US20080135124A1 - Webbing for seat belt - Google Patents

Webbing for seat belt Download PDF

Info

Publication number
US20080135124A1
US20080135124A1 US11/802,680 US80268007A US2008135124A1 US 20080135124 A1 US20080135124 A1 US 20080135124A1 US 80268007 A US80268007 A US 80268007A US 2008135124 A1 US2008135124 A1 US 2008135124A1
Authority
US
United States
Prior art keywords
filaments
webbing
yarns
seat belt
synthetic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US11/802,680
Inventor
Sadayuki Shimazaki
Itsuo Tabayashi
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Takata Corp
Original Assignee
Takata Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Takata Corp filed Critical Takata Corp
Assigned to TAKATA CORPORATION reassignment TAKATA CORPORATION ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: SHIMAZAKI, SADAYUKI, TABAYASHI, ISTUO
Publication of US20080135124A1 publication Critical patent/US20080135124A1/en
Abandoned legal-status Critical Current

Abstract

A webbing can be used in a passenger restraint belt. The webbing includes warp yarns and wefts comprising synthetic filaments and woven so as to extend orthogonally to each other. At least one of the warp yarns and the weft yarns are formed using synthetic filaments comprising first filaments and second filaments in which the second filaments are provided in the first filaments and have a melting temperature lower than that of the first filaments. The synthetic filaments are middle shrinking synthetic filaments which are contracted at a dimensional shrinkage rate of 15% to 20% after the second filaments are melted under conditions of 150° C. or more for 180 seconds or more. The webbing has a weight of 60 g/m or less, a tensile strength of 25 kN or more, and a retention rate after hexagonal bar abrasion of 70% or more.

Description

    BACKGROUND
  • The present invention relates to a technique for forming a passenger restraint belt used for restraining a passenger when a vehicle accident occurs.
  • A conventional technique for forming this type of passenger restraint belt has been described, for example, in Japanese Unexamined Patent Application Publications No. 2004-315984 (hereinafter known as “JP2004-315984”). JP2004-315984 discloses a seat belt for use as a long passenger restraint belt for restraining a vehicle passenger, the possibility of forming a seat belt having superior compactness and comfort by improving the filament yarn bundles used for the seat belt, a woven configuration of the bundles and the like.
  • When this type of seat belt is designed, a basic property of rigidity capable of restraining a passenger in the case of a vehicle accident is required. In addition, considering the comfort when the seat belt is worn as disclosed in JP2004-315984 and the properties of withdrawing the seat belt from a retractor, a reduction in weight of the long seat belt is also desired. Accordingly, in order to reduce the weight of a seat belt, it is conceived that the number of filaments forming the seat belt is reduced. By simply reducing the number of filaments, the reduction in weight can be achieved; however, the decrease in rigidity caused by the reduction in number of filaments may become a concern. As a result, the essential basic property of restraining a passenger may not be sufficiently obtained in some cases. Further, considering the transportation of this type of seat belt, it is desired to form a passenger restraint belt of which the property of a filament yarn is hardly affected by high temperature conditions during transportation.
  • Accordingly, the present invention has been conceived in consideration of the problem described above, and an object of an embodiment of the present invention may be to provide an effective technique to simultaneously achieve the increase in strength and the reduction in weight of a passenger restraint belt which is installed in a vehicle. In addition, it may be another object of an embodiment of the present invention to provide a passenger restraint belt suitable for transportation in which the property of a filament yarn is hardly changed under the high temperature conditions during transportation.
  • Accordingly, an embodiment of the present invention may be applied to a technique for forming a seat belt or a safety belt, which is used as a means for restraining a passenger in a vehicle such as an automobile.
  • SUMMARY
  • The webbing for a passenger restraint belt according to an embodiment of the present invention may be used as a passenger restraint belt such as a long seat belt which is retracted or withdrawn by a seat belt retractor or a safety belt of an air plane. This webbing for a passenger restraint belt is formed as a webbing in which warp yarns (vertical yarns) and weft yarns (horizontal yarns), both of which are made of synthetic filaments, are woven to extend orthogonally to each other.
