US20060073998A1 - Supercritical carbon dioxide/chemical formulation for ashed and unashed aluminum post-etch residue removal - Google Patents

Supercritical carbon dioxide/chemical formulation for ashed and unashed aluminum post-etch residue removal Download PDF

Info

Publication number
US20060073998A1
US20060073998A1 US11273637 US27363705A US2006073998A1 US 20060073998 A1 US20060073998 A1 US 20060073998A1 US 11273637 US11273637 US 11273637 US 27363705 A US27363705 A US 27363705A US 2006073998 A1 US2006073998 A1 US 2006073998A1
Authority
US
Grant status
Application
Patent type
Prior art keywords
composition
post
cleaning
aluminum
etch residue
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US11273637
Inventor
Michael Korzenski
Eliodor Ghenciu
Chongying Xu
Thomas Baum
Original Assignee
Korzenski Michael B
Ghenciu Eliodor G
Chongying Xu
Baum Thomas H
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date

Abstract

A post-etch residue cleaning composition for cleaning ashed or unashed aluminum/SiN/Si post-etch residue from small dimensions on semiconductor substrates. The cleaning composition contains supercritical CO2 (SCCO2), alcohol, fluoride source, an aluminum ion complexing agent and, optionally, corrosion inhibitor. Such cleaning composition overcomes the intrinsic deficiency of SCCO2 as a cleaning reagent, viz., the non-polar character of SCCO2 and its associated inability to solubilize species such as inorganic salts and polar organic compounds that are present in the post-etch residue and that must be removed from the semiconductor substrate for efficient cleaning. The cleaning composition enables damage-free, residue-free cleaning of substrates having ashed or unashed aluminum/SiN/Si post-etch residue thereon.

Description

    FIELD OF THE INVENTION
  • The present invention relates to supercritical carbon dioxide-based compositions useful in semiconductor manufacturing for the removal of ashed and unashed aluminum/SiN/Si/Si post-etch residues from substrates having such residues thereon, and to methods of using such compositions for removal of post-etch residues from semiconductor substrates.
  • DESCRIPTION OF THE RELATED ART
  • Semiconductor manufacturing involves the use of photoresists that are applied to wafer substrates and subsequently developed to produce specific patterned regions and structures on the wafer. Subsequent to etching and optionally ashing of the exposed photoresist, residue remains on the substrate. This residue must be removed to ensure proper operation of the microelectronic device that is the ultimate product of the semiconductor manufacturing process, and to avoid interference or deficiency in relation to subsequent process steps in the manufacturing process.
  • Significant and continuing efforts have been made in the semiconductor manufacturing industry to develop formulations for removing photoresist and residue thereof from the semiconductor substrate, particularly in device structures including aluminum metalization and aluminum-based interconnect elements. This effort has been frustrated by the continuing and rapid decrease in critical dimensions.
  • As critical dimensions of chip architectures become smaller, e.g., <100 nanometers, it becomes progressively more difficult to remove residue from patterned semiconductor wafers with high aspect ratio trenches and vias. Conventional wet-cleaning methods suffer substantial limitations as critical dimension widths decrease below 100 nm due to the high surface tension characteristics of liquids used in the cleaning solution. Additionally, the use of aqueous cleaning solutions has the major deficiency that the aqueous solutions can strongly affect important material properties of porous low-k dielectric materials, including mechanical strength, moisture uptake, coefficient of thermal expansion, and adhesion to different substrates.
  • It would therefore be a significant advance in the art to provide a cleaning composition that overcomes such deficiencies of the prior and conventional cleaning compositions used for removal of ashed and non-ashed post-etch residue on semiconductor substrates.
  • SUMMARY OF THE INVENTION
  • The present invention relates to supercritical carbon dioxide-based compositions useful in semiconductor manufacturing for the removal of ashed and unashed aluminum/SiN/Si post-etch residues from substrates having such residues thereon, and methods of using such compositions for removal of post-etch residues from semiconductor substrates.
