US20030203691A1 - Nonwoven materials having surface features - Google Patents

Nonwoven materials having surface features Download PDF

Info

Publication number
US20030203691A1
US20030203691A1 US10136805 US13680502A US2003203691A1 US 20030203691 A1 US20030203691 A1 US 20030203691A1 US 10136805 US10136805 US 10136805 US 13680502 A US13680502 A US 13680502A US 2003203691 A1 US2003203691 A1 US 2003203691A1
Authority
US
Grant status
Application
Patent type
Prior art keywords
nonwoven web
macroscopic
feature
plane
surface
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US10136805
Inventor
Christopher Fenwick
Bryan Haynes
Kurtis Brown
Susan Paul
Christian Trusock
Melpo Lambidonis
Stephen Baratian
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kimberly-Clark Worldwide Inc
Original Assignee
Kimberly-Clark Worldwide Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date

Abstract

A three-dimensional nonwoven web having a regional, bulk density of less than 0.04 grams per cubic centimeter, a top-side base surface that defines an x,y-plane and at least one macroscopic surface feature extending out of the x,y-plane wherein a macroscopic surface feature is characterized as a feature having an apex that extends at least about 1 millimeter above the x,y-plane of the top-side base surface is provided. The macroscopic feature maintains a height of at least 1 millimeter above the x,y-plane of the top-side base surface under a 1.2 kPa load (Pf) and results in contact of an object resting on the macroscopic feature such that the percent contact area of the nonwoven web with an article resting on the macroscopic surface feature at a 1.2 kPa load (Pf) is less than 50 percent of the bulk area of the nonwoven web supporting the article.