  • In particular, in the webbing for a passenger restraint belt according to an embodiment of the present invention, at least either one of the weft yarns and warp yarns are formed using synthetic filaments composed of first filaments and second filaments. The second filaments are provided in the first filaments and have a melting temperature lower than that of the first filaments. The synthetic filaments are middle shrinking synthetic filaments which are contracted at a dimensional shrinkage rate of 15% to 20% after the second filaments are melted under conditions of 150° C. or more for 180 seconds or more. The state in which the second filaments are provided in the first filaments includes the state in which the second filaments are substantially evenly dispersed between the first filaments or the state in which the second filaments are unevenly scattered in the first filaments. The middle shrinking synthetic filaments are called “middle shrinking type synthetic filaments” or “middle shrinking yarns” which have a middle dimensional shrinkage rate of less than 20% and more than 15%. In addition, according to one embodiment of the present invention, the case in which the warp yarns or the weft yarns are formed using the middle shrinking synthetic filaments and the case in which the warp yarns and the weft yarns are both formed using the middle shrinking synthetic filaments may be included. In this case, the warp yarns and/or the weft yarns may be partly or entirely formed using middle shrinking synthetic filaments. For the middle shrinking synthetic filaments, polyester-based filaments may be used. The dimensional shrinkage rate of filaments, such as the warp yarns and the weft yarns, that is, the degree of shrinkage in the longitudinal direction, can be represented by the following equation, ((length after process−length before process)/length after process)×100, the lengths being obtained before and after the process performed under the above process conditions. The dimensional shrinkage rate can be obtained using a process method or a measurement method in accordance with, for example, JIS L 1013.
  • In the webbing for a passenger restraint belt, according to an embodiment of the present invention, when at least either one of the warp yarns and the weft yarns are formed using middle shrinking synthetic filaments having a dimensional shrinkage rate of 15% to 20%, and when the webbing is heated in accordance with the above process conditions, the second filaments having a low melting point of the middle shrinking synthetic filaments are preferentially melted, and shrinkage and convergence of the warp yarns and/or the weft yarns occur in the longitudinal direction. As a result, the cross-sectional area of the filament yarn material of the warp yarns and/or the weft yarns after the shrinkage is increased, and the hardness is increased, so that the rigidity of the webbing is increased as a whole. Hence, corresponding to the increase in rigidity of the webbing formed using yarns containing middle shrinking synthetic filaments, the weight can be decreased by reducing the number of the warp yarns and/or the weft yarns. Consequently, a webbing for a passenger restraint belt having a weight of 60 g/m or less, a tensile strength of 25 kN or more, and a retention rate after hexagonal bar abrasion of 70% or more can be obtained, so that a passenger restraint belt having both rigidity and lightweight properties can be provided. In this case, the tensile strength of the webbing can be measured by a method in accordance with the JIS D4604 method, and the retention rate after hexagonal bar abrasion of the webbing can be measured by a method in accordance with the JIS D4604 method.
  • In addition, considering the transportation of a passenger restraint belt, it is desired to form the belt of which the property of a filament yarn is hardly affected by high temperature conditions during transportation. The webbing for a passenger restraint belt according to an embodiment of the present invention is effective in forming a passenger restraint belt suitable for transportation in which the property of a filament yarn is hardly changed under the high temperature conditions during transportation because the shrinking of the filament yarn is limited.
  • Further, the webbing for a passenger restraint belt according to an embodiment of the present invention has the structure in which the weft density is set to 20 picks per inch or less in the aforementioned webbing for a passenger restraint belt.
  • In a cross-sectional structure of this type of webbing, the warp yarns are extended to form a curved shape, a so-called “crimping (undulating phenomenon),” in contrast to the weft yarns which are linearly extended. Crimping is a particular phenomenon caused by a weaving method for a woven structure in which the weft yarns are woven between warp yarns which are shed alternately. In the structure as described above, when the weft density is set to 20 picks per inch or less and preferably set to 17 picks per inch or less, the degree of meanderings of the curved crimped shape can be decreased, and the stress concentrated on the curved portions can be alleviated. As a result, in order to simultaneously achieve the increase in strength of the webbing and the reduction in weight thereof, the properties can be further improved.