  • In one aspect, the invention relates to a post-etch residue cleaning composition, comprising SCCO2, alcohol, fluorine source, an aluminum ion complexing agent and, optionally, corrosion inhibitor.
  • In another aspect, the invention relates to a post-etch residue cleaning composition, comprising SCCO2, methanol, ammonium fluoride, salicylic acid, and boric acid, wherein ammonium fluoride is present at a concentration of from about 0.01 to about 2.0 wt. %, salicylic acid is present at a concentration of from about 0.01 to about 4.0 wt. %, and boric acid is present at a concentration of from about 0.01 to about 2.0 wt. %, based on the total weight of the cleaning composition.
  • A further aspect of the invention relates to a method of removing aluminum/SiN/Si post-etch residue from a substrate having same thereon, said method comprising contacting the post-etch residue with a cleaning composition comprising SCCO2/alcohol solution, a fluorine source, an aluminum ion complexing agent and, optionally, corrosion inhibitor, for sufficient time and under sufficient contacting conditions to remove the aluminum/SiN/Si post-etch residue from the substrate.
  • Other aspects, features and embodiments of the invention will be more fully apparent from the ensuing disclosure and appended claims.
  • BRIEF DESCRIPTION OF THE DRAWINGS
  • FIG. 1 is a scanning electron microscope (SEM) image at 50 K magnification of an ashed post aluminum etch control wafer clearly showing the crystalline residue including crystallites on the ashed surfaces.
  • FIG. 2 is a scanning electron microscope (SEM) image at 25 K magnification of a corresponding post-cleaned sample, which was cleaned of residue by contact of the ashed residue-bearing substrate with a cleaning composition containing SCCO2/methanol, ammonium fluoride and salicylic acid.
  • FIG. 3 is a scanning electron microscope (SEM) image at 60 K magnification of an unashed post aluminum etch control wafer showing “dog-ear-like” residue on the wafer surface at either side of the trench structure.
  • FIG. 4 is a corresponding scanning electron microscope (SEM) image at 35 K magnification of the unashed post aluminum etch control wafer of FIG. 3, showing the “dog-ear-like” residue on the wafer surface at either side of the trench structure.
  • FIG. 5 is a scanning electron microscope (SEM) image at 100 K magnification of the unashed post aluminum etch wafer of FIGS. 3-4 after cleaning thereof by contact of the unashed substrate with the cleaning composition containing SCCO2/methanol, ammonium fluoride and salicylic acid, showing that the “dog-ear-like” residue on the wafer surface at either side of the trench structure as present in the FIGS. 3-4 micrographs has been fully removed.
  • FIG. 6 is a scanning electron microscope (SEM) image at 60 K magnification of the unashed post aluminum etch wafer of FIGS. 3-4 after cleaning thereof by contact of the unashed substrate with the cleaning composition containing SCCO2/methanol, ammonium fluoride and salicylic acid, showing that the “dog-ear-like” residue on the wafer surface at either side of the trench structure as present in the FIGS. 3-4 micrographs has been fully removed.
  • DETAILED DESCRIPTION OF THE INVENTION, AND PREFERRED EMBODIMENTS THEREOF
  • The present invention is based on the discovery of a supercritical carbon dioxide-based cleaning composition that is highly efficacious for the removal of post-etch residue, including both ashed post-etch residue and non-ashed post-etch residue, from semiconductor substrates on which same is present.
  • Supercritical carbon dioxide (SCCO2) might at first glance be regarded as an attractive reagent for removal of aluminum post-etch residues, since supercritical CO2 has the characteristics of both a liquid and a gas. Like a gas, it diffuses rapidly, has low viscosity, near-zero surface tension, and penetrates easily into deep trenches and vias. Like a liquid, it has bulk flow capability as a “wash” medium.
