US20130252808A1 - Catalysts for thermochemical fuel production and method of producing fuel using thermochemical fuel production - Google Patents
Catalysts for thermochemical fuel production and method of producing fuel using thermochemical fuel production Download PDFInfo
- Publication number
- US20130252808A1 US20130252808A1 US13/600,948 US201213600948A US2013252808A1 US 20130252808 A1 US20130252808 A1 US 20130252808A1 US 201213600948 A US201213600948 A US 201213600948A US 2013252808 A1 US2013252808 A1 US 2013252808A1
- Authority
- US
- United States
- Prior art keywords
- thermochemical
- fuel
- temperature
- catalyst
- fuel production
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
- 238000004519 manufacturing process Methods 0.000 title claims abstract description 178
- 239000000446 fuel Substances 0.000 title claims abstract description 143
- 239000003054 catalyst Substances 0.000 title claims abstract description 90
- 238000000034 method Methods 0.000 title claims abstract description 43
- 229910052760 oxygen Inorganic materials 0.000 claims abstract description 26
- 239000001301 oxygen Substances 0.000 claims abstract description 26
- QVGXLLKOCUKJST-UHFFFAOYSA-N atomic oxygen Chemical compound [O] QVGXLLKOCUKJST-UHFFFAOYSA-N 0.000 claims abstract description 25
- 229910052761 rare earth metal Inorganic materials 0.000 claims abstract description 7
- 229910052783 alkali metal Inorganic materials 0.000 claims abstract description 5
- 150000001340 alkali metals Chemical class 0.000 claims abstract description 5
- 229910052784 alkaline earth metal Inorganic materials 0.000 claims abstract description 5
- 150000001342 alkaline earth metals Chemical class 0.000 claims abstract description 5
- 229910052752 metalloid Inorganic materials 0.000 claims abstract description 5
- 229910052723 transition metal Inorganic materials 0.000 claims abstract description 5
- 239000001257 hydrogen Substances 0.000 claims description 121
- 229910052739 hydrogen Inorganic materials 0.000 claims description 121
- XLYOFNOQVPJJNP-UHFFFAOYSA-N water Chemical compound O XLYOFNOQVPJJNP-UHFFFAOYSA-N 0.000 claims description 32
- VNWKTOKETHGBQD-UHFFFAOYSA-N methane Chemical compound C VNWKTOKETHGBQD-UHFFFAOYSA-N 0.000 claims description 29
- OKKJLVBELUTLKV-UHFFFAOYSA-N Methanol Chemical compound OC OKKJLVBELUTLKV-UHFFFAOYSA-N 0.000 claims description 23
- 229910052742 iron Inorganic materials 0.000 claims description 20
- CURLTUGMZLYLDI-UHFFFAOYSA-N Carbon dioxide Chemical compound O=C=O CURLTUGMZLYLDI-UHFFFAOYSA-N 0.000 claims description 19
- 239000002994 raw material Substances 0.000 claims description 13
- 229910002092 carbon dioxide Inorganic materials 0.000 claims description 12
- 239000007789 gas Substances 0.000 claims description 12
- 229910052748 manganese Inorganic materials 0.000 claims description 12
- 229910052719 titanium Inorganic materials 0.000 claims description 11
- 238000010438 heat treatment Methods 0.000 claims description 10
- 229910052746 lanthanum Inorganic materials 0.000 claims description 10
- 229910052712 strontium Inorganic materials 0.000 claims description 8
- 238000006467 substitution reaction Methods 0.000 claims description 8
- 239000001569 carbon dioxide Substances 0.000 claims description 7
- 229910052802 copper Inorganic materials 0.000 claims description 7
- 230000008569 process Effects 0.000 claims description 7
- 229910052749 magnesium Inorganic materials 0.000 claims description 6
- 229910052759 nickel Inorganic materials 0.000 claims description 6
- 229910052788 barium Inorganic materials 0.000 claims description 5
- 229910052791 calcium Inorganic materials 0.000 claims description 5
- 229910052804 chromium Inorganic materials 0.000 claims description 5
- 229910052720 vanadium Inorganic materials 0.000 claims description 5
- 239000002918 waste heat Substances 0.000 claims description 5
- 229910052725 zinc Inorganic materials 0.000 claims description 5
- 229910052706 scandium Inorganic materials 0.000 claims description 4
- 229910052799 carbon Inorganic materials 0.000 claims description 3
- 229910052732 germanium Inorganic materials 0.000 claims description 3
- 230000001590 oxidative effect Effects 0.000 claims description 3
- 229910052710 silicon Inorganic materials 0.000 claims description 3
- 229910052726 zirconium Inorganic materials 0.000 claims description 3
- 229910052782 aluminium Inorganic materials 0.000 claims description 2
- 229910052733 gallium Inorganic materials 0.000 claims description 2
- 229910052738 indium Inorganic materials 0.000 claims description 2
- 229910052718 tin Inorganic materials 0.000 claims description 2
- 125000004435 hydrogen atom Chemical class [H]* 0.000 claims 1
- UFHFLCQGNIYNRP-UHFFFAOYSA-N Hydrogen Chemical compound [H][H] UFHFLCQGNIYNRP-UHFFFAOYSA-N 0.000 description 115
- XEEYBQQBJWHFJM-UHFFFAOYSA-N iron Substances [Fe] XEEYBQQBJWHFJM-UHFFFAOYSA-N 0.000 description 75
- 239000011572 manganese Substances 0.000 description 72
- 238000006243 chemical reaction Methods 0.000 description 28
- 239000010936 titanium Substances 0.000 description 17
- 239000011777 magnesium Substances 0.000 description 13
- CETPSERCERDGAM-UHFFFAOYSA-N ceric oxide Chemical compound O=[Ce]=O CETPSERCERDGAM-UHFFFAOYSA-N 0.000 description 12
- 229910000422 cerium(IV) oxide Inorganic materials 0.000 description 12
- 229910000473 manganese(VI) oxide Inorganic materials 0.000 description 12
- PXHVJJICTQNCMI-UHFFFAOYSA-N nickel Substances [Ni] PXHVJJICTQNCMI-UHFFFAOYSA-N 0.000 description 12
- WGLPBDUCMAPZCE-UHFFFAOYSA-N Trioxochromium Chemical compound O=[Cr](=O)=O WGLPBDUCMAPZCE-UHFFFAOYSA-N 0.000 description 8
- 239000010949 copper Substances 0.000 description 7
- 230000003247 decreasing effect Effects 0.000 description 7
- 239000008188 pellet Substances 0.000 description 7
- 239000000126 substance Substances 0.000 description 7
- 230000007704 transition Effects 0.000 description 6
- 239000011701 zinc Substances 0.000 description 6
- PWHULOQIROXLJO-UHFFFAOYSA-N Manganese Chemical compound [Mn] PWHULOQIROXLJO-UHFFFAOYSA-N 0.000 description 5
- 150000002431 hydrogen Chemical class 0.000 description 5
- 238000002441 X-ray diffraction Methods 0.000 description 4
- 125000004429 atom Chemical group 0.000 description 4
- 239000011575 calcium Substances 0.000 description 4
- 230000003197 catalytic effect Effects 0.000 description 4
- 239000011651 chromium Substances 0.000 description 4
- FZLIPJUXYLNCLC-UHFFFAOYSA-N lanthanum atom Chemical compound [La] FZLIPJUXYLNCLC-UHFFFAOYSA-N 0.000 description 4
- 238000007254 oxidation reaction Methods 0.000 description 4
- 238000006722 reduction reaction Methods 0.000 description 4
- RYGMFSIKBFXOCR-UHFFFAOYSA-N Copper Chemical compound [Cu] RYGMFSIKBFXOCR-UHFFFAOYSA-N 0.000 description 3
- 230000003466 anti-cipated effect Effects 0.000 description 3
- 230000008901 benefit Effects 0.000 description 3
- 239000000463 material Substances 0.000 description 3
- KDLHZDBZIXYQEI-UHFFFAOYSA-N palladium Substances [Pd] KDLHZDBZIXYQEI-UHFFFAOYSA-N 0.000 description 3
- BASFCYQUMIYNBI-UHFFFAOYSA-N platinum Substances [Pt] BASFCYQUMIYNBI-UHFFFAOYSA-N 0.000 description 3
- CIOAGBVUUVVLOB-UHFFFAOYSA-N strontium atom Chemical compound [Sr] CIOAGBVUUVVLOB-UHFFFAOYSA-N 0.000 description 3
- XKRFYHLGVUSROY-UHFFFAOYSA-N Argon Chemical compound [Ar] XKRFYHLGVUSROY-UHFFFAOYSA-N 0.000 description 2
- 229910052692 Dysprosium Inorganic materials 0.000 description 2
- 229910052691 Erbium Inorganic materials 0.000 description 2
- 229910052693 Europium Inorganic materials 0.000 description 2
- 229910052688 Gadolinium Inorganic materials 0.000 description 2
- 229910052689 Holmium Inorganic materials 0.000 description 2
- KFZMGEQAYNKOFK-UHFFFAOYSA-N Isopropanol Chemical compound CC(C)O KFZMGEQAYNKOFK-UHFFFAOYSA-N 0.000 description 2
- 229910052765 Lutetium Inorganic materials 0.000 description 2
- 229910052779 Neodymium Inorganic materials 0.000 description 2
- 229910052777 Praseodymium Inorganic materials 0.000 description 2
- 229910052773 Promethium Inorganic materials 0.000 description 2
- 229910052772 Samarium Inorganic materials 0.000 description 2
- 229910052771 Terbium Inorganic materials 0.000 description 2
- 229910052775 Thulium Inorganic materials 0.000 description 2
- 229910052769 Ytterbium Inorganic materials 0.000 description 2
- 238000002835 absorbance Methods 0.000 description 2
- 238000013459 approach Methods 0.000 description 2
- 229910000421 cerium(III) oxide Inorganic materials 0.000 description 2
- 230000002542 deteriorative effect Effects 0.000 description 2
- KBQHZAAAGSGFKK-UHFFFAOYSA-N dysprosium atom Chemical compound [Dy] KBQHZAAAGSGFKK-UHFFFAOYSA-N 0.000 description 2
- 230000000694 effects Effects 0.000 description 2
- 238000005516 engineering process Methods 0.000 description 2
- UYAHIZSMUZPPFV-UHFFFAOYSA-N erbium Chemical compound [Er] UYAHIZSMUZPPFV-UHFFFAOYSA-N 0.000 description 2
- OGPBJKLSAFTDLK-UHFFFAOYSA-N europium atom Chemical compound [Eu] OGPBJKLSAFTDLK-UHFFFAOYSA-N 0.000 description 2
- 238000002474 experimental method Methods 0.000 description 2
- UIWYJDYFSGRHKR-UHFFFAOYSA-N gadolinium atom Chemical compound [Gd] UIWYJDYFSGRHKR-UHFFFAOYSA-N 0.000 description 2
- 239000010931 gold Substances 0.000 description 2
- KJZYNXUDTRRSPN-UHFFFAOYSA-N holmium atom Chemical compound [Ho] KJZYNXUDTRRSPN-UHFFFAOYSA-N 0.000 description 2
- UQSXHKLRYXJYBZ-UHFFFAOYSA-N iron oxide Inorganic materials [Fe]=O UQSXHKLRYXJYBZ-UHFFFAOYSA-N 0.000 description 2
- 229910002075 lanthanum strontium manganite Inorganic materials 0.000 description 2
- OHSVLFRHMCKCQY-UHFFFAOYSA-N lutetium atom Chemical compound [Lu] OHSVLFRHMCKCQY-UHFFFAOYSA-N 0.000 description 2
- 239000000203 mixture Substances 0.000 description 2
- QEFYFXOXNSNQGX-UHFFFAOYSA-N neodymium atom Chemical compound [Nd] QEFYFXOXNSNQGX-UHFFFAOYSA-N 0.000 description 2
- 239000010955 niobium Substances 0.000 description 2
- 239000000843 powder Substances 0.000 description 2
- PUDIUYLPXJFUGB-UHFFFAOYSA-N praseodymium atom Chemical compound [Pr] PUDIUYLPXJFUGB-UHFFFAOYSA-N 0.000 description 2
- VQMWBBYLQSCNPO-UHFFFAOYSA-N promethium atom Chemical compound [Pm] VQMWBBYLQSCNPO-UHFFFAOYSA-N 0.000 description 2
- 239000010948 rhodium Substances 0.000 description 2
