US20100167839A1 - Golf Club Head - Google Patents
Golf Club Head Download PDFInfo
- Publication number
- US20100167839A1 US20100167839A1 US12/685,220 US68522010A US2010167839A1 US 20100167839 A1 US20100167839 A1 US 20100167839A1 US 68522010 A US68522010 A US 68522010A US 2010167839 A1 US2010167839 A1 US 2010167839A1
- Authority
- US
- United States
- Prior art keywords
- core
- resin
- filament
- club head
- mold
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A golf club head is disclosed. The head has a shell with an inner surface defining a hollow interior portion. The inner surface has a plurality of inwardly extending ribs made of resin and a single continuous filament located in the resin.
Description
- This application is a division of Ser. No. 11/435,653, filed May 17, 2006, which is incorporated by reference in its entirety and which is pending as of the filing date of this application.
- 1. Field of the Invention
- The present invention relates to golf club heads, more particularly of the composite metal “wood” type, and a method of making golf club heads.
- 2. Description of the Background and Relevant Information
- Wood-type golf club heads traditionally were made from wood, e.g., persimmon. However, with advances in materials, wood-type golf club heads are currently predominantly made from high performance metals such as titanium, and other materials such as fiber-reinforced plastics. Many club heads made from fiber resin composite materials are compression molded around relatively rigid molding cores. In instances where a hollow interior cavity is desired, dispersible cores made from meltable materials such as wax or low melting point metals have been employed.
- Wood-type club heads made predominantly of metal may be fabricated by welding or adhesively joining together edges of two or more thin sections of a club head shell made of metal such as stainless steel, beryllium copper, aluminum, titanium, etc., thereby producing a one-piece shell.
- For some years now, heads made entirely of a composite material, with the exception of the sole, have been manufactured. Such types of constructions are rarely favored by professional players because they are most often made of a single element, by the compression molding method, without any particular regard to the distribution of mass.
- A head made of a plastic material is disclosed in British Patent Publication No. 2,128,539. This head is made of a single thermoplastic element injected into a mold around a meltable core. The head thus manufactured does not allow a good control over the trajectory of the balls because the problem of balancing the club is not resolved.
- U.S. Pat. No. 5,000,454 discloses a head made of a reinforced plastic material and comprising an element acting both as the reinforcement of the striking face and as the balancing weight. However, such a structure does not yet permit the club to be balanced satisfactorily.
- U.S. Pat. No. 6,824,636 B2 is directed to a method for the manufacture of a hollow three-dimensional fiber golf club head wherein a fluid-removable core shaped in the general form of the golf club head is placed in a flexible pressurizable bladder surrounding the core. At least one ply fiber impregnated with a curable resin is wrapped over the core and bladder, and a cured part is formed by pressurizing the bladder while the core, bladder and impregnated fiber is in a female mold to force the plies against the inner surface of the mold. After heating to cure the resin, the bladder and the fluid removable core is removed from the interior of the cured part by disintegrating the core with a fluid sufficient to allow removal of the bladder. This method is complex and difficult of reproduction on a commercial scale.
- It is an object of the present invention to overcome the disadvantages inherent to the above described and traditional methods and resulting structures of club heads, and to provide a new head design as well as a new method of manufacturing such head.
- Thus, one of the more specific objects of the invention is to provide a manufacturing method enabling a more efficient new head structure to be obtained, especially as regards distribution of mass, durability, and finishing quality. The method according to the invention is particularly adapted to the large scale production of elements requiring a minimum number of operations to produce what might be considered a complex yet highly advantageous golf club head.
- Thus, according to the invention, a method of manufacturing a golf club is disclosed. The method is comprised of the following steps. A single continuous filament is wound multiple times about a soluble core. The wound core is then located in a mold. The wound core is then pressure coated with a resin in the mold. The resin disperses among the filament windings. The resin is allowed to cure and form a filament and resin shell about the core. The soluble core is then removed from the shell while the continuous filament is retained within the shell.
