrochemical characterizations of NiP₂, NiP_1.93Se_0.07, NiP_0.09Se_1.91, and NiSe₂nanostructures on graphite disk for HER electrocatalysis in 0.5 M H₂SO₄, including (FIG. 8a ) Polarization curves, (FIG. 8b ) the corresponding Tafel plots, (FIG. 8c ) the plots showing the extraction of the double-layer capacitance (C_dl), and (FIG. 8d ) surface area normalized Tafel plots.

FIG. 9 shows SEM images of NiP_1.93Se_0.07nanostructures on carbon fiber paper.

FIGS. 10a-10b show the electrochemical characterizations of the NiP_1.93Se_0.07nanostructures on carbon fiber paper of FIG. 9. FIG. 10a shows the polarization curves and FIG. 10b shows the corresponding Tafel plot.

DETAILED DESCRIPTION

Ternary pyrite-phase transition metal phosphochalcogenide electrocatalysts, methods of making the electrocatalysts, and methods of using the electrocatalysts to catalyze electrochemical reactions (e.g., the hydrogen evolution reaction) are provided. It is found that the catalytic performance of the disclosed ternary pyrite-phase transition metal phosphochalcogenide electrocatalysts is superior to known electrocatalysts made of earth-abundant elements, such as transition metal chalcogenides and transition metal phosphides, and is approaching the catalytic performance of platinum and other noble metal elements. In addition, it is found that performance of the disclosed ternary pyrite-phase transition metal phosphochalcogenide electrocatalysts in solar-driven hydrogen production via the hydrogen evolution reaction is surprisingly competitive with the significantly more expensive platinum containing photoelectrodes.
A method for catalyzing an electrochemical reaction may comprise exposing ternary pyrite-phase transition metal phosphochalcogenide to a fluid comprising an oxidant to be reduced in the presence of free electrons. The free electrons induce the reduction of the oxidant at the ternary pyrite-phase transition metal phosphochalcogenide-fluid interface to form a reduction product, which may be separated from the fluid and collected. The free electrons may be derived from an external power source in electrical communication with the ternary pyrite-phase transition metal phosphochalcogenide such that the reduction reaction is an electrochemical reduction. The free electrons may be derived from the absorption of light by a semiconductor and collection of photoexcited carriers, the semiconductor in electrical communication with the ternary pyrite-phase transition metal phosphochalcogenide, such that the reduction reaction is a photoelectrochemical reduction. The benefits of using the more efficient ternary pyrite-phase transition metal phosphochalcogenides include reducing the overpotential needed for the reduction reactions and the kinetic barriers associated with the reduction reactions.
The ternary pyrite-phase transition metal phosphochalcogenide electrocatalysts may be used to catalyze the hydrogen evolution reaction (HER), an electrochemical reaction in which hydrogen (H₂) is produced via the electrolysis of water (H₂O). The hydrogen evolution reaction may be carried out in a reaction cell comprising an anode and a cathode immersed in an aqueous solution (e.g., a solution of water and a water-soluble electrolyte such as H₂SO₄). The aqueous solution may be acidic, neutral or basic. The anode and cathode may be separated by a membrane. When an electrical potential is applied across the anode and the cathode, dissociated hydrogen ions (H⁺) migrate to the cathode where they are reduced to produce H₂, which may be separated from the aqueous solution and collected. At the anode, water reacts to form oxygen (O₂), hydrogen ions and electrons. The ternary pyrite-phase transition metal phosphochalcogenide electrocatalysts may be used to catalyze the reduction reaction of HER, i.e., the reduction of hydrogen ions to H₂at the cathode.
However, the ternary pyrite-phase transition metal phosphochalcogenide electrocatalysts may be used to catalyze other electrochemical reactions besides HER. In some embodiments, the electrochemical reaction is a polysulfide reduction reaction. In other embodiments, the electrochemical reaction is a triiodide reduction reaction. Both reactions may be carried out in a reaction cell similar to that described above for HER. In a polysulfide reduction reaction, elemental sulfur dissolved in aqueous solution (in the forms of various S_x ^n-ions, the so-called polysulfide ions) is reduced by the free electrons at the electrocatalyst-electrolyte interface at the cathode to form S^2-ions. In a triiodide reduction reaction, I₂molecules complexed with Γ dissolved in aqueous solution (e.g. the triiodide ions (I₃ ⁻)) are reduced by the free electrons at the electrocatalyst-electrolyte interface at the cathode to form iodide ions (I⁻). In yet other embodiments, the electrochemical reaction is a carbon dioxide (CO₂) reduction reaction. In such a reaction, CO₂may be reduced by the free electrons at the electrocatalyst-electrolyte interface at the cathode to form products such as CO. The benefits of using the more efficient ternary pyrite-phase transition metal phosphochalcogenides include reducing the kinetic overpotentials needed for these reduction reactions.
For purposes of this disclosure, the term “ternary pyrite-phase transition metal phosphochalcogenide” refers to a solid material of a ternary compound of a transition metal, phosphorous (P), and a chalcogen, the solid material characterized by a substantially single, ternary alloy phase having a pyrite crystal structure. Thus, the ternary pyrite-phase transition metal phosphochalcogenides are distinguished from solid materials having two or more distinct phases. The ternary pyrite-phase transition metal phosphochalcogenide may have the formula MPX, wherein M is a transition metal selected from Co, Ni, Fe and Mn, P is phosphorus, and X is a chalcogen selected from S, Se and Te. In some embodiments, the ternary pyrite-phase transition metal phosphochalcogenide is ternary pyrite-phase cobalt phosphosulfide. In some embodiments, the ternary pyrite-phase transition metal phosphochalcogenide is ternary pyrite-phase cobalt phosphoselenide. Each of these formulae also encompasses solid materials in which the amount of phosphorous and the amount of chalcogen in the solid material deviate slightly from ideal, e.g., non-stoichiometric CoP_0.83S_1.35versus stoichiometric CoPS. In such materials, the amount of phosphorous and the amount of chalcogen may be considered to be “substantially stoichiometric.” Larger deviations are also encompassed, e.g., NiP_1.93Se_0.07, which may be referred to as Se-doped NiP₂.
In some embodiments, the ternary pyrite-phase transition metal phosphochalcogenide is an alloyed ternary pyrite-phase transition metal phosphochalcogenide including more than one transition metal (e.g., two), phosphorous (P) and a chalcogen. An alloyed ternary pyrite-phase transition metal phosphochalcogenide is also a solid material characterized by a substantially single, ternary alloy phase having a pyrite crystal structure. Alloyed ternary pyrite-phase transition metal phosphochalcogenides may have the formula MPX as described above, but the transition metal component M includes more than one type of transition metal, e.g., M₁and M₂. As described above, the transition metals may be selected from Co, Ni, Fe and Mn.
As described in the Examples, below, the ternary pyrite-phase transition metal phosphochalcogenide electrocatalysts are distinguished from electrocatalysts which may be composed of a transition metal element, phosphorous and a chalcogen, but which are characterized by distinct chemical species in distinct regions of the material, e.g., bulk chemical species which differ from surface chemical species. By way of illustration, the ternary pyrite-phase transition metal phosphochalcogenide electrocatalysts are distinguished from MoPlS, which is the compound MoP having a surface modified with sulfur atoms. (See reference 18.) That is, the ternary pyrite-phase transition metal phosphochalcogenide electrocatalysts do not include MoPlS. By contrast, the ternary pyrite-phase transition metal phosphochalcogenide electrocatalysts are characterized by exhibiting substantial chemical uniformity and homogeneity throughout the material. This means that the type(s) of chemical species existing in the bulk of the material are the same (although not necessarily perfectly the same) as the type(s) of chemical species existing at the surface of the material. Such chemical uniformity and homogeneity may be confirmed using the techniques described in the Examples below, e.g., via X-ray photoelectron spectroscopy (XPS) measurements.
The ternary pyrite-phase transition metal phosphochalcogenide may be provided as a film or layer or coating of the solid material disposed on an underlying substrate to provide an electrode (e.g., cathode) that can be immersed in the fluid comprising the oxidant. A variety of substrates may be used, and may depend upon whether the reduction reaction to be catalyzed is an electrochemical reduction or a photoelectrochemical reduction. The substrate is typically a conductive substrate. By way of illustration, carbon substrates (e.g., graphite, glassy carbon, carbon fiber paper, carbon cloth, porous carbon, carbon nanotube networks, interconnected graphene networks, etc.) and stable metal substrates (e.g., Ti foil or plate) are suitable substrates for electrochemical reductions.
For photoelectrochemical reductions, the substrate comprises a semiconductor capable of absorbing light (e.g., solar radiation) to produce free electrons which are collected and transported to the ternary pyrite-phase transition metal phosphochalcogenide-fluid interface where they induce the reduction reaction. Various semiconductors may be used, and may depend upon the wavelength(s) of light to be absorbed. By way of illustration, silicon, indium phosphide (InP), and gallium phosphide (GaP) are suitable substrates. The substrate may further comprise an emitter layer (e.g., n⁺ doped silicon) disposed on a surface of the semiconductor, the emitter layer configured to mitigate or eliminate the influence of the ternary pyrite-phase transition metal phosphochalcogenide on band bending in the selected semiconductor. The substrate may further comprise a back surface field layer (e.g., p⁺ doped silicon) disposed on an opposing surface of the semiconductor, the back surface field layer configured to facilitate collection of the electrons generated by the absorption of light. The surfaces of the semiconductor may be structured or textured to enhance light harvesting. By way of illustration, the surfaces may comprise a plurality of micropyramids extending away from the surfaces. The micropyramids may exhibit an average maximum dimension of a few microns or less, e.g., about 5 μm or less, about 2 μm or less in the range of from about 1 μm to about 5 μm, etc. Nanopyramids may also be used.
Various morphologies of the ternary pyrite-phase transition metal phosphochalcogenide may be used. The ternary pyrite-phase transition metal phosphochalcogenide may be nanostructured, by which it is meant that the material is composed of distinct, distinguishable nanostructures (e.g., as visualized via scanning electron microscope images) having at least one dimension of about 1000 nm or less, i.e., in the range of from about 1 nm to about 1000 nm. In some embodiments, the nanostructures are roughly spherical in shape having an average diameter (or average maximum width for irregularly shaped nanostructures) of less than about 1000 nm. Typically, the average diameter (or average maximum width) is much smaller, e.g., less than about 100 nm, less than about 10 nm, or in the range of from about 1 nm to about 5 nm. For purposes of this disclosure, such roughly spherical nanostructures will be referred to as “nanoparticles.”
In other embodiments, the nanostructures are in the form of nanowires having an average diameter which is on the order of nanometers, i.e., in the range of from about 1 nm to about 1000 nm. Typically the average diameter is much smaller, e.g., less than about 100 nm, less than about 50 nm, or in the range of from about 10 nm to about 100 nm. The average length of the nanowires, which is greater than the average diameter of the nanowires, may be on the order of microns, e.g., in the range of from about 1 μm to about 10 μm. The nanowires may extend substantially vertically away from the surface of the underlying substrate.
In other embodiments, the nanostructures are in the form of nanoplates which are akin to flattened nanowires. Nanoplates may also be referred to as nanoflakes or nanosheets. The nanoplates may have an average thickness which is on the order of nanometers, i.e., in the range of from about 1 nm to about 1000 nm. Typically the average thickness is much smaller, e.g., less than about 100 nm, less than about 50 nm, or in the range of from about 10 nm to about 100 nm. The average length of the nanoplates, which is greater than the average thickness of the nanoplates, may be on the order of microns, e.g., in the range of from about 1 μm to about 10 μm. The average width of the nanoplates is typically also greater than the average thickness, but the average width may be on the order of nanometers, e.g., in the range of from about 100 nm to 1000 nm. Such nanoplates may adopt a porous pumice-like structure in which the nanoplates are randomly oriented and edges of neighboring nanoplates are merged to define a plurality of irregularly shaped cavities or pores dispersed throughout the structure.
Other nanostructures may be used, including branched nanostructures.
The selection of the underlying substrate may provide additional morphological elements to the ternary pyrite-phase transition metal phosphochalcogenide electrodes. By way of illustration, ternary pyrite-phase transition metal phosphochalcogenide nanoparticles disposed on a graphite substrate provides coated flakes having an average diameter or average maximum width on the order of microns, e.g., in the range of from about 1 μm to about 10 μm. Ternary pyrite-phase transition metal phosphochalcogenide nanowires disposed on a graphite substrate provides blooms composed of nanowires extending and radiating outwardly from a common center. The blooms may have an average diameter on the order of microns, e.g., in the range of from about 5 μm to about 20 μm. Ternary pyrite-phase transition metal phosphochalcogenide nanoplates disposed on carbon fiber paper provides coated elongated rods having an average diameter on the order of microns, e.g., in the range of from about 10 μm to about 20 μm.
The particular morphology of the ternary pyrite-phase transition metal phosphochalcogenide, the selection of the underlying substrate, and the average thickness or surface coverage of the ternary pyrite-phase transition metal phosphochalcogenide may be selected to maximize overall catalytic performance, facilitate hydrogen bubble nucleation and release and/or to minimize interference with the absorption of light by a semiconductor of the underlying substrate (if present).
The ternary pyrite-phase transition metal phosphochalcogenide electrodes may be made via thermal conversion of a transition metal-containing precursor disposed on a substrate in a chalcogen-phosphorous atmosphere. In one embodiment, a transition metal-containing precursor disposed on a substrate is exposed to a chalcogen-phosphorous atmosphere at an elevated temperature and for a period of time sufficient to convert the transition metal-containing precursor to the ternary pyrite-phase transition metal phosphochalcogenide. By way of illustration, a suitable range of temperature is from about 400° C. to about 700° C. and a suitable range of time is from about 5 minutes to about 2 hours for the thermal conversion. The temperature and time may depend upon the thickness of the film or layer or coating of the transition metal-containing precursor. The chalcogen-phosphorous atmosphere may further comprise an inert gas, e.g., argon. However, the chalcogen-phosphorous atmosphere may be substantially free of any air or oxygen. The chalcogen-phosphorous atmosphere may be formed by the thermal evaporation of a substantially 1:1 stoichiometric mixture of phosphorous and chalcogen elemental powders under an inert gas. Selection of the chalcogen depends upon the desired ternary pyrite-phase transition metal phosphochalcogenide. Any of the substrates described herein may be used.
The ternary pyrite-phase transition metal phosphochalcogenide electrodes may also be made by carrying out the thermal conversion reaction in solution in a suitable solvent, e.g., water in a hydrothermal environment or other high boiling point solvents. In this case, the temperature may be in the range of from about 150° C. to about 300° C.
Selection of the transition metal-containing precursor depends upon the desired ternary pyrite-phase transition metal phosphochalcogenide as well as the desired nanostructure or microstructure morphology. The transition metal-containing precursor may be a film of a transition metal, which may be deposited on a substrate. e.g., via thermal evaporation. Thermal conversion of the film of transition metal as described herein provides the substrate coated with ternary pyrite-phase transition metal phosphochalcogenide nanoparticles.
Alternatively, the transition metal-containing precursor may be a layer or a coating of transition metal-containing nanostructures, e.g., nanowires or nanoplates. By way of illustration, transition metal hydroxide carbonate hydrate nanowires may be grown on a substrate, e.g., via a hydrothermal growth technique. Thermal conversion of the transition metal hydroxide carbonate hydrate nanowires as described herein provides the substrate coated with ternary pyrite-phase transition metal phosphochalcogenide nanowires. As another illustration, transition metal hydroxide carbonate hydrate nanoplates may be grown via a two-step process. First, transition metal oxide nanoparticles may be deposited on a substrate, e.g., via dip-coating the substrate in an ink of the transition metal oxide nanoparticles. Second, the coated substrate may be subjected to the same hydrothermal growth technique described herein to grow transition metal hydroxide carbonate hydrate nanoplates on the substrate. Thermal conversion of the transition metal hydroxide carbonate hydrate nanoplates as described herein provides the substrate coated with ternary pyrite-phase transition metal phosphochalcogenide nanoplates. Other transition-metal containing nanostructures besides transition metal hydroxide carbonate hydrates may be thermally converted to ternary pyrite-phase transition metal phosphochalcogenide nanostructures using procedures described above. Such other transition-metal containing nanostructures may include transition metal oxides, oxyhyrdoxides, hydroxides, fluorides, chlorides, and bromides.
The electrochemical reactions to be catalyzed by the ternary pyrite-phase transition metal phosphochalcogenide electrocatalysts may be conducted in an electrochemical reaction system. The electrochemical reaction system may comprise a reaction cell configured to contain a fluid comprising an oxidant to be reduced; a ternary pyrite-phase transition metal phosphochalcogenide electrode immersed in the fluid; and a counter electrode. A membrane may be included to separate the ternary pyrite-phase transition metal phosphochalcogenide electrode and the counter electrode. Any of the ternary pyrite-phase transition metal phosphochalcogenide electrodes described herein may be used. The selection of fluid depends upon the particular electrochemical reaction to be catalyzed by the ternary pyrite-phase transition metal phosphochalcogenide. For the hydrogen evolution reaction, the fluid may be an aqueous electrolyte solution (e.g., a solution of water and a water-soluble electrolyte such as H₂SO₄), the oxidants may comprise hydrogen ions and the reduction product may comprise hydrogen gas. Various materials for the counter electrode may be used (e.g., graphite). The counter electrode may be immersed in the fluid. The counter electrode may be in electrical communication with the ternary pyrite-phase transition metal phosphochalcogenide electrode. The electrochemical reaction system may further comprise a collection cell configured to collect the reduction product from the reaction cell.
The electrochemical reaction system may further comprise a power source in electrical communication with the ternary pyrite-phase transition metal phosphochalcogenide electrode and the counter electrode, the power source configured to apply an electrical potential across the ternary pyrite-phase transition metal phosphochalcogenide electrode and the counter electrode in order to generate the free electrons for electrochemically inducing the reduction reaction.
Alternatively, or in addition, the electrochemical reaction system may further comprise a light source configured to illuminate at least a portion of the ternary pyrite-phase transition metal phosphochalcogenide electrode with light to generate the free electrons for photoelectrochemically inducing the reduction reaction. The light source may be selected to emit light having a wavelength capable of being absorbed by the selected semiconductor substrate of the ternary pyrite-phase transition metal phosphochalcogenide electrode to produce the free electrons. However, since the light source may simply be solar radiation an external light source may not be necessary.
Also provided are electrocatalysts in which arsenic is used in place of phosphorous in the ternary pyrite-phase transition metal phosphochalcogenide. The description of such electrocatalysts, electrochemical reaction systems comprising such electrocatalysts, methods of using such electrocatalysts and methods of making such electrocatalysts follows that described above with respect to the ternary pyrite-phase transition metal phosphochalcogenides, except that arsenic replaces phosphorous. Such compounds may be referred to as ternary pyrite-phase transition metal arsenochalcogenide electrocatalysts.