- KZUNJOHGWZRPMI-UHFFFAOYSA-N samarium atom Chemical compound [Sm] KZUNJOHGWZRPMI-UHFFFAOYSA-N 0.000 description 2
- SIXSYDAISGFNSX-UHFFFAOYSA-N scandium atom Chemical compound [Sc] SIXSYDAISGFNSX-UHFFFAOYSA-N 0.000 description 2
- 239000011669 selenium Substances 0.000 description 2
- 239000011734 sodium Substances 0.000 description 2
- GZCRRIHWUXGPOV-UHFFFAOYSA-N terbium atom Chemical compound [Tb] GZCRRIHWUXGPOV-UHFFFAOYSA-N 0.000 description 2
- NAWDYIZEMPQZHO-UHFFFAOYSA-N ytterbium Chemical compound [Yb] NAWDYIZEMPQZHO-UHFFFAOYSA-N 0.000 description 2
- 229910052727 yttrium Inorganic materials 0.000 description 2
- VWQVUPCCIRVNHF-UHFFFAOYSA-N yttrium atom Chemical compound [Y] VWQVUPCCIRVNHF-UHFFFAOYSA-N 0.000 description 2
- ZOXJGFHDIHLPTG-UHFFFAOYSA-N Boron Chemical compound [B] ZOXJGFHDIHLPTG-UHFFFAOYSA-N 0.000 description 1
- OYPRJOBELJOOCE-UHFFFAOYSA-N Calcium Chemical compound [Ca] OYPRJOBELJOOCE-UHFFFAOYSA-N 0.000 description 1
- OKTJSMMVPCPJKN-UHFFFAOYSA-N Carbon Chemical compound [C] OKTJSMMVPCPJKN-UHFFFAOYSA-N 0.000 description 1
- 239000004215 Carbon black (E152) Substances 0.000 description 1
- UGFAIRIUMAVXCW-UHFFFAOYSA-N Carbon monoxide Chemical compound [O+]#[C-] UGFAIRIUMAVXCW-UHFFFAOYSA-N 0.000 description 1
- VYZAMTAEIAYCRO-UHFFFAOYSA-N Chromium Chemical compound [Cr] VYZAMTAEIAYCRO-UHFFFAOYSA-N 0.000 description 1
- LFQSCWFLJHTTHZ-UHFFFAOYSA-N Ethanol Chemical compound CCO LFQSCWFLJHTTHZ-UHFFFAOYSA-N 0.000 description 1
- DGAQECJNVWCQMB-PUAWFVPOSA-M Ilexoside XXIX Chemical compound C[C@@H]1CC[C@@]2(CC[C@@]3(C(=CC[C@H]4[C@]3(CC[C@@H]5[C@@]4(CC[C@@H](C5(C)C)OS(=O)(=O)[O-])C)C)[C@@H]2[C@]1(C)O)C)C(=O)O[C@H]6[C@@H]([C@H]([C@@H]([C@H](O6)CO)O)O)O.[Na+] DGAQECJNVWCQMB-PUAWFVPOSA-M 0.000 description 1
- 229910002148 La0.6Sr0.4MnO3 Inorganic materials 0.000 description 1
- 229910002328 LaMnO3 Inorganic materials 0.000 description 1
- 229910018281 LaSrMnO3 Inorganic materials 0.000 description 1
- WHXSMMKQMYFTQS-UHFFFAOYSA-N Lithium Chemical compound [Li] WHXSMMKQMYFTQS-UHFFFAOYSA-N 0.000 description 1
- FYYHWMGAXLPEAU-UHFFFAOYSA-N Magnesium Chemical compound [Mg] FYYHWMGAXLPEAU-UHFFFAOYSA-N 0.000 description 1
- ZOKXTWBITQBERF-UHFFFAOYSA-N Molybdenum Chemical compound [Mo] ZOKXTWBITQBERF-UHFFFAOYSA-N 0.000 description 1
- 108010060806 Photosystem II Protein Complex Proteins 0.000 description 1
- ZLMJMSJWJFRBEC-UHFFFAOYSA-N Potassium Chemical compound [K] ZLMJMSJWJFRBEC-UHFFFAOYSA-N 0.000 description 1
- KJTLSVCANCCWHF-UHFFFAOYSA-N Ruthenium Chemical compound [Ru] KJTLSVCANCCWHF-UHFFFAOYSA-N 0.000 description 1
- BUGBHKTXTAQXES-UHFFFAOYSA-N Selenium Chemical compound [Se] BUGBHKTXTAQXES-UHFFFAOYSA-N 0.000 description 1
- -1 SrCO2 Inorganic materials 0.000 description 1
- RTAQQCXQSZGOHL-UHFFFAOYSA-N Titanium Chemical compound [Ti] RTAQQCXQSZGOHL-UHFFFAOYSA-N 0.000 description 1
- HCHKCACWOHOZIP-UHFFFAOYSA-N Zinc Chemical compound [Zn] HCHKCACWOHOZIP-UHFFFAOYSA-N 0.000 description 1
- QCWXUUIWCKQGHC-UHFFFAOYSA-N Zirconium Chemical compound [Zr] QCWXUUIWCKQGHC-UHFFFAOYSA-N 0.000 description 1
- 238000011481 absorbance measurement Methods 0.000 description 1
- 238000004458 analytical method Methods 0.000 description 1
- 229910052787 antimony Inorganic materials 0.000 description 1
- WATWJIUSRGPENY-UHFFFAOYSA-N antimony atom Chemical compound [Sb] WATWJIUSRGPENY-UHFFFAOYSA-N 0.000 description 1
- 229910052786 argon Inorganic materials 0.000 description 1
- 229910052785 arsenic Inorganic materials 0.000 description 1
- RQNWIZPPADIBDY-UHFFFAOYSA-N arsenic atom Chemical compound [As] RQNWIZPPADIBDY-UHFFFAOYSA-N 0.000 description 1
- 229910052789 astatine Inorganic materials 0.000 description 1
- RYXHOMYVWAEKHL-UHFFFAOYSA-N astatine atom Chemical compound [At] RYXHOMYVWAEKHL-UHFFFAOYSA-N 0.000 description 1
- DSAJWYNOEDNPEQ-UHFFFAOYSA-N barium atom Chemical compound [Ba] DSAJWYNOEDNPEQ-UHFFFAOYSA-N 0.000 description 1
- 230000009286 beneficial effect Effects 0.000 description 1
- 229910052790 beryllium Inorganic materials 0.000 description 1
- ATBAMAFKBVZNFJ-UHFFFAOYSA-N beryllium atom Chemical compound [Be] ATBAMAFKBVZNFJ-UHFFFAOYSA-N 0.000 description 1
- 230000015572 biosynthetic process Effects 0.000 description 1
- 229910052796 boron Inorganic materials 0.000 description 1
- 229910052793 cadmium Inorganic materials 0.000 description 1
- BDOSMKKIYDKNTQ-UHFFFAOYSA-N cadmium atom Chemical compound [Cd] BDOSMKKIYDKNTQ-UHFFFAOYSA-N 0.000 description 1
- 229910052792 caesium Inorganic materials 0.000 description 1
- TVFDJXOCXUVLDH-UHFFFAOYSA-N caesium atom Chemical compound [Cs] TVFDJXOCXUVLDH-UHFFFAOYSA-N 0.000 description 1
- 229910002091 carbon monoxide Inorganic materials 0.000 description 1
- 229910000420 cerium oxide Inorganic materials 0.000 description 1
- 229910017052 cobalt Inorganic materials 0.000 description 1
- 239000010941 cobalt Substances 0.000 description 1
- GUTLYIVDDKVIGB-UHFFFAOYSA-N cobalt atom Chemical compound [Co] GUTLYIVDDKVIGB-UHFFFAOYSA-N 0.000 description 1
- 238000002485 combustion reaction Methods 0.000 description 1
- 239000000470 constituent Substances 0.000 description 1
- 230000001419 dependent effect Effects 0.000 description 1
- 238000000113 differential scanning calorimetry Methods 0.000 description 1
- 238000000635 electron micrograph Methods 0.000 description 1
- 230000005281 excited state Effects 0.000 description 1
- 229910052730 francium Inorganic materials 0.000 description 1
- KLMCZVJOEAUDNE-UHFFFAOYSA-N francium atom Chemical compound [Fr] KLMCZVJOEAUDNE-UHFFFAOYSA-N 0.000 description 1
- GNPVGFCGXDBREM-UHFFFAOYSA-N germanium atom Chemical compound [Ge] GNPVGFCGXDBREM-UHFFFAOYSA-N 0.000 description 1
- PCHJSUWPFVWCPO-UHFFFAOYSA-N gold Chemical compound [Au] PCHJSUWPFVWCPO-UHFFFAOYSA-N 0.000 description 1
- 229910052737 gold Inorganic materials 0.000 description 1
- 229910052735 hafnium Inorganic materials 0.000 description 1
- VBJZVLUMGGDVMO-UHFFFAOYSA-N hafnium atom Chemical compound [Hf] VBJZVLUMGGDVMO-UHFFFAOYSA-N 0.000 description 1
- 229930195733 hydrocarbon Natural products 0.000 description 1
- 150000002430 hydrocarbons Chemical class 0.000 description 1
- XLYOFNOQVPJJNP-UHFFFAOYSA-M hydroxide Chemical compound [OH-] XLYOFNOQVPJJNP-UHFFFAOYSA-M 0.000 description 1
- 230000006872 improvement Effects 0.000 description 1
- 229910052741 iridium Inorganic materials 0.000 description 1
- GKOZUEZYRPOHIO-UHFFFAOYSA-N iridium atom Chemical compound [Ir] GKOZUEZYRPOHIO-UHFFFAOYSA-N 0.000 description 1
- JEIPFZHSYJVQDO-UHFFFAOYSA-N iron(III) oxide Inorganic materials O=[Fe]O[Fe]=O JEIPFZHSYJVQDO-UHFFFAOYSA-N 0.000 description 1
- MRELNEQAGSRDBK-UHFFFAOYSA-N lanthanum oxide Inorganic materials [O-2].[O-2].[O-2].[La+3].[La+3] MRELNEQAGSRDBK-UHFFFAOYSA-N 0.000 description 1
- 229910052744 lithium Inorganic materials 0.000 description 1
- 239000011656 manganese carbonate Substances 0.000 description 1
- WPBNNNQJVZRUHP-UHFFFAOYSA-L manganese(2+);methyl n-[[2-(methoxycarbonylcarbamothioylamino)phenyl]carbamothioyl]carbamate;n-[2-(sulfidocarbothioylamino)ethyl]carbamodithioate Chemical compound [Mn+2].[S-]C(=S)NCCNC([S-])=S.COC(=O)NC(=S)NC1=CC=CC=C1NC(=S)NC(=O)OC WPBNNNQJVZRUHP-UHFFFAOYSA-L 0.000 description 1
- 229910000016 manganese(II) carbonate Inorganic materials 0.000 description 1
- 238000004949 mass spectrometry Methods 0.000 description 1
- 238000011089 mechanical engineering Methods 0.000 description 1
- 150000002738 metalloids Chemical class 0.000 description 1
- 238000003801 milling Methods 0.000 description 1
- 230000003278 mimic effect Effects 0.000 description 1
- 230000004048 modification Effects 0.000 description 1
- 238000012986 modification Methods 0.000 description 1
- 229910052750 molybdenum Inorganic materials 0.000 description 1
- 239000011733 molybdenum Substances 0.000 description 1
- 229910052758 niobium Inorganic materials 0.000 description 1
- GUCVJGMIXFAOAE-UHFFFAOYSA-N niobium atom Chemical compound [Nb] GUCVJGMIXFAOAE-UHFFFAOYSA-N 0.000 description 1
- QJGQUHMNIGDVPM-UHFFFAOYSA-N nitrogen group Chemical group [N] QJGQUHMNIGDVPM-UHFFFAOYSA-N 0.000 description 1
- 229910052762 osmium Inorganic materials 0.000 description 1
- SYQBFIAQOQZEGI-UHFFFAOYSA-N osmium atom Chemical compound [Os] SYQBFIAQOQZEGI-UHFFFAOYSA-N 0.000 description 1
- 230000003647 oxidation Effects 0.000 description 1
- BMMGVYCKOGBVEV-UHFFFAOYSA-N oxo(oxoceriooxy)cerium Chemical compound [Ce]=O.O=[Ce]=O BMMGVYCKOGBVEV-UHFFFAOYSA-N 0.000 description 1
- KTUFCUMIWABKDW-UHFFFAOYSA-N oxo(oxolanthaniooxy)lanthanum Chemical compound O=[La]O[La]=O KTUFCUMIWABKDW-UHFFFAOYSA-N 0.000 description 1
- 125000004430 oxygen atom Chemical group O* 0.000 description 1
- 229910052763 palladium Inorganic materials 0.000 description 1
- 230000029553 photosynthesis Effects 0.000 description 1
- 238000010672 photosynthesis Methods 0.000 description 1
- 229910052697 platinum Inorganic materials 0.000 description 1
- 229910052699 polonium Inorganic materials 0.000 description 1
- HZEBHPIOVYHPMT-UHFFFAOYSA-N polonium atom Chemical compound [Po] HZEBHPIOVYHPMT-UHFFFAOYSA-N 0.000 description 1
- 239000011148 porous material Substances 0.000 description 1
- 229910052700 potassium Inorganic materials 0.000 description 1
- 239000011591 potassium Substances 0.000 description 1
- 229910052705 radium Inorganic materials 0.000 description 1
- HCWPIIXVSYCSAN-UHFFFAOYSA-N radium atom Chemical compound [Ra] HCWPIIXVSYCSAN-UHFFFAOYSA-N 0.000 description 1
- 150000002910 rare earth metals Chemical class 0.000 description 1
- 238000011084 recovery Methods 0.000 description 1
- 238000006479 redox reaction Methods 0.000 description 1
- 230000009467 reduction Effects 0.000 description 1
- 239000011369 resultant mixture Substances 0.000 description 1
- 229910052702 rhenium Inorganic materials 0.000 description 1
- WUAPFZMCVAUBPE-UHFFFAOYSA-N rhenium atom Chemical compound [Re] WUAPFZMCVAUBPE-UHFFFAOYSA-N 0.000 description 1
- 229910052703 rhodium Inorganic materials 0.000 description 1
- MHOVAHRLVXNVSD-UHFFFAOYSA-N rhodium atom Chemical compound [Rh] MHOVAHRLVXNVSD-UHFFFAOYSA-N 0.000 description 1
- 229910052701 rubidium Inorganic materials 0.000 description 1
- IGLNJRXAVVLDKE-UHFFFAOYSA-N rubidium atom Chemical compound [Rb] IGLNJRXAVVLDKE-UHFFFAOYSA-N 0.000 description 1
- 229910052707 ruthenium Inorganic materials 0.000 description 1
