US20060117736A1 - Exhaust system for a diesel engine comprising a nox- trap - Google Patents

Exhaust system for a diesel engine comprising a nox- trap Download PDF

Info

Publication number
US20060117736A1
US20060117736A1 US10530166 US53016605A US2006117736A1 US 20060117736 A1 US20060117736 A1 US 20060117736A1 US 10530166 US10530166 US 10530166 US 53016605 A US53016605 A US 53016605A US 2006117736 A1 US2006117736 A1 US 2006117736A1
Authority
US
Grant status
Application
Patent type
Prior art keywords
exhaust
absorbent
trap
gas
system
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US10530166
Inventor
Martyn Twigg
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Johnson Matthey PLC
Original Assignee
Johnson Matthey PLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date

Abstract

An exhaust system for a diesel engine includes a NOx-trap having at least one first NOx absorbent and platinum. The exhaust system also has at least one second NOx absorbent disposed upstream of the NOx trap. The at least one second NOx absorbent is alumina, ceria, or both.

Description

  • [0001]
    The present invention relates to an exhaust system for a diesel engine, which system comprising a first nitrogen oxide (NOx)-trap comprising at least one first NOx absorbent and platinum.
  • [0002]
    Exhaust gases from compression ignition engines, such as diesel engines, comprise a mixture of pollutants including carbon monoxide (CO), unburned hydrocarbons (HC), nitrogen oxides (NOx) and particulate matter (PM) including volatile and soluble organic fractions (VOF and SOF respectively). The NOx component can comprise nitrogen monoxide NO) and nitrogen dioxide (NO2). The level of these pollutants in exhaust gases from internal combustion engines it is permissible to exhaust to atmosphere is regulated by legislation. Such legislation can be met by engine design, engine management and/or exhaust gas after treatment, and typically a combination of all three measures.
  • [0003]
    In conventional diesel engines, present legislated limits for HC and CO can be met using a platinum (Pt)-based diesel oxidation catalyst (DOC). Diesel nitrogen oxides (NOx) emissions are presently controlled by engine management, such as exhaust gas recirculation (EGR). As a consequence, however, PM emissions including VOF and SOF are increased. The DOC is used to treat VOF and SOF in order to meet presently legislated limits for PM.
  • [0004]
    Another prior art exhaust system primarily for treating diesel exhaust comprises an oxidation catalyst for oxidising NO in the exhaust gas to NO2 and a downstream filter for trapping PM. A process for treating diesel PM that uses this arrangement is described in EP 0341382 or U.S. Pat. No. 4,902,487, both of which are incorporated herein by reference. The process comprises passing diesel exhaust gas including PM and NO unfiltered over an oxidation catalyst to convert the NO to NO2, collecting soot on the filter and combusting the collected soot by reaction with the NO2. This technology is commercially available as Johnson Matthey's Continuously Regenerating Trap or CRT®. Combustion of the PM in NO2 results in CO and NO, with a potential side-reaction leading to the complete reduction of the NO2 to N2 as described in SAE 890404.
  • [0005]
    A problem with the process described in EP 0341382 and in the use of exhaust gas after treatment catalysts such as DOC is that, as exhaust emission legislation is tightened, legislative bodies have begun to discuss limiting the amount of NO2 it is permissible to exhaust to atmosphere. For example, the California Air Resources Board (CARB) has proposed that a maximum of 20% of tailpipe NOx of the relevant drive cycle is emitted as NO2 (see CARB's Diesel Risk Reduction Program and Final Regulation Order Chapter 14 “Verification procedure, warranty and in-use compliance requirements for in-use strategies to control emissions from diesel engines”, section 2706). NO2 is toxic and can cause headaches, dizziness and nausea in low doses. It also has an objectionable smell. In the process of EP 0341832, if there is insufficient PM on the filter to react with NO2 generated over the oxidation catalyst or the temperature of the exhaust gas is below a preferred range for combustion of PM in NO2, NO2 can slip past the filter and be undesirably exhausted to atmosphere.
  • [0006]
    At low exhaust gas temperatures, e.g. about 200-250° C., and part-load, a modern diesel engine produces a relatively high amount of NOx in the form of NO2. If, as is typical in an exhaust system for a lean-burn internal combustion engine including a NOx-trap, the exhaust gas is first passed over a platinum oxidation catalyst, the NO2 can be removed by facile low temperature oxidation of hydrocarbons present in the exhaust gas. This process is known as lean NOx catalysis. In any event, the NOx absorbent material can poison the lean NOx activity of the platinum, thereby reducing the conversion efficiency of the process. At higher temperatures, e.g. above about 300-350° C., the oxidation of NO to NO2 becomes sufficiently rapid for significant quantities of NO2 to be formed and a conventional platinum containing NOx-trap then starts to become effective.