EXAMPLES

Example 1

Cobalt Phosphosulfide Electrocatalysts

Abstract

The scalable and sustainable production of hydrogen fuel through water splitting demands efficient and robust earth-abundant catalysts for the hydrogen evolution reaction (HER). Building on promising metal compounds with high HER catalytic activity, such as pyrite structure cobalt disulfide (CoS₂), and substituting non-metal elements to tune the hydrogen adsorption free energy has been shown in this example to lead to further improvements in catalytic activity. A combined theoretical and experimental study is presented in this example to establish ternary pyrite-type cobalt phosphosulfide (CoPS) as a high-performance earth-abundant catalyst for electrochemical and photoelectrochemical hydrogen production. Nanostructured CoPS electrodes achieved geometrical catalytic current density of 10 mA/cm²at overpotentials as low as 48 mV with outstanding long-term operation stability. Integrated photocathodes of CoPS on n⁺-p-p⁺ silicon micropyramids achieved photocurrents up to 35 mA/cm²at 0 V vs the reversible hydrogen electrode (RHE) and onset photovoltages as high as 450 mV vs RHE, and the most efficient solar-driven hydrogen generation from earth-abundant systems.

Introduction

As noted in the background, certain pyrite compounds have exhibited HER catalytic activity. However, there is no direct evidence for the active site(s) and mechanism responsible for the high HER catalytic activity of these pyrite compounds. Yet, strong similarities between the active metal centers of Fe-only hydrogenase^26,27and the reduced coordination environment of the intrinsic {100} pyrite surface²⁴suggest that the active sites are the square-pyramidal surface metal centers bridged by dichalcogenide dumbbells (FIG. 1b ). Such similarities may suggest that the HER mechanism of pyrite compounds could involve a distorted octahedral metal hydride. Thus, its stability and reactivity (hydricity) can be influenced by the electron-donating character of the chalcogen ligands (X)²⁸. Therefore, the inventors investigated whether the HER catalytic activity of metal chalcogenides could be improved through tuning the hydrogen adsorption free energy by changing the atomic components of the X₂ ²⁻ dumbbells, while still preserving the pyrite structure. Given the weaker electronegativity of phosphorus in comparison to sulfur and the absence of thermodynamically stable metal diphosphides under ambient conditions²⁹, this example presents the investigation of pyrite-type cobalt phosphosulfide (CoPS) as a novel ternary catalyst for HER.
Cobalt phosphosulfide was identified in the 1960s to be a pyrite compound analogous to the naturally occurring mineral cobaltite (CoAsS)³⁰, but its properties have not been investigated. The cubic crystal structure of CoPS can be visualized similarly to that of CoS₂(FIG. 1a ), but instead of Co²⁺ octahedra and S₂ ^2-dumbbells, CoPS has Co³⁺ octahedra and dumbbells with homogeneous distribution of P^2-and S⁻ atoms (FIG. 1c ), and a smaller lattice constant (a=5.422 Å vs. 5.538 Å for CoS₂). In contrast to CoS₂, which is a half-metal, CoPS has one less valence electron, making it a semiconductor isoelectronic to iron pyrite. Since the Co octahedra in CoPS contain P^2-ligands with higher electron-donating character than S⁻ ligands, the inventors investigated whether this ternary pyrite compound could have higher HER catalytic activity than CoS₂due to a more thermoneutral hydrogen adsorption at the active sites. Despite the potential for tunable electronic and chemical properties, ternary or more complex metal compounds, especially those containing different non-metal elements, have rarely been explored for electrocatalysis⁴. Herein the theoretical study of the hydrogen evolution activity for CoPS surface, the synthesis of CoPS nanostructures and their excellent performance toward HER electrocatalysis and solar-driven hydrogen production is reported for the first time.
Methods
Free Energy Calculations for Atomic Hydrogen Adsorption (ΔG_H*).
Chemisorption free energies were obtained for both CoS₂and CoPS using density functional theory (DFT) calculations. All calculations were performed using the Vienna Ab-initio Simulation Package (VASP)^46-48using the Perdew-Burke-Ernzerhof (PBE) GGA exchange-correlation functional and the projector augmented wave (PAW) method^49,50for describing the interaction between core electrons and valence electrons. All calculations were run with an energy cut-off of 280 eV, normal precision, Methfessel-Paxton smearing, and accounting for spin polarization. The Brillouin zone was sampled with a 9×9×1 Monkhorst-Pack grid. The experimentally reported crystal structure of CoPS consists of S and P disordered lattice (a=5.422 Å, ICSD collection code #62414)³⁰. A simple model of CoPS was obtained by substituting each dumbbell within the unit cell with P and S atoms and adjusting the lattice constant to match the experimental value of CoPS. Chemisorption was modeled on the CoS₂(a=5.5388 Å, ICSD collection code #86351) and CoPS {100} surfaces, while ensuring a stable surface termination where the dichalcogenide dumbbells remain intact. The resulting slab model consists of four layers, separated by an approximately 10 Å vacuum gap. For the resulting surface unit cell, adsorption of a single H atom onto Co corresponds to half coverage. Chemisorption energies of atomic hydrogen were calculated relative to H₂(g) by:
$Δ E = E (surf + nH) - (E (surf) + \frac{1}{2} E (H_{2}))$
All structures were relaxed to a tolerance of less than 0.1 eV/Å. The associated free energy of chemisorption was then calculated by correcting for both the zero point vibrational energy and the loss of translation entropy of H₂(g) upon adsorption, and neglecting the smaller vibrational entropy terms. The zero point contributions for CoS₂and CoPS are essentially identical, yielding ΔG=ΔE+0.29 eV.
Synthesis of Cobalt Precursor Materials.
Co Films.
The Co films were prepared on graphite disk substrates (6.0 mm (d)×1 mm (t), Ultra Carbon Corp., Ultra “F” Purity) and borosilicate glass substrates by electron-beam evaporating 100 nm Co (Kurt J. Lesker, 99.95%) onto the substrate at 1 Å s⁻¹deposition rate.
CHCH Nanowires (NWs).
The graphite substrates were first treated by annealing in air at 800° C. for 10 min to improve the surface hydrophilicity. Then cobalt hydroxide carbonate hydrate (CHCH, Co(OH)(CO₃)_0.5.xH₂O) NWs were synthesized on these graphite substrates by following a published procedure¹⁰with minor modifications. In a typical synthesis, 1.5 mmol of Co(NO₃)₂.6H₂O, 3 mmol NH₄F (Sigma-Aldrich, ≧98.0%), and 7.5 mmol (NH₂)₂CO (Riedel-de Haën, 99.5-100.5%) were dissolved in 50 mL of distilled water. Then, 16 mL of this solution was transferred to a 23-mL PTFE-lined stainless steel autoclave containing the graphite substrate, which was sealed and heated at 110° C. for 5 h. After cooling, the substrate was removed, rinsed with ethanol and water, and dried under a stream of nitrogen.
CHCH Nanoplates (NPIs).
Cobalt hydroxide carbonate hydrate (Co(OH)(CO₃)_0.5.xH₂O, “CHCH”) nanoplates (NPIs) were synthesized on carbon fiber paper (Toray Paper 060 from Fuel Cell Earth. Teflon Treated. Thickness 0.19 mm) that has been treated by annealing in air at 800° C. for 10 min to make it hydrophilic. The NPIs were synthesized in a two-step process. In the first step, cobalt oxide (CoO) nanoparticles were deposited on the substrate (1 cm×3 cm) following a published procedure¹¹with slight modifications. In a typical synthesis, 0.4 g cobalt (II) nitrate hexahydrate and 0.05 g polyvinylpyrrolidone (PVP) were dissolved in 0.55 g dimethylformamide (DMF) under vigorous stirring at 80° C. for 2 h to make an ink. A treated carbon paper substrate was dip-coated in the ink and then dried under a stream of nitrogen. The substrate was then placed in the center of a fused silica tube (1 inch O.D.) heated to 600° C. in a tube furnace (Lindberg/Blue M) at a pressure of 100 mTorr and a 50 sccm argon flow rate. In the second step, the cobalt oxide nanoparticle-coated carbon fiber paper was used as the substrate in the CHCH synthesis described above to result in the formation of NPIs instead of NWs.
Synthesis of CoPS Nanostructures.
An alumina boat containing 1 g of a 1:1 mixture of sulfur (Sigma-Aldrich, 99.5-100.5%) and phosphorus (Alfa Aesar, 98.9%) powders was covered with a piece of glass and placed in the center of a fused silica tube reactor equipped with pressure and gas flow controllers and heated in a tube furnace (Lindberg/Blue M). The Co film, CHCH NW and CHCH NPI precursor substrates were placed on an alumina plate (4 mm thick) at the downstream end of the tube, outside of the heating area of the furnace. After the tube was purged with Ar carrier gas (99.999%) at 25 sccm and 780 Torr, the furnace was first heated to 200° C. for 10 min, then opened and allowed to cool naturally to make a thiophosphate (P_xS_y) paste-like product in the alumina boat. Then, without opening the tube to atmosphere, by manipulating a magnetic stir bar inside the reactor, the cover was taken off of the alumina thiophosphate precursor boat, the boat was moved to the upstream edge of the furnace, and the cobalt precursor substrates were moved to the center of the furnace. The furnace was then heated to 500° C. for 1 h to covert these precursors to CoPS before the furnace was cooled down naturally.
Synthesis of Films and Nanowires of CoP_x, CoP_x|H₂S, CoP_x|S, CoS₂|P and CoS₂|P+H₂as Comparative Samples.
CoP_xFilm and NWs.
The synthesis of highly catalytic CoP_xmaterial with a predominant CoP composition and a minor CoP₂phase was achieved via thermal conversion of 100 nm thick Co film on borosilicate glass or graphite disk and CHCH NWs on graphite disk at 500° C. for 45 min in a phosphorus (0.3 g of red phosphorus in an alumina crucible at ˜425-450° C.) and hydrogen gas (25 sccm Hz and 25 sccm argon gas) atmosphere.
CoP_x/H₂S and CoP_x/S Film and NWs.
The CoP_x|H₂S and CoP_x|S film and NW samples were prepared by thermal annealing of CoP_xfilm and CoP_xNWs on borosilicate glass or graphite disk at 500° C. for 20 min in a sulfur (saturated) or hydrogen sulfide (25 sccm 10% H₂S in helium and 25 sccm argon gas) atmosphere.
CoS₂/P and CoS₂/P+H₂Film and NWs.
The CoS₂|P and CoS₂|P+H₂film or NW samples were prepared by thermal annealing of CoS₂film and CoS₂NWs on borosilicate glass or graphite disk¹⁰at 500° C. for 20 min in a phosphorus (0.3 g of red phosphorus in an alumina crucible at ˜425-450° C.) or phosphorus and hydrogen gas (25 sccm H₂and 25 sccm argon gas) atmosphere.
Structural Characterization.
The as-prepared CoPS film and CoPS NWs on graphite substrates, and CoPS NPIs on carbon fiber paper and other comparison samples were characterized using a LEO SUPRA 55 VP field-emission scanning electron microscope (SEM) with energy dispersive spectroscopy (EDS) capabilities, and a Bruker D8 ADVANCE powder X-ray diffractometer (PXRD) using Cu Kα radiation. Note that the PXRD patterns for CoPS film and various other thin film samples were taken using borosilicate glass as substrate. Raman spectra were taken using a Thermo Scientific DXR confocal Raman microscope using a 532 nm excitation laser. High-resolution XPS measurements for Co 2p were taken using a Thermo Al Kα XPS with a 180° double focusing hemispherical analyzer and 128-channel detector (60° angular acceptance), which under effective operating conditions had an analyzer resolution of 0.8 eV. All X-ray photoelectron spectra were shifted so that the adventitious carbon Cis peak was at 284.8 eV. S 2p peaks were fitted using doublets with a 1:0.5 (3/2p:1/2p) area ratio, 1.18 eV apart, and with the same full width at half maximum (FWHM). P 2p were fitted using doublets with a 1:0.5 (3/2p:1/2p) area ratio, 0.87 eV apart, and with the same FWHM.
Electrochemical Characterization of Catalytic Activity Toward HER.