- The shell has an inside surface and an outside surface. The inside surface defines a substantially hollow interior portion and the inside surface has a plurality of ribs that extend into the interior portion. The ribs and the shell are substantially comprised of the resin and the single continuous filament located within the resin.
- The above, as well as other advantages of the present invention, will become readily apparent to those skilled in the art from the following detailed description when considered in the light of the accompanying drawings in which:
-
FIG. 1 is a schematic, perspective view of an embodiment of a component for use in the method of the present invention; -
FIG. 1A depicts a cross-sectional view of a mold for forming the component depicted inFIG. 1 ; -
FIG. 2 is a schematic view of one embodiment of a filament winding machine and the component ofFIG. 1 of the present invention; -
FIG. 3 is a schematic, cross-sectional view of one embodiment of a mold for use in the method of the present invention; -
FIG. 4 is a schematic, perspective view of another component of the present invention; -
FIG. 5 is a schematic, cross section of a preferred embodiment of a structure for creating a shaft-receiving portion in the present invention; -
FIG. 6 is a schematic, perspective view of one embodiment of the present invention; -
FIG. 7 is a schematic, perspective view of one embodiment of the present invention; -
FIG. 8 is a schematic, cut-away view of one embodiment of a club head of the invention; -
FIG. 9 is a schematic, perspective view of one embodiment of the bottom of a club head of the invention; and -
FIG. 10 is a schematic, perspective view of one embodiment of a club head produced in accordance with the invention. - It is to be understood that the invention may assume various alternative orientations and step sequences, except where expressly specified to the contrary. It is also to be understood that the specific devices and processes illustrated in the attached drawings, and described in the following specification are simply exemplary embodiments of invention. Hence, specific dimensions, directions or other physical characteristics relating to the embodiments disclosed are not to be considered as limiting, unless expressly stated otherwise.
- Referring to
FIG. 1 , a preferred embodiment of a golfclub head core 20 is depicted. The golfclub head core 20 is preferably made by the process and materials described in U.S. Pat. No. 3,692,551, which is incorporated by reference in its entirety into the present specification. - By way of example only,
FIG. 1A depicts a preferred embodiment of a mold 11 which may be used to form the core 20 depicted inFIG. 1 . The mold 11 preferably has afirst half 12 and asecond half 13 which are separable from one another. Thefirst half 12 and thesecond half 13 define aninterior chamber 14 having a substantially similar shape to the shape of thecore 20. A corefront face block 15 is preferably located with theinterior chamber 14. The corefront face block 15 has a plurality ofribs 16 extending into theinterior chamber 14. Theribs 16 will be used to form grooves in the front face of the core 20, which are described in detail below. - A plurality of
ribs 19 extend into theinterior chamber 14 from thefirst half 12 and thesecond half 13. Theribs 19 will be used to form grooves in the upper surface of thecore 20 and the lower surface of the core 20, as described below. - Those skilled in the art will appreciate that the core
front face block 15 may have any design, including any pattern of ribs or shapes to create a core 20 having any desired shape. - The mold 11 preferably has at least one
sprue 19A for introducing the core material (not shown) into theinterior chamber 14 from outside of the mold 11. The mold 11 may have means to heat or cool to solidify the core material so that the core material conforms to the corefront face block 15. Alternatively, if the core material does not require heat and/or cooling to set up, then such means are not required. Theribs interior chamber 14 from the corefront face block 15 form grooves in the core material, discussed below. The heat and/or pressure, if required, exerted by the mold 11 on the core material create a core 20 which, in a preferred embodiment, looks like the core 20 depicted inFIG. 1 . - Referring to