- 229910052711 selenium Inorganic materials 0.000 description 1
- 239000010703 silicon Substances 0.000 description 1
- 229910052709 silver Inorganic materials 0.000 description 1
- 239000004332 silver Substances 0.000 description 1
- 229910052708 sodium Inorganic materials 0.000 description 1
- 238000003746 solid phase reaction Methods 0.000 description 1
- 238000010671 solid-state reaction Methods 0.000 description 1
- 238000001228 spectrum Methods 0.000 description 1
- 238000000629 steam reforming Methods 0.000 description 1
- 238000003786 synthesis reaction Methods 0.000 description 1
- 229910052715 tantalum Inorganic materials 0.000 description 1
- GUVRBAGPIYLISA-UHFFFAOYSA-N tantalum atom Chemical compound [Ta] GUVRBAGPIYLISA-UHFFFAOYSA-N 0.000 description 1
- 229910052713 technetium Inorganic materials 0.000 description 1
- GKLVYJBZJHMRIY-UHFFFAOYSA-N technetium atom Chemical compound [Tc] GKLVYJBZJHMRIY-UHFFFAOYSA-N 0.000 description 1
- 229910052714 tellurium Inorganic materials 0.000 description 1
- PORWMNRCUJJQNO-UHFFFAOYSA-N tellurium atom Chemical compound [Te] PORWMNRCUJJQNO-UHFFFAOYSA-N 0.000 description 1
- 230000009466 transformation Effects 0.000 description 1
- WFKWXMTUELFFGS-UHFFFAOYSA-N tungsten Chemical compound [W] WFKWXMTUELFFGS-UHFFFAOYSA-N 0.000 description 1
- 229910052721 tungsten Inorganic materials 0.000 description 1
- 239000010937 tungsten Substances 0.000 description 1
- 238000004235 valence bond calculation Methods 0.000 description 1
- LEONUFNNVUYDNQ-UHFFFAOYSA-N vanadium atom Chemical compound [V] LEONUFNNVUYDNQ-UHFFFAOYSA-N 0.000 description 1
Images
Classifications
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
- B01J23/70—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper
- B01J23/76—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36
- B01J23/83—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36 with rare earths or actinides
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
- B01J23/70—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper
- B01J23/76—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36
- B01J23/84—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36 with arsenic, antimony, bismuth, vanadium, niobium, tantalum, polonium, chromium, molybdenum, tungsten, manganese, technetium or rhenium
- B01J23/889—Manganese, technetium or rhenium
- B01J23/8892—Manganese
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
- B01J23/16—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of arsenic, antimony, bismuth, vanadium, niobium, tantalum, polonium, chromium, molybdenum, tungsten, manganese, technetium or rhenium
- B01J23/32—Manganese, technetium or rhenium
- B01J23/34—Manganese
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
- B01J23/002—Mixed oxides other than spinels, e.g. perovskite
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
- B01J23/16—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of arsenic, antimony, bismuth, vanadium, niobium, tantalum, polonium, chromium, molybdenum, tungsten, manganese, technetium or rhenium
- B01J23/24—Chromium, molybdenum or tungsten
- B01J23/26—Chromium
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
- B01J23/70—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper
- B01J23/76—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36
- B01J23/84—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36 with arsenic, antimony, bismuth, vanadium, niobium, tantalum, polonium, chromium, molybdenum, tungsten, manganese, technetium or rhenium
- B01J23/889—Manganese, technetium or rhenium
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J35/00—Catalysts, in general, characterised by their form or physical properties
- B01J35/30—Catalysts, in general, characterised by their form or physical properties characterised by their physical properties
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J35/00—Catalysts, in general, characterised by their form or physical properties
- B01J35/70—Catalysts, in general, characterised by their form or physical properties characterised by their crystalline properties, e.g. semi-crystalline
- B01J35/733—Perovskite-type
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
- B01J37/08—Heat treatment
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
- C01B13/00—Oxygen; Ozone; Oxides or hydroxides in general
- C01B13/02—Preparation of oxygen
- C01B13/0229—Purification or separation processes
- C01B13/0233—Chemical processing only
- C01B13/024—Chemical processing only by reduction
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
- C01B3/00—Hydrogen; Gaseous mixtures containing hydrogen; Separation of hydrogen from mixtures containing it; Purification of hydrogen
- C01B3/02—Production of hydrogen or of gaseous mixtures containing a substantial proportion of hydrogen
- C01B3/04—Production of hydrogen or of gaseous mixtures containing a substantial proportion of hydrogen by decomposition of inorganic compounds, e.g. ammonia
- C01B3/042—Decomposition of water
- C01B3/045—Decomposition of water in gaseous phase
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
- C01B3/00—Hydrogen; Gaseous mixtures containing hydrogen; Separation of hydrogen from mixtures containing it; Purification of hydrogen
- C01B3/02—Production of hydrogen or of gaseous mixtures containing a substantial proportion of hydrogen
- C01B3/06—Production of hydrogen or of gaseous mixtures containing a substantial proportion of hydrogen by reaction of inorganic compounds containing electro-positively bound hydrogen, e.g. water, acids, bases, ammonia, with inorganic reducing agents
- C01B3/061—Production of hydrogen or of gaseous mixtures containing a substantial proportion of hydrogen by reaction of inorganic compounds containing electro-positively bound hydrogen, e.g. water, acids, bases, ammonia, with inorganic reducing agents by reaction of metal oxides with water
- C01B3/063—Cyclic methods
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
- C01B3/00—Hydrogen; Gaseous mixtures containing hydrogen; Separation of hydrogen from mixtures containing it; Purification of hydrogen
- C01B3/02—Production of hydrogen or of gaseous mixtures containing a substantial proportion of hydrogen
- C01B3/32—Production of hydrogen or of gaseous mixtures containing a substantial proportion of hydrogen by reaction of gaseous or liquid organic compounds with gasifying agents, e.g. water, carbon dioxide, air
- C01B3/34—Production of hydrogen or of gaseous mixtures containing a substantial proportion of hydrogen by reaction of gaseous or liquid organic compounds with gasifying agents, e.g. water, carbon dioxide, air by reaction of hydrocarbons with gasifying agents
- C01B3/38—Production of hydrogen or of gaseous mixtures containing a substantial proportion of hydrogen by reaction of gaseous or liquid organic compounds with gasifying agents, e.g. water, carbon dioxide, air by reaction of hydrocarbons with gasifying agents using catalysts
- C01B3/40—Production of hydrogen or of gaseous mixtures containing a substantial proportion of hydrogen by reaction of gaseous or liquid organic compounds with gasifying agents, e.g. water, carbon dioxide, air by reaction of hydrocarbons with gasifying agents using catalysts characterised by the catalyst
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
- C01B32/00—Carbon; Compounds thereof
- C01B32/40—Carbon monoxide
-
- C—CHEMISTRY; METALLURGY
- C07—ORGANIC CHEMISTRY
- C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
- C07C1/00—Preparation of hydrocarbons from one or more compounds, none of them being a hydrocarbon
- C07C1/02—Preparation of hydrocarbons from one or more compounds, none of them being a hydrocarbon from oxides of a carbon
-
- C—CHEMISTRY; METALLURGY
- C07—ORGANIC CHEMISTRY
- C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
- C07C1/00—Preparation of hydrocarbons from one or more compounds, none of them being a hydrocarbon
- C07C1/20—Preparation of hydrocarbons from one or more compounds, none of them being a hydrocarbon starting from organic compounds containing only oxygen atoms as heteroatoms
-
- C—CHEMISTRY; METALLURGY
- C07—ORGANIC CHEMISTRY
- C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
- C07C29/00—Preparation of compounds having hydroxy or O-metal groups bound to a carbon atom not belonging to a six-membered aromatic ring
- C07C29/15—Preparation of compounds having hydroxy or O-metal groups bound to a carbon atom not belonging to a six-membered aromatic ring by reduction of oxides of carbon exclusively
- C07C29/151—Preparation of compounds having hydroxy or O-metal groups bound to a carbon atom not belonging to a six-membered aromatic ring by reduction of oxides of carbon exclusively with hydrogen or hydrogen-containing gases
- C07C29/153—Preparation of compounds having hydroxy or O-metal groups bound to a carbon atom not belonging to a six-membered aromatic ring by reduction of oxides of carbon exclusively with hydrogen or hydrogen-containing gases characterised by the catalyst used
-
- C—CHEMISTRY; METALLURGY
- C07—ORGANIC CHEMISTRY
- C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
- C07C29/00—Preparation of compounds having hydroxy or O-metal groups bound to a carbon atom not belonging to a six-membered aromatic ring
- C07C29/15—Preparation of compounds having hydroxy or O-metal groups bound to a carbon atom not belonging to a six-membered aromatic ring by reduction of oxides of carbon exclusively
- C07C29/159—Preparation of compounds having hydroxy or O-metal groups bound to a carbon atom not belonging to a six-membered aromatic ring by reduction of oxides of carbon exclusively with reducing agents other than hydrogen or hydrogen-containing gases
-
- C—CHEMISTRY; METALLURGY
- C07—ORGANIC CHEMISTRY
- C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
- C07C31/00—Saturated compounds having hydroxy or O-metal groups bound to acyclic carbon atoms
- C07C31/02—Monohydroxylic acyclic alcohols
- C07C31/04—Methanol
-
- C—CHEMISTRY; METALLURGY
- C07—ORGANIC CHEMISTRY
- C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
- C07C9/00—Aliphatic saturated hydrocarbons
- C07C9/02—Aliphatic saturated hydrocarbons with one to four carbon atoms
- C07C9/04—Methane