All electrochemical measurements were performed in a three-electrode configuration using a rotating disk electrode (RDE) setup (Bioanalytical Systems, Inc.; RDE-2) and recorded using a Bio-Logic SP-200 potentiostat. Each measurement was performed in 0.5 M H₂SO₄(aq) electrolyte continuously purged with H₂(g) (99.999%) using a saturated Hg/HgSO₄reference electrode (CH Instruments), a graphite rod (National Carbon Co., AGKSP Spectroscopic Electrode) as the counter electrode, and a CoPS film, NW, or NPI or other sample substrate affixed to a glassy carbon RDE tip using silver paint (Ted Pella, PELCO colloidal silver) as the working electrode. Graphite paint (Ted Pella, PELCO isopropanol based graphite paint) was further used to isolate the silver paint contact from the electrolyte solution. Linear sweep voltammograms were measured from open circuit voltage at a scan rate of 2 mV/s, while the working electrode was rotated at 2000 RPM. The Hg/HgSO₄reference electrode was calibrated against the reversible hydrogen potential (RHE) using a platinum wire (Kurt J. Lesker, 99.99%; 0.50 mm diameter) as the working and a platinum mesh as the counter electrodes after each measurement. The Pt reference trace was recorded using a Pt wire as the working electrode. All polarization curves were corrected for iR losses unless otherwise noted. Electrochemical impedance spectroscopy was performed in potentiostatic mode at 0 V vs RHE, applying a sinusoidal voltage with an amplitude of 10 mV and scanning frequency from 250 kHz to 1 mHz.
Fabrication of n⁺-p-p⁺ Micropyramid Silicon Substrates Coated with CoPS Films.
Micropyramid silicon arrays were fabricated on both sides of 150 μm-thick p-type (100) Si wafers (dopant concentration of 5×10¹⁵cm⁻³) by electrodeless chemical etching in a solution of potassium hydroxide (KOH, 45 vol %) and isopropyl alcohol (IPA). 300 nm of n⁺ emitter layer (dopant concentration of 9×10¹⁹cm⁻³) was formed by the thermal diffusion processes of POCl₄at 1000° C. 300 nm of p⁺ back surface field layer (dopant concentration of 3×10²⁰cm⁻³) was fabricated by screen printed Al annealed at 500° C. Cobalt films of varying thicknesses were deposited on planar p-type silicon (resistivity of 1-2.5 Ω-cm, B doped, (100) orientation, prime grade, 525 μm thickness) and n⁺-p-p⁺ micropyramid silicon substrates by electron-beam evaporating cobalt (Kurt J. Lesker, 99.95%) at 0.1 Å/s deposition rate. Then the cobalt films were converted to CoPS using the procedure described above except that an alumina boat containing 200 mg of 1:1 mixture of sulfur and phosphorus powders was used and, in the last step, the furnace was heated to 450° C. for 10 min.
Photoelectrochemical Characterization.
The photoelectrochemical characteristics were measured in a three-electrode configuration under simulated 1 Sun irradiation (100 mW/cm²) supplied by 1 kW Xe lamp solar simulator (Newport Corp. Model 91191: AM 1.5G filter) using a Bio-Logic SP-200 potentiostat. The light intensity was calibrated with a Si photodiode (Thorlabs) to generate a photocurrent equal to that at 100 mW/cm²light intensity. All measurements were performed in 0.5 M H₂SO₄electrolyte constantly purged with H₂gas (99.999%), using a graphite rod (National Carbon Co., AGKSP Spectroscopic Electrode) as the counter electrode, and a saturated Hg/HgSO₄reference electrode (CH Instruments). The Hg/HgSO₄reference electrode was calibrated against the reversible hydrogen potential using a platinum wire as the working and a platinum mesh as the counter electrodes after each measurement. The electrolyte was vigorously stirred to minimize mass transport limitations and remove accumulated hydrogen gas bubbles on the electrode surface. The current density vs potential (J-V) curves were measured at a scan rate of 10 mV/s and were not corrected for any uncompensated resistance losses or any other extrinsic losses.
Results and Discussion
Hydrogen evolution activity has been shown to be strongly correlated with the chemisorption energy of atomic hydrogen to the electrocatalyst surface³¹. Density function theory (DFT) was used to calculate the free energy for atomic hydrogen adsorption (ΔG_H*) on the {100} surface of CoPS in comparison to CoS₂(see Methods for details), to evaluate whether CoPS is a promising HER catalyst. The main results are shown in FIG. 1d . The ΔG_H*for hydrogen adsorption at the Co sites of CoPS is more favorable in comparison to CoS₂. Moreover, DFT calculations show that after spontaneous hydrogen adsorption at open P sites (FIG. 1d ), the ΔG_H*at the adjacent Co sites becomes spontaneous and almost thermoneutral (FIG. 1d ), reaching a ΔG_H*comparable to that of platinum³¹. This dramatic change in ΔG_H*can be attributed to a reduction of Co³⁺ sites to Co²⁺ upon hydrogen adsorption at an adjacent open P site, which then enables the oxidation of Co²⁺ sites back to Co³⁺ upon subsequent hydrogen adsorption. An analogous change in the ΔG_H*for CoS₂was not observed since adsorption at Co sites was found to be more favorable than open S sites. Therefore, DFT calculations support the concept of CoPS as a very promising earth-abundant HER catalyst.
CoPS electrodes were synthesized through conversion of cobalt-based nanostructured precursor materials at 500° C. in a thiophosphate (P_xS_y) atmosphere produced by the thermal evaporation of a 1:1 stoichiometric mixture of phosphorus and sulfur elemental powders under an argon atmosphere (see Methods for detail). The homogenous reaction with both phosphorus and sulfur was optimized by melting the elemental powder mixture in a crucible first at 200° C. for 5-10 min under argon atmosphere and then carrying out the thermal conversion right away with preloaded cobalt precursors without air exposure to the highly hydroscopic paste-like P_xS_y. CoPS films and CoPS nanowires (NWs) were synthesized using thermally evaporated 100 nm thick cobalt films and hydrothermally grown cobalt hydroxide carbonate hydrate [CHCH, Co(OH)(CO3)0.5.xH2O] NWs³²as precursor materials on graphite disk substrates. Graphite was used as a convenient conductive substrate, however. CoPS films and CoPS NWs can be synthesized on other substrates compatible with the thermal conversion conditions (such as borosilicate glass). Scanning electron microscopy (SEM) (FIG. 2a ) shows the polycrystalline CoPS film with particle sizes of roughly 5 nm (FIG. 2a , inset) obtained upon conversion of 100 nm thick cobalt film on graphite. The flake-like appearance of the CoPS film is due to the native roughness of the graphite substrate, which was purposely used to enhance the mechanical stability and surface area of CoPS film. Conversion of the CHCH NWs at 500° C. results in CoPS NWs with identical morphology, but with a polycrystalline structure and similar particle size to CoPS film samples (FIG. 2b ). High surface area CoPS nanoplates (NPIs) were converted from CHCH NPIs grown on carbon fiber paper substrate (FIG. 2c, 2d ). The CHCH NPIs were synthesized using the same procedures for CHCH NWs³², but using carbon paper substrates that were precoated with cobalt oxide (CoO) nanoparticles (see Methods for detail)¹¹. FIG. 2c shows that the CHCH NPIs thoroughly and uniformly cover the carbon fibers and efficiently utilize the high surface area of the carbon paper. Similar to the case of CoPS NWs, thermal conversion at 500° C. results in polycrystalline CoPS NPIs (FIG. 2d ).
The crystal structure and stoichiometry of these nanostructures were first characterized. Energy dispersive X-ray spectrometry (EDS) revealed the presence of cobalt, phosphorus, and sulfur in elemental compositions of CoP_0.83S_1.35, CoP_0.88S_1.07, and CoP_1.02S_0.97, respectively, for the CoPS film, CoPS NW, and CoPS NPI electrodes (FIG. 2e ). The apparent better stoichiometry of CoPS NPIs can be attributed to the presence of excess thiophosphates (P_xS_y), which will be evident from the discussion of the powder X-ray diffraction (PXRD) patterns. Confocal micro-Raman spectra (FIG. 2f ) show two peaks at ˜322 cm⁻¹and 427 cm⁻¹for all CoPS samples. These Raman peaks correspond to the characteristic active modes of libration (E_g) and in-phase stretch (A_g) for the chalcogenide dumbbells in a pyrite crystal lattice. In comparison to the peaks for CoS₂(vertical dash lines in FIG. 2f ), the Raman peaks for CoPS electrodes are blue-shifted which can be attributed to the smaller unit cell of CoPS. The presence of only one set of E_gand A_gpeaks suggest a ternary CoPS compound rather than a mixture of two solid phases, in contrast, two sets of Raman peaks corresponding to CoPS and CoS₂were observed when unsuccessful thermal conversion was carried out using a 1:3 phosphorus to sulfur ratio (data not shown)³³, which further supports that the obtained CoPS products are indeed a distinctive ternary alloy phase. X-ray photoelectron spectroscopy (XPS) measurements showed an absence of multiplet splitting of the cobalt 2p peak for CoPS film in comparison to CoS₂film (data not shown), which indicates a spin paired electronic configuration for cobalt and an oxidation state of Co³⁺ in CoPS^34,35. Therefore, XPS also supports that the obtained CoPS products are indeed a distinctive ternary alloy phase. The PXRD patterns (FIG. 2g ) of the film, NWs and NPIs can be indexed to phosphorus-deficient pyrite-type CoPS phase, since the diffraction peaks match the simulated pattern for cubic CoPS (space group Pa-3, a=5.422 Å, ICSD collection code #62414), but are very slightly shifted toward the standard pattern of CoS₂(a=5.538 Å, JCPDS #41-1471). Refinement of the lattice parameter revealed a lattice constant of a=5.44 Å, which suggests a stoichiometry of ˜CoP_0.84S_1.16based on Vegard's law. The PXRD patterns for CoPS film and NWs are in agreement with the phosphorus deficiency suggested by the EDS spectra, while the PXRD pattern for CoPS NPIs indicates that its apparent EDS stoichiometry can be attributed to the presence of excess P_xS_y. Phosphorus deficiencies in CoPS samples could be a result of the preferential formation and stability of sulfur-rich P_xS_y ³⁶precursor species and the different diffusivity of elements at the synthetic temperature of 500° C.
The electrochemical characteristics of the CoPS film, CoPS NW and CoPS NPI electrodes corresponding to the HER catalytic performance were measured using 0.5 M H₂SO₄and rotating disk electrode (RDE) at a rate of 2000 rpm, in comparison to platinum wire (see Methods for detail). FIG. 3a shows that these CoPS electrodes achieved geometric current densities of −10 mA/cm²at very low overpotentials of −128 mV, −61 mV and −48 mV vs the reversible hydrogen electrode (RHE), respectively. They also exhibited outstanding long-term operation stability beyond 36 h (FIG. 3b ) and little change in the film morphology (data not shown). In comparison, high density CoS₂NWs¹⁰on graphite and high surface area CoSe₂nanoparticles on carbon fiber paper¹¹have been reported to achieve −10 mA/cm²at overpotentials of −145 mV and −180 mV vs RHE. The CoPS electrodes also show lower catalytic overpotential than non-pyrite structure metal phosphides, such as CoP (−75 mV at 10 mA/cm²)¹²and Ni₂P (−115 mV at 10 mA/cm²)¹⁴suggesting that ternary pyrite structure-type CoPS is an outstanding HER catalyst. From the extrapolation of the linear region of a plot of overpotential vs log J (FIG. 3c ), the Tafel slopes of 48, 56, and 57 mV/decade were obtained for CoPS film. NW and NPI electrodes, respectively. Such Tafel slope values suggest a two electron transfer process following a Volmer-Tafel mechanism of bimolecular adsorption and hydrogen evolution (theoretical slope of 45 mV/decade)³¹. From the intercept of the linear region of the Tafel plots, exchange current densities (J_{0,geometrical}) of 56 μA/cm², 554 μA/cm², and 984 μA/cm²were obtained for CoPS film, CoPS NWs and CoPS NPIs electrodes. The exchange currents for CoPS electrodes are 1-2 orders of magnitude larger than those observed for CoS₂ ¹⁰and CoSe₂ ¹¹materials, which explains the better HER catalytic performance of CoPS. Furthermore, films and NWs of CoP with minor CoP₂phase impurity (CoP_x), CoP_x|S, CoP_x|H₂S, CoS₂|P and CoS₂|P+H₂were prepared (see Methods for details) and PXRD and XPS characterization was carried out (data not shown). HER electrochemical measurements were also conducted (data not shown) in comparison with the CoPS samples. Table 2 provides a summary of the electrochemical properties of CoPs, CoP_x|H₂S, CoP_x|S, CoS₂|P and CoS₂|P+H₂electrodes in comparison with CoPS electrodes. These experiments unequivocally demonstrate that the catalytic HER performance of CoPS electrodes can be attributed exclusively to this ternary pyrite structure-type compound, instead of potential cobalt phosphide impurities or anion substituted doping on the surface of CoPS. Therefore, these CoPS nanostructures are the most catalytically active pyrite-type materials and among the very best earth-abundant catalysts' that have been reported to date for HER catalysis.