  • In the webbing for a passenger restraint belt according to an embodiment of the present invention, at least either one of the warp yarns and the weft yarns may be formed using a filament yarn material made of twist yarns or a filament yarn material made of entangled non-twist yarns. The present invention may include the case in which the warp yarns or the weft yarns are formed using a filament yarn material made of twist yarns or a filament yarn material made of entangled non-twist yarns or the case in which the warp yarns and the weft yarns are both formed using a filament yarn material made of twist yarns or a filament yarn material made of entangled non-twist yarns. By using the filament yarn material as described above, because the entanglement among the filaments is increased, and the cohesion is enhanced, the rigidity of the webbing can be further improved. In particular, when the filament yarn material made of entangled non-twist yarns is used, the material cost can be reduced as compared to that in the case in which the filament yarn material mode of twist yarns is used. As a result, the production cost of the webbing for a passenger restraint belt can also be reduced.
  • The seat belt according to an embodiment of the present invention may be a passenger restraint belt for restraining a vehicle passenger and formed using the aforementioned webbing for a passenger restraint belt According to the structure as described above, the increase in strength of the seat belt and the reduction in weight thereof can be achieved at the same time. In addition, it may be possible to provide a seat belt suitable for transportation in which the property of a filament yarn is hardly changed under the high temperature conditions during transportation.
  • The seat belt device according to an embodiment of the present invention may comprise at least the aforementioned scat belt, a seat belt retractor, a buckle, and a tongue. The seat belt retractor may have a function of retracting and withdrawing the scat belt and have a spool which is received in a retractor housing. The seat belt retractor may have a drive mechanism to drive the spool and a control mechanism to control the drive mechanism. In addition, the tongue provided for the seat belt may be configured to be engaged with the buckle fixed to a vehicle when the seat belt is worn. According to the structure described above, a seat belt device can be provided in which the increase in strength of the seat belt and the reduction in weight thereof are achieved at the same time. In addition, the seat belt device can be provided with a seat belt suitable for transportation in which the property of the filament yarn is hardly changed under the high temperature conditions during transportation.
  • As described above, according to an embodiment of the present invention, in the webbing for a passenger restraint belt in which the warp yarns and the weft yarns, both of which are made of synthetic filaments, are woven so as to extend orthogonally to each other, at least either one of the warp yarns and the weft yarns are formed using middle shrinking synthetic filaments, so that a technique effective to simultaneously obtain the increase in strength of a passenger restraint belt, the reduction in weight thereof and the improvement in the transportation performance can be provided.
  • It is to be understood that both the foregoing general description and the following detailed description are exemplary and explanatory only, and are not restrictive of the invention as claimed.
  • BRIEF DESCRIPTION OF THE DRAWINGS
  • The features, aspects, and advantages of the present invention will become apparent from the following description, appended claims, and the accompanying exemplary embodiments shown in the drawings, which are briefly described below.
  • FIG. 1 is a view showing a schematic structure of a seat belt device 100 of an embodiment according to the present invention.
  • FIG. 2 is a table showing weaving conditions and webbing properties of webbings for a seat belt, the webbings being formed in one embodiment (the “example”) and a comparative example.
  • FIG. 3 is a schematic view showing a low-melting-point polyester filament (middle shrinking yarn).
  • DETAILED DESCRIPTION
  • Hereinafter, an embodiment of the present invention will be described in detail with reference to the FIGS.
  • The embodiment relates to a seat belt device installed in an automobile and proposes an optimum seat belt forming the seat belt device and a manufacturing method of the seat belt.
  • First, with reference to FIG. 1, the structure of a seat belt device 100 will be described. FIG. 1 shows a schematic structure of the seat belt device 100 according to an embodiment of the present invention.
  • As shown in FIG. 1, the seat belt device 100 may be a seat belt device for a vehicle, which is installed in a vehicle, and is primarily composed, for example, of a seat belt retractor 101, a seat belt 110, a tongue 104, and a buckle 106.