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J2235/00—Indexing scheme associated with group B01J35/00, related to the analysis techniques used to determine the catalysts form or properties
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J2235/00—Indexing scheme associated with group B01J35/00, related to the analysis techniques used to determine the catalysts form or properties
- B01J2235/15—X-ray diffraction
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J2235/00—Indexing scheme associated with group B01J35/00, related to the analysis techniques used to determine the catalysts form or properties
- B01J2235/30—Scanning electron microscopy; Transmission electron microscopy
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J2523/00—Constitutive chemical elements of heterogeneous catalysts
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
- C01B2203/00—Integrated processes for the production of hydrogen or synthesis gas
- C01B2203/02—Processes for making hydrogen or synthesis gas
- C01B2203/0266—Processes for making hydrogen or synthesis gas containing a decomposition step
- C01B2203/0277—Processes for making hydrogen or synthesis gas containing a decomposition step containing a catalytic decomposition step
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
- C01B2203/00—Integrated processes for the production of hydrogen or synthesis gas
- C01B2203/08—Methods of heating or cooling
- C01B2203/0805—Methods of heating the process for making hydrogen or synthesis gas
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
- C01B2203/00—Integrated processes for the production of hydrogen or synthesis gas
- C01B2203/10—Catalysts for performing the hydrogen forming reactions
- C01B2203/1041—Composition of the catalyst
- C01B2203/1088—Non-supported catalysts
-
- C—CHEMISTRY; METALLURGY
- C07—ORGANIC CHEMISTRY
- C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
- C07C2523/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group C07C2521/00
- C07C2523/16—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group C07C2521/00 of arsenic, antimony, bismuth, vanadium, niobium, tantalum, polonium, chromium, molybdenum, tungsten, manganese, technetium or rhenium
- C07C2523/24—Chromium, molybdenum or tungsten
- C07C2523/26—Chromium
-
- C—CHEMISTRY; METALLURGY
- C07—ORGANIC CHEMISTRY
- C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
- C07C2523/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group C07C2521/00
- C07C2523/16—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group C07C2521/00 of arsenic, antimony, bismuth, vanadium, niobium, tantalum, polonium, chromium, molybdenum, tungsten, manganese, technetium or rhenium
- C07C2523/32—Manganese, technetium or rhenium
- C07C2523/34—Manganese
-
- C—CHEMISTRY; METALLURGY
- C07—ORGANIC CHEMISTRY
- C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
- C07C2523/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group C07C2521/00
- C07C2523/70—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group C07C2521/00 of the iron group metals or copper
- C07C2523/76—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group C07C2521/00 of the iron group metals or copper combined with metals, oxides or hydroxides provided for in groups C07C2523/02 - C07C2523/36
- C07C2523/84—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group C07C2521/00 of the iron group metals or copper combined with metals, oxides or hydroxides provided for in groups C07C2523/02 - C07C2523/36 with arsenic, antimony, bismuth, vanadium, niobium, tantalum, polonium, chromium, molybdenum, tungsten, manganese, technetium or rhenium
- C07C2523/889—Manganese, technetium or rhenium
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
- Y02C—CAPTURE, STORAGE, SEQUESTRATION OR DISPOSAL OF GREENHOUSE GASES [GHG]
- Y02C20/00—Capture or disposal of greenhouse gases
- Y02C20/10—Capture or disposal of greenhouse gases of nitrous oxide (N2O)
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
- Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
- Y02E60/00—Enabling technologies; Technologies with a potential or indirect contribution to GHG emissions mitigation
- Y02E60/30—Hydrogen technology
- Y02E60/36—Hydrogen production from non-carbon containing sources, e.g. by water electrolysis
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
- Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
- Y02P20/00—Technologies relating to chemical industry
- Y02P20/10—Process efficiency
- Y02P20/129—Energy recovery, e.g. by cogeneration, H2recovery or pressure recovery turbines
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
- Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
- Y02P20/00—Technologies relating to chemical industry
- Y02P20/10—Process efficiency
- Y02P20/133—Renewable energy sources, e.g. sunlight
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
- Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
- Y02P20/00—Technologies relating to chemical industry
- Y02P20/50—Improvements relating to the production of bulk chemicals
- Y02P20/52—Improvements relating to the production of bulk chemicals using catalysts, e.g. selective catalysts
Definitions
- the present invention relates to catalysts for thermochemical fuel production, and a method of producing fuel using thermochemical fuel production.
- thermochemical fuel generating method is a technology of producing a chemical fuel from thermal energy that may be obtained from sunlight and the like, and of storing the thermal energy as a chemical fuel.
- the fuel is produced by a two-step thermal cycle (thermochemical cycle) which includes a step performed under a high temperature (first temperature) and a step performed under a low temperature (second temperature).
- thermal cycle thermal cycle
- first temperature high temperature
- second temperature low temperature
- a catalyst oxide absorbs oxygen from a raw material, and thus fuels such as a syngas, methane, hydrocarbon, alcohol, and hydrogen may be produced.
- oxide-based catalysts mainly, ZnO—Zn, Fe 2 O 3 —FeO, CeO 2 —Ce 2 O 3 , CeO 2 having a nonstoichiometric composition, mixtures thereof, a partially substituted oxide, and the like have been reported.
- Water vapor modification of methane (CH 4 +H 2 O ⁇ 6H 2 +CO) using LaSrMnO 3 -based perovskite oxide has been reported, but this is completely different from thermochemical fuel generation (H 2 O ⁇ H 2 +1 ⁇ 2O 2 , or CO 2 ⁇ CO+1 ⁇ 2O 2 ) using water or carbon dioxide, and thermochemical fuel production using a perovskite oxide AXO 3 has not been reported until now.
- hydrogen is a clean energy source that generates only water after combustion, and thus hydrogen is expected as renewable energy.
- thermochemical cycle which includes a step performed under a high temperature (first temperature) and a step performed under a low temperature (second temperature), with respect to the high temperature heating
- a technology using solar energy for example, Japanese Unexamined Patent Application, First Publication No. 2009-263165.
- thermodynamic efficiency is calculated to be 15 to 75% depending on the oxide systems including ZnO—Zn, Fe 2 O 3 —FeO, CeO 2 —Ce 2 O 3 , nonstoichiometric CeO 2 systems, and some combinations between them. Other systems have been largely unexplored.
- a record solar-fuel conversion efficiency is 0.8% in a solar-thermochemical cycle of 800 to 1,630° C. using undoped ceria, with 1.3 to 1.5 liters of carbon monoxide and hydrogen production.
- cerium oxide As catalyst oxides that are used in the thermochemical fuel generation method, cerium oxide (ceria) is known as indicated in the specification of US Patent Application Publication No. 2009/0107044.
- the solar reactor lost energy of 50% or less as heat, specifically above 1,250° C., and energy of 40% or less as solar re-reflection from the aperture.
- a mechanical engineering approach and a materials science approach are possible.
- a heat recovery system might also be integrated. The challenge in this route is how to choose an appropriate oxide structure as well as materials chemistry process from millions of candidate oxides that might show the desired properties. Combinatorial synthesis might be very useful to make candidate oxides, but a rapid way to check fuel productivity at high temperatures is required.
- An object of the invention is to provide a catalyst, which is formed from a perovskite oxide, for thermochemical fuel production, and a method of producing fuel using thermochemical fuel production that is capable of allowing a fuel to be produced in a thermochemical manner.
- the invention proposes catalysts for thermochemical fuel production, particularly, bio-inspired catalytic perovskite for solar thermochemical water splitting.
- Natural photosynthesis specifically, water oxidation is catalyzed in the Mn 4 CaO 5 cluster that possesses the cubic-like frame with a projection. It is anticipated that the artificial water splitting might occur in a similar cubic-like structure containing manganese elements. This hypothesis led to the thermochemical water splitting experiment using manganese-based perovskite (a cubic-like structure, a structure shown on the right of graph in FIG. 3 ).
- the perovskite splits water and produces hydrogen with the amount exceeding the amount of hydrogen the ceria produces.
- thermochemical water splitting using nonstoichiometric perovskite oxides.
- the Sr-doped LaMnO 3 perovskites were utilized in the steam reforming of methane, but no thermochemical water splitting has been demonstrated in perovskite oxides.
- the black color of the perovskite, compared with the white color of ceria, would be beneficial in efficient solar absorbance, thus making possible efficient solar-fuel conversion.
- the two-step thermochemical cycle reaction which uses the perovskite oxide as catalyst for hydrogen production as an example of the catalyst for the thermochemical fuel production, includes the following two steps of an oxygen releasing reaction and a hydrogen generating reaction.
- thermochemical cycle reaction which uses the perovskite oxide as a catalyst for thermochemical methane production as an example of the catalyst for the thermochemical fuel production, includes the following two steps of an oxygen releasing reaction and a methane generating reaction.