To understand the origin of the differences in the overall catalytic performance among CoPS electrodes, their relative electrochemically active surface areas were estimated using cyclic voltammetry measurements by extracting the double layer capacitance (C_dl) (FIG. 3d )¹⁰. The geometrical exchange current densities were then normalized to compare HER performance relative to the electrochemically active surface area. As shown in Table 1, the relative surface areas for CoPS NWs and CoPS NPIs are 1.71 and 10.1 times larger than CoPS film, respectively. The normalized exchange current (J_0,normalized) for CoPS NW electrode is larger than the J_0,normalizedfor CoPS film (data not shown), indicating that the higher catalytic activity of CoPS NWs can be mainly attributed to the larger surface area. On the other hand, the J_0,normalizedof CoPS NPIs is smaller than that of CoPS film despite a surface area ˜10 times larger and similar Tafel slope, which suggests a reduction in the turnover rate per active site. This is likely caused by a mass-transport limited³⁷HER catalytic activity for CoPS NPIs at a RDE rate of 2000 rpm. Circuit model fitting analysis of the electrochemical impedance spectroscopy (EIS) for the CoPS film and CoPS NWs (FIG. 3e ) shows that both electrodes can be modeled using a modified Randles circuit consisting of a series resistance (R_S), constant phase element (CPE), charge transfer resistance (R_CT), and modified mass-transport impedance element (Ma). In contrast, the EIS of the CoPS NPIs (FIG. 3f ) can be fitted using just R_Sand Ma, which is indicative of mass transport control caused by a negligible charge transfer resistance and a very high surface area. Qualitatively, it was observed that the semicircular arc corresponding to CPE and R_CTimpedance elements seen for the CoPS film significantly decreases for CoPS NWs and completely disappears for CoPS NPIs. Also observed was a significant reduction in the overall impedance following the same trend. All of these indicate that the R_CTdecreases with increasing surface area. The moderate increase in HER catalytic performance seen in the CoPS NPI electrode in comparison to the CoPS film electrode despite a much larger surface area can be explained by a mass-transport limited HER performance for the CoPS NPIs. In other words, the HER catalytic reaction is so efficient such that the diffusion of H⁺ ions cannot keep up with the reaction over the large surface area of CoPS NPI electrode, leading to a reduction in the exchange current per surface area or active site, which benefits the long-term operation stability. Therefore, CoPS NPIs represent an upper bound for the effects of surface area on enhancing the overall electrocatalytic performance of CoPS.
Given the high electrocatalytic activity of CoPS toward HER, CoPS as a catalyst together with p-type silicon photocathodes was further studied for solar-driven hydrogen production. The direct integration of catalysts with homogenously doped semiconductors places strong requirements for the intrinsic electronic and optical properties of the catalyst²⁰. For example, a high absorption coefficient and a very anodic surface work function for a catalyst can affect the light absorption and band bending of the semiconductor. Therefore, in the fabrication of CoPS electrocatalysts and silicon cathodes for PEC HER, the interfacial properties and CoPS layer thickness must be considered. CoPS/p-Si photocathodes were first fabricated by thermal conversion of a 10 nm cobalt film evaporated on planar p-type silicon. However, the J-V curve of CoPS/p-Si (FIG. 4a ) shows no photoresponse and characteristics similar to those of CoPS electrodes. Such J-V characteristics suggest the formation of an ohmic junction, which can be attributed to an accumulation band bending induced by the work function of CoPS or the formation of interfacial defect states.
To eliminate the influence of the CoPS catalyst layer on the silicon band bending, the surface of p-type silicon was doped degenerately n-type (n⁺) to obtain an optimized and “fixed” surface depletion region³⁸. The surface of the n⁺-p-silicon substrate was further nanostructured into micropyramids to enhance light harvesting^39,40. Furthermore, the back of the silicon substrates was doped degenerately p-type (p⁺) to improve the majority carrier collection. FIG. 4b, 4c show a top-down and cross-section view of a CoPS/n⁺-p-p⁺ micropyramid silicon photocathode prepared by thermal conversion of an evaporated 10 nm thick cobalt film at 450° C. The PEC J-V curves of various CoPS/n⁺-p-p⁺-Si photocathodes with different initial cobalt thicknesses (FIG. 4a ) show the highest catalytic onset potential due to CoPS. The best CoPS/n⁺-p-p⁺-Si photocathode, which was prepared by thermal conversion of a 10 nm cobalt film, achieved a photocurrent density of 0.5 mA/cm²at a potential of 440 mV vs RHE, a J_SCof 26 mA/cm², and a fill factor of 40%. This corresponds to an overall Faradaic solar-to-hydrogen production efficiency of 4.7%. These are the highest photovoltage onset and efficiency reported so far for any earth-abundant catalyst directly integrated with p-silicon^41-43or n⁺-p silicon^44,45. In comparison, 5 nm Pt/n⁺-p-p⁺-Si photocathode achieved 0.5 mA/cm²at a potential of 530 mV vs RHE and a J_SCof 36 mA/cm². The difference in onset voltage of ˜80 mV can be attributed to the difference in catalytic activity between CoPS and Pt, while the lower J_SCsuggests that part of the incoming light was blocked by the CoPS catalyst layer. An optical absorbance spectrum of such a CoPS layer was obtained (data not shown). When the thickness of the cobalt precursor film was reduced to 7.5 and 5 nm, the J_SCof the photocathode increased to ˜33-35 mA/cm². However, the onset voltage also decreased, which suggests a higher light intensity reaching the semiconductor but a less complete CoPS catalyst coverage. On the other hand, when a 15 nm cobalt layer was used as precursor, both the J_SCand onset voltage decreased while the rectifying behavior was preserved, suggesting that much less light reached the semiconductor due to an increased light absorption from the thicker CoPS film. These trends clearly show that optimization of the catalyst thickness and coverage is important to balancing the light absorption and catalytic performance to maximize the PEC performance^20,42.
A further description of the supplementary data obtained, but not shown, is provided below.
XPS measurements of Co 2p, P 2p and S 2p for CoP_xin comparison to CoPS and CoS₂demonstrated that all the surface chemical species for CoPS are different from CoP_xand CoS₂. For CoP_x, main peaks and minor peaks corresponded to bulk CoP and surface CoP₂layer. These XPS results clearly show that the surface of CoPS catalyst does not contain minor CoP or CoP₂chemical species.
Powder X-ray diffraction (PXRD) patterns for CoP_x, CoP_x|H₂S and CoP_x|S were obtained in comparison with the standard patterns for CoP (Pnma, a=5.076 Å, b=3.277 Å, c=5.599 Å, JCPDS #65-2593), CoP₂(P2_l/c, a=5.61 Å, b=5.591 Å, c=5.643 Å, JCPDS #26-0481) and CoS₂(Pa-3, a=5.538 Å, JCPDS #41-1471). All PXRD peaks for CoP_xand CoP_x|H₂S can be indexed to CoP and CoP₂phase. On the other hand, PXRD peaks for CoP_x|S can be indexed to CoP₂and CoS₂phase.
X-ray photoelectron spectroscopy (XPS) measurements of Co 2p, S 2p and P 2p peaks for CoP_x, CoP_x|H₂S and CoP_x|S film on graphite were obtained. In CoP_x|S the Co 2p peak fitting is quite complex, however, it was seen by comparison with the XPS measurements described above that the main Co 2p peak supports the presence of CoS₂on the surface. The P 2p peak and S 2p peak for CoP_x|S showed a high concentration of metaphosphides and polysulfide species. On the other hand, Co 2p and P 2p species for CoP_x|H₂S resembled the chemical species for CoP_x, but were slightly shifted towards higher binding energies suggestive of doping. CoP_x|H₂S also showed the absence of polysulfide chemical species for the S 2p peak. Overall, the surface chemical species for CoP, S or CoP_x|H₂S does not resemble any chemical species seen for CoPS.
The electrochemical characteristics of the CoP_x, CoP_x|H₂S and CoP_x|S film and NW electrodes (on graphite) corresponding to the HER catalytic performance were measured using 0.5 M H₂SO₄and rotating disk electrode (RDE) at a rate of 2000 rpm, in comparison to CoPS film and CoPS NWs. Data showed that the HER catalytic performance of CoPS electrodes was superior to CoP_x, CoP_x|H₂S and CoP_x|S electrodes for the respective electrode morphology (film or NWs). CoP_x|H₂S electrodes showed a small improvement in HER catalytic performance in comparison to CoPs electrodes which can be attributed to anion substitution doping. In contrast, CoP_x|S electrodes showed a significant decrease in performance that could be attributed to the presence of CoS₂, metaphosphides and polysulfides on the electrode surface. These results for the HER catalytic performance of CoP_x, CoP_x|H₂S and CoP_x|S electrodes (summarized in Table 2) demonstrate that the high catalytic activity of CoPS electrodes cannot be explained by a hypothetical presence of CoP-related minor phases. Furthermore, these results demonstrate that the synthetic approach is a unique strategy for preparing ternary-pyrite cobalt phosphosulfide (CoPS) HER catalyst since the synthesis of this ternary compound cannot be achieved through anion substitution doping strategies for CoP_x.
Powder PXRD patterns for CoS₂, CoS₂|P and CoS₂|P+H₂were obtained in comparison with the standard patterns for CoP (Pnma, a=5.076 Å, b=3.277 Å, c=5.599 Å, JCPDS #65-2593), CoP₂(P2₁/c, a=5.61 Å, b=5.591 Å, c=5.643 Å, JCPDS #26-0481), Co_1-xS (P6₃/mmc, a=3.38 Å, b=3.38 Å, c=5.185 Å, JCPDS #42-0826) and CoS₂(Pa-3, a=5.538 Å, JCPDS #41-1471). The PXRD pattern for CoS₂|P showed mostly CoS₂diffraction peaks. While the PXRD pattern for CoS₂|P++H₂showed mostly CoS₂, and some minor Co_1-xS and CoP diffraction peaks.
XPS measurements of Co 2p, S 2p and P 2p for CoS₂|P and CoS₂|P+H₂film on graphite were obtained in comparison with CoPS. In CoS₂|P, the Co 2p and P 2p peaks resembled CoPs, but the P 2p peak showed a high concentration of metaphosphides. The bulk S 2p species for CoS₂|P were significantly shifted towards lower binding energy in comparison to CoS₂. On the other hand, Co 2p, P 2p and S 2p species for CoS₂|P+H₂suggested the formation of a surface CoP_xlayer, primarily due to the similarities between the main P 2p species for CoS₂|P+H₂and the minor P 2p species for CoP_x. Overall, the surface chemical species for CoS₂|P and CoS₂|P+H₂did not resemble those seen for the ternary compound CoPS.
The electrochemical characteristics of the CoS₂|P+H₂and CoS₂|P film and NW electrodes (on graphite) corresponding to the HER catalytic performance were measured using 0.5 M H₂SO₄and rotating disk electrode (RDE) at a rate of 2000 rpm, in comparison with CoPS film and CoPS NWs. Data showed that the HER catalytic performance of CoPS electrodes was superior to CoS₂|P+H₂and CoS₂|P electrodes for the respective electrode morphology (film or NWs). CoS₂|P+H₂electrodes showed HER catalytic performance very similar to the CoP_xelectrodes which can be attributed to the presence of CoP_xphases at the surface. In contrast, CoS₂|P electrodes showed significantly lower HER catalytic performance in comparison to CoS₂|P+H₂electrodes, which can be attributed to the high concentration of metaphosphides on the electrode surface. These results for the HER catalytic performance of CoS₂|P+H₂and CoS₂|P electrodes (summarized in Table 2) also indicate that the high catalytic activity of CoPS electrodes cannot be explained by a hypothetical presence of CoP-related minor phases. Furthermore, these results demonstrate that the synthetic approach is a unique strategy for preparing the outstanding ternary-pyrite cobalt phosphosulfide HER catalyst since the synthesis of this ternary compound cannot be achieved readily through anion substitution doping strategies for CoS₂.

