US20110028623A1 - Thermoplastic elastomers exhibiting superior barrier properties - Google Patents
Thermoplastic elastomers exhibiting superior barrier properties Download PDFInfo
- Publication number
- US20110028623A1 US20110028623A1 US12/936,372 US93637209A US2011028623A1 US 20110028623 A1 US20110028623 A1 US 20110028623A1 US 93637209 A US93637209 A US 93637209A US 2011028623 A1 US2011028623 A1 US 2011028623A1
- Authority
- US
- United States
- Prior art keywords
- compound
- organoclay
- polyamide
- agents
- weight percent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Description
- This application claims priority from U.S. Provisional Patent Application Ser. No. 61/047,047 bearing Attorney Docket Number 12008012 and filed on Apr. 22, 2008, which is incorporated by reference.
- This invention relates to thermoplastic elastomers containing organoclay-filled polyamide to provide barrier properties.
- The world of polymers has progressed rapidly to transform material science from wood and metals of the 19th Century to the use of thermoset polymers of the mid-20th Century to the use of thermoplastic polymers of later 20th Century.
- An example of a popular rubber is butyl rubber which has excellent gas barrier properties. But butyl rubber is not capable of being injection molded.
- Thermoplastic elastomers (TPEs) combine the benefits of elastomeric properties of thermoset polymers, such as vulcanized rubber, with the processing properties of thermoplastic polymers. Therefore, TPEs are preferred because they can be made into articles using injection molding equipment. But often, TPEs lack gas barrier properties comparable to butyl rubber.
- U.S. Pat. No. 7,150,294 (Katayama et al.) discloses a two layer hose with an outer layer of a blend of styrene-isobutylene block copolymer and polyamide, and preferably also including a compatibilizer.
- What the art needs is a new formulation of thermoplastic elastomer (TPE) that has gas barrier properties approaching those of butyl rubber.
- The present invention solves that problem by using a TPE formulation that includes organoclay-filled polyamide.
- One aspect of the invention is a thermoplastic elastomer compound, comprising (a) styrene-isobutylene-styrene and (b) polyamide including organoclay dispersed in the polyamide.
- Features of the invention will become apparent with reference to the following embodiments.
- One type of TPE is based on styrene (also called “TPE-S”). The present invention uses a TPE-S based on styrene-isobutylene-styrene (“SIBS”) as the matrix polymer for the TPE. A commercial source of SIBS is Kaneka of Japan. SIBS is becoming increasingly popular as a high-value TPE-S, as noted in U.S. Pat. No. 7,150,294 (Katayama et al.)
- Typically, commercial grades of TPE-S are a complex combination of TPE, plasticizer, processing aid (mold release agent), filler, antioxidant, and one or more secondary polymers, such as polyolefins.
- Polyamide as Secondary Polymer
- In the present invention, the TPE-S includes polyamide as a secondary polymer. The polyamide can be amorphous or crystalline. Any amorphous or crystalline polyamide among the following list is a candidate for use in this invention: polyamide 6; polyamide 6,6; polyamide 9,9; polyamide 6,10; polyamide 6,12; polyamide 11; polyamide 9,10; polyamide 9,12; polyamide 12; a copolymer of polyamide 6 and polyamide 6,6; a copolymer of polyamide 6 and polyamide 12; and combinations thereof.
- Regardless of the polyamide employed, the polyamide needs to have dispersed therein an organoclay. Despite the considerable difference in cohesive energy densities between SIBS and polyamide, an organoclay filled polyamide (“Nanonylon” for convenience in this application) provides unexpected superior barrier properties over even that of SIBS and polyamide alone, which itself is a considerable improvement over SIBS alone.
- Organoclay
- Organoclay is obtained from inorganic clay usually from the smectite family. Smectites have a unique morphology, featuring one dimension in the nanometer range. Montmorillonite clay is the most common member of the smectite clay family. The montmorillonite clay particle is often called a platelet, meaning a sheet-like structure where the dimensions in two directions far exceed the particle's thickness.
- Inorganic clay becomes commercially significant if intercalated with an organic intercalant to become an organoclay. An intercalate is a clay-chemical complex wherein the clay gallery spacing has increased, due to the process of surface modification by an intercalant. Under the proper conditions of temperature and shear, an intercalate is capable of exfoliating in a resin polyolefin matrix. An intercalant is an organic or semi-organic chemical capable of entering the montmorillonite clay gallery and bonding to the surface. Exfoliation describes a dispersion of an organoclay (surface treated inorganic clay) in a plastic matrix. In this invention, organoclay is exfoliated at least to some extent.