FIG. 1 , thecore 20 is preferably shaped to have a somewhat curvilinearfront face 26, a curvilinear upper surface 28 and the curvilinearlower surface 24. InFIG. 1 , thecore 20 is located upside down so that at least twocore prints 112 can be clearly seen. - Preferably, an
insert 30 is at least partially formed into the core 20 about eachcore print 112. Theinsert 30, thus, is positioned within thecore 20 when thecore 20 is formed as described above. Theinsert 30 may have a firstcircumferential ring 31A (seen inFIG. 3 ) which helps secure theinsert 30 in thecore 20. Theinsert 30 also preferably has a secondcircumferential ring 31B (seen inFIGS. 1 and 3 ) which will be received within a resin, described in more detail below. - As best seen in
FIG. 9 , theinserts 30 are preferably cylindrical in shape with a hollowinterior portion 30A. Theinserts 30 have a threadedinner surface 30B. - The upper surface 28 and the
lower surface 24 preferably taper away from thefront face 26 until they meet at arearward portion 32 of thecore 20.Side portions 34 of the upper andlower surfaces 24, 28 also preferably taper toward one another. Although a preferred embodiment of the upper andlower surfaces 24, 28 is depicted in the figures, those skilled in the art will appreciate that the core 20 can be constructed with any number of surfaces, edges, depressions or curves and have any shape or size. By way of example only, the upper andlower surfaces 24, 28 can taper to a rear surface (not shown), rather than to arounded edge 36. Additionally, theside portions 34 of the upper andlower surfaces 24, 28 can taper to side surfaces 34, rather than to rounded side edges 38, as shown inFIG. 1 . - In the preferred embodiment, a
depression 40 in thecore 20 is provided adjacent one side of thefront face 26. Thedepression 40 will be used to form a portion of the finished golf club head that will receive a shaft, as described in more detail below. - Preferably, the at least two
core prints 112 extend away in a substantially perpendicular fashion from thelower surface 24 of thecore 20. Eachcore print 112 is preferably positioned in an area of thelower surface 24 of the core 20 adjacent one of theside portions 34. The core prints 112 can be positioned in any area on thelower surface 24 between thefront face 26 and therearward portion 32 of thecore 20. However, in the preferred embodiment, the core prints 112 are closer to therearward portion 32 than thefront face 26 of the core 20 to lower the center of gravity of the finished golf club head. - Referring to
FIG. 1 , a plurality ofgrooves 42 is preferably located across thefront face 26, thelower surface 24 and the upper surface 28 of thecore 20. Thegrooves 42 extend diagonally across thefront face 26 of the core 20 to intersect one another; however, it is within the scope of the present invention to extend thegrooves 42 across thefront face 26 in any orientation, whether intersecting or not. Additionally, althoughFIG. 1 depicts thegrooves 42 continuously extending across theface 26, it is within the scope of the present invention to interrupt one or more of thegrooves 42, either on thefront face 26 of the core 20, or in any other area of thecore 20. The preferred embodiment of the invention also locates thegrooves 42 at a constant depth in thecore 20, although variable depths are within the scope of the invention. - In the preferred embodiment, the
grooves 42 extend from thefront face 26 rearward across thelower surface 24 of thecore 20 and rearward from thefront face 26 across the upper surface 28 of thecore 20. Although thegrooves 42 are depicted as parallel to one another on thelower surface 24 of the core 20, and they are preferably located parallel to one another on the upper surface 28, it is within the scope of the present invention for thegrooves 42 to extend in a non-parallel fashion across thelower surface 24 and the upper surface 28 of thecore 20. - As shown in
FIG. 2 , the above-describedcore 20 is located in afilament winding machine 44, known to those skilled in the art, for winding acontinuous filament 46 about a workpiece.Filament winding machines 44 within the scope of the present invention, but which in no way limit the present invention, are those made by McClean Anderson of Schofield, Wis.Such machines 44 typically have a supply offilament 48 on at least onespool 50. Thespool 50 is preferably moveable via control by a computer (not shown) through multiple axes of rotation with respect to the core 20 located in abit mechanism 52. - The