Conclusion

In conclusion, pyrite-type cobalt phosphosulfide (CoPS) has been shown to be a novel high-performance earth-abundant catalyst for robust electrochemical and solar-driven hydrogen production. The electrocatalytic performance of this novel pyrite-type ternary material can be further enhanced through the synthesis of high surface area CoPS nanowires and nanoplates on conducting graphite or carbon fiber paper substrates using a simple thermal conversion reaction. These CoPS nanostructures achieved stable catalytic performance superior to that reported for metal chalcogenides (especially the parent metal pyrites) and metal phosphides, and are among the most active earth-abundant HER catalysts reported to date. These results illustrate that in addition to a high concentration of available catalytic sites, controlling the hydrogen adsorption energy of the active sites by tuning their electronic structure and reactivity by substituting non-metal atomic constituents in ternary or more complex compounds can serve as a new and general strategy to enhance the electrocatalytic activity of transition metal compounds. Furthermore, CoPS-based photocathodes fabricated by direct growth of CoPS on n⁺-p-p⁺ micropyramid silicon achieved competitive performance for solar-driven hydrogen production in comparison to Pt/n⁺-p-p⁺-Si photocathodes. The photoelectrochemical studies also show that both the work function and light absorption of the surface catalyst layer in integrated devices are crucial factors for achieving efficient solar-driven hydrogen generation.

TABLE 1

Summary of the electrochemical properties of CoPS electrodes with different morphologies.

	η (mV vs	η (mV vs.
	RHE) for	RHE) for					Relative
	J = −10	J = −20	R_s	Tafel slope	J_{0, geometrical}	C_dl	Surface	J_{0, normalized}
Sample	mA/cm²	mA/cm²	(Ω cm²)	(mV/decade)	(μA/cm²)	(mF/cm²)	Area	(μA/cm²)

CoPS film	−128	−145	2.64	57	56	9.84	1.00	56
CoPS NWs	−61	−75	1.30	48	554	16.9	1.72	90
CoPS NPls	−48	−65	1.42	56	984	99.6	10.1	38

TABLE 2

Summary of the electrochemical properties of CoP_x, CoP_x\|H₂S,
CoP_x\|S, CoS₂\|P and CoS₂\|P + H₂electrodes in comparison with CoPS electrodes.

	η (mV vs	η (mV vs
	RHE) for	RHE) for
	J = −10	J = −20	Rs	Tafel slope	J_{0, geometrical}
Sample	mA/cm²	mA/cm²	(Ω cm²)	(mV/decade)	(μA/cm²)

CoPS NWs	−61	−75	1.30	48	554
CoPS film	−128	−145	2.64	57	56
CoP_xNWs	−85	−102	0.92	56	294
CoP_xFilm	−150	−169	1.12	63	41
CoP_x\|H₂S NWs	−81	−96	0.90	50	244
CoP_x\|H₂S Film	−148	−165	1.17	55	21
CoP_x\|S NWs	−136	−158	0.88	69	105
CoP_x\|S Film	−202	−220	1.10	64	7.4
CoS₂\|P NWs	−131	−152	1.02	72	152
CoS₂\|P Film	−193	−214	1.18	70	18
CoS₂\|P + H₂NWs	−87	−104	0.93	56	273
CoS₂\|P + H₂Film	−143	−161	1.17	59	37

Example 2

Cobalt Phosphoselenide Electrocatalysts

The procedures in Example 1 were followed to synthesize and test pyrite-phase cobalt phosphoselenide, CoPSe. This electrocatalyst was found to achieve an electrocatalytic current density of 10 mA/cm²at an overpotential of 122 mV and a Tafel slope of 64.6 mV/dec.