  • [0007]
    A NOx-trap is purposely designed for absorbing and storing NOx in lean exhaust gases (lambda >1 conditions), and releasing and catalytically reducing the stored NOx in rich exhaust gases (1 >lambda conditions). To remove the stored NOx typically the engine is controlled so that periodically it is run rich during normal lean-running operation. A NOx-trap typically includes active materials for three functions: an oxidation catalyst, such as platinum; a NOx absorbent, for example a compound of an alkali metal e.g. a potassium and/or a caesium, an alkaline earth compound typified by barium oxide or a compound of a rare earth metal, such as lanthamum; and a reduction catalyst, such as rhodium. In the exhaust gas the or each alkali metal and alkaline earth metal compound is present as an oxide, although it may also be present in use as a hydroxide or a carbonate.
  • [0008]
    A convention used herein is to refer to a “NOx-trap” as a composition comprising a NOx absorbent and at least one catalytic material, such as a platinum group metal. NOx absorbent refers to a material, e.g. alkaline earth metal compound, alkali metal compound or rare earth metal compound, capable of absorbing NO2 in lean exhaust gas.
  • [0009]
    An oxidation catalyst is purposely designed to provide for the reaction of gaseous components with oxygen, typically in as wide a temperature range as possible, especially at lower temperatures. The catalyst oxidises whenever oxygen is available for reaction in the gas stream Active components of an oxidation catalyst can include platinum, palladium or a base metal active for oxidation such as manganese, copper, molybdenum, cobalt or any other transition element that is active for oxidation.
  • [0010]
    An oxygen storage component (OSC) is purposely designed to absorb oxygen from lean exhaust gases and to release oxygen in rich exhaust gas conditions. Examples of suitable OSC include ceria doped with transition metals, e.g. zirconium, or other rare earth metals and manganese-based materials.
  • [0011]
    According to the present specification, “adsorb” and “absorb” in relation to the storage of NOx on suitable basic materials have the same meaning.
  • [0012]
    Our WO 02/18753 (incorporated herein by reference) describes an exhaust system for a lean-burn internal combustion engine, including a diesel engine, comprising an oxidation catalyst upstream of a NOx-trap for oxidising relatively large amounts of unburned hydrocarbons present in exhaust gas in normal lean-running conditions and for oxidising NO in the exhaust gas to NO2 in lean-running conditions. In one embodiment, a clean-up catalyst comprising an oxygen storage component such as ceria, an oxidation component, such as platinum, a NOx reducing component, for example rhodium, and a component for suppressing H2S, for example NiO, Fe2O3, MnO2, CoO and CrO2, is disposed downstream of the NOx-trap.
  • [0013]
    In WO 01/94760, we disclose an exhaust system for a diesel engine comprising a solid NOx absorbent for absorbing NOx from relatively cool exhaust gas and desorbing adsorbed NOx and passing it to atmosphere by intermittently increasing the temperature of the exhaust gas.
  • [0014]
    We have now found that by using a NOx-absorbent which is free of platinum to absorb relatively low temperature engine-derived NO2 upstream of a NOx-trap comprising platinum when the NOx-trap is too cool to catalytically reduce the NO2 to N2 and to thermally release stored NOx when the NOx reducing function of the NOx-trap is up to temperature, the exhaust system as a whole is able to treat NOx more efficiently. More particularly, we have found that the system slips less NO2 to atmosphere than a system comprising a conventional NOx-trap comprising a NOx absorbent and platinum as the sole NOx absorbent-containing component.
  • [0015]
    According to one aspect, the invention provides an exhaust system for a diesel engine, which system comprising a first NOx-trap comprising at least one first NOx absorbent and platinum, characterised in that at least one second NOx absorbent is disposed upstream of the first NOx-trap, which at least one second NOx absorbent is not associated with platinum.
  • [0016]
    A further advantage of this system over the above-mentioned prior art system is that the system of the invention generates less N2O by lean NOx catalysis over the platinum component of the first NOx-trap.
  • [0017]
    An aspect of the present invention is the concept of absorbing NO2 on the second NOx absorbent at relatively low temperature when the downstream first NOx trap is too cool to catalyse the reduction of NOx to N2, and thermally releasing the NOx when the first NOx-trap is up to temperature, e.g. >200° C., such as >225° C., >250° C., >275° C. or >300° C.