bit mechanism 52 comprises a taperedpoint 54 on one end for engaging oneside portion 34 of thecore 20 and aclamp 56 on the other end for engaging theopposite side portion 34 of thecore 20. Theclamp 56 may be, by way of example, a contoured fit split clamp. Preferably, thebit mechanism 52 is rotated about at least one axis by a motor (not shown) controlled by the same computer to coordinate the rotation of thebit mechanism 52 with the movement of thespool 50. - Machines capable of having a plurality of supplies of
filament 48 and which are capable of controlling more than onespool 50 to simultaneously wind a plurality ofcores 20 are also within the scope of the present invention. - In the preferred embodiment, the
filament 46 on thefilament winding machine 44 is a continuous strand of carbon fiber filament. Other continuous strands offilament 46, such as Kevlar® manufactured by the E.I. Du Pont Nemours Company of Wilmington, Del., may be used without departing from the scope of the present invention. Regardless of the composition of thefilament 46 selected, thefilament 46 should have physical and performance characteristics comparable to carbon fiber filament or Kevlar® filaments. - The filament-winding
machine 44 may also comprise one ormore tensioners 58 for providing a pre-determined amount of tension to thefilament 46. Themachine 44 may also comprise a resin dispenser (not shown) or a resin bath or drum (not shown) for applying resin to thefilament 46. - In the preferred embodiment, the
filament 46 is first wound into thegrooves 42 of thecore 20. By way of example only, thefilament 46 is started in onegroove 42 on oneside portion 34 of thecore 20 and thefilament 46 is wound across the core 20 in afirst direction 60. When thefilament 46 is wound about thelast groove 42 on theopposite side portion 34 of the core 20, thefilament 46 is moved inwardly to continue winding across thechannels 42 in asecond direction 62. Those skilled in the art will appreciate that the first andsecond directions FIG. 2 . - Preferably,
filament 46 is repeatedly wound within thegrooves 42 as described above until thefilament 46 within thegrooves 42 is substantially planar with thefront face 26, the upper surface 28 and/or thelower surface 24. In the preferred embodiment, the same strand ofcontinuous filament 46 is then wound across thefront face 26, the upper surface 28 and thelower surface 24 to substantially cover each of those surfaces. Thefilament 46 is preferably wound across the core 20 from thefirst direction 60 to thesecond direction 62. The present invention also includes winding thefilament 46 across the core 20 in any pattern, design or orientation after thegrooves 42 have been wound. The curvilinear shape of the core 20 may prevent winding theentire core 20 in substantially one direction as thefilament 46 can slide off one of theside portions 34, however, it is preferred to cover each of thesurfaces filament 46. - In the preferred embodiment, the
core 20 is wrapped in the continuous strand offilament 46 to provide a layer offilament 46 above at least one of thesurfaces - In another embodiment, the
core 20 may be wrapped, e.g., vertically, withadditional filament 46 after the initial layer ofcontinuous filament 46 has been completed. Theadditional filament 46 may be continuous or non-continuous and it may be located across theentire core 20, or only selected portions of the core 20, for example, the ends. Theadditional filament 46 may be of the same material as the initial layer, or it may be of a different material. - The
wound core 20 is then removed from the filament-windingmachine 44 and located in a mold. A preferred embodiment of a cross-section of a mold is depicted inFIG. 3 . The mold may be an injection mold, a transfer mold, or a compression mold, as known by those skilled in the art. - In the embodiment depicted in
FIG. 3 , atransfer mold 64 is shown. Themold 64 has amaterial reservoir 66 in fluid communication with achamber 68 via at least onechannel 70. One or moreelectric coils 72 are located throughout themold 64 for heating themold 64, although channels (not shown) for heated oil and/or steam may also be used in conjunction with theelectric coils 72 or alone. - A
removable insert 74 is located within thechamber 68. Theinsert 74 has awall 76 having a complementary shape to at least thewound front face 26 of thecore 20.Inserts 74 havingwalls 76 at various angles, which determines loft in degrees of the club face, and sizes with respect to thewound front face 26 of the core 20 may be used to locate aface plate 78 at various desired angles. - The present invention also comprises the