  • The seat belt retractor 101 may have the structure in which at least a tubular spool 102 is received in a retractor housing 101 a, and retracting and withdrawing of the seat belt 110 can be performed with this spool 102. The spool 102 is driven by a driving means formed using a spring, a motor, or the like. According to the example shown in FIG. 1, this seat belt retractor 101 is arranged in an accommodation space of a B-pillar 10 of the vehicle.
  • The seat belt 110 may be a long belt to restraint a vehicle passenger C or to release the restraint and is a belt formed from a long belt-shaped member (webbing) made of a synthetic filament yarn material. This seat belt 110 may be withdrawn from the seat belt retractor 101 which is fixed to the vehicle and is connected to an outer anchor 105 via a shoulder guide anchor 103 provided in a passenger shoulder part region of the vehicle passenger C and the tongue 104. In addition, when the tongue 104 is inserted into (or engaged with) the buckle 106 which is fixed to the vehicle, the seat belt 110 is in a seat belt wearing state for the vehicle passenger C.
  • In order to form a seat belt which is excellent for practical use, the inventors of the present invention wove a webbing for a seat belt in accordance with predetermined weaving conditions which will be described later, and webbing properties of the webbing for a seat belt were evaluated.
  • The weaving conditions of the webbing for the seat belt 110 shown in FIG. 1 and the webbing properties of an example of this embodiment and a comparative example are shown in FIG. 2. The webbing for a seat belt of the example of this embodiment and the comparative example are each formed as a fabric in which vertical yarns (also called “warp yarns”) and horizontal yarns (also called “weft yarns”), both of which are formed from synthetic filaments, are woven so as to extend orthogonally to each other. In particular, in the example of this embodiment, middle shrinking yarns in the longitudinal direction of the filaments are used as the weft yarns. In me comparative example, the middle shrinking yarns are not used as the weft yarns.
  • As shown in FIG. 2, in the “example,” a filament yarn bundle of warp yarns each consisting of 144 filaments having a dtex of 1670, which was a weight-reduced filament yarn bundle obtained by reducing 34 warp yarns from a normal product (in which the number of warp yarns was 280), was used as a first filament yarn bundle. By this reduction, the number of the warp yarns was decreased to 246. As the first filament yarn bundle, a yarn material made of entangled non-twist yarns was used. In addition, as a second filament yarn bundle, weft yarns were used which were formed from high-melting-point polyester filaments each consisting of 96 filaments having a dtex of 560 and low-melting-point polyester filaments each consisting of 12 filaments having a dtex of 84, that is, middle shrinking yarns having a thermal shrinkage rate of 20% under process conditions of 150° C. for 30 minutes. This shrinkage rate is the degree of shrinkage of the filaments in the longitudinal direction and corresponds to the “dimensional shrinkage rate.” As the middle shrinking yarn, a yarn which has a thermal shrinkage rate of 15% to 20% (that is a yarn which has a middle dimensional shrinkage rate of less than 20% and more than 15%) under process conditions of 150° C. or more for 180 seconds or more may be optionally selected.
  • As for the blending of the weft yarns between the high-melting-point polyester filaments and the low-melting-point polyester filaments, for example, one high-melting-point polyester filament consisting of 96 filaments having a dtex of 560 and one low-melting-point polyester filaments (middle shrinking yarns) each consisting of 12 filaments having a dtex of 84 (48 filaments having a dtex of 280) may be blended together.
  • As the high-melting-point polyester filaments forming the weft yarns, typically, a polymer material of polyethylene terephthalate is used which is manufactured by an esterification reaction using terephthalic acid and ethylene glycol. In addition, for the low-melting-point polyester filaments (middle shrinking yarn) forming the weft yarns, typically, a copolymer material of the above polyethylene terephthalate and polyethylene isophthalate, which is manufactured by an esterification reaction using terephthalic acid, isophthalic acid, and ethylene glycol, is used.