- In exfoliated form, inorganic clay platelets have a flexible sheet-type structure which is remarkable for its very small size, especially the thickness of the sheet. The length and breadth of the particles range from 1.5 μm down to a few tenths of a micrometer. However, the thickness is astoundingly small, measuring only about a nanometer (a billionth of a meter). These dimensions result in extremely high average aspect ratios (200-500). Moreover, the miniscule size and thickness mean that a single gram contains over a million individual particles.
- Nanocomposites are the combination of the organoclay and the plastic matrix. In this invention, Nanonylon is the nanocomposite which provides the unexpected results. In polymer compounding, a nanocomposite is a very convenient means of delivery of the organoclay into the ultimate compound, provided that the plastic matrix is compatible with the principal polymer resin components of the compounds. In such manner, nanocomposites are available in concentrates, masterbatches, and compounds from CP Polymers of Pasadena, Calif., Nanocor, Inc. of Arlington Heights, Ill. (www.nanocor.com) and PolyOne Corporation of Avon Lake, Ohio (www.polyone.com) in a variety of nanocomposites. Particularly preferred organoclays are I24TL, I30P, I44P, and I44W from Nanocor, Inc. which can then be dispersed into amorphous or crystalline polyamide.
- Nanocomposites offer flame-retardancy properties because such nanocomposite formulations burn at a noticeably reduced burning rate and a hard char forms on the surface. They also exhibit minimum dripping and fire sparkling.
- Nanocomposites also have improved barrier properties as compared with the plastic matrix without organoclay.
- The amount of organoclay in the Nanonylon can range from about 1 to about 8 weight percent, and preferably from about 3 to about 8 weight percent.
- Optional Additives
- The compound of the present invention can include conventional plastics additives in an amount that is sufficient to obtain a desired processing or performance property for the compound. The amount should not be wasteful of the additive nor detrimental to the processing or performance of the compound. Those skilled in the art of thermoplastics compounding, without undue experimentation but with reference to such treatises as Plastics Additives Database (2004) from Plastics Design Library (www.williamandrew.com), can select from many different types of additives for inclusion into the compounds of the present invention.
- Non-limiting examples of optional additives include adhesion promoters; biocides (antibacterials, fungicides, and mildewcides), anti-fogging agents; anti-static agents; bonding, blowing and foaming agents; dispersants; fillers and extenders; fire and flame retardants and smoke suppresants; impact modifiers; initiators; lubricants; micas; pigments, colorants and dyes; oils and plasticizers; processing aids; release agents; silanes, titanates and zirconates; slip and anti-blocking agents; stabilizers; stearates; ultraviolet light absorbers; viscosity regulators; waxes; and combinations of them.
- Table 1 shows the acceptable and desirable ranges of ingredients for the TPE-S of the present invention. All but the SIBS and Nanonylon are optional for the present invention.
-
TABLE 1 Ranges of Ingredients Ingredient (Wt. Percent) Acceptable Desirable SIBS 20-90% 30-85% Nanonylon 5-50% 10-30% Plasticizer 0-70% 0-50% Other Polymer(s) 0-50% 0-15% Processing Aid- 0-2% 0-0.5% Mold Release Filler 0-40% 0-15% Anti-oxidant 0-1% 0-0.2% Other Optional 0-10% 0-5% Additives - Processing
- The preparation of compounds of the present invention is uncomplicated. The compound of the present can be made in batch or continuous operations.
- Mixing in a continuous process typically occurs in an extruder that is elevated to a temperature that is sufficient to melt the polymer matrix with addition either at the head of the extruder or downstream in the extruder of the solid ingredient additives. Plasticizer oil can be pre-mixed with the SEBS, if SEBS is included in the formulation, in a ribbon blender or optionally added downstream by injection. Extruder speeds can range from about 50 to about 500 revolutions per minute (rpm), and preferably from about 100 to about 300 rpm. Typically, the output from the extruder is pelletized for later extrusion or molding into polymeric articles.
- Mixing in a batch process typically occurs in a Banbury mixer that is also elevated to a temperature that is sufficient to melt the polymer matrix to permit addition of the solid ingredient additives. The mixing speeds range from 60 to 1000 rpm and temperature of mixing can be ambient. Also, the output from the mixer is chopped into smaller sizes for later extrusion or molding into polymeric articles.
- Subsequent extrusion or molding techniques are well known to those skilled in the art of thermoplastics polymer engineering. Without undue experimentation but with such references as “Extrusion, The Definitive Processing Guide and Handbook”; “Handbook of Molded Part Shrinkage and Warpage”; “Specialized Molding Techniques”; “Rotational Molding Technology”; and “Handbook of Mold, Tool and Die Repair Welding”, all published by Plastics Design Library (www.williamandrew.com), one can make articles of any conceivable shape and appearance using compounds of the present invention.