face plate 78 and asole plate 80, as shown inFIGS. 3 and 4 . Theface plate 78 and thesole plate 80 may be two separate pieces, but preferably, theface place 78 and thesole plate 80 have either been welded together, integrally formed together, or otherwise joined. Theface plate 78 and thesole plate 80 are preferably constructed of a highly wear resistant material, such as titanium, titanium alloys or steel alloys, for instance stainless steel. Anouter surface 82 of theface plate 78 may have one or more vertical and/orhorizontal grooves 86. Thegrooves 86 help impart, or decrease, spin to a golf ball depending on groove design. -
Face plates 78 andsole plates 80 of various sizes and shapes may be used to create club heads having different appearances. By way of example only, aface plate 78 that is slightly larger than thewound core 20 may be used, or aface plate 78 that is about the same size as thewound core 20 may be used. In the latter embodiment, theface plate 78 will be substantially flush with the finished club head. In the former embodiment, theface plate 78 will be slightly larger than the finished club head. - In the preferred embodiment, the
face plate 78 and thesole plate 80 are located within themold 64 adjacent theremovable insert 74, as shown inFIG. 3 . Themold 64 and at least onewall 76 of theinsert 74 may be designed to securely receive theface plate 78 and/orsole plate 80 to prevent movement of the core during the molding step described below. For example, themold 64 andwall 76 may have a complementary shape to theface plate 78 and/or thesole plate 80. Alternatively, it is well within the scope of the present invention to locate one or more mechanical fasteners (not shown), such as screws or pins, into theface plate 78 and/orsole plate 80 to removably secure theface plate 78 and thesole plate 80 with the core 20 in themold 64. - Inside surfaces 84 of the
face plate 78 and/or thesole plate 80 may be scored or scuffed, for instance by sand blasting or other known methods, to provide a gripping surface for the molding material described below. - As best seen in
FIG. 3 , thewound core 20 is located into thechamber 68 within themold 64 where thechamber 68 has a substantially complementary shape to thewound core 20. The core prints 112 on the core 20 preferably fit into complementary shapedrecesses 85 in themold 64 to assist in locating the core 20 in a precise position within themold 64. Preferably, a predetermined gap, orwall stock 88, is left between thewound core 20 and thechamber walls 89. - Weights to satisfy design criteria, i.e., center of gravity, may be positioned in the core mold and molded in place. The weights, if required, will be secured to the club head by the overmolding step described below.
- Preferably, the
wound core 20 is positioned in thechamber 68 so that it is approximately half above and approximately half below thechannel 70. Thechannel 70 functions as a gate, as known by those skilled in the art. Those skilled in the art will appreciate that the core 20 can be located in thechamber 68 in any position, angle or orientation with respect to thechannel 70. - One or
more spacers 90 may also be located between theface plate 78 and thesole plate 80 and thewound core 20. Thespacers 90 may be of any shape, size or dimension. In one embodiment, thespacers 90 are T-shaped (not shown) to provide a large surface area with which molding material, described below, comes in contact. Thespacers 90 may have a knurled, or rough, outer surface to assist them becoming secured within a resin, described below. - The
spacers 90 may be used to provide, i.e., control the thickness of, thewall stock 88 between theface plate 78, thesole plate 80 and thewound core 20. - As shown in
FIG. 5 , at least oneaperture 92 is located in theface plate 78 and at least oneaperture 94 is located in thesole plate 80. Theapertures face plate 78 and thesole plate 80 are formed, or theapertures plates tube 96 is preferably located through theapertures face plate 78 and thesole plate 80 and secured by a press fit or friction fit, adhesive, brazing and/or welding. Theapertures face plate 78 and thesole plate 80 are preferably located and aligned so that thetube 96, when inserted in theapertures depression 40 in thecore 20 for the shaft. - Referring now back to