  • [0018]
    As is typical for engines including exhaust systems comprising NOx-traps, the engine can include an engine control unit (ECU) programmed, in use, intermittently to adjust to the exhaust gas composition to the rich side for regenerating the at least one first NOx absorbent.
  • [0019]
    Whilst the at least one second NOx-absorbent can be associated with a base metal catalyst, e.g. a manganese compound, a cobalt compound or a copper compound, for oxidising nitrogen monoxide (NO) to nitrogen dioxide (NO2) in lean exhaust gas or a non-platinum platinum group metal, such as rhodium or iridium for reducing NOx to N2 in rich exhaust gas, or other non-platinum PGMs such as palladium, osmium and ruthenium, preferably the at least one second NOx-absorbent is free from components other than the NOx-absorbent and optional support.
  • [0020]
    Each first and second NOx absorbent can be selected from alkaline earth metal compounds, alkali metal compounds or rare-earth metal compounds. Suitable alkaline earth metals include calcium, magnesium, strontium and barium Alkali metals can be potassium and/or caesium and rare earth metals can be cerium, yttrium or praseodymium.
  • [0021]
    The first and second NOx absorbent can be supported on a suitable support, such as particulate alumina, silica, zirconia, titania, ceria or a mixture or composite oxide according to any two or more thereof, such as ceria-zirconia or alumina-silica “Composite oxide” as defined herein means a largely amorphous oxide material comprising oxides of at least two elements which are not true mixed oxides consisting of the at least two elements.
  • [0022]
    Alternatively, the NOx-absorbent can comprise the support e.g. ceria per se or alumina per se.
  • [0023]
    In use, compounds according to the invention can be oxides, although they may be present as nitrates, hydroxides or carbonates in exhaust gas containing NOx, CO and H2O.
  • [0024]
    The first NOx-trap can be coated on a flow-through monolith, but in one embodiment, it is coated on a particulate filter. In a further embodiment according to the latter aspect, the particulate filter can include a DOC, optionally comprising supported platinum and/or palladium Alternatively, the first NOx trap can be disposed downstream of the filter, which arrangement adopting the process of EP 0341832 and disclosed in EP 0758713.
  • [0025]
    Optionally there may be a catalyst for oxidising NO to NO2, such as platinum on an alumina support, disposed between the at least one second NOx absorbent and the first NOx-trap as described in our WO 02/18753.
  • [0026]
    During NOx-trap regeneration, pulses of rich exhaust gas can be produced by the engine to convert stored NOx to nitrogen. During this process, hydrocarbon or carbon monoxide could pass through the system to atmosphere. To prevent this, the gas downstream of the first NOx-trap can be passed over an oxidation catalyst comprising an oxygen storage component, so even if the gas is overall reducing, reductants can still be oxidised, and prevented from entering the atmosphere. In one embodiment, the oxidation catalyst comprises platinum or palladium supported on a bulk ceria-zirconia composite oxide oxygen storage component.
  • [0027]
    According to a further aspect, the invention provides a diesel engine, optionally a light-duty diesel engine (as defined by the relevant legislation) comprising an exhaust system according to the invention.
  • [0028]
    According to a further aspect the invention provides a flow-through substrate comprising a NOx-trap comprising a first zone coated with a composition comprising at least one first NOx absorbent and platinum and a second zone coated with a composition comprising at least one second NOx-absorbent, which at least one second NOx absorbent is not associated with platinum.
  • [0029]
    According to a further aspect, the invention provides a method of treating NOx in the exhaust gas of a diesel engine, which method comprising (i) absorbing NO2 from lean exhaust gas in at least one second NOx absorbent when a downstream first NOx-trap comprising at least one first NOx absorbent and platinum is inactive for reducing NOx using a suitable reductant; (ii) thermally desorbing stored NOx; and (iii) reducing thermally desorbed NOx on the first NOx-trap using a suitable reductant.
  • [0030]
    In one embodiment, the method comprises the step between steps (i) and (ii) of adsorbing thermally desorbed NOx on the at least one first NOx absorbent.
  • [0031]
    In order that the invention may be more fully understood, the following embodiment and Examples are provided by way of illustration only and by reference to the accompanying drawings, in which:
  • [0032]