  • Despite these ostensible advantages, however, supercritical CO2 is non-polar. Accordingly, it will not solubilize many species, including inorganic salts and polar organic compounds that are present in the post-etch residue and that must be removed from the semiconductor substrate for efficient cleaning. The non-polar character of SCCO2 thus has been an impediment to the use of such reagent for aluminum post-etch residue removal subsequent to deposition or formation of aluminum on the substrate, e.g., for fabrication of interconnects, contacts, electrodes, metallization, conductive base layers for field emitter elements, etc.
  • Such deficiency of supercritical CO2 has been overcome by the present invention in the provision of a SCCO2-based composition that is highly effective for cleaning of aluminum post-etch residues containing Al3+ ions as well as slightly fluorinated residues and combinations thereof, and achieves damage-free, residue-free cleaning of the substrate, e.g., a patterned wafer, initially having such residues thereon.
  • More specifically, the present invention contemplates a post-etch residue cleaning composition including a SCCO2/alcohol solution containing (i) fluorine source, (ii) an aluminum ion complexing agent and (iii) optionally, a corrosion inhibitor, e.g., boric acid (H3BO3).
  • The composition of the invention has utility for cleaning both ashed and unashed aluminum/SiN/Si post-etch residue from small dimensions on semiconductor substrates without further attack on the aluminum surface or Si-containing regions. As used in this context, the term “aluminum/SiN/Si” refers to aluminum post-etch residue and/or SiN post-etch residue on a silicon substrate, each being amenable to high-efficiency cleaning by the cleaning composition of the present invention.
  • In the cleaning composition, the fluorine source aids in the removal of residual photoresist as well as any silicon impurities that reside on the post-etch crystalline residue or on the surface of the etched and patterned aluminum. The fluorine source may be of any suitable type, e.g., a fluorine-containing compound or other fluoro species. Illustrative fluorine source components include hydrogen fluoride (HF), triethylamine trihdyrogen fluoride or other amine trihydrogen fluoride compound of the formula NR3(HF)3 wherein each R is independently selected from hydrogen and lower alkyl (C1-C8 alkyl), hydrogen fluoride-pyridine (pyr-HF), and ammonium fluorides of the formula R4NF, wherein each R is independently selected from hydrogen and lower (C1-C8 alkyl), etc. Ammonium fluoride (NH4F) is a presently preferred fluorine source in compositions of the invention, although any other suitable fluoro source component(s) may be employed with equal success.
  • The aluminum ion complexing agent in the cleaning composition may comprise any suitable agent that functions to efficiently complex to Al3+ ions that are present in the residue deriving from aluminum carbides and aluminum silicides therein. Salicylic acid (2-hydroxy benzoic acid, C7H6O3) is preferred for such purpose, however, other strong aluminum ion complexing agents such as acids (e.g., beta-diketones) and amines may also be used, including for example EDTA, oxalic acid, gallic acid, nitrilotriacetic acid, 3-hydroxy-2-naphthoic acid, and oxine.
  • The optional corrosion inhibitor functions to protect the exposed silicon regions of the developed wafer (i.e. trenches) from corrosion. Boric acid is a presently preferred corrosion inhibitor, although other oxidation inhibitor agents may also be advantageously employed for such purpose.
  • The alcohol used to form the SCCO2/alcohol solution as the solvent phase of the cleaning composition may be of any suitable type. In one embodiment of the invention, such alcohol comprises a C1-C4 alcohol (i.e., methanol, ethanol, propanol, or butanol), or a mixture of two or more of such alcohol species.
  • In a preferred embodiment, the alcohol is methanol. The presence of the alcoholic co-solvent with the SCCO2 serves to increase the solubility of the composition for inorganic salts and polar organic compounds present in the aluminum/SiN/Si post-etch residue. In general, the specific proportions and amounts of SCCO2 and alcohol in relation to each other may be suitably varied to provide the desired solubilizing (solvating) action of the SCCO2/alcohol solution for such inorganic salts and polar organic compounds, as readily determinable within the skill of the art without undue effort.