Description

    CROSS-REFERENCE TO RELATED APPLICATIONS
  • This application is related to commonly assigned U.S. patent application Ser. No. __/______ entitled “METHODS FOR MAKING NONWOVEN MATERIALS ON A SURFACE HAVING SURFACE FEATURES AND NONWOVEN MATERIALS HAVING SURFACE FEATURES” filed by Express Mail Procedure EL471213680 US contemporaneously herewith and which is hereby incorporated by reference herein.[0001]
  • FIELD
  • The present invention is directed to nonwoven materials having surface features. [0002]
  • BACKGROUND
  • Nonwoven fabrics are useful for a wide variety of applications, including absorbent personal care products, garments, medical products, and cleaning products. Nonwoven personal care products include infant care items such as diapers, child care items such as training pants, feminine care items such as sanitary napkins, and adult care items such as incontinence products. Nonwoven garments include protective workwear and medical apparel such as surgical gowns. Other nonwoven medical products include nonwoven wound dressings and surgical dressings. Cleaning products that contain nonwovens include towels and wipes. Still other uses of nonwoven fabrics are well known. The foregoing list is not considered exhaustive. [0003]
  • Various properties of nonwoven fabrics determine the suitability of nonwoven fabrics for different applications. Nonwoven fabrics may be engineered to have different combinations of properties to suit different needs. Variable properties of nonwoven fabrics include liquid-handling properties such as wettability, distribution, and absorbency, strength properties such as tensile strength and tear strength, softness properties, durability properties such as abrasion resistance, and aesthetic properties. The physical shape of a nonwoven fabric also affects the functionality and aesthetic properties of the nonwoven fabric. Nonwoven fabrics are initially made into sheets which, when laid on a flat surface, may have a substantially planar, featureless surface or may have an array of surface features such as apertures or projections, or both. Nonwoven fabrics with apertures or projections are often referred to as three-dimensional or shaped nonwoven fabrics. The present invention relates to three-dimensional or shaped nonwoven fabrics. [0004]
  • The manufacture of nonwoven fabrics is a highly developed art. Generally, nonwoven webs and their manufacture involve forming filaments or fibers and depositing the filaments or fibers on a carrier in such a manner so as to cause the filaments or fibers to overlap or entangle. Depending on the degree of web integrity desired, the filaments or fibers of the web may then be bonded by means such as an adhesive, the application of heat or pressure, or both, sonic bonding techniques, or entangling by needles or water jets, and so forth. There are several methods of producing fibers or filaments within this general description; however, two commonly used processes are known as spunbonding and meltblowing and the resulting nonwoven fabrics are known as spunbond and meltblown fabrics, respectively. [0005]
  • Generally described, the process for making spunbond nonwoven fabrics includes extruding thermoplastic material through a spinneret, quenching and drawing the extruded material into filaments with a stream of high-velocity air to form a random web on a forming surface. Such a method is referred to as meltspinning. Spunbond processes are generally defined in numerous patents including, for example, U.S. Pat. No. 3,802,817 to Matsuki et al.; U.S. Pat. No. 4,692,618 to Dorschner, et al.; U.S. Pat. No. 4,340,563 to Appel, et al.; U.S. Pat. Nos. 3,338,992 and 3,341,394 to Kinney; U.S. Pat. No. 3,502,538 to Levy; U.S. Pat. Nos. 3,502,763 and 3,909,009 to Hartmann; U.S. Pat. No. 3,542,615 to Dobo, et al.; and Canadian Patent No. 803,714 to Harmon. [0006]
  • On the other hand, meltblown nonwoven fabrics are made by extruding a thermoplastic material through one or more dies, blowing a high-velocity stream of air, usually heated air, past the extrusion dies to generate an air-conveyed meltblown fiber curtain and depositing the curtain of fibers onto a forming surface to form a random nonwoven web. Meltblowing processes are generally described in numerous publications including, for example, an article titled “Superfine Thermoplastic Fibers” by Wendt in [0007] Industrial and Engineering Chemistry, Vol. 48, No. 8, (1956), at pp.1342-1346, which describes work done at the Naval Research Laboratory in Washington, D.C.; Naval Research Laboratory Report 111437, dated Apr. 15, 1954; U.S. Pat. Nos. 4,041,203, 3,715,251, 3,704,198, 3,676,242 and 3,595,245; and British Specification 1,217,892.
  • Spunbond and meltblown nonwoven fabrics can usually be distinguished by the diameters and the molecular orientation of the filaments or fibers that form the fabrics. The diameter of spunbond and meltblown filaments or fibers is the average cross-sectional dimension. Spunbond filaments or fibers typically have average diameters greater than 6 microns and often have average diameters in the range of 12 to 40 microns. Meltblown fibers typically have average diameters of less than 6 microns. However, because larger meltblown fibers, having diameters of at least 6 microns may also be produced, molecular orientation can be used to distinguish spunbond and meltblown filaments and fibers of similar diameters. For a given fiber or filament size and polymer, the molecular orientation of a spunbond fiber or filament is typically greater than the molecular orientation of a meltblown fiber. Relative molecular orientation of polymeric fibers or filament can be determined by measuring the tensile strength and birefringence of fibers or filaments having the same diameter. [0008]