- thermochemical cycle reaction which uses the perovskite oxide as a catalyst for thermochemical methanol production as an example of the catalyst for the thermochemical fuel production, includes the following two steps of an oxygen releasing reaction and a methane generating reaction.
- the invention provides the following means.
- a catalyst for thermochemical fuel production which is used for producing the fuel from thermal energy by using a two-step thermochemical cycle of a first temperature and a second temperature that is equal to or lower than the first temperature, wherein the catalyst is formed from a perovskite oxide having a compositional formula of AXO 3 ⁇ (provided that, 0 ⁇ 1).
- A represents one or more of a rare-earth element (excluding Ce), an alkaline earth metal element, and an alkali metal element
- X represents one or more of a transition metal element and a metalloid element
- O represents oxygen.
- thermochemical fuel production wherein the element A is one or more selected from a group consisting of La, Mg, Ca, Sr, and Ba, and the element X is one or more selected from a group consisting of Mn, Fe, Ti, Zr, V, Cr, Co, Ni, Cu, Zn, Mg, Al, Ga, In, C, Si, Ge, and Sn.
- thermochemical fuel production wherein the element A is La, and the element X is Mn.
- thermochemical fuel production A method of producing fuel using thermochemical fuel production, wherein the catalyst for thermochemical fuel production according to any one of (1) to (11) is used.
- thermochemical fuel production which produces the fuel from thermal energy by using the catalyst for thermochemical fuel production according to any one of (1) to (11) and by using a two-step thermochemical cycle of a first temperature and a second temperature that is equal to or lower than the first temperature, wherein the first temperature is 600 to 1,600° C., and the second temperature is 400 to 1,600° C.
- thermochemical fuel production according to (13) wherein the first temperature is attained by irradiation of condensed sunlight energy and heating, or by heating using waste heat.
- thermochemical fuel production which produces the fuel from thermal energy by using a two-step thermochemical cycle of a first temperature and a second temperature that is equal to or lower than the first temperature, the method including: a process of heating a perovskite oxide having a compositional formula of AXO 3 ⁇ (provided that, 0 ⁇ 1) to the first temperature to reduce the perovskite oxide; and a process of bringing a raw material gas into contact with the reduced perovskite oxide and oxidizing the perovskite oxide to produce the fuel.
- thermochemical fuel production according to (15), wherein the fuel is any one of hydrogen, methane, and methanol.
- thermochemical fuel production is a concept broadly extending to a concept of “thermochemical hydrogen production” in which water is decomposed into oxygen and hydrogen in relatively mild thermal conditions by combination of a plurality of chemical reactions to fuels including hydrogen.
- the case of “partially substituted with” is that in which the concentration (x) of the substituted element is in the range of more than 0 to less than 1 when the amount of the element to be substituted before substitution is set to 1.
- thermochemical fuel production is possible by changing an atmosphere, but in a case where the atmosphere is the same in each case, the “second temperature” represents a temperature lower than the “first temperature”.
- thermochemical fuel production it is possible to provide a catalyst, which is formed from a perovskite oxide, for thermochemical fuel production, and a method of producing fuel using thermochemical fuel production that is capable of allowing a fuel to be produced in a thermochemical manner.
- the present invention provides a new catalyst for thermochemical fuel production by using perovskite oxide AXO 3 .
- elements such as iron and manganese, which are, at present, abundantly found in the Earth's crust, are used, and thus the used amount of rare-earth elements may be reduced. Therefore, it is possible to provide a catalyst for thermochemical fuel production and a method of producing fuel using thermochemical fuel production, in which significant cost reduction may be anticipated, and this will enable the conversion of solar energy into chemical fuel in high efficiency and the storage thereof.
- FIG. 2 is secondary electron microscope photographs of La 0.8 Sr 0.2 Mn 1-x Fe x O 3 ⁇ .
- FIG. 3 is a graph illustrating a hydrogen production amount in the case of using La 0.8 Sr 0.2 Mn 1-x Fe x O 3 ⁇ as a catalyst for thermochemical fuel (hydrogen) production.
- FIG. 4 is a graph illustrating dependency of a hydrogen production (generation) amount on an iron concentration (x) in the case of using La 0.8 Sr 0.2 Mn 1-x Fe x O 3 ⁇ as a catalyst for thermochemical fuel (hydrogen) production.
- FIG. 5 is a graph illustrating a cycle characteristic of the hydrogen production amount in the case of using La 0.8 Sr 0.2 Mn 1-x Fe x O 3 ⁇ .
- FIG. 6A is a graph illustrating a cycle characteristic of the hydrogen production amount and an oxygen production amount in the case of using La 0.8 Sr 0.2 Mn 1-x Fe x O 3 ⁇
- FIG. 6B is a graph illustrating a cycle characteristic of the hydrogen production amount and the oxygen production amount.
- FIG. 7 is a graph illustrating a hydrogen production amount in the case of using (La 0.8 Sr 0.2 )MnO 3 ⁇ , (La 0.8 Sr 0.2 )(Mn 0.85 Ti 0.15 )O 3 ⁇ , (La 0.8 Sr 0.2 )(Mn 0.85 Fe 0.15 )O 3 ⁇ , (La 0.8 Sr 0.2 )(Mn 0.85 Ni 0.15 )O 3 ⁇ , (La 0.8 Sr 0.2 )(Mn 0.85 Mg 0.15 )O 3 ⁇ , and La(Mn 0.5 Mg 0.5 )O 3 ⁇ as a catalyst for thermochemical hydrogen production, respectively.
- FIG. 8 is a graph illustrating a cycle characteristic of the hydrogen production amount in the case of using (La 0.8 Sr 0.2 )MnO 3 ⁇ , (La 0.8 Sr 0.2 )(Mn 0.85 Ti 0.15 )O 3 ⁇ , (La 0.8 Sr 0.2 )(Mn 0.85 Fe 0.15 )O 3 ⁇ , (La 0.8 Sr 0.2 )(Mn 0.85 Ni 0.15 )O 3 ⁇ , and (La 0.8 Sr 0.2 )(Mn 0.85 Mg 0.15 )O 3 ⁇ as a catalyst for producing thermochemical hydrogen, respectively.
- FIG. 9 is a graph illustrating a hydrogen production amount and an oxygen production amount in a case where (La 0.8 Sr 0.2 )CrO 3 ⁇ as a catalyst for producing thermochemical hydrogen is used, a first temperature is set to 1,300° C., and a second temperature is set to 800° C.
- FIG. 10 is a graph illustrating a hydrogen production amount and an oxygen production amount in a case where (La 0.8 Sr 0.2 )CrO 3 ⁇ as a catalyst for producing thermochemical hydrogen is used, a first temperature is set to 1,500° C., and a second temperature is set to 800° C.
- FIG. 11 is a graph illustrating a hydrogen production amount in the case of using Ba(Ti 0.6 Mn 0.4 )O 3 ⁇ as a catalyst for thermochemical hydrogen production.
- FIG. 13 is a graph illustrating a hydrogen production amount in the case of using (La 0.8 Sr 0.2 )MnO 3 ⁇ and (La 0.8 Ba 0.2 )MnO 3 ⁇ as a catalyst for thermochemical hydrogen production.
- FIG. 14 is a graph illustrating a hydrogen production amount in the case of using (La 0.8 Ba 0.2 )(Mn 0.25 Fe 0.75 )O 3 ⁇ as a catalyst for thermochemical hydrogen production.
- the catalyst for thermochemical fuel production according to the invention is a catalyst for thermochemical fuel production, which is used for producing the fuel from thermal energy by using a two-step thermochemical cycle of a first temperature and a second temperature that is equal to or lower than the first temperature.
- the catalyst is formed from a perovskite oxide having a compositional formula of AXO 3 ⁇ (provided that, 0 ⁇ 1).
- A represents one or more of a rare-earth element (excluding Ce), an alkaline earth metal element, and an alkali metal element
- X represents one or more of a transition metal element and a metalloid (semi-metallic) element
- O represents oxygen.
- a value of ⁇ may be determined in a range not deteriorating an effect of the invention.
- rare-earth element examples include Sc (scandium), Y (yttrium), La (lanthanum), Pr (praseodymium), Nd (neodymium), Pm (promethium), Sm (samarium), Eu (europium), Gd (gadolinium), Tb (terbium), Dy (dysprosium), Ho (holmium), Er (erbium), Tm (thulium), Yb (ytterbium), Lu (lutetium), and the like.
- alkaline earth metal element examples include Be (beryllium), Mg (magnesium), Ca (calcium), Sr (strontium), Ba (barium), and Ra (radium).
- alkali metal examples include Li (lithium), Na (sodium), K (potassium), Rb (rubidium), Cs (cesium), and Fr (francium).
- transition metal element examples include first transition elements (3d transition elements) such as Sc (scandium), Ti (titanium), V(vanadium), Cr (chromium), Mn (manganese), Fe (iron), Co (cobalt), Ni (nickel), Cu (copper), and Zn (zinc), second transition elements (4d transition elements) such as Y (yttrium), Zr (zirconium), Nb (niobium), Mo (molybdenum), Tc (technetium), Ru (ruthenium), Rh (rhodium), Pd (palladium), Ag (silver), and Cd (cadmium), and third transition elements (4f transition elements) such as La (lanthanum), Pr (praseodymium), Nd (neodymium), Pm (promethium), Sm (samarium), Eu (europium), Gd (gadolinium), Tb (terbium), Dy (dysprosium), Ho (holmium), Er (erbium), T
- metalloid element examples include B (boron), Si (silicon), Ge (germanium), As (arsenic), Sb (antimony), Te (tellurium), Se (selenium), Po (polonium), and At (astatine).
- a method of producing fuel using thermochemical fuel production according to an embodiment of the invention is a method of producing fuel using thermochemical fuel production, which produces the fuel from thermal energy by using the catalyst for thermochemical fuel production of the invention and by using a two-step thermochemical cycle of a first temperature and a second temperature that is equal to or lower than the first temperature.
- the first temperature is 600 to 1,600° C.
- the second temperature is 400 to 1,600° C.
- the first temperature and/or the second temperature are attained, for example, by irradiation of condensed sunlight energy and heating, or by heating using waste heat.
- waste heat for example, waste heat of a power generator, a blast furnace, and the like may be used.
- the first temperature may be set to 600 to 1,600° C. (for example, 1,400° C.), and the second temperature may be set to 400 to 1,600° C. (for example, 800° C.).
- the first temperature may be set to 600 to 1,600° C. (for example, 1,400° C.), and the second temperature may be set to 300 to 1,600° C. (for example, 450° C.).
- the first temperature may be set to 600 to 1,600° C. (for example, 1,400° C.), and the second temperature may be set to 200 to 1,600° C. (for example, 350° C.).
- a method of producing fuel using thermochemical fuel production is a method of producing fuel using thermochemical fuel production, which produces the fuel from thermal energy by using a two-step thermochemical cycle of a first temperature and a second temperature that is equal to or lower than the first temperature.
- the method includes a process of heating a perovskite oxide having a compositional formula of AXO 3 ⁇ (provided that, 0 ⁇ 1) to the first temperature to reduce the perovskite oxide, and a process of bringing a raw material gas into contact with the reduced perovskite oxide and oxidizing the perovskite oxide to produce the fuel.
- a value of ⁇ may be determined in a range not deteriorating an effect of the invention.