  • In one embodiment, the cleaning composition of the invention includes SCCO2, alcohol, ammonium fluoride, salicylic acid, and boric acid.
  • In a preferred composition of such character, as particularly adapted to cleaning of unashed aluminum/SiN/Si post-etch residue, ammonium fluoride is present at a concentration of from about 0.01 to about 1.0 wt. %, salicylic acid is present at a concentration of from about 0.01 to about 2.0 wt. %, and boric acid is present at a concentration of from about 0.01 to about 1.0 wt. %, based on the total weight of the cleaning composition. Such cleaning composition is hereinafter referred to as a Type 1 composition, denoting the particular suitability of the composition for cleaning of unashed aluminum/SiN/Si post-etch residue on substrates having same thereon.
  • A particularly preferred Type 1 cleaning composition in accordance with the invention includes ammonium fluoride, salicylic acid, and boric acid in a molar ratio of about 1.50:1.53:1.0 (ammonium fluoride:salicylic acid:boric acid).
  • Type 1 compositions in the general practice of the invention may be contacted with the residue-bearing substrate under any suitable process conditions, as readily determinable by empirical determination, to remove the unashed aluminum/SiN/Si post-etch residue from the substrate having same thereon.
  • In a preferred embodiment, the specific Type 1 cleaning composition described above is employed to contact a substrate having unashed aluminum/SiN/Si post-etch residue thereon at a pressure in a range of from about 2000 to about 4000 psi for sufficient time to effect the desired removal of the unashed residue from the substrate, e.g., for a contacting time in a range of from about 1 to about 15 minutes, although greater or lesser contacting durations may be advantageously employed in the broad practice of the present invention, where warranted.
  • In another preferred composition including SCCO2, alcohol, ammonium fluoride, salicylic acid, and boric acid, as particularly adapted to cleaning of ashed aluminum/SiN/Si post-etch residue, ammonium fluoride is present at a concentration of from about 0.2 to about 2.0 wt. %, salicylic acid is present at a concentration of from about 0.2 to about 4.0 wt. %, and boric acid is present at a concentration of from about 0.2 to about 2.0 wt. %, based on the total weight of the cleaning composition. Such cleaning composition is hereinafter referred to as a Type 2 composition, denoting the particular suitability of the composition for cleaning of ashed aluminum/SiN/Si post-etch residue on substrates having same thereon.
  • A particularly preferred Type 2 cleaning composition in accordance with the invention includes ammonium fluoride, salicylic acid, and boric acid in a molar ratio of about 1.10:1.0:0.73 (ammonium fluoride:salicylic acid:boric acid).
  • Type 2 compositions in the general practice of the invention may be contacted with the residue-bearing substrate under any suitable process conditions, as readily determinable by empirical determination, to remove the ashed aluminum/SiN/Si post-etch residue from the substrate having same thereon.
  • In a preferred embodiment, the specific Type 2 cleaning composition described above is employed to contact a substrate having ashed aluminum/SiN/Si post-etch residue thereon at a pressure in a range of from about 2000 to about 4000 psi for sufficient time to effect the desired removal of the ashed residue from the substrate, e.g., for a contacting time in a range of from about 15 to about 35 minutes, although greater or lesser contacting durations may be advantageously employed in the broad practice of the present invention, where warranted.
  • The cleaning process in a particularly preferred embodiment includes sequential processing steps including dynamic flow of the cleaning composition over the substrate having the ashed residue thereon, followed by a static soak of the substrate in the cleaning composition, with the respective dynamic flow and static soak steps being carried out alternatingly and repetitively, in a cycle of such alternating steps.
  • For example, the dynamic flow/static soak steps may be carried out for three successive cycles in the aforementioned illustrative embodiment of contacting time of from about 15 to about 35 minutes, as including a sequence of 2.5 to 10 minutes dynamic flow, 2.5 to 10 minutes static soak, 2.5 to 10 minutes dynamic flow, 2.5 to 10 minutes static soak, 2.5 to 10 minutes dynamic flow, and 2.5 to 10 minutes static soak.