Example 3

Nickel Phosphoselenide Electrocatalysts

Introduction

In this Example, the synthesis of pyrite-phase nickel phosphoselenides was investigated and a series of NiP₂, Se-doped NiP₂, P-doped NiSe₂, and NiSe₂nanostructures was prepared through thermal conversion of Ni(OH)₂precursor nanostructures in appropriate P and/or Se vapors. This facile synthetic method makes it convenient to systematically compare the structural property and catalytic activity for HER and establish the relationship between synthesis, structure, and catalytic activity. It was found that the doping of NiP₂with Se not only reduced the overpotential, but also decreased the Tafel slope and increased exchange current density, thus significantly improving the HER catalytic performance. Se-doped NiP₂(NiP_1.93Se_0.07) is a highly active and stable electrocatalyst for HER and shows the best performance among the four pyrite-phase compounds, followed by NiP₂, P-doped NiSe₂(NiP_0.09Se_1.91), and NiSe₂. Se-doped NiP₂(NiP_1.93Se_0.07) grown on carbon fiber paper can achieve a catalytic current density of 10 mA cm⁻²at an overpotential of 84 mV with a Tafel slope of 41 mV decade⁻¹, which establishes NiP_1.93Se_0.07as a highly-active, earth-abundant, and stable electrocatalyst for the HER.
Methods
All chemicals were purchased from Sigma-Aldrich and used without further purifications unless otherwise noted.
Synthesis of Electrocatalyst Materials.
Ni(OH)₂Nanoflake Precursor.
Nickel hydroxide hydrate (Ni(OH)₂.0.75H₂O) nanoflakes were synthesized on graphite disks and carbon fiber paper electrodes by modifying a reported procedure for synthesizing cobalt hydroxide nanostructure analogs.¹⁰6 mmol of Ni(NO₃)₂.6H₂O (≧98.5%), 12 mmol NH₄F (≧98.0%), and 30 mmol (NH₂)₂CO (99.5-100.5%) were dissolved in 200 mL of 18.2 MΩ de-ionized water. 16 mL of the solution was transferred to a 23-mL PTFE-lined stainless steel autoclave containing the substrate leaned against the autoclave wall. After the sealed autoclave was heated at 110° C. for 3 h, it was cooled down. Then the substrate was removed, washed with water and ethanol, and dried in an oven at 80° C. for 20 min.
Graphite Disk Substrate and Carbon Fiber Paper Preparation.
Graphite disk substrates (6.0 mm diameter; ˜1 mm thick) were prepared by cutting and mechanically thinning slices of a graphite rod (Ultra Carbon Corp., Ultra “F” Purity). Slices of the graphite rod were polished on both sides with sand paper. The graphite disks were cleaned by sequentially sonicating (100 W) in ethanol and deionized water for 10 min, respectively. Then the clean graphite disks were dried in a forced-air oven at 120° C.
Carbon fiber paper substrates were purchased from Fuel Cell Earth Corp. with a thickness of 0.19 mm. The cut carbon fiber paper was etched by plasma for 10 min at 150 W firstly, then heated to 700° C. for 10 min to make it hydrophilic.
Thermal Conversion.
The graphite or carbon paper substrates covered with the nanoflakes were placed in the center of a fused silica tube in a Lindberg/Blue M tube furnace equipped with both pressure regulators and gas flow controllers. An alumina boat containing a total of 10 mmol of phosphorous (99.5-100.5%) and selenium (99.5-100.5%) powders with varying ratios (pure P, 3:1, 3:2, 3:3, 2:3, pure Se) was placed at the farthest upstream position within the reactor tube. The tube was purged 3 times with Argon and maintained at 780 Torr under a steady flow of Ar carrier gas (99.999%) at 25 sccm. The furnace temperature was ramped to 500° C. and held for 30 min. After cooling under Ar flow, the samples were removed and rinsed with CS₂(99.9%) for 10 min, then washed with ethanol, and dried in a flow of N₂gas.
Structural Characterization.
Scanning electron microscope (SEM) and energy dispersive X-ray spectroscopy (EDS) were performed using a LEO SUPRA 55 VP field-emission SEM with EDS capabilities. The voltages for SEM imaging and EDS mapping were 3 keV and 15 keV, respectively. Raman spectra were collected on a Horiba Jobin Yvon Labram Aramis Confocal Raman microscope with a 532 nm laser and ˜16 μm diameter laser spot size. Powder X-ray diffraction (PXRD) data were acquired on a Bruker D8 ADVANCE powder X-ray diffractometer equipped with a Cu Kα source. The transmission electron microscopy (TEM) samples were prepared by immersing and sonicating the samples grown on graphite disk in ethanol for 30 s, and drop-casting the suspension onto Cu TEM grids with lacey carbon support (Ted Pella, #01890-F). TEM images were taken on an FEI Titan aberration-corrected scanning transmission electron microscope operated at an accelerating voltage of 200 kV in TEM mode.
Electrochemical Characterization.
All electrochemical measurements were conducted in a three-electrode setup with a rotating disk electrode (RDE, Bioanalytical Systems, Inc.; RDE-2) using a Bio-Logic SP-200 potentiostat. The measurements were performed in 0.5 M H₂SO₄(aq) electrolyte continuously purged with H₂(g) (99.999%), with a saturated calomel reference electrode (SCE) (CH Instruments), a graphite rod (National Carbon Co., AGKSP Spectroscopic Electrode) counter electrode, and a graphite disk or carbon fiber paper supported sample affixed to a glassy carbon RDE tip using silver paint (Ted Pella, PELCO Colloidal Silver) as the working electrode. Linear sweep voltammetry (LSV) measurements were performed at a scan rate of 3 mV s⁻¹while rotating the working electrode at 1000 RPM. The SCE was calibrated against the reversible hydrogen potential (RHE) using platinum wire (Kurt J. Lesker, 99.99%; 0.50 mm diameter) as both the working and counter electrodes in 0.5 M H₂SO₄(E(RHE)=E(SCE)+0.268 V). All measurements were corrected for a small ohmic loss (<3.5Ω) determined via impedance spectroscopy. Electrochemical impedance spectroscopy was performed in potentiostatic mode at −0.13 V vs. RHE with an applied sinusoidal voltage with an amplitude of 10 mV and scanning frequency from 200 kHz to 100 mHz. The data were fitted using a simplified Randles equivalent circuit (not shown) to investigate the electrode kinetics. To determine the double-layer capacitance (C_dl) for each electrode, two CV cycles were recorded from 100 mV to 200 mV vs. RHE at scan rates of 40, 60, 80, 100, and 120 mV s⁻¹. Then, for each scan rate, ΔJ was measured at 150 mV vs. RHE and plotted against the scan rate. These data were then fit to a line, the slope of which is equal to twice the geometric C_dl.
Results and Discussion
NiP₂, NiSe₂, and various NiP_2-xSe_xnanostructures were prepared by thermal conversion of precursor Ni(OH)₂nanostructures in different P and Se vapor environments. The precursor Ni(OH)₂nanoflakes (images not shown) were grown directly on conductive graphite disk (or carbon paper) substrates using the solution growth method as described above. Then, a total of 10 mmol of P and Se powders with varying ratios were mixed in a crucible, evaporated in the tube reactor at approximately 250° C., and reacted with the as-prepared Ni(OH)₂nanoflakes at 500° C. for 30 min in Ar atmosphere. FIGS. 5a-5b show the PXRD patterns of the products at different n(P) and n(Se) ratios (3:1, 3:2, 3:3, 2:3) compared with pure NiP₂(3:0) and NiSe₂(0:3) synthesized in pure P or Se environment under the same conditions. Both NiP₂and NiSe₂synthesized under these conditions are the cubic pyrite-structure phase (NiP₂, JCPDS 21-0590, space group Pa 3, a=5.471 Å; NiSe₂, JCPDS 65-1843, space group Pa 3, a=5.960 Å). The observed peak shifts of the samples converted with mixed precursors when compared with NiP₂and NiSe₂indicate the successful doping of NiP₂with Se or NiSe₂with P that causes the expansion or contraction of the crystal lattice, respectively. It is interesting that when n(P) was larger than n(Se), such as 3:2 and 3:1, NiP₂-like compounds (NiP_2-xSe_x, x is small) were formed (FIG. 5a ); when n(Se) was equal or larger than n(P), NiSe₂-like compounds were formed (FIG. 5b ). For Se-doped NiP₂, the peaks shift to smaller 2-θ angles compared with NiP₂(FIG. 5a inset), which suggests the expansion of the crystal lattice caused by the larger radius of Se compared with P. The opposite effect was observed in P-doped NiSe₂when compared with NiSe₂(FIG. 5b inset). Using Vegard's law, the chemical compositions of the samples were calculated based on the observed peak shifts: for the sample prepared with a ratio of n(P):n(Se)=3:2, the composition was NiP_1.93Se_0.07; for the sample prepared with a ratio of n(P):n(Se)=1:1 the composition was NiP_0.09Se_1.91.
The remaining discussion focuses on four representative samples: NiP₂, NiP_1.93Se_0.07, NiP_0.09Se_1.91, and NiSe₂. Also examined was the influence of the reaction temperature on the conversion for the precursor ratio of n(P):n(Se)=3:2 (SEM images and XRD patterns not shown). At 400° C., the peaks were very weak, which may be caused by the incomplete conversion and poor crystallinity of the product. At 500 and 600° C., there were strong peaks and all of the peaks shifted. However, the variations in the peak shifts from the sample prepared at 600° C. indicated that the conversion at 600° C. was not as consistent. Thus, 500° C. was chosen as the optimized conversion temperature.
The morphologies of NiP₂, NiP_1.93Se_0.07, NiP_0.09Se_1.91, and NiSe₂were characterized by scanning electron microscope (SEM) and transmission electron microscopy (TEM) as shown in FIGS. 6a-6h . Both NiP₂and NiP_1.93Se_0.07are flakes comprised of nanoparticles around 10 nm in diameter. In comparison, NiP_0.09Se_1.91and NiSe₂form larger particles with ˜500 nm diameter. The difference in the particle size and morphology between the NiP₂or doped NiP₂and NiSe₂or doped NiSe₂is noticeable, which is likely due to the different crystal growth behaviors during the conversion reactions. The energy dispersive X-ray spectroscopy (EDS) spectra proved the nanoflakes were composed of Ni, P, and Se (FIG. 7a ). Also, elemental mapping images showed that the distribution of Ni, P, and Se atoms in the nanoflakes was homogeneous (data not shown), which is consistent with the PXRD result and further confirms the composition.
Furthermore, Raman spectroscopy was employed to confirm the formation of pure and doped pyrite-phase products (FIG. 7b ). Typical pyrite-structure compounds show two peaks corresponding to X₂(X=S, Se, P) libration (E_g) and in-phase stretch (A_g) for the X-X dumbbells.²²The sharp peak in NiSe₂at 205 cm⁻¹corresponds to the Se-Se stretching mode of cubic NiSe₂, while NiP₂shows two peaks at 286 and 454 cm⁻¹, all of which are in agreement with what was reported for pyrites.¹¹The Raman spectra of NiP_1.93Se_0.07and NiP_0.09Se_1.91are quite similar to those of NiP₂and NiSe₂, respectively, which further confirms the pyrite structure and doping. The Raman peak positions also confirm that formation of pure or alloy phase of NiP₂for the bottom two samples without impurity phases close to NiSe₂, and the formation of pure or alloy phase of NiSe₂for the top two samples without impurity phases close to NiP₂.
The electrocatalytic HER activities of NiP₂, NiP_1.93Se_0.07, NiP_0.09Se_1.91, and NiSe₂nanostructures were measured using a standard three-electrode setup in 0.5 M H₂SO₄(aq) with continuously purging H₂. The graphite disks with samples were adhered on the glassy carbon working electrode of standard RDE apparatus by silver paint. It is worth noting that graphite disk and silver paint were inactive for HER and it was very convenient to perform characterizations on it. In addition, the direct growth of nanostructures on graphite disk ensures the good electrical contact between the substrate and the electrocatalysts. All data were iR corrected and the ohmic losses were always <3.5Ω. The polarization curves (FIG. 8a ) show the overpotentials needed for NiP₂, NiP_1.93Se_0.07, NiP_0.09Se_1.91, and NiSe₂to achieve a catalytic current density of 10 mA cm⁻²are 135, 102, 167, and 173 mV vs reversible hydrogen potential (RHE), respectively. The corresponding Tafel plots (FIG. 8b ) show all the Tafel plots can be well described with the Tafel equation in a relatively wide range (approximately 70 mV). The Tafel slopes of NiP₂, NiP_1.93Se_0.07, NiP_0.09Se_1.91, and NiSe₂are calculated to be 48, 42, 44, 31 mV decade⁻¹, respectively.
Although these samples were all converted from the same Ni(OH)₂precursor nanostructures and have similar morphologies and surface areas, there were still some variations between samples. In order to compare them in a more meaningful fashion, cyclic voltammetry (CV) scans were carried out to determine the double-layer capacitance (C_dl) (FIG. 8c ), which can be used to estimate the relative electrochemically active surface area assuming that the two are linearly proportional.¹⁰Using such relative surface areas, the electrochemical data can be normalized to determine the normalized Tafel slope and normalized exchange current density.¹⁰The geometric exchange current density (J_0,geometric), double-layer capacitance (C_dl), relative electrochemically active surface area, normalized Tafel slope, and normalized exchange current density (J_0,normalized) of each electrode are summarized in Table 3. The normalized exchange current densities of NiP₂, NiP_1.93Se_0.07, NiP_0.09Se_1.91, and NiSe₂were found to be 12, 31, 1.4, and 0.038 μA cm⁻², respectively. The doping of NiP₂with Se significantly improved the HER performance as evidenced by the J_0,normalizedof NiP_1.93Se_0.07, which was 2.6 times larger than that of NiP₂, suggesting the higher intrinsic HER activity of NiP_1.93Se_0.07. The doping of NiP₂with Sc also reduced the Tafel slope (normalized) of NiP₂from 51 to 43 mV decade⁻¹(FIG. 8d ), which is desirable to drive a large catalytic current density at a low overpotential. Additionally, it was found that NiP₂was catalytically more active than NiSe₂for HER (although the Tafel slope for NiSe₂is lower at 33 mV decade⁻¹). Although P-doping of NiSe₂improved the catalytic performance, it could not surpass the performance of NiP₂or Sc-doped NiP₂. These results again confirm that the Se-doped NiP₂(NiP_1.93Se_0.07) has the highest catalytic activity among these four compounds. The substitution of P by Se in the pyrite-phase NiP₂is suggested to modify the electronic structure of NiP₂, which could further tune the hydrogen absorption free energy on the catalyst and improve the catalytic activity, as demonstrated in Example 1 for pyrite-phase CoPS.