    FIG. 1 is a schematic diagram of a diesel engine comprising an exhaust system according to the invention;
  • [0033]
    FIG. 2 is a trace of time against NO2 concentration (ppm) and temperature showing the experimental conditions used in the Examples;
  • [0034]
    FIG. 3 is a trace showing NO2 adsorption and desorption for a conventional NOx trrp comprising 5:1 Pt:Pd at a total loading of 120 gft−3(4.25 g litres−1);
  • [0035]
    FIG. 3A is a trace showing HC detected downstream of the NOx absorbent in the experiment shown in FIG. 3;
  • [0036]
    FIG. 4 is a trace showing NO2 adsorption and desorption for a washcoat component containing Pt at a loading of 80 gft−3;
  • [0037]
    FIG. 4A is a trace showing HC detected downstream of the NOx absorbent in the experiment shown in FIG. 4;
  • [0038]
    FIG. 5 is a trace showing NO2 adsorption and desorption for the washcoat component of the FIG. 4 material without platinum;
  • [0039]
    FIG. 5A is a trace showing HC detected downstream of the NOx absorbent in the experiment shown in FIG. 5.
  • [0040]
    In the exhaust system 10 shown in FIG. 1, 12 is a diesel engine; 14 is a Pt-free NOx-trap comprising a second NOx-absorbent, e.g. alumina, barium supported on alumina or ceria; 16 is a NOx-trap comprising a first NOx-absorbent, such as barium supported on alumina, platinum and rhodium; 18 is the exhaust tailpipe. Optional components include an oxidation catalyst 20, such as platinum on alumina, and/or an oxidation catalyst 22 comprising an OSC, such as ceria-zirconium composite oxide.
  • [0041]
    We believe that FIG. 1 is self explanatory, in combination with the above description.
  • EXAMPLE 1
  • [0042]
    A ceramic flow through monolith 1.5 inch (38 mm) diameter and 3 inches (76 mm) long was coated with a conventional NOx-trap formulation containing platinum and rhodium at a ratio of 5:1 and total loading of 120 gft−3 (4.25 g litres−1) and a barium on alumina NOx-absorbent The catalyst was fitted into a standard gas flow rig and a synthetic gas mixture passed over it at a space velocity of 30,000 hr−1. The gas mixture composition is shown in Table 1 and remained lean for all the tests.
    TABLE 1
    Synthetic Gas Mixture used for Tests
    Gas Concentration
    NO2 200 or 250 ppm
    CO 0.05%
    CO2 6%
    H2O 6%
    O2 15%
    C3H6(Cl) 300 ppm
    N2 Balance
  • [0043]
    The gas mixture (without NO2) flowing through the catalyst was heated to 500° C. and held at this temperature for 5 minutes in order to purge the catalyst. The gas was allowed to cool to 120° C. and held at this temperature while the NO2 was added for a period of 5 minutes. The NO2 was switched off and the gas temperature increased to 500° C. for 5 minutes to purge the catalyst (FIG. 2). Throughout the test the NO and NOx/NO2 at the outlet to the catalyst was continuously measured so that adsorption (storage) and desorption could be monitored (FIG. 3).
  • [0044]
    From FIG. 3 it can be seen that there was some storage of NO2 at low temperatures on this NOx trap. The majority of the NO2 entering the catalyst was converted to NO, which was not adsorbed by the storage component in the NOx trap. When the temperature was increased NOx began to desorb at 430° C. and was complete at 500° C. When NO2 was absent from the gas feed, hydrocarbons (HC) were oxidised over Pt sites, but when the NO2 was introduced the HC reacted preferentially with it partially reducing it to NO (FIG. 3A).
  • EXAMPLE 2
  • [0045]
    A washcoat, containing Pt, was coated onto a monolith, as in Example 1, to give a loading of 2.5 g in−3 (0.15 g cm−1) with a Pt loading of 80 gft−3 (2.82 g litres−1) and evaluated as in Example 1. The results (shown in FIG. 4) show that NO2 was not stored at 120° C., but was all converted to NO by reaction with HC (FIG. 4A).
  • EXAMPLE 3
  • [0046]
    The same washcoat, but excluding Pt, as used in Example 2 was coated on the same size monolith to give a loading of 2.5 g in−3 (0.15 g cm−3) and evaluated in the same way. The results show (FIG. 5) that the Pt free washcoat stored NO2. Considerably less NO2 was reduced to NO than with the equivalent washcoat containing Pt, confirmed by the lower HC conversion (FIG. 5A). Desorption of NOx began as the temperature increased to 350° C.
  • [0047]
    The results show that the Pt free washcoat system stored the most NO2 which was then desorbed at a sufficiently high temperature to ensure a Pt containing NOx trap fitted downstream would be at its working temperature.
  • [0048]
    From these results, it appears that Pt free adsorber does not catalyse the reaction between HC and NO2, reducing NO2 to NO, to the same extent as a formulation containing Pt. NO2 is more easily adsorbed than NO leading to an advantage for NO2 adsorption of a Pt free adsorber at temperatures where the NO oxidation reaction is slow over Pt.
  • [0049]
    Similar results to those shown in Example 3 were obtained from a barium on alumina NOx absorbent material.