  • A schematic view of the low-melting-point polyester filament (middle shrinking yarn) of an embodiment is shown in FIG. 3. As shown in FIG. 3, this low-melting-point polyester filament has the structure in which polyethylene isophthalate is dispersed in polyethylene terephthalate. That is, this low-melting-point polyester filament has the structure in the form of a copolymer in which polyethylene isophthalate having a low melting point is mixed in polyethylene terephthalate having a high melting point. In this embodiment, a filament yarn material, which is a bundle composed of the low-melting-point polyester filaments (monofilaments) and which is a so-called multifilament, is used as some of the weft yarns. When a webbing formed from the weft yarns as described above is heated, the polyethylene isophthalate (low-melting-point filaments) having a low melting point relative to that of the polyethylene terephthalate is preferentially melted, monofilaments are melted together, and as a result, shrinkage and convergence occur. Hence, when multifilaments adjacent to each other form a monofilament by convergence, the hardness is increased. As a result, the cross-sectional area of a filament material after the shrinkage of the weft yarns is increased, and the hardness is increased, so that the rigidity of the webbing is increased as a whole.
  • In this low-melting-point polyester filament, as a copolymerization ratio of polyethylene isophthalate, that is, the amount thereof, is increased, the melting point of the filament yarn is decreased. For example, when the copolymerization ratio of polyethylene isophthalate is 10% (that is, the ratio of polyethylene terephthalate is 90%), the melting point of the low-melting-point polyester filament is set to 230° C., and when the copolymerization ratio of polyethylene isophthalate is 30% (that is, the ratio of polyethylene terephthalate is 70%), the melting point of the low-melting-point polyester filament is set to 160° C. In this embodiment, a low-melting-point polyester filament having a copolymerization ratio of polyethylene isophthalate of 10% and a melting point of 230° C. is used as the middle shrinking yarn.
  • Next, the first filament yarn bundles and the second filament yarn bundles of the “example” were woven by a needle type loom in accordance with the weaving conditions shown in FIG. 2, so that a webbing for a seat belt (the webbing for evaluation) was obtained. In this weaving, the weft density was set to 19 picks per inch. Subsequently, after a dyeing process and a pre-drying process were performed for the webbing for evaluation whenever necessary, a heat stabilization process was performed. In this heat stabilization process, the webbing for evaluation was passed through a heating furnace at a controlled temperature of approximately 150° C. for approximately 30 minutes. The conditions for this heat stabilization process may be optionally selected from the range in which the temperature is 150° C. or more and the time is 180 seconds or more. For example, process conditions of 150° C. for 180 seconds or process conditions of 150° C. for 5 minutes may also be selected. Furthermore, when the webbing properties shown in FIG. 2 were measured, after the webbing for evaluation was cut into a test piece having a predetermined size, followed by spontaneous drying, the test piece was exposed under predetermined constant temperature and humidity conditions (20° C. and 65% RH).
  • In the “example,” for example, by the reduction in the number of the warp yarns performed to obtain the first filament yarn bundle, the weight per unit length of the entire webbing for the seat belt was 54.52 g/m, and the weight reduction rate was 11.49%.
  • On the other hand, in the “comparative example,” a filament yarn bundle of warp yarns each consisting of 144 filaments having a dtex of 1670, in which the number of the warp yarns is normal (280 warp yarns), was used as the first filament yarn bundle. As this first filament yarn bundle, a yarn material made of entangled non-twist yarns was used. In addition, for the second filament yarn bundle, a filament yarn bundle of weft yarns each consisting of 96 filaments having a dtex of 830 and containing no middle shrinking yarns (which were used in the “example”) was used, and the weft density for the second filament yarn bundle was set to 19 picks per inch.
  • In this comparative example, the weight per unit length of the entire webbing for the seat belt was 61.60 g/m, and this weight was defined as a weight-reduction standard.
  • For evaluation of the webbing properties, items shown below were measured for the webbings for the seat belt of the “example” and the comparative example by the inventors of the present invention, the webbings being formed in accordance with the weaving conditions described above. For every measurement item, at least 5 test pieces were prepared from each of the webbings, and the repeatability was confirmed from the measurement results.
  • (Measurement Items)
  • “Tensile strength” (also called “intensity” or “strength”) and “retention rate after hexagonal bar abrasion” were used as the measurement items for evaluating the webbing properties of the webbing for a seat belt.