FIG. 3 , a pre-determined quantity of a thermosetting-engineeredresin 98 that is compatible with carbon fibers, e.g., epoxy or polyester resins, preferably epoxies, is located in thereservoir 66 of themold 64. A thermoplastic-engineered resin that is compatible with carbon fibers may also be used. In the event a thermoplastic resin is employed, provision is made to cool the mold to effect cure of the resin. - Preferably,
non-continuous filaments 100 of carbon and/or Kevlar®, orfilaments 100 having specified physical and performance characteristics, are equally distributed and suspended within theresin 98. Theresin 98 may be comprised of approximately 20% to approximately 70% filaments 100, but preferably theresin 98 is comprised of approximately 50% filaments 100. - The
thermosetting resin 98 may be liquefied before being located in thereservoir 66, or it may be liquefied within thereservoir 66. Thevarious resins 98 which may be used with the present invention have a liquefying point between 200 degrees Fahrenheit and 400 degrees Fahrenheit. Typically, themold 64 is approximately 300 degrees Fahrenheit to 400 degrees Fahrenheit, so if theresin 98 is not liquefied before entering thereservoir 66, it will quickly become liquefied. In either case, the liquefiedresin 98 is urged out of thereservoir 66 by any known means, including but not limited to, a pump, and/or aplunger 102. Theplunger 102 may be driven by a clamping device such as a hydraulic press holding the two halves of themold 64 closed together. - Those skilled in the art will also appreciate that an injection type mold can also be used without departing from the scope of the present invention. In an injection type mold (not shown), a rotating helical mixing device is located within the reservoir. The helical mixing device, when rotating, will decrease the length of any carbon and/or Kevlar® filaments within the resin.
- In comparison, the
transfer type mold 64 described and depicted herein does not have a mixing device so that thefilaments 100 in theresin 98 retain their original length. Therefore, depending on the desiredfilament 100 length in theresin 98, either the injection type mold or the transfer type mold may be interchangeably used with the present invention. - The liquefied
resin 98 flows under pressure from thereservoir 66 and through thechannel 70, as through a gate as known by those skilled in the art. As described above, thewound core 20 is located within themold 64 so that approximately half of thewound core 20 is located above thechannel 70 and approximately half of the wound core is located below thechannel 70. The liquefiedresin 98 flows in substantially equal quantities around thewound core 20 in thewall stock 88 about thewound core 20. Theresin 98 also flows around theinserts 30. - The liquefied
resin 98 flows through thewall stock 88 to overmold thewound core 20. Thepressurized resin 98 flows into any voids not filled by thecontinuous filament 46 on thecore 20 and it permeates through thefilament 46 located over the upper surface 28, thelower surface 24, thefilament 46 over thefront face 26 and thefilament 46 in thegrooves 42. Theresin 98 is also located in thewall stock 88 between thewound core 20 and theface plate 78 and thesole plate 80 and between thetube 96 and thewound core 20. - A fiber filled resin coating (or an unfilled pure resin in circumstances where the resin is used for an improved surface finish) over the
wound core 20 having a thickness of between approximately one five thousandths (0.005″) of an inch to approximately one ninety thousandths (0.090″) of an inch is desirable. - The
resin 98 is allowed to cure under heat and pressure in themold 64 for a pre-determined amount of time. Once theresin 98 is sufficiently cured, theovermolded core 20, now having theface plate 78, thesole plate 80 and theinserts 30 secured thereto and thetube 96 secured therein, referred hereinafter as theclub head 104, is removed from themold 64. Anouter surface 106 of theclub head 104 that was located adjacent themold chamber walls 89 now has a surface dependent on fiber content. For example, the surface can be smooth, as shown inFIG. 6 , or variegated. - Those skilled in the art will also appreciate that the