  • Tensile strength of fibers and filaments is a measure of the stress required to stretch the fiber or filament until the fiber or filament breaks. Birefringence numbers are calculated according to the method described in the spring 1991 issue of [0009] INDA Journal of Nonwovens Research, (Vol. 3, No. 2, p. 27). The tensile strength and birefringence numbers of polymeric fibers and filaments vary depending on the particular polymer and other factors; however, for a given fiber or filament size and polymer, the tensile strength of a spunbond fiber or filament is typically greater than the tensile strength of a meltblown fiber and the birefringence number of a spunbond fiber or filament is typically greater than the birefringence number of a meltblown fiber.
  • A number of patents describe methods for making shaped or three-dimensional nonwoven fabrics: for example, U.S. Pat. Nos. 5,575,874 and 5,643,653 issued to Griesbach et al.; U.S. Pat. No.4,741,941 issued to Engelbert et al.; and U.S. Pat. Nos. 6,331,268, 6,331,345 and 6,455,319 issued to Kauschke et al. Despite prior advances in the art, there is still a need for improved nonwoven fabrics having surface features and methods for forming such nonwoven fabrics. [0010]
  • To avoid confusion it is important to clarify the terminology used throughout the body of the application in describing pressures and loads. The practices used for determining these values are detailed in the methods section. For the purposes of describing the resiliency of surface features, the average pressure exerted on a surface feature is denoted P[0011] f . For the purposes of material characterization of the web and techniques used for bulk compressometry a different pressure is reported. This is the pressure exerted on the web or Pw. Pw is the pressure that would be exerted on a flat material having 100 percent contact with the load or force.
  • SUMMARY
  • In response to the difficulties and problems encountered in the prior art, new nonwoven materials have been discovered. In accordance with the present invention nonwoven fabrics having one or more macroscopic surface features are described. [0012]
  • The present invention provides a three-dimensional nonwoven web having a regional, bulk density of less than 0.04 grams per cubic centimeter wherein the nonwoven web includes a top-side base surface that defines an x,y-plane and at least one macroscopic surface feature extending out of the x,y-plane wherein a macroscopic surface feature is characterized as a feature having an apex that extends at least about 1 millimeters above the x,y-plane of the top-side base surface and the maintains a height of at least 1 millimeter above the x,y-plane of the top-side base surface under a 1.2 kPa load (P[0013] f) and wherein the macroscopic feature minimizes contact of an object resting on the macroscopic feature such that the area of contact of the nonwoven web with an article resting on the macroscopic surface feature at a 1.2 kPa load (Pf) of article to contact area of nonwoven web is less than 50 percent of the bulk area of the nonwoven web supporting the article.
  • In one embodiment, a macroscopic feature is characterized as a feature having an apex that extends at least 1.5 millimeters above the x,y-plane. In another embodiment, a macroscopic feature is characterized as a feature having an apex that extends at least 3 millimeters above the x,y-plane. In yet another embodiment, a macroscopic feature is characterized as a feature having an apex that extends at least 5 millimeters above the x,y-plane. In still yet another embodiment, a macroscopic feature is characterized as a feature having an apex that extends at least about 6 millimeters above the x,y-plane. [0014]
  • The area of contact of the nonwoven web with an article resting on the macroscopic surface feature at a 1.2 kPa load (P[0015] f) of article to contact area of nonwoven web may be less than 40, 30 and even less than 25 percent of the bulk area of the nonwoven web supporting the article. The nonwoven may include a plurality of macroscopic features and the frequency of macroscopic features is at least 1 macroscopic surface feature per 100, 50, 10 and even 1 square centimeter of nonwoven web in the x,y-plane. The regional bulk density of the nonwoven web may be less than 0.03 and even less than 0.02 grams per cubic centimeter.
  • In one particular embodiment, the macroscopic features maintain a height of at least 1.5 millimeters above the x,y-plane of the top-side base surface under a 1.2 kPa load (P[0016] f). In other embodiments, the macroscopic features maintain a height of at least 3 and even 6 millimeters above the x,y-plane of the top-side base surface under a 1.2 kPa load (Pf). In another particular embodiment, the macroscopic feature maintains a height of at least 1 millimeter above the x,y-plane of the top-side base surface under a 1.8 kPa load (Pf). In other embodiments, the macroscopic feature maintains a height of at least 1.5, 3 and even 6 millimeters above the x,y-plane of the top-side base surface under a 1.8 kPa load (Pf). In yet another particular embodiment, the macroscopic feature maintains a height of at least 1 millimeter above the x,y-plane of the top-side base surface under a 10 kPa load. In other embodiments, the macroscopic feature maintains a height of at least 1.5, 3 and even 6 millimeters above the x,y-plane of the top-side base surface under a 10 kPa load.
  • The nonwoven webs of the present invention may include macroscopic features that provide at least 0.08 cubic centimeters of air space, 0.09 cubic centimeters of air space and even greater than 0.10 cubic centimeters of air space per square centimeter between the top surface of the nonwoven web and an article resting on the macroscopic surface feature at a 0.3450 kPa load on the web (P[0017] w). In several of the embodiments, the nonwoven web has a uniform composition in the x and y directions. In several of the embodiments, the nonwoven web is a laminate. The nonwoven web may be made from bicomponent fibers.
  • BRIEF DESCRIPTION OF THE DRAWINGS
  • FIG. 1A is a perspective view of a nonwoven web of the present invention. [0018]
  • FIG. 1B is a cross-sectional view of the nonwoven web illustrated in FIG. 1A. [0019]
  • FIG. 1C is a top-side plan view of the nonwoven web illustrated in FIG. 1A. [0020]
  • FIG. 2A is a perspective view of a substantially planar article supported on the nonwoven web of FIGS. 1A, 1B and [0021] 1C.