  • (Measurement of Intensity)
  • The tensile strength of the webbing was measured by a method in accordance with the JIS D4604 method. When the tensile strength of the webbing is designed so as to be 25 kN or more, the desired load bearing characteristics required for a seat belt can be obtained.
  • (Measurement of Retention Rate After Hexagonal Bar Abrasion)
  • The retention rate after hexagonal bar abrasion of the webbing was measured by a method in accordance with the JIS D4604 method. When the webbing is designed to have the retention rate after hexagonal bar abrasion of, for example, 70% or more, the desired abrasion resistance required for a seat belt can be obtained.
  • (Evaluation Items)
  • Next, the inventors evaluated the webbings for the seat belt of the “example” and the comparative example based on the above measurement results. As the evaluation items, “lightweight properties,” “strength,” “abrasion resistance” and the like were used.
  • As shown in FIG. 2, the webbing of the “example” has a weight reduction rate of 11.49% based on the result of the comparative example by the reduction of 34 warp yarns for forming the first filament yarn bundle, and hence it is confirmed that the webbing of the “example” is exceptionally superior in terms of its lightweight properties. In addition, although the other evaluation items, that is, the tensile strength and the hexagonal anti-abrasion resistance, are slightly inferior to those of the comparative example, both of them satisfy the respective predetermined levels, that is, a tensile strength of 25 kN or more and a retention rate after hexagonal bar abrasion of 70% or more, and hence it is confirmed that the strength and the abrasion resistance are also superior.
  • (Overall Evaluation)
  • In accordance with the evaluation results shown in FIG. 2, the overall evaluation is represented by
    Figure US20080135124A1-20080612-P00001
    because it is understood that the webbings of the “example” can be formed into superior seat belts in terms of all the evaluation items, that is, the lightweight properties, the strength, and the abrasion resistance. On the other hand, the level of the webbing for a seat belt of the comparative example is inferior to a desired level, and hence the overall evaluation is represented by “x” because it is understood that when the lightweight properties, the strength, and the abrasion resistance are evaluated in an integrated manner (in particular, because the weight of the webbing for a seat belt of the “comparative example” is more than 60 g/m), the lightweight properties thereof are not satisfactory.
  • As described above, according to an embodiment of the present invention, a practical seat belt (or webbing) having superior lightweight properties, strength, and abrasion resistance and a seat belt device formed by using this seat belt can be provided.
  • That is, the webbings for a seat belt of the “example” which are formed by weaving in this embodiment are totally superior to the webbing of the “comparative example” in terms of the lightweight properties, the tensile strength, and the retention rate after hexagonal bar abrasion, and hence the above webbings are effectively used when the weight of the seat belt is reduced while the decrease in strength thereof is suppressed.
  • In particular, in the “example,” because the weft yarns are used in which middle shrinking low-melting-point polyester filaments (middle shrinking yarns), which are contracted at a thermal shrinkage rate of 15 to 20% after being melted under process conditions of 150° C. for 30 minutes or more, are blended with high-melting-point polyester filaments, the cross-section of the single yarn material after the shrinkage of the weft yarns is increased, and the rigidity can be increased. Corresponding to this increase in rigidity, the weight reduction can be performed by reducing the number of weft yarns. Accordingly, a webbing for the seat belt can be obtained which has a weight of 60 g/m or less, a tensile strength of 25 kN or more, and a retention rate after hexagonal bar abrasion of 70% or more, and as a result, a seat belt having both rigidity and lightweight properties can be provided. In addition, the thermal shrinkage rate of the filaments, that is, the degree of contraction in the longitudinal direction, can be represented by the following equation, ((length after process−length before process)/length after process)×100, the lengths being obtained before and after the process performed under the above process conditions. By a process method or a measurement method in accordance with, for example, JIS L 1013, the thermal shrinkage rate can be obtained.