TABLE 3

Summary of the electrochemical properties of NiP_2,NiP_1.93Se_0.07, NiP_0.09Se_1.91,
and NiSe₂on graphite disk (GD) and NiP_1.93Se_0.07on carbon fiber paper (CP). The best
values for each parameter among four samples on GD were highlighted with bold fonts.

	η (mV vs.
	RHE) for				Relative	Tafel slope
	J = −10	Tafel slope	J_{0, geometric}	C_dl	Surface	_normalized(mV	J_{0, normalized}
Sample/Substrate	mA cm ⁻²	(mV decade⁻¹)	(μA cm⁻²)	(mF cm⁻²)	Area	decade⁻¹)	(μA cm⁻²)

NiP₂/GD	135	48	15	8.96	1.84	51	12
NiP_1.93Se_0.07/GD	102	42	39	6.49	1.34	43	31
NiP_0.09Se_1.91/GD	167	44	1.4	4.86	1.00	44	1.4
NiSe₂/GD	173	31	0.031	7.35	1.51	33	0.038
NiP_1.93Se_0.07/CP	84	41	100	27.6	5.68	42	20

Furthermore, the stability of the most catalytically active NiP_1.93Se_0.07catalyst for HER was measured. The electrode of NiP_1.93Se_0.07nanostructures on graphite disk can maintain a current density of 10 mA cm⁻²for ˜14 h at an overpotential of 0.1 V (data not shown). The charge transfer resistance of the electrode only increased slightly from 4.5Ω to 10Ω (data not shown). The morphology of NiP_1.93Se_0.07changed very little after this 14 h test (data not shown). Also, the PXRD patterns of NiP_1.93Se_0.07after the test showed no significant changes (data not shown). These results demonstrate the excellent stability of NiP_1.93Se_0.07.
Finally, to further improve the overall catalytic performance of NiP_1.93Se_0.07for HER, carbon fiber paper (CP) was employed, which has large surface area and good electrical conductivity, as the substrate to prepare high surface area three-dimensional (3D) electrodes in otherwise similar synthesis conditions. FIG. 9 displays the SEM images of NiP_1.93Se_0.07nanostructures on carbon fiber paper. The PXRD patterns, polarization curves (FIG. 10a ), and the corresponding Tafel plot (FIG. 10b ) of NiP_1.93Se_0.07nanostructures on carbon fiber paper were also obtained. The results show that the NiP_1.93Se_0.07/CP electrodes achieved a catalytic current density of 10 mA cm⁻²at an overpotential of 84 mV vs. RHE with a Tafel slope of 41 mV decade⁻¹.

Conclusion

In summary, a facile method has been developed to synthesize nanostructures of pyrite-phase NiP₂, nickel phosphoselenide (NiP_1.93Se_0.07, NiP_0.09Se_1.91), and NiSe₂. Their similar structures enable a systematic and fair comparison of their structural properties and catalytic activities for HER. The results prove that Se-doped NiP₂(NiP_1.93Se_0.07) exhibits the highest electrocatalytic activity among the four compounds. Specifically, NiP_1.93Se_0.07nanostructures grown on carbon fiber paper achieved a current density of 10 mA cm⁻²at −84 mV (vs. RHE) with a small Tafel slope of 41 mV decade⁻¹. These results establish NiP_1.93Se_0.07as a highly active, stable, and earth-abundant electrocatalyst for HER.