- TPE-S of the present invention, based on SIBS and Nanonylon provides gas barrier properties comparable to butyl rubber. As such, and with the advantage of being capable of being injection molded, plastic articles can be made from formulations of the present invention for such uses as seals, closures, and other articles previously made from butyl rubber. Other articles can be made from the TPE-S nanocomposites of the present invention, such as the following industrial and consumer products: food and drink container seals, printer cartridge seals, medical container seals, baby pacifiers, and other products needing both flexibility and barrier properties, as a suitable replacement for butyl rubber.
- Table 2 shows two examples of the present invention, in comparison with a control (Comparative Example A) and four comparison examples (Comparative Examples B-E) representing a TPE-S with either amorphous or crystalline nylon which does not contain organoclay.
- All formulations of Examples 1-2 and Comparative Examples A-E had the same SIBS TPE-S matrix. All formulations of Examples 1-2 and Comparative Examples B-E had the same SIBS TPE-S matrix and antioxidant. Comparative Examples B and D offered a direct comparison with Example 1, while Comparative Examples C and E offered a direct comparison with Example 2. Only the type of polyamide was different.
- All of Examples 1-2 and B-E were made using a twin-screw extruder set at 238° C. in all zones, rotating at 500 rpm. All ingredients were added before Zone 1. The melt-mixed compound was pelletized for further handling.
- Pellets of all Examples 1-2 and A-E were molded into tensile test bars using a Demag injection molding machine, operating at 190° C. temperature and high pressure. Table 3 shows experimental results.
-
TABLE 2 Formulations Ingredient/Commercial Source (Parts by Weight) Purpose Comp. A Comp. B Comp. C Comp. D Comp. E 1 2 Sibstar 073T SIBS TPE-S 100 85 70 85 70 85 70 (Mw = 83,000) (Kaneka, Japan) Matrix Selar 3426 Amorphous polyamide Barrier 15 30 (DuPont, Wilmington, DE, USA) Ultramid 8202 polyamide 6 (BASF, Barrier 15 30 Florham Park, NJ, USA) CRESS-ALON A NE2740 Injection Barrier 15 30 Grade Nanonylon (CP Polymers, Pasadena, CA, USA) (Contains polyamide 6 and 4% organoclay) Irganox 1010 Antioxidant Antioxidant/ 0.1 0.1 0.1 0.1 0.1 0.1 (Ciba, Switzerland) UV package -
TABLE 3 Physical Properties Ingredient/Commercial Source (Parts by Weight) Comp. A Comp. B Comp. C Comp. D Comp. E 1 2 Shore A Hardness 50 55 64 56 70 68 89 (ASTM D2240, 10 s delay) Specific Gravity (ASTM D792) 0.96 0.99 1.01 0.97 1.00 0.97 0.99 Tensile Strength, psi (ASTM D412, Die C) 1195 1431 1816 1391 1779 1196 1855 Elongation, % (ASTM D412, Die C) 422 254 151 327 226 292 83 Tear Strength, pli (ASTM D624) 155 135 158 166 296 234 386 Oxygen Transmission Rate (OTR), cc · mil/m2 · day 3010 1880 1210 1610 410 570 55 (ASTM D3985) Percent OTR Improvement of Example 1 Over 528% 329% 282% Comparative Examples A, B, and D Percent OTR Improvement of Example 2 Over 5472% 2200% 745% Comparative Examples A, C, and E - Table 3 shows the physical properties of Examples 1-2 and Comparative Examples A-E are comparable or manageable for Shore A hardness, Specific Gravity, Tensile Strength, Percent Elongation, and Tear Strength.
- What is totally unexpected is the amount of oxygen transmission rate decrease in Examples 1 and 2, when compared to neat SIBS (Comparative Example A) or SIBS and amorphous nylon (Comparative Examples B and C) or SIBS and crystalline nylon (Comparative Examples D and E).
- Example 1 with Nanonylon at 15 parts by weight has two to three times the oxygen barrier performance over use of amorphous or crystalline nylon at the same weight percent. Example 2 with Nanonylon at 30 parts by weight has seven to 22 times the oxygen barrier performance over use of amorphous or crystalline nylon at the same weight percent.
- Therefore, using Examples 1 and 2 and other explanations of the present invention in this document, one of ordinary skill in the art, without undue experimentation, will be able to formulate to achieve the appropriate balance of physical processing and physical performance properties while at the same time achieving extraordinarily and unexpectedly superior oxygen barrier properties.
- The invention is not limited to the above embodiments. The claims follow.
Claims (20)