- Examples of the fuel which may be produced by the method of producing fuel using thermochemical fuel production of the invention, include hydrogen, methane, and methanol, but are not limited thereto.
- water vapor may be exemplified, but it is not limited thereto.
- Hydrogen may be produced by using the water vapor.
- carbon dioxide and water vapor may be exemplified.
- Methane or methanol may be produced by using carbon dioxide and water vapor.
- perovskite oxide In the production of the catalyst for thermochemical hydrogen, a known method of producing perovskite oxide may be used. For example, powders of raw materials (oxide, hydroxide, oxide-hydroxide, and the like) including elements of a desired perovskite oxide are weighed to obtain a target compositional ratio, and are mixed and crushed. Then, the resultant mixture is calcined, and then the resultant calcined material is fired to produce the catalyst for producing thermochemical hydrogen.
- Porous pellet of La 0.8 Sr 0.2 Mn 1-x Fe x O 3 ⁇ were synthesized via solid-state reaction.
- raw material oxides La 2 O 3 , SrCO 2 , MnCO 3 , and Fe 2 O 3
- These powders, that were obtained, were put into a die with isopropanol and were sintered at 1,500° C. for 10 hours to obtain the porous pellets.
- the pellet of La 0.8 Sr 0.2 Mn 1-x Fe x O 3 ⁇ had a perovskite structure by X-ray diffraction (refer to FIG. 1 ).
- the resultant porosity of the pellet was approximately 60%.
- the resultant pellets had various sizes of pores, ranging from a few to over 100 ⁇ m from a secondary electron microscopy image (refer to FIG. 2 ).
- the production of hydrogen may be carried out as described below by using the catalyst for thermochemical hydrogen production.
- the porous pallet was placed inside an infrared furnace and was heated up to 1,400° C. (corresponding to the “first temperature” of the two-step thermochemical cycle) in dry nitrogen containing 10 ppm of oxygen. At this time, it was observed that oxygen was released from the pellet by using mass spectroscopy. Then, the pellet was cooled down to 800° C. (corresponding to the “second temperature” of the two-step thermochemical cycle), followed by flowing 10% water vapor containing argon gas. Hydrogen evolution was observed at 800° C. with an amount of 3 ml/g (corresponding to 60% or less of a hydrogen evolution amount in the case of using undoped ceria). The hydrogen evolution reaction was completed within 10 minutes as shown in FIG. 3 .
- La 0.8 Sr 0.2 Mn 1-x Fe x O 3 ⁇ in which manganese is partially replaced with iron that has a higher electronegativity in the valence bond theory was synthesized. Analysis results of La 0.8 Sr 0.2 Mn 1-x Fe x O 3 ⁇ are shown below.
- FIG. 1 shows a graph illustrating X-ray diffraction results of La 0.8 Sr 0.2 Mn 1-x Fe x O 3 ⁇ .
- the perovskite structure is maintained at the entire iron concentrations (x) of La 0.8 Sr 0.2 Mn 1-x Fe x O 3 ⁇ . Differential scanning calorimetry also showed no evidence in phase transformation up to 1,400° C.
- FIG. 2 shows secondary electron microscope photographs of La 0.8 Sr 0.2 Mn 1-x Fe x O 3 ⁇ .
- (a), (c), (e), (g), and (i) represent the secondary electron microscope photographs before the thermal cycle
- (b), (d), (f), (h), and (j) represent the secondary electron microscope photographs after the thermal cycle of 800 to 1400° C.
- the iron concentration x is 0, in (c) and (d)
- the iron concentration x is 0.3
- the iron concentration x is 0.5
- the iron concentration x is 0.75
- in (i) and (j) the iron concentration x is 1.
- porous structure is maintained after the thermal cycle in any specimen.
- FIG. 3 shows a graph illustrating a hydrogen production amount in the case of using La 0.8 Sr 0.2 Mn 1-x Fe x O 3 ⁇ as a catalyst for thermochemical hydrogen production.
- the first temperature and the second temperature of the thermal (thermochemical) cycle were 1,400° C. and 800° C., respectively.
- FIG. 4 shows a graph illustrating dependency of a hydrogen production (generation) amount on an iron concentration (x) in the case of using La 0.8 Sr 0.2 Mn 1-x Fe x O 3 ⁇ as a catalyst for thermochemical hydrogen production.
- the first temperature and the second temperature of the thermal cycle were 1,400° C. and 800° C., respectively.
- Results indicated by a white circle represent first cycle results, and results indicated by a black circle represent ninth cycle results.
- FIG. 5 shows a graph illustrating a cycle characteristic of the hydrogen production amount in the case of using La 0.8 Sr 0.2 Mn 1-x Fe x O 3 ⁇ as the catalyst for thermochemical hydrogen production.
- the first temperature and the second temperature of the thermal cycle were 1,400° C. and 800° C., respectively.
- the hydrogen production amount gradually increased with the cycle.
- the hydrogen production amount became constant at fifteen cycles.
- FIG. 6A shows a graph illustrating a cycle characteristic of the hydrogen production amount and the oxygen production amount in the case of using La 0.8 Sr 0.2 Mn 1-x Fe x O 3 ⁇
- FIG. 6B shows a graph illustrating a cycle characteristic of the hydrogen production amount and the oxygen production amount.
- the first temperature and the second temperature of the thermal cycle were 1,400° C. and 800° C., respectively.
- a ratio (H 2 amount/O 2 amount) of the hydrogen production amount and the oxygen production amount is approximately two, and FIG. 6B shows results of water splitting.
- FIG. 7 shows a graph illustrating a hydrogen production amount in the case of using (La 0.8 Sr 0.2 )MnO 3 ⁇ , (La 0.8 Sr 0.2 )(Mn 0.85 Ti 0.15 )O 3 ⁇ , (La 0.8 Sr 0.2 )(Mn 0.85 Fe 0.15 )O 3 ⁇ , (La 0.8 Sr 0.2 )(Mn 0.85 Ni 0.15 )O 3 ⁇ , (La 0.8 Sr 0.2 )(Mn 0.85 Mg 0.15 )O 3 ⁇ , and La(Mn 0.5 Mg 0.5 )O 3 ⁇ as a catalyst for thermochemical hydrogen production.
- the hydrogen production amount is indicated by a flow rate (ml/min/g) per unit gram.
- the first temperature and the second temperature of the thermal (thermochemical) cycle were 1,400° C. and 800° C.
- hydrogen may be produced in a thermochemical manner.
- FIG. 8 shows a graph illustrating a cycle characteristic of the hydrogen production amount in the case of using (La 0.8 Sr 0.2 )MnO 3 ⁇ , (La 0.8 Sr 0.2 )(Mn 0.85 Ti 0.15 )O 3 ⁇ , (La 0.8 Sr 0.2 )(Mn 0.85 Fe 0.15 )O 3 ⁇ , (La 0.8 Sr 0.2 )(Mn 0.85 Ni 0.15 )O 3 ⁇ , and (La 0.8 Sr 0.2 )(Mn 0.85 Mg 0.15 )O 3 ⁇ as a catalyst for thermochemical hydrogen production.
- the first temperature and the second temperature of the thermal cycle were 1,400° C. and 800° C., respectively.
- FIG. 9 shows a graph illustrating a hydrogen production amount and an oxygen production amount in a case of using (La 0.8 Sr 0.2 )CrO 3 ⁇ as the catalyst for thermochemical hydrogen production.
- the production amount is indicated by a flow rate (ml/min/g) per unit gram.
- the first temperature and the second temperature of the thermal (thermochemical) cycle were 1,400° C. and 800° C., respectively.
- FIG. 10 shows a graph illustrating a hydrogen production amount and an oxygen production amount in the case of using (La 0.8 Sr 0.2 )CrO 3 ⁇ as the catalyst for producing thermochemical hydrogen similarly to FIG. 9 .
- the first temperature and the second temperature of the thermal (thermochemical) cycle were 1,500° C. and 800° C., respectively.
- FIG. 11 shows a graph illustrating the hydrogen production amount in the case of using Ba(Ti 0.6 Mn 0.4 )O 3 ⁇ as the catalyst for thermochemical hydrogen production.
- the first temperature and the second temperature of the thermal (thermochemical) cycle were 1,400° C. and 800° C., respectively.
- the production amount is indicated by a flow rate (sccm/g) per unit gram.
- the first temperature and the second temperature of the thermal (thermochemical) cycle were 1,500° C. and 800° C., respectively.
- FIG. 13 shows a graph illustrating a hydrogen production amount in the case of using (La 0.8 Sr 0.2 )MnO 3 ⁇ and (La 0.8 Ba 0.2 )MnO 3 ⁇ as a catalyst for thermochemical hydrogen production.
- the production amount is indicated by a flow rate (ml/min/g) per unit gram.
- the first temperature and the second temperature of the thermal (thermochemical) cycle were 1,400° C. and 800° C., respectively.
- FIG. 14 is a graph illustrating the hydrogen production amount in the case of using (La 0.8 Ba 0.2 )(Mn 0.25 Fe 0.75 )O 3 ⁇ as the catalyst for thermochemical hydrogen production.
- the production amount is indicated by a flow rate (ml/min/g) per unit gram.
- the first temperature of the thermal (thermochemical) cycle was 1,400° C., but the second temperatures thereof were 700° C., 800° C., and 1,000° C., respectively.
- the hydrogen production amount did not vary largely. However, conversely, in the case where the second temperature was 1,000° C., the hydrogen production amount decreased compared to the case in which the second temperatures were 700° C. and 800° C. by approximately 10%.
- the concentrated solar energy needs to be absorbed by the perovskite oxide.
- the solar spectrum ranges from ultraviolet to visible and infrared region (250 nm to over 2700 nm).
- the absorbed photon excites electrons from the lower-state to the excited state, which will eventually be converted to heat via phonon.
- the solar absorbance measurement shows that the La 0.8 Sr 0.2 Mn 0.25 Fe 0.75 O 3 ⁇ perovskite absorbs solar energy quite efficiently, at 4 times of ceria.
- the elements composed in the perovskite are quite earth abundant.
- the earth abundance of iron and manganese are 35 and 0.6 times the earth abundance of carbon, respectively.
- Strontium (Sr) exists in the earth crust 5 times more than copper (Cu), and the lanthanum (La) is a half of copper.
- the present inventors developed catalytic La 0.8 Sr 0.2 Mn 1-x Fe x O 3 ⁇ perovskites for thermochemical hydrogen production by mimicking the catalytic center of Mn 4 CaO 5 cluster in photosystem II.
- La 0.8 Sr 0.2 Mn 0.25 Fe 0.75 O 3 ⁇ produces 5.3 ml/g of hydrogen in the thermochemical cycle between 800 and 1400° C.
- the advantages of utilizing nonstoichiometric perovskite over undoped ceria are more efficient solar absorbance by 4 times or less, the earth abundant element utilization for scalable solar fuel production, and lower temperature operation at 1200 to 1400° C.
- the strontium which is abundant in the Earth in this system is completely soluble in lanthanum, and it is possible to mimic the rare-earth utilization in the catalytic perovskite.
- the invention will allow the conversion of solar energy into chemical fuel in high efficiency and the storage thereof, and the obtained chemical fuel will be used as clean energy in the field of each industry and as clean industrial raw materials in chemical industry.