REFERENCES

1 Lewis, N. S. & Nocera, D. G. Powering the planet: Chemical challenges in solar energy utilization. Proc. Natl. Acad. Sci. U.S.A. 103. 15729-15735 (2006).
2 Nocera. D. G. The Artificial Leaf. Acc. Chem. Res. 45, 767-776 (2012).
3 Turner, J. A. Sustainable Hydrogen Production. Science 305, 972-974 (2004).
4 Faber, M. S. & Jin, S. Earth-abundant inorganic electrocatalysts and their nanostructures for energy conversion applications. Energy Environ. Sci. 7, 3519-3542 (2014).
5 Lukowski, M. A., Daniel, A. S., Meng, F., Forticaux, A., Li, L. S. & Jin, S. Enhanced Hydrogen Evolution Catalysis from Chemically Exfoliated Metallic MoS₂Nanosheets. J. Am. Chem. Soc. 135, 10274-10277 (2013).
6 Benck, J. D., Hellstern, T. R., Kibsgaard, J., Chakthranont, P. & Jaramillo, T. F. Catalyzing the Hydrogen Evolution Reaction (HER) with Molybdenum Sulfide Nanomaterials. ACS Catal. 4, 3957-3971 (2014).
7 Voiry, D., Yamaguchi, H., Li, J. W., Silva, R., Alves, D. C. B., Fujita, T., Chen, M. W., Asefa, T., Shenoy, V. B., Eda, G. & Chhowalla, M. Enhanced catalytic activity in strained chemically exfoliated WS₂nanosheets for hydrogen evolution. Nature Mater. 12, 850-855 (2013).
8 Lukowski, M. A., Daniel, A. S., English, C. R., Meng, F., Forticaux, A., Hamers, R. J. & Jin, S. Highly active hydrogen evolution catalysis from metallic WS₂nanosheets. Energy Environ. Sci. 7, 2608-2613 (2014).
9 Merki, D., Fierro, S., Vrubel, H. & Hu, X. L. Amorphous molybdenum sulfide films as catalysts for electrochemical hydrogen production in water. Chem. Sci. 2, 1262-1267 (2011).
10 Faber, M. S., Dziedzic, R., Lukowski, M. A., Kaiser, N. S., Ding, Q. & Jin, S. High-Performance Electrocatalysis Using Metallic Cobalt Pyrite (CoS₂) Micro- and Nanostructures. J. Am. Chem. Sec. 136, 10053-10061 (2014).
11 Kong, D. S., Wang, H. T., Lu, Z. Y. & Cui, Y. CoSe₂Nanoparticles Grown on Carbon Fiber Paper: An Efficient and Stable Electrocatalyst for Hydrogen Evolution Reaction. J. Am. Chem. Soc. 136, 4897-4900 (2014).
12 Popczun, E. J., Read, C. G., Roske, C. W., Lewis, N. S. & Schaak, R. E. Highly Active Electrocatalysis of the Hydrogen Evolution Reaction by Cobalt Phosphide Nanoparticles. Angew. Chem. Int. Ed. 53, 5427-5430 (2014).
13 Liu, Q., Tian, J., Cui, W., Jiang, P., Cheng, N., Asiri, A. M. & Sun, X. Carbon Nanotubes Decorated with CoP Nanocrystals: A Highly Active Non-Noble-Metal Nanohybrid Electrocatalyst for Hydrogen Evolution. Angewandte Chemie 126, 6828-6832 (2014).
14 Popczun, E. J., McKone, J. R., Read, C. G., Biacchi, A. J., Wiltrout, A. M., Lewis, N. S. & Schaak, R. E. Nanostructured Nickel Phosphide as an Electrocatalyst for the Hydrogen Evolution Reaction. J. Am. Chem. Soc. 135, 9267-9270 (2013).
15 Callejas, J. F., McEnaney, J. M., Read, C. G., Crompton, J. C., Biacchi, A. J., Popczun, E. J., Gordon, T. R., Lewis, N. S. & Schaak, R. E. Electrocatalytic and Photocatalytic Hydrogen Production from Acidic and Neutral-pH Aqueous Solutions Using Iron Phosphide Nanoparticles. ACS Nano 8, 11101-11107 (2014).
16 Xiao, P., Sk, M. A., Thia, L., Ge, X., Lim, R. J., Wang. J.-Y., Lim, K. H. & Wang, X. Molybdenum phosphide as an efficient electrocatalyst for the hydrogen evolution reaction. Energy Environ. Sci. 7, 2624-2629 (2014).
17 McEnaney, J. M., Crompton, J. C., Callejas, J. F., Popczun, E. J., Biacchi, A. J., Lewis, N. S. & Schaak, R. E. Amorphous Molybdenum Phosphide Nanoparticles for Electrocatalytic Hydrogen Evolution. Chem. Mater. 26, 4826-4831 (2014).
18 Kibsgaard, J., Jaramillo, T. F. Molybdenum Phosphosulfide: An Active, Acid-Stable, Earth-Abundant Catalyst for the Hydrogen Evolution Reaction. Angew. Chem. Int. Ed. 53, 14433-14437 (2014).
19 McKone, J. R., Sadder, B. F., Werlang, C. A., Lewis, N. S. & Gray, H. B. Ni—Mo Nanopowders for Efficient Electrochemical Hydrogen Evolution. ACS Catal. 3, 166-169 (2013).
McKone, J. R., Lewis, N. S. & Gray. H. B. Will Solar-Driven Water-Splitting Devices See the Light of Day? Chem. Mater. 26, 407-414 (2014).
21 Faber, M. S., Park, K., Cabin-Acevedo, M., Santra, P. K. & Jin, S. Earth-Abundant Cobalt Pyrite (CoS₂) Thin Film on Glass as a Robust, High-Performance Counter Electrode for Quantum Dot-Sensitized Solar Cells. J. Phys. Chem. Lett. 4, 1843-1849 (2013).
22 Faber, M. S., Lukowski, M. A., Ding, Q., Kaiser, N. S. & Jin, S. Earth-Abundant Metal Pyrites (FeS2, CoS2, NiS2, and Their Alloys) for Highly Efficient Hydrogen Evolution and Polysulfide Reduction Electrocatalysis. J. Phys. Chem. C 118, 21347-21356 (2014).
23 Kong, D. S., Cha, J. J., Wang, H. T., Lee, H. R. & Cui, Y. First-row transition metal dichalcogenide catalysts for hydrogen evolution reaction. Energy Environ. Sci. 6, 3553-3558 (2013).
24 Cabin-Acevedo, M., Kaiser, N. S., English, C. R., Liang, D., Thompson, B. J., Chen, H.-E., Czech, K. J., Wright, J. C., Hamers, R. J. & Jin, S. Ionization of High-Density Deep Donor Defect States Explains the Low Photovoltage of Iron Pyrite Single Crystals. J. Am. Chem. Soc. 136, 17163-17179 (2014).
25 Ennaoui, A., Fiechter, S., Pettenkofer, C., Alonso-Vante, N., Büker, K., Bronold, M., Höpfher, C. & Tributsch, H. Iron disulfide for solar energy conversion. SoI. Energy Mater. SoI. Cells 29, 289-370 (1993).
26 Stiebritz, M. T. & Reiher, M. A Unifying Structural and Electronic Concept for Hmd and [FeFe] Hydrogenase Active Sites. Inorg. Chem. 49, 5818-5823 (2010).
27 Thauer, R. K., Kaster, A.-K., Goenrich, M., Schick, M., Hiromoto, T. & Shima, S. Hydrogcnases from Methanogenic Archaea, Nickel, a Novel Cofactor, and Hz Storage. Annual Review of Biochemistry 79, 507-536 (2010).
28 Kubas, G. J. Metal Dihydrogen and s-Bond Complexes: Structure, Theory, and Reactivity. (Springer Science & Business Media, 2001).
29 Ishida, K. & Nishizawa, T. The Co—P (Cobalt-Phosphorus) system. Bulletin of Alloy Phase Diagrams 11, 555-560 (1990).
Hulliger, F. New Compounds with Cobaltite Structure. Nature 198, 382-383 (1963).
31 Nerskov, J. K., Bligaard, T., Logadottir. A., Kitchin, J. R., Chen, J. G., Pandelov, S. & Stimming, U. Trends in the Exchange Current for Hydrogen Evolution. J. Electrochem. Soc. 152, J23-J26 (2005).
32 Xia, X., Chao, D., Qi, X., Xiong, Q., Zhang, Y., Tu, J., Zhang, H. & Fan, H. J. Controllable Growth of Conducting Polymers Shell for Constructing High-Quality Organic/Inorganic Core/Shell Nanostructures and Their Optical-Electrochemical Properties. Nano Lett. 13, 4562-4568 (2013).
33 Lyapin. S. G., Utyuzh, A. N., Petrova, A. E., Novikov, A. P., Lograsso, T. A. & Stishov, S. M. Raman studies of nearly half-metallic ferromagnetic CoS₂ . Journal of Physics: Condensed Matter 26, 396001 (2014).
34 Moulder, J. F., Stickle W. F., Sobol P. E. & Bomben K. D. Handbook of X-ray Photoelectron Spectroscopy. (Perkin-Elmer Corp, 1992).
35 Biesinger, M. C., Lau, L. W. M., Gerson, A. R. & Smart, R. S. C. Resolving surface chemical states in XPS analysis of first row transition metals, oxides and hydroxides: Sc, Ti, V, Cu and Zn. Appl. Surf Sci. 257, 887-898 (2010).
36 Okamoto H. P—S(Phosphorus-Sulfur). J. Phase Equilib. 12, 706-707 (1991).
37 Dai, P., Xie, J., Mayer, M. T., Yang, X., Zhan, J. & Wang, D. Solar Hydrogen Generation by Silicon Nanowires Modified with Platinum Nanoparticle Catalysts by Atomic Layer Deposition. Angew. Chem. Int. Ed. 52, 11119-11123 (2013).
38 Boettcher, S. W., Warren, E. L., Putnam, M. C., Santori, E. A., Turner-Evans, D., Kelzenberg, M. D., Walter, M. G., McKone, J. R., Brunschwig, B. S., Atwater, H. A. & Lewis, N. S. Photoelectrochemical Hydrogen Evolution Using Si Microwire Arrays. J. Am. Chem. Soc. 133, 1216-1219 (2011).
39 Wang, H.-P., Lin, T.-Y., Hsu, C.-W., Tsai, M.-L., Huang, C.-H., Wei, W.-R., Huang, M.-Y., Chien, Y.-J., Yang, P.-C., Liu, C.-W., Chou, L.-J. & He, J.-H. Realizing High-Efficiency Omnidirectional n-Type Si Solar Cells via the Hierarchical Architecture Concept with Radial Junctions. ACS Nano 7, 9325-9335 (2013).
40 Kelzenberg, M. D., Boettcher, S. W., Petykiewicz, J. A., Turner-Evans, D. B., Putnam, M. C., Warren, E. L., Spurgeon, J. M., Briggs, R. M., Lewis, N. S. & Atwater, H. A. Enhanced absorption and carrier collection in Si wire arrays for photovoltaic applications. Nat Mater 9, 239-244 (2010).
41 Zhang, X., Meng, F., Mao, S., Ding, Q., Shearer, M. J., Faber, M. S., Chen, J., Hamners, R. J. & Jin, S. Amorphous MoS_xCl_yelectrocatalyst supported by vertical graphene for efficient electrochemical and photoelectrochemical hydrogen generation. Energy Environ. Sci. (2015).
42 Ding, Q., Meng, F., English, C. R., Cabhn-Acevedo, M., Shearer. M. J., Liang, D., Daniel, A. S., Hamers, R. J. & Jin, S. Efficient Photoelectrochemical Hydrogen Generation Using Heterostructures of Si and Chemically Exfoliated Metallic MoS₂ . J. Am. Chem. Soc. 136, 8504-8507 (2014).
43 Huang, Z., Chen, Z., Chen, Z., Lv, C., Meng, H. & Zhang, C. Ni₁₂P₅Nanoparticles as an Efficient Catalyst for Hydrogen Generation via Electrolysis and Photoelectrolysis. ACS Nano 8. 8121-8129 (2014).
44 Hou, Y., Abrams, B. L., Vesborg, P. C. K., Björketun, M. E., Herbst, K., Bech, L., Setti, A. M., Damsgaard, C. D., Pedersen, T., Hansen, O., Rossmeisl, J., Dahl, S., Nørskov, J. K. & Chorkendorff, I. Bioinspired molecular co-catalysts bonded to a silicon photocathode for solar hydrogen evolution. Nat Mater 10, 434-438 (2011).
45 Benck, J. D., Lee, S. C., Fong, K. D., Kibsgaard, J., Sinclair, R. & Jaramillo, T. F. Designing Active and Stable Silicon Photocathodes for Solar Hydrogen Production Using Molybdenum Sulfide Nanomaterials. Adv. Energy Mater. 4, 1400739 (2014).
46 Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169 (1996).
47 Kresse, G. & Hafner, J. Ab initio molecular-dynamics simulation of the liquid-metal-amorphous-semiconductor transition in germanium. Phys. Rev. B 49, 14251 (1994).
48 Kresse, G. & Hafner, J. Ab initio molecular dynamics for liquid metals. Phys. Rev. B 47, 558 (1993).
49 Blöchl, P. E. Projector augmented-wave method. Phys. Rev. B 50, 17953 (1994).
50 Kresse, G. & Joubert, D. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev B 59, 1758 (1999).

The word “illustrative” is used herein to mean serving as an example, instance, or illustration. Any aspect or design described herein as “illustrative” is not necessarily to be construed as preferred or advantageous over other aspects or designs. Further, for the purposes of this disclosure and unless otherwise specified, “a” or “an” means “one or more”.
The foregoing description of illustrative embodiments of the invention has been presented for purposes of illustration and of description. It is not intended to be exhaustive or to limit the invention to the precise form disclosed, and modifications and variations are possible in light of the above teachings or may be acquired from practice of the invention. The embodiments were chosen and described in order to explain the principles of the invention and as practical applications of the invention to enable one skilled in the art to utilize the invention in various embodiments and with various modifications as suited to the particular use contemplated. It is intended that the scope of the invention be defined by the claims appended hereto and their equivalents.

Claims

What is claimed is:

1. An electrode for catalyzing an electrochemical reaction, the electrode comprising a ternary pyrite-phase transition metal phosphochalcogenide disposed on a substrate, wherein the ternary pyrite-phase transition metal phosphochalcogenide is a solid material of a ternary compound of a transition metal, phosphorous (P), and a chalcogen, the solid material characterized by a substantially single, ternary alloy phase having a pyrite crystal structure.

2. The electrode of claim 1, wherein the chemical species at the surface of the solid material are substantially the same as the chemical species in the bulk of the solid material.

3. The electrode of claim 1, wherein the ternary pyrite-phase transition metal phosphochalcogenide is a ternary pyrite-phase cobalt phosphochalcogenide, a ternary pyrite-phase nickel phosphochalcogenide, or combinations thereof.

4. The electrode of claim 1, wherein the ternary pyrite-phase transition metal phosphochalcogenide is ternary pyrite-phase cobalt phosphosulfide, ternary pyrite-phase cobalt phosphoselenide, ternary pyrite-phase nickel phosphosulfide, ternary pyrite-phase nickel phosphoselenide, or combinations thereof.

5. The electrode of claim 1, wherein the ternary pyrite-phase transition metal phosphochalcogenide has a formula MPX, wherein M is a transition metal selected from Co, Ni, Fe, and Mn; P is phosphorous; and X is a chalcogen selected from S, Se, and Te.

6. The electrode of claim 5, wherein M is a transition metal selected from Co and Ni; P is phosphorous; and X is a chalcogen selected from S and Sc.

7. The electrode of claim 5, wherein the ternary pyrite-phase transition metal phosphochalcogenide is CoPS, CoPSe, NiPSe, or combinations thereof.

8. The electrode of claim 7, wherein the NiPSe is Se-doped NiP₂.

9. The electrode of claim 1, wherein the solid material is in the form of nanostructures.

10. The electrode of claim 9, wherein the nanostructures are nanoparticles, nanowires, nanoplates, or combinations thereof.

11. The electrode of claim 1, wherein the substrate is a carbon substrate, a metal substrate or a glass substrate.

12. The electrode of claim 1, wherein the substrate comprises a semiconductor capable of absorbing light to produce free electrons.

13. The electrode of claim 1, wherein the transition metal is alloyed with one or more other transition metals such that the ternary pyrite-phase transition metal phosphochalcogenide is an alloyed ternary pyrite-phase transition metal phosphochalcogenide.

14. The electrode of claim 13, wherein the alloyed ternary pyrite-phase transition metal phosphochalcogenide has a formula M₁M₂PX, wherein M₁and M₂are transition metals independently selected from Co, Ni, Fe, and Mn; P is phosphorous; and X is a chalcogen selected from S, Se, and Te.

15. An electrochemical reaction system comprising a reaction cell configured to contain a fluid comprising an oxidant to be reduced; the electrode of claim 1 in contact with the fluid; and a counter electrode.

16. A method for catalyzing an electrochemical reaction, the method comprising: exposing an electrode to a fluid comprising an oxidant to be reduced in the presence of free electrons, wherein the electrode comprises a ternary pyrite-phase transition metal phosphochalcogenide disposed on a substrate, wherein the ternary pyrite-phase transition metal phosphochalcogenide is a solid material of a ternary compound of a transition metal, phosphorous (P), and a chalcogen, the solid material characterized by a substantially single, ternary alloy phase having a pyrite crystal structure, whereby the free electrons induce the reduction of the oxidant at the ternary pyrite-phase transition metal phosphochalcogenide-fluid interface to form a reduction product.

17. The method of claim 16, wherein the free electrons are generated by applying an electrical potential across the electrode and a counter electrode in electrical communication with the electrode.

18. The method of claim 16, wherein the substrate comprises a semiconductor capable of absorbing light to produce free electrons, and further wherein the free electrons are generated by exposing the electrode to the light.

19. The method of claim 16, wherein the electrochemical reaction is the hydrogen evolution reaction, the fluid is an aqueous electrolyte solution, the oxidant comprises hydrogen ions, and the reduction product comprises hydrogen gas.

20. A method for making an electrode, the method comprising exposing a transition metal-containing precursor disposed on a substrate to a chalcogen-phosphorous atmosphere at an elevated temperature and for a period of time sufficient to convert the transition metal-containing precursor to a ternary pyrite-phase transition metal phosphochalcogenide, wherein the ternary pyrite-phase transition metal phosphochalcogenide is a solid material of a ternary compound of a transition metal, phosphorous (P), and a chalcogen, the solid material characterized by a substantially single, ternary alloy phase having a pyrite crystal structure.