  • In addition, considering the transportation of a passenger restraint belt such as a scat belt, it is desired to form the belt of which the property of a filament yarn is hardly affected by high temperature conditions during transportation. The webbing for a passenger restraint belt according to an embodiment of the present invention is effective in forming a seat belt suitable for transportation in which the property of a filament yarn is hardly changed under the high temperature conditions during transportation because the shrinking of the filament yarn for the weft yarn (filament yarns in which high-melting-point polyester and low-melting-point polyester are blended) is limited.
  • In the present invention, the types of filaments for use as the warp yarns and weft yarns, the process conditions and the like may be optionally changed whenever necessary as long as at least a webbing for a seat belt having a weight of 60 g/m or less, a tensile strength of 25 kN or more, and a retention rate after hexagonal bar abrasion of 70% or more is obtained by optionally using middle shrinking synthetic filaments having a thermal shrinkage rate (dimensional shrinkage rate) in the range of 15% to 20% under process conditions of 150° C. or more for 180 seconds or more. In the above embodiment, the weft yarns are formed by blending the high-melting-point polyester filaments with the low-melting-point polyester filaments (middle shrinking yarns). However, for example, the types of high-melting-point filaments and low-melting-point filaments, the combination between the high-melting-point filaments and the low-melting-point filaments, and the blending ratio therebetween may be optionally changed whenever necessary.
  • In the webbings for the scat belt of the “example” which are formed by weaving, the warp yarns may be formed from a yarn material made of twist yarns or a yarn material made of entangled non-twist yarns. Accordingly, because the entanglement among filaments is increased, and the cohesion is enhanced, the rigidity of the webbing can be further improved. In particular, when the yarn material made of entangled yarns is used, the material cost can be reduced as compared to that in the case in which the yarn material made of twist yarns is used, and as a result, the production cost of the webbing can also be reduced.
  • In a cross-sectional structure of the webbing, the warp yarns may be extended to form a curved shape, a so-called “crimping (undulating phenomenon),” in contrast to the weft yarns which are linearly extended. Crimping is a particular phenomenon caused by a weaving method to form a woven structure in which weft yarns are woven between warp yarns which are shed alternately. Accordingly, as is the case of the webbings for the seat belt of the “example,” when the weft density is decreased to 20 picks per inch or less, the degree of meanderings of the curved crimped shape can be decreased, and stress concentrated on the curved portions can be alleviated. As a result, in order to simultaneously achieve the increase in strength of the webbing and the reduction in weight thereof, the properties can be further improved. In the present invention, when the weft density can be optionally set in the range of 20 picks per inch or less, and when the desired webbing properties can be obtained by using middle shrinking synthetic filaments, the weft density may be set to more than 20 picks per inch in some cases.
  • (Other Embodiments)
  • Incidentally, the present invention is not limited to the above embodiment, and various modifications and changes may be performed. For example, the following may be carried out based on the above embodiment.
  • In the above embodiment, the case is described in which, of the warp yarns and the weft yarns, only the weft yarns are formed using middle shrinking synthetic filaments. According to embodiments of the present invention, however, only the warp yarns or both the weft yarns and the warp yarns may be formed using middle shrinking synthetic filaments
  • In the above embodiment, a case is only described in which, of the warp yarns and the weft yarns, the warp yarns made of a yarn material which includes entangled non-twist yarns arc only used. According to embodiments of the present invention, however, only the weft yarns or both the weft yarns and the warp yarns may be formed using a yarn material made of twist yarns or a yarn material made of entangled non-twist yarns. In addition, according to embodiments of the present invention, when desired webbing properties are obtained by using middle shrinking synthetic filaments, the warp yarns and the weft yarns may be formed without using a yarn material made of twist yarns or a yarn material made of entangled non-twist yarns.
  • In addition, in the above embodiment, the seat belt device 100 for a driver of an automobile is described. However, in addition to that, the present invention may be applied to the structure of a seat belt which restrains a passenger in a front passenger seat or in a rear seat and to the structure of a seat belt used in an airplane or a ship.
  • The priority application Japanese Patent Application No. 2006-333601, filed Dec. 11, 2006, is incorporated by reference herein.