Landscapes
- Chemical & Material Sciences (AREA)
- Organic Chemistry (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Inorganic Chemistry (AREA)
- General Health & Medical Sciences (AREA)
- Combustion & Propulsion (AREA)
- Health & Medical Sciences (AREA)
- General Chemical & Material Sciences (AREA)
- Thermal Sciences (AREA)
- Physics & Mathematics (AREA)
- Analytical Chemistry (AREA)
- Oil, Petroleum & Natural Gas (AREA)
- Catalysts (AREA)
- Carbon And Carbon Compounds (AREA)
- Organic Low-Molecular-Weight Compounds And Preparation Thereof (AREA)
- Low-Molecular Organic Synthesis Reactions Using Catalysts (AREA)
- Oxygen, Ozone, And Oxides In General (AREA)
Priority Applications (8)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US13/600,948 US20130252808A1 (en) | 2012-03-23 | 2012-08-31 | Catalysts for thermochemical fuel production and method of producing fuel using thermochemical fuel production |
EP13764774.9A EP2829321A4 (en) | 2012-03-23 | 2013-03-22 | CATALYST FOR PRODUCING A THERMOCHEMICAL FUEL AND METHOD FOR PRODUCING A THERMOCHEMICAL FUEL |
PCT/JP2013/058431 WO2013141385A1 (ja) | 2012-03-23 | 2013-03-22 | 熱化学燃料製造用触媒及び熱化学燃料製造方法 |
CN201380015007.4A CN104203403B (zh) | 2012-03-23 | 2013-03-22 | 热化学燃料制造用催化剂及热化学燃料制造方法 |
JP2013549447A JP5594800B2 (ja) | 2012-03-23 | 2013-03-22 | 熱化学燃料製造用触媒及び熱化学燃料製造方法 |
TW102110240A TWI603779B (zh) | 2012-03-23 | 2013-03-22 | 熱化學燃料製造用觸媒及熱化學燃料製造方法 |
KR1020147029479A KR101790093B1 (ko) | 2012-03-23 | 2013-03-22 | 열화학 연료 제조용 촉매 및 열화학 연료 제조 방법 |
US14/595,130 US9873109B2 (en) | 2012-03-23 | 2015-01-12 | Catalysts for thermochemical fuel production and method of producing fuel using thermochemical fuel production |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US201261615122P | 2012-03-23 | 2012-03-23 | |
US13/600,948 US20130252808A1 (en) | 2012-03-23 | 2012-08-31 | Catalysts for thermochemical fuel production and method of producing fuel using thermochemical fuel production |
Related Child Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US14/595,130 Division US9873109B2 (en) | 2012-03-23 | 2015-01-12 | Catalysts for thermochemical fuel production and method of producing fuel using thermochemical fuel production |
Publications (1)
Publication Number | Publication Date |
---|---|
US20130252808A1 true US20130252808A1 (en) | 2013-09-26 |
Family
ID=49212343
Family Applications (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US13/600,948 Abandoned US20130252808A1 (en) | 2012-03-23 | 2012-08-31 | Catalysts for thermochemical fuel production and method of producing fuel using thermochemical fuel production |
US14/595,130 Active US9873109B2 (en) | 2012-03-23 | 2015-01-12 | Catalysts for thermochemical fuel production and method of producing fuel using thermochemical fuel production |
Family Applications After (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US14/595,130 Active US9873109B2 (en) | 2012-03-23 | 2015-01-12 | Catalysts for thermochemical fuel production and method of producing fuel using thermochemical fuel production |
Country Status (7)
Country | Link |
---|---|
US (2) | US20130252808A1 (zh) |
EP (1) | EP2829321A4 (zh) |
JP (1) | JP5594800B2 (zh) |
KR (1) | KR101790093B1 (zh) |
CN (1) | CN104203403B (zh) |
TW (1) | TWI603779B (zh) |
WO (1) | WO2013141385A1 (zh) |
Cited By (14)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20130266504A1 (en) * | 2012-04-06 | 2013-10-10 | California Institute Of Technology | Methods and Materials for the Thermochemical Production of Hydrogen From Water |
US20160122261A1 (en) * | 2013-03-15 | 2016-05-05 | Siluria Technologies, Inc. | Catalysts for petrochemical catalysis |
US9718054B2 (en) | 2010-05-24 | 2017-08-01 | Siluria Technologies, Inc. | Production of ethylene with nanowire catalysts |
US9751079B2 (en) | 2014-09-17 | 2017-09-05 | Silura Technologies, Inc. | Catalysts for natural gas processes |
US9751818B2 (en) | 2011-11-29 | 2017-09-05 | Siluria Technologies, Inc. | Nanowire catalysts and methods for their use and preparation |
US9868636B1 (en) * | 2012-12-06 | 2018-01-16 | National Technology & Engineering Solutions Of Sandia, Llc | Thermochemically active iron titanium oxide materials |
US9956544B2 (en) | 2014-05-02 | 2018-05-01 | Siluria Technologies, Inc. | Heterogeneous catalysts |
US9963402B2 (en) | 2011-05-24 | 2018-05-08 | Siluria Technologies, Inc. | Catalysts for petrochemical catalysis |
US10189708B2 (en) * | 2016-08-18 | 2019-01-29 | The United States Of America As Represented By The U.S. Environmental Protection Agency | Ruthenium on chitosan (ChRu): concerted catalysis for water splitting and reduction |
CN109745991A (zh) * | 2018-12-13 | 2019-05-14 | 大连海事大学 | 用于煤气化的复合金属氧化物催化剂的制备方法及应用 |
US10604854B2 (en) | 2014-07-17 | 2020-03-31 | The Board Of Trustees Of The Leland Stanford Junior University | Heterostructures for ultra-active hydrogen evolution electrocatalysis |
US11370724B2 (en) | 2012-05-24 | 2022-06-28 | Lummus Technology Llc | Catalytic forms and formulations |
CN114904511A (zh) * | 2022-03-24 | 2022-08-16 | 南京航空航天大学 | 一种基于SmMnO3钙钛矿的CO2热化学转化材料制备方法和应用 |
US11634322B2 (en) | 2019-04-03 | 2023-04-25 | California Institute Of Technology | Integration of thermochemical water splitting with CO2 direct air capture |
Families Citing this family (18)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
KR101856726B1 (ko) * | 2014-12-08 | 2018-05-10 | 주식회사 엘지화학 | 유무기 하이브리드 페로브스카이트 화합물, 이의 제조방법 및 이를 포함하는 태양전지 |
GB201511855D0 (en) * | 2015-07-07 | 2015-08-19 | Univ Newcastle | Chemical looping |
WO2017104331A1 (ja) * | 2015-12-14 | 2017-06-22 | 京セラ株式会社 | 水素製造用部材および水素製造装置 |
US11198607B2 (en) | 2016-02-25 | 2021-12-14 | Kyocera Corporation | Light absorbing member, member for hydrogen production, and hydrogen production apparatus |
US10946362B1 (en) * | 2017-02-24 | 2021-03-16 | University Of South Florida | Perovskite oxides for thermochemical conversion of carbon dioxide |
JP6787826B2 (ja) * | 2017-03-28 | 2020-11-18 | 京セラ株式会社 | 水素生成用セル、集光型水素生成用セルおよび水素製造装置 |
JP6945252B2 (ja) * | 2018-04-12 | 2021-10-06 | 国立研究開発法人物質・材料研究機構 | 六方晶系6h型バリウムゲルマニウム酸化物、その製造方法、焼結体、および、ターゲット |
CN110152678B (zh) * | 2019-06-05 | 2021-12-14 | 内蒙古元瓷新材料科技有限公司 | 一种电催化还原CO2为能源的纳米Cu-Yb合金催化剂 |
FR3102764B1 (fr) * | 2019-11-06 | 2022-05-13 | Psa Automobiles Sa | Dispositif de production d’hydrogene par boucle chimique avec un materiau porteur d’oxygene de type perovskite |
JP7417224B2 (ja) * | 2020-01-31 | 2024-01-18 | Eneos株式会社 | 水素の製造方法、一酸化炭素の製造方法および反応媒体 |
CN111285327B (zh) * | 2020-02-18 | 2021-10-19 | 西北大学 | 一种甲烷化学链部分氧化制合成气的方法 |
CN112076755B (zh) * | 2020-10-19 | 2023-02-28 | 宁夏大学 | 一种co2加氢催化剂的制备方法及应用 |
CN113582240B (zh) * | 2020-12-11 | 2022-09-23 | 浙江大学 | 热化学储热材料、热化学储热模块及制备方法 |
WO2022163819A1 (ja) * | 2021-01-28 | 2022-08-04 | 積水化学工業株式会社 | 酸素キャリアおよびガスの製造方法 |
EP4299509A1 (en) | 2021-02-26 | 2024-01-03 | Kyocera Corporation | Hydrogen production device |
WO2022181619A1 (ja) * | 2021-02-26 | 2022-09-01 | 京セラ株式会社 | 水素製造装置及び水素製造方法 |
JPWO2022196729A1 (zh) * | 2021-03-17 | 2022-09-22 | ||
JPWO2023119956A1 (zh) * | 2021-12-24 | 2023-06-29 |
Citations (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5380692A (en) * | 1991-09-12 | 1995-01-10 | Sakai Chemical Industry Co., Ltd. | Catalyst for catalytic reduction of nitrogen oxide |
US6033632A (en) * | 1993-12-08 | 2000-03-07 | Eltron Research, Inc. | Solid state oxygen anion and electron mediating membrane and catalytic membrane reactors containing them |
US20050245391A1 (en) * | 2002-07-09 | 2005-11-03 | Hirohisa Tanaka | Catalyst for exhaust gas purification |
US20070105715A1 (en) * | 2004-12-24 | 2007-05-10 | Hisashi Suda | Particulate matter oxidation catalyst and filter |
US20100278709A1 (en) * | 2007-10-24 | 2010-11-04 | David Waller | Catalyst for production of nitric oxide |
US20110082030A1 (en) * | 2009-10-01 | 2011-04-07 | Gm Global Technology Operations, Inc. | Washcoating technique for perovskite catalysts |
US20110297666A1 (en) * | 2008-07-10 | 2011-12-08 | Epcos Ag | Heating Apparatus and Method for Producing the Heating Apparatus |
Family Cites Families (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN1095455C (zh) * | 2000-01-03 | 2002-12-04 | 中国科学院物理研究所 | 掺锰钛酸钡薄膜材料及其制备方法 |
JP2004269296A (ja) * | 2003-03-06 | 2004-09-30 | Kurosaki Harima Corp | 水の分解による水素製造法とそれに使用する反応媒体 |
US8167961B2 (en) | 2007-10-26 | 2012-05-01 | California Institute Of Technology | Thermochemical synthesis of fuels for storing thermal energy |
JP2009263165A (ja) | 2008-04-25 | 2009-11-12 | Tokyo Institute Of Technology | 反応性セラミックスおよびその製造方法、ならびに水素製造方法および水素製造装置 |
JP2011529531A (ja) * | 2008-07-29 | 2011-12-08 | イエダ・リサーチ・アンド・デベロツプメント・カンパニー・リミテツド | 化学ポテンシャルエネルギー生成のためのシステム及び方法 |
CN102030311A (zh) * | 2009-09-28 | 2011-04-27 | 琳德股份公司 | 氢气和合成气的生产方法 |
US8435486B2 (en) * | 2010-05-24 | 2013-05-07 | Toyota Jidosha Kabushiki Kaisha | Redox material for thermochemical water splitting, and method for producing hydrogen |
-
2012
- 2012-08-31 US US13/600,948 patent/US20130252808A1/en not_active Abandoned
-
2013
- 2013-03-22 JP JP2013549447A patent/JP5594800B2/ja active Active
- 2013-03-22 EP EP13764774.9A patent/EP2829321A4/en active Pending
- 2013-03-22 TW TW102110240A patent/TWI603779B/zh not_active IP Right Cessation
- 2013-03-22 KR KR1020147029479A patent/KR101790093B1/ko active IP Right Grant
- 2013-03-22 CN CN201380015007.4A patent/CN104203403B/zh active Active
- 2013-03-22 WO PCT/JP2013/058431 patent/WO2013141385A1/ja active Application Filing
-
2015