  • Following the contacting of the cleaning composition with the substrate bearing the ashed or unashed residue, the substrate thereafter preferably is washed with copious amounts of SCCO2/alcohol solution (not containing any ammonium fluoride, salicylic acid (or other Al ion complexing agent), or boric acid components), in a first washing step, to remove any residual precipitated chemical additives from the substrate region in which removal of post-etch residue has been effected, and finally with copious amounts of pure SCCO2, in a second washing step, to remove any residual alcohol co-solvent and/or precipitated chemical additives from the substrate region.
  • The features and advantages of the invention are more fully shown by the empirical efforts and results discussed below.
  • FIG. 1 is a scanning electron microscope (SEM) image at 50 K magnification of an ashed post aluminum etch control wafer clearly showing the crystalline residue including crystallites on the ashed surfaces.
  • FIG. 2 is a scanning electron microscope (SEM) image at 25 K magnification of a corresponding post-cleaned sample, which was cleaned of residue by contact of the ashed residue-bearing substrate with a cleaning composition containing SCCO2/methanol, ammonium fluoride and salicylic acid.
  • FIG. 3 is a scanning electron microscope (SEM) image at 60 K magnification of an unashed post aluminum etch control wafer showing “dog-ear-like” residue on the wafer surface at either side of the trench structure.
  • FIG. 4 is a corresponding scanning electron microscope (SEM) image at 35 K magnification of the unashed post aluminum etch control wafer of FIG. 3, showing the “dog-ear-like” residue on the wafer surface at either side of the trench structure.
  • FIG. 5 is a scanning electron microscope (SEM) image at 100 K magnification of the unashed post aluminum etch wafer of FIGS. 3-4 after cleaning thereof by contact of the unashed substrate with the cleaning composition containing SCCO2/methanol, ammonium fluoride and salicylic acid, showing that the “dog-ear-like” residue on the wafer surface at either side of the trench structure as present in the FIGS. 3-4 micrographs has been fully removed.
  • FIG. 6 is a scanning electron microscope (SEM) image at 60 K magnification of the unashed post aluminum etch wafer of FIGS. 3-4 after cleaning thereof by contact of the unashed substrate with the cleaning composition containing SCCO2/methanol, ammonium fluoride and salicylic acid, showing that the “dog-ear-like” residue on the wafer surface at either side of the trench structure as present in the FIGS. 3-4 micrographs has been fully removed.
  • The above-described micrographs of FIGS. 1-6 thus evidence the efficacy of cleaning compositions in accordance with the invention, for removal of post etch residue on wafer substrates.
  • The cleaning compositions of the present invention are readily formulated by simple mixing of ingredients, e.g., in a mixing vessel under gentle agitation.
  • Once formulated, such cleaning compositions are applied to the substrate for contacting with the residue thereon, at suitable elevated pressures, e.g., in a pressurized contacting chamber to which the cleaning composition is supplied at suitable volumetric rate and amount to effect the desired contacting operation for removal of the post etch residue removal.
  • It will be appreciated that specific contacting conditions for the cleaning compositions of the invention are readily determinable within the skill of the art, based on the disclosure herein, and that the specific proportions of ingredients and concentrations of ingredients in the cleaning compositions of the invention may be widely varied while achieving desired removal of the post etch residue from the substrate.
  • Accordingly, while the invention has been described herein in reference to specific aspects, features and illustrative embodiments of the invention, it will be appreciated that the utility of the invention is not thus limited, but rather extends to and encompasses numerous other aspects, features and embodiments. Accordingly, the claims hereafter set forth are intended to be correspondingly broadly construed, as including all such aspects, features and embodiments, within their spirit and scope.