  • Given the disclosure of the present invention, one versed in the art would appreciate that there may be other embodiments and modifications within the scope and spirit of the invention. Accordingly, all modifications attainable by one versed in the art from the present disclosure within the scope and spirit of the present invention are to be included as further embodiments of the present invention. The scope of the present invention is to be defined as set forth in the following claims.

Claims (11)

1. A webbing for a passenger restraint belt, comprising:
warp yarns and weft yarns comprising synthetic filaments and woven so as to extend orthogonally to each other,
wherein at least one of the warp yarns and the weft yarns are formed using synthetic filaments comprising first filaments and second filaments,
wherein the second filaments are provided in the first filaments and have a melting temperature lower than that of the first filaments,
wherein the synthetic filaments are middle shrinking synthetic filaments which are contracted at a dimensional shrinkage rate of 15% to 20% after the second filaments are melted under conditions of 150° C. or more for 180 seconds or more, and
wherein the webbing has a weight of 60 g/m or less, a tensile strength of 25 kN or more, and a retention rate after hexagonal bar abrasion of 70% or more.
2. The webbing for a passenger restraint belt according to claim 1, wherein the weft density is 20 picks per inch or less.
3. The webbing for a passenger restraint belt according to claim 2, wherein the weft density is 17 picks per inch or less.
4. The webbing for a passenger restraint belt according to claim 1, wherein at least one of the warp yarns and the weft yarns are formed using a filament yarn material made of twist yarns or a filament yarn material made of entangled non-twist yarns.
5. The webbing for a passenger restraint belt according to claim 4, wherein both the warp yarns and the weft yarns are formed using a filament yarn material made of twist yarns or a filament yarn material made of entangled non-twist yarns.
6. The webbing for a passenger restraint belt according to claim 1, wherein both the warp yarns and the weft yarns arc formed using the synthetic filaments comprising the first filaments and the second filaments.
7. The webbing for a passenger restraint belt according to claim 1, wherein the first filaments comprise polyethylene terephthalate.
8. The webbing for a passenger restraint belt according to claim 1, wherein the second filaments comprise polyethylene terephthalate and polyethylene isophthalate.
9. The webbing for a passenger restraint belt according to claim 1, wherein the first filaments comprise high-melting-point polyester filaments and the second filaments comprise low-melting-point polyester filaments.
10. A seat belt for restraining a passenger, comprising:
a webbing, wherein the webbing comprises warp yarns and weft yarns comprising synthetic filaments and woven so as to extend orthogonally to each other,
wherein at least one of the warp yarns and the weft yarns are formed using synthetic filaments comprising first filaments and second filaments,
wherein the second filaments are provided in the first filaments and have a melting temperature lower than that of the first filaments,
wherein the synthetic filaments are middle shrinking synthetic filaments which are contracted at a dimensional shrinkage rate of 15% to 20% after the second filaments are melted under conditions of 150° C. or more for 180 seconds or more, and
wherein the webbing has a weight of 60 g/m or less, a tensile strength of 25 kN or more, and a retention rate after hexagonal bar abrasion of 70% or more.
11. A seat belt device comprising:
the seat belt comprising a webbing;
a seat belt retractor configured to retract and withdraw the scat belt;
a buckle configured to be fixed to a vehicle; and
a tongue provided for the seat belt and is engaged with the buckle when the seat belt is worn,
wherein the webbing comprises warp yarns and weft yarns comprising synthetic filaments and woven so as to extend orthogonally to each other,
wherein at least one of the warp yarns and the weft yarns are formed using synthetic filaments comprising first filaments and second filaments,
wherein the second filaments are provided in the first filaments and have a melting temperature lower than that of the first filaments,
wherein the synthetic filaments are middle shrinking synthetic filaments which are contracted at a dimensional shrinkage rate of 15% to 20% after the second filaments are melted under conditions of 150° C. or more for 180 seconds or more, and
wherein the webbing has a weight of 60 g/m or less, a tensile strength of 25 kN or more, and a retention rate after hexagonal bar abrasion of 70% or more.
US11/802,680 2006-12-11 2007-05-24 Webbing for seat belt Abandoned US20080135124A1 (en)