- 2015-01-12 US US14/595,130 patent/US9873109B2/en active Active
Patent Citations (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5380692A (en) * | 1991-09-12 | 1995-01-10 | Sakai Chemical Industry Co., Ltd. | Catalyst for catalytic reduction of nitrogen oxide |
US6033632A (en) * | 1993-12-08 | 2000-03-07 | Eltron Research, Inc. | Solid state oxygen anion and electron mediating membrane and catalytic membrane reactors containing them |
US6214757B1 (en) * | 1993-12-08 | 2001-04-10 | Eltron Research, Inc. | Solid state oxygen anion and electron mediating membrane and catalytic membrane reactors containing them |
US20050245391A1 (en) * | 2002-07-09 | 2005-11-03 | Hirohisa Tanaka | Catalyst for exhaust gas purification |
US20070105715A1 (en) * | 2004-12-24 | 2007-05-10 | Hisashi Suda | Particulate matter oxidation catalyst and filter |
US20100278709A1 (en) * | 2007-10-24 | 2010-11-04 | David Waller | Catalyst for production of nitric oxide |
US20110297666A1 (en) * | 2008-07-10 | 2011-12-08 | Epcos Ag | Heating Apparatus and Method for Producing the Heating Apparatus |
US20110082030A1 (en) * | 2009-10-01 | 2011-04-07 | Gm Global Technology Operations, Inc. | Washcoating technique for perovskite catalysts |
Non-Patent Citations (3)
Title |
---|
Keith et al., "Synthesis, Crystal Structure, and Characterization of Ba(Ti1/2Mn1/2)O3: A High Permittivity 12R-Type Hexagonal Perovskite," Chem. Mater. 2004, 16, 2007-2015. * |
Kindermann et al., "Chemical Interactions between La-Sr-Mn-Fe-O Based Perovskites and Yttria-Stabilized Zirconia," J. Am. Chem. Soc., 80 [4] 909-14 (1997). * |
Langhammer et al., "Crystal Structure and Related Properties of Manganese-Doped Barium Titanate Ceramics," J. Am. Chem. Soc., 83 [3] 605-11 (2000). * |
Cited By (26)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US10195603B2 (en) | 2010-05-24 | 2019-02-05 | Siluria Technologies, Inc. | Production of ethylene with nanowire catalysts |
US9718054B2 (en) | 2010-05-24 | 2017-08-01 | Siluria Technologies, Inc. | Production of ethylene with nanowire catalysts |
US9963402B2 (en) | 2011-05-24 | 2018-05-08 | Siluria Technologies, Inc. | Catalysts for petrochemical catalysis |
US11795123B2 (en) | 2011-05-24 | 2023-10-24 | Lummus Technology Llc | Catalysts for petrochemical catalysis |
US10654769B2 (en) | 2011-05-24 | 2020-05-19 | Siluria Technologies, Inc. | Catalysts for petrochemical catalysis |
US11078132B2 (en) | 2011-11-29 | 2021-08-03 | Lummus Technology Llc | Nanowire catalysts and methods for their use and preparation |
US9751818B2 (en) | 2011-11-29 | 2017-09-05 | Siluria Technologies, Inc. | Nanowire catalysts and methods for their use and preparation |
US8940269B2 (en) * | 2012-04-06 | 2015-01-27 | California Institute Of Technology | Methods and materials for the thermochemical production of hydrogen from water |
US9206042B2 (en) | 2012-04-06 | 2015-12-08 | California Institute Of Technology | Methods and materials for the catayltic reduction of carbon dioxide |
US20130266504A1 (en) * | 2012-04-06 | 2013-10-10 | California Institute Of Technology | Methods and Materials for the Thermochemical Production of Hydrogen From Water |
US11370724B2 (en) | 2012-05-24 | 2022-06-28 | Lummus Technology Llc | Catalytic forms and formulations |
US9868636B1 (en) * | 2012-12-06 | 2018-01-16 | National Technology & Engineering Solutions Of Sandia, Llc | Thermochemically active iron titanium oxide materials |
US20160122261A1 (en) * | 2013-03-15 | 2016-05-05 | Siluria Technologies, Inc. | Catalysts for petrochemical catalysis |
US9738571B2 (en) * | 2013-03-15 | 2017-08-22 | Siluria Technologies, Inc. | Catalysts for petrochemical catalysis |
US10865166B2 (en) | 2013-03-15 | 2020-12-15 | Siluria Technologies, Inc. | Catalysts for petrochemical catalysis |
US10308565B2 (en) | 2013-03-15 | 2019-06-04 | Silura Technologies, Inc. | Catalysts for petrochemical catalysis |
US10780420B2 (en) | 2014-05-02 | 2020-09-22 | Lummus Technology Llc | Heterogeneous catalysts |
US9956544B2 (en) | 2014-05-02 | 2018-05-01 | Siluria Technologies, Inc. | Heterogeneous catalysts |
US10604854B2 (en) | 2014-07-17 | 2020-03-31 | The Board Of Trustees Of The Leland Stanford Junior University | Heterostructures for ultra-active hydrogen evolution electrocatalysis |
US10300465B2 (en) | 2014-09-17 | 2019-05-28 | Siluria Technologies, Inc. | Catalysts for natural gas processes |
US11000835B2 (en) | 2014-09-17 | 2021-05-11 | Lummus Technology Llc | Catalysts for natural gas processes |
US9751079B2 (en) | 2014-09-17 | 2017-09-05 | Silura Technologies, Inc. | Catalysts for natural gas processes |
US10189708B2 (en) * | 2016-08-18 | 2019-01-29 | The United States Of America As Represented By The U.S. Environmental Protection Agency | Ruthenium on chitosan (ChRu): concerted catalysis for water splitting and reduction |
CN109745991A (zh) * | 2018-12-13 | 2019-05-14 | 大连海事大学 | 用于煤气化的复合金属氧化物催化剂的制备方法及应用 |
US11634322B2 (en) | 2019-04-03 | 2023-04-25 | California Institute Of Technology | Integration of thermochemical water splitting with CO2 direct air capture |
CN114904511A (zh) * | 2022-03-24 | 2022-08-16 | 南京航空航天大学 | 一种基于SmMnO3钙钛矿的CO2热化学转化材料制备方法和应用 |
Also Published As
Publication number | Publication date |
---|---|
JPWO2013141385A1 (ja) | 2015-08-03 |
CN104203403B (zh) | 2019-07-09 |
KR101790093B1 (ko) | 2017-10-25 |
CN104203403A (zh) | 2014-12-10 |
KR20150008861A (ko) | 2015-01-23 |
EP2829321A1 (en) | 2015-01-28 |
US9873109B2 (en) | 2018-01-23 |
EP2829321A4 (en) | 2016-05-11 |
WO2013141385A1 (ja) | 2013-09-26 |
TW201410321A (zh) | 2014-03-16 |
US20150125383A1 (en) | 2015-05-07 |
JP5594800B2 (ja) | 2014-09-24 |
TWI603779B (zh) | 2017-11-01 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US9873109B2 (en) | Catalysts for thermochemical fuel production and method of producing fuel using thermochemical fuel production | |
Scheffe et al. | Oxygen exchange materials for solar thermochemical splitting of H2O and CO2: a review | |
Zhao et al. | Synergistic improvements in stability and performance of the double perovskite-type oxides La2− xSrxFeCoO6 for chemical looping steam methane reforming | |
Orfila et al. | Perovskite materials for hydrogen production by thermochemical water splitting | |
Gokon et al. | Thermochemical two-step water splitting cycle using perovskite oxides based on LaSrMnO3 redox system for solar H2 production | |
Jouannaux et al. | Lanthanum manganite perovskite ceramic powders for CO2 splitting: Influence of Pechini synthesis parameters on sinterability and reactivity | |
Gokon et al. | Thermochemical reactivity of 5–15 mol% Fe, Co, Ni, Mn-doped cerium oxides in two-step water-splitting cycle for solar hydrogen production | |
Liu et al. | Ca-and Ga-doped LaMnO3 for solar thermochemical CO2 splitting with high fuel yield and cycle stability | |
Perez et al. | Hydrogen production by thermochemical water splitting with La0. 8Al0. 2MeO3-δ (Me= Fe, Co, Ni and Cu) perovskites prepared under controlled pH | |
Hussein et al. | Production of CO from CO2 over mixed-metal oxides derived from layered-double-hydroxides | |
KR20190013447A (ko) | 고순도 수소 생산 장치 및 고순도 수소 생산 방법 | |
US20240083755A1 (en) | CO2 hydrogenation catalysts for the commercial production of syngas | |
Carrillo et al. | Redox oxides for thermochemical energy storage | |
Rony et al. | Recent advances in the solar thermochemical splitting of carbon dioxide into synthetic fuels | |
ES2926393B2 (es) | Metodo de obtencion de h2, co y/o gas de sintesis empleando materiales de tipo perovskita y uso de estos materiales | |
Zheng et al. | Research progress on metal oxide oxygen carrier materials for two-step solar thermochemical cycles in the last five years | |
Wu et al. | Emerging natural and tailored perovskite-type mixed oxides–based catalysts for CO2 conversions | |
Murugan | Iron-containing perovskite materials for stable hydrogen production by chemical looping water splitting | |
Yuan et al. | Solar-driven fuel production by metal-oxide thermochemical cycles | |
Chen et al. | Thermochemical splitting of CO2 on perovskites for CO production-a review | |
Dharanipragada | CO2 utilization by chemical looping: iron oxides characterization by in situ XRD and XAS | |
US11584658B2 (en) | Compositions, methods of making compositions, and hydrogen production via thermo-chemical splitting | |
Tada et al. | O2 releasing reactivity of ceria-based reactive ceramics on irradiation of concentrated solar beam for solar hydrogen production | |
da Silva Albuquerque et al. | Evaluating the reactivity of CuO-TiO2 oxygen carrier for energy production technology with CO2 capture | |
Ungut | Approaching the design of novel oxygen carrier materials for hydrogen production via the chemical looping water-gas shift process in a packed bed reactor |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: CALIFORNIA INSTITUTE OF TECHNOLOGY, CALIFORNIA Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:HAILE, SOSSINA M.;YANG, CHIH-KAI;SIGNING DATES FROM 20130519 TO 20130520;REEL/FRAME:030517/0557 |
|
AS | Assignment |
Owner name: JAPAN SCIENCE AND TECHNOLOGY AGENCY, JAPAN Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:YAMAZAKI, YOSHIHIRO;REEL/FRAME:030527/0580 Effective date: 20130509 |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION |
|
AS | Assignment |
Owner name: NATIONAL SCIENCE FOUNDATION, VIRGINIA Free format text: CONFIRMATORY LICENSE;ASSIGNOR:CALIFORNIA INSTITUTE OF TECHNOLOGY;REEL/FRAME:035705/0118 Effective date: 20130312 |