Claims (20)

  1. 1. An exhaust system for a diesel engine, which system comprises a NOx-trap comprising at least one first NOx absorbent and platinum; and
    at least one second NOx absorbent consisting essentially of at least one of alumina and ceria disposed upstream of the NOx-trap.
  2. 2. An exhaust system according to claim 1, wherein the first NOx-absorbent is selected from the group consisting of alkaline earth metal compounds, alkali metal compounds, rare earth metal compounds and mixtures of any two or more thereof.
  3. 3. An exhaust system according to claim 2, wherein the or each alkaline earth metal compounds is selected from the group consisting of barium, magnesium, strontium and calcium.
  4. 4. An exhaust system according to claim 2, wherein the or each alkali metal compounds is selected from the group consisting of potassium and caesium.
  5. 5. An exhaust system according to claim 2, wherein the or each rare earth metal compounds is selected from the group consisting of cerium, yttrium, lanthanum and praseodymium.
  6. 6. An exhaust system according to claim 2, wherein the or each alkaline earth metal compounds, the or each alkali metal compounds or the or each rare earth metal compounds is supported on a support material.
  7. 7. An exhaust system according to claim 6, wherein the support is selected from the group consisting of alumina, silica, titania, zirconia, ceria and mixtures or a composite oxide of any two or more thereof.
  8. 8. An exhaust system according to claim 2, wherein the first NOx absorbent is a support for the platinum.
  9. 9. An exhaust system according to claim 1, further comprising a catalyst for oxidising NO to NO2 disposed between the at least one second NOx absorbent and the NOx-trap.
  10. 10. An exhaust system according to claim 9, wherein the NO oxidation catalyst is platinum on an alumina support.
  11. 11. An exhaust system according to claim 9, further comprising a particulate filter disposed between the oxidation catalyst and the NOx-trap.
  12. 12. An exhaust system according to claim 1, wherein the NOx-trap further comprises a particulate filter.
  13. 13. An exhaust system according to claim, 1 further comprising a catalyst comprising a catalyst component for oxidising hydrocarbon and carbon monoxide to water and carbon dioxide and an oxygen storage component, wherein the catalyst is disposed downstream of the NOx-trap.
  14. 14. An exhaust system according to claim 13, wherein the oxidation catalyst comprises platinum or palladium supported on a bulk ceria-zirconia mixed oxide oxygenation storage component.
  15. 15. A diesel engine comprising an exhaust system according to claim 1.
  16. 16. A light-duty diesel engine according to claim 15.
  17. 17. An engine according to claim 15, comprising an engine control unit, when in use, intermittently to adjust the exhaust gas composition to the rich side for regenerating the at least one first NOx absorbent.
  18. 18. A flow-through substrate comprising: a NOx-trap comprising a first zone coated with a composition comprising at least one first NOx absorbent and platinum, and a second zone coated with a composition comprising at least one second NOx-absorbent, which at least one second NOx absorbent consists essentially of alumina and/or ceria.
  19. 19. A method of treating NOx in the exhaust gas of a diesel engine, which method comprising:
    (i) absorbing NOx from lean exhaust gas in at least one second NOx absorbent consisting essentially of alumina and ceria, when a downstream NOx-trap comprising at least one first NOx absorbent and platinum is inactive for reducing NOx;
    (ii) thermally desorbing NOx from the at least one second NOx absorbent; and
    (iii) reducing NOx on the downstream NOx-trap using a suitable reductant.
  20. 20. A method according to claim 19, further comprising the step between steps (i) and (ii) of adsorbing NOx on the at least one second NOx absorbent of the downstream NOx-trap.
US10530166 2002-10-05 2003-10-01 Exhaust system for a diesel engine comprising a nox- trap Abandoned US20060117736A1 (en)