walls 89 of thechamber 68 can be provided with any surface to provide a smoothouter surface 106 of theclub head 104 or thewalls 89 can be designed to create any design or pattern on theouter surface 106 of theclub head 104. By way of example only, thewalls 89 of thechamber 68 can be designed to create a leather-like or wood-like appearance on theouter surface 106 of theclub head 104, or they can be designed to create a non-reflective surface on theouter surface 106 of theclub head 104. - In any event, with a soluble core of the type described in U.S. Pat. No. 3,692,551, in the molded
plastic club head 104, the core material/binder can be quite readily removed from the club head with water. For example, with a core 20 in which both the hardened salt binder and skin are water soluble, thehead 104 with thecore 20 is placed in a bath of water in a container or tank and a stream of water employed, with the bath, to dissolve the binder and flush the core material from thehead 104. With this procedure, the shape of thecore 20 is destroyed within thehead 104 and the destruction product or core material dispersed therefrom. - The liquid/solvent can directly contact the core 20 through a
hole 107. Thehole 107 was created during the above-described molding step as theresin 98 flowed around theinsert 30 containing the core prints 112. Those skilled in the art will appreciate that one ormore holes 107 may be located in theclub head 104, such as, for example, by drilling. The dissolved binder and core material can be poured out from theclub head 104, as shown inFIG. 7 . -
FIG. 8 schematically depicts a cut away view of theclub head 104 with the core 20 removed and aninsert 30 located in theclub head 104. The overmoldedcontinuous filament 46 in thewalls 108 and ribs 110 formed by thegrooves 42 of theclub head 104 can be seen. Individual pieces offilament 100 can also be seen in thewalls 108 of theclub head 104. -
FIG. 9 depicts theclub head 104 with two molded ininserts 30. Those skilled in the art will appreciate that theinserts 30 can also be threaded into place and/or an adhesive or cement can be used. -
Plugs 114, having a set of complementary threads to the threaded inserts 30, are threaded into theinserts 30. Theplugs 114 cover thehollow inserts 30 and they can also be weighted to customize the weight of theclub head 104. Theplugs 114 can be equally weighted or they can have different weights.Channels 118 within the heads of theplugs 114 have a complementary design to a Phillips head screwdriver, standard head screwdriver, or hex wrench so theplugs 114 can be readily inserted or removed. - Those skilled in the art will appreciate that instead of, or in addition to, locating the weights as described above, the
club head 104 can be drilled and inserts 30 and plugs 114 can be inserted in the holes, or weighted inserts can be molded into the core at selected areas. - A golf
club head shaft 120 is frictionally and/or adhesively attached through ashaft locator aperture 122 in theface plate 78 and into theclub head 104, as shown inFIG. 10 . Within theclub head 104, theshaft 120 is located within thetube 96 and secured thereto with friction and/or an adhesive as known to those skilled in the art. - The
golf club head 104 assembled according to the steps described above robustly supports theface plate 78 to reduce, or prevent, deflection of theface plate 78 upon contact with a golf ball. Reducing, or preventing, deflection of theface plate 78 decreases energy absorption into thegolf club head 104 and concentrates energy to the golf ball. Additionally, it can be appreciated that golf club heads 104 made according to the steps described herein may have different appearances than the preferred embodiment depicted inFIG. 10 . For instance, thewalls 108, theface plate 78 and thesole plate 80 of theclub head 104 may have any shape or size in accordance with United States Golf Association standards. - In accordance with the provisions of the patent statutes, the present invention has been described in what is considered to represent its preferred embodiments. However, it should be noted that the invention can be practiced otherwise than as specifically illustrated and described without departing from its spirit or scope.
Claims (1)
1. A golf club head, comprising a shell having an inside surface and an outside surface, said inside surface defining a substantially hollow interior portion of said shell and wherein said inside surface has a plurality of inwardly extending ribs, wherein said ribs and said shell being substantially comprised of a resin and a single continuous filament located within said resin.