Claims (21)

  1. 1-44. (canceled)
  2. 45. A post-etch residue cleaning composition, comprising SCCO2, alcohol, fluorine source, an aluminum ion complexing agent and, optionally, corrosion inhibitor.
  3. 46. The composition of claim 45, wherein the alcohol comprises at least one C1-C4 alcohol.
  4. 47. The composition of claim 45, wherein the alcohol comprises methanol.
  5. 48. The composition of claim 45, wherein the fluorine source comprises a fluorine-containing compound selected from the group consisting of hydrogen fluoride (HF), amine trihydrogen fluoride compounds of the formula NR3(HF)3 wherein each R is independently selected from hydrogen and lower alkyl, hydrogen fluoride-pyridine (pyr-HF), and ammonium fluorides of the formula R4NF, wherein each R is independently selected from hydrogen and lower alkyl.
  6. 49. The composition of claim 45, wherein the fluorine source comprises ammonium fluoride (NH4F).
  7. 50. The composition of claim 45, wherein the aluminum ion complexing agent comprises a complexing agent selected from the group consisting of salicylic acid, EDTA, oxalic acid, beta-diketones, gallic acid, nitrilotriacetic acid, 3-hydroxy-2-naphthoic acid, and oxine.
  8. 51. The composition of claim 45, wherein the aluminum ion complexing agent comprises salicylic acid.
  9. 52. The composition of claim 45, comprising corrosion inhibitor.
  10. 53. The composition of claim 52, wherein said corrosion inhibitor includes boric acid.
  11. 54. The composition of claim 45, wherein the alcohol has a concentration that increases the solubility of the composition for inorganic salts and polar organic compounds present in aluminum/SiN/Si post-etch residue, relative to a corresponding composition lacking such alcohol.
  12. 55. The composition of claim 49, comprising ammonium fluoride, salicylic acid and boric acid.
  13. 56. The composition of claim 55, wherein ammonium fluoride has a concentration of from about 0.01 to about 1.0 wt. %, based on the total weight of the cleaning composition.
  14. 57. The composition of claim 45, wherein the aluminum ion complexing agent has a concentration of from about 0.01 to about 2.0 wt. %, based on the total weight of the cleaning composition.
  15. 58. The composition of claim 45, comprising corrosion inhibitor, wherein the corrosion inhibitor has a concentration of from about 0.01 to about 1.0 wt. %, based on the total weight of the cleaning composition.
  16. 59. The composition of claim 49, comprising ammonium fluoride, salicylic acid, and boric acid in a molar ratio of about 1.50:1.53:1.0 (ammonium fluoride:salicylic acid:boric acid).
  17. 60. The composition of claim 59, wherein ammonium fluoride has a concentration of from about 0.2 to about 2.0 wt. %, based on the total weight of the cleaning composition.
  18. 61. The composition of claim 45, wherein the aluminum ion complexing agent has a concentration of from about 0.2 to about 4.0 wt. %, based on the total weight of the cleaning composition.
  19. 62. The composition of claim 45, comprising corrosion inhibitor, wherein the corrosion inhibitor has a concentration of from about 0.2 to about 2.0 wt. %, based on the total weight of the cleaning composition.
  20. 63. The composition of claim 49, comprising ammonium fluoride, salicylic acid, and boric acid in a molar ratio of about 1.10:1.0:0.73 (ammonium fluoride:salicylic acid:boric acid).
  21. 64. A method of removing aluminum/SiN/Si post-etch residue from a substrate having same thereon, said method comprising contacting the post-etch residue with a cleaning composition comprising SCCO2, alcohol, fluorine source, an aluminum ion complexing agent and, optionally, corrosion inhibitor, for sufficient time and under sufficient contacting conditions to remove the aluminum/SiN/Si post-etch residue from the substrate.
US11273637 2002-10-31 2005-11-14 Supercritical carbon dioxide/chemical formulation for ashed and unashed aluminum post-etch residue removal Abandoned US20060073998A1 (en)