  • FIG. 2B is a cross-sectional view of a substantially planar article supported on the nonwoven web of FIGS. 1A, 1B and [0022] 1C.
  • FIG. 2C is a top-side plan view of a substantially planar article supported on the nonwoven web of FIGS. 1A, 1B and [0023] 1C.
  • FIG. 3A is a perspective view of an embossing plate. [0024]
  • FIG. 3B is a perspective view of an opposing embossing plate. [0025]
  • FIG. 3C is a cross-sectional view of the embossing plates of FIGS. 3A and 3B forming a nonwoven web of the present invention. [0026]
  • FIG. 4A is a perspective view of another embossing plate. [0027]
  • FIG. 4B is a perspective view of another opposing embossing plate. [0028]
  • FIG. 5A is a perspective view of another nonwoven web of the present invention. [0029]
  • FIG. 5B is a cross-sectional view of the nonwoven web illustrated in FIG. 5A. [0030]
  • FIG. 5C is a top-side plan view of the nonwoven web illustrated in FIG. 5A. [0031]
  • FIG. 6 is a cutaway view of an absorbent article incorporating a nonwoven fabric of the invention. [0032]
  • FIG. 7 is a partial cross-sectional view of the absorbent article of FIG. 6. [0033]
  • FIG. 8 is a perspective view of yet another nonwoven web of the present invention. [0034]
  • DEFINITIONS
  • As used herein the following terms have the specified meanings, unless the context demands a different meaning, or a different meaning is expressed; also, the singular generally includes the plural, and the plural generally includes the singular unless otherwise indicated. [0035]
  • Words of degree, such as “about”, “substantially”, and the like are used herein in the sense of “at, or nearly at, when given the manufacturing and material tolerances inherent in the stated circumstances” and are used to prevent the unscrupulous infringer from unfairly taking advantage of the invention disclosure where exact or absolute FIGS. are stated as an aid to understanding the invention. [0036]
  • As used herein, the term “absorbent product” or “personal care absorbent product” means diapers, training pants, swim wear, absorbent underpants, adult incontinence products, sanitary wipes, wipes, feminine hygiene products, wound dressings, nursing pads, time release patches, bandages, mortuary products, veterinary products, hygiene and so forth. [0037]
  • As used herein, the term “airlaid web” refers to nonwoven webs made by “airlaying”. Airlaying is a well-known process by which a fibrous nonwoven layer can be formed. In the airlaying process, bundles of small fibers having typical lengths ranging from about 3 to about 52 millimeters (mm) are separated and entrained in an air supply and then deposited onto a forming screen, usually with the assistance of a vacuum supply. The randomly deposited fibers then are bonded to one another using, for example, hot air or a spray adhesive. Airlaying is taught in, for example, U.S. Pat. No. 4,640,810 to Laursen et al. [0038]
  • As used herein, the term “apex” refers to the highest or furthest portion of a feature and is meant to include points as well as planes and other surfaces that are not sharp ends. [0039]
  • As used herein, the term “bonded carded web” refers to webs that are made from staple fibers which are sent through a combing or carding unit, which separates or breaks apart and aligns the staple fibers in the machine direction to form a generally machine direction-oriented fibrous nonwoven web. This material may be bonded together by methods that include point bonding, through air bonding, ultrasonic bonding, adhesive bonding, etc. [0040]
  • As used herein, the terms “comprises”, “comprising” and other derivatives from the root term “comprise” are intended to be open-ended terms that specify the presence of any stated features, elements, integers, steps, or components, but do not preclude the presence or addition of one or more other features, elements, integers, steps, components, or groups thereof. [0041]
  • As used herein, the term “fabric” refers to all of the woven, knitted and nonwoven fibrous webs. [0042]
  • As used herein, the term “hydrophilic” describes fibers, materials or the surfaces of fibers materials that are wetted by the aqueous liquids in contact with the fibers or other materials. The degree of wetting of the materials can, in turn, be described in terms of the contact angles and the surface tensions of the liquids and materials involved. Equipment and techniques suitable for measuring the wettability of particular fiber materials can be provided by a Cahn SFA-222 Surface Force Analyzer System, or a substantially equivalent system. When measured with this system, fibers having contact angles less than 90° are designated “wettable” or hydrophilic, while fibers having contact angles equal to or greater than to 90° are designated “nonwettable” or hydrophobic. [0043]
  • As used herein, the term “macroscopic surface features” describes three-dimensional features that extend from the surface and are large enough to be perceived or examined with the unaided eye, desirably such features have at least one dimension that is greater than {fraction (3/32)} of an inch (˜1 mm), more desirably such features have at least one dimension that is greater than one sixteenth of an inch (˜1.5 mm), still more desirably such features have at least one dimension greater than one eighth of an inch (˜3 mm) and even more desirably such features have at least one dimension greater than one quarter of an inch (˜6 mm). [0044]
  • As used herein the term “meltblown fibers” means fibers formed by extruding a molten thermoplastic material through a plurality of fine, usually circular, die capillaries as molten threads or filaments into converging high velocity, usually hot, gas (e.g. air) streams which attenuate the filaments of molten thermoplastic material to reduce their diameter, which may be to microfiber diameter. Thereafter, the meltblown fibers are carried by the high velocity gas stream and are deposited on a forming surface to form a web of randomly dispersed meltblown fibers. Such a process is disclosed, for example, in U.S. Pat. No. 3,849,241 to Butin et al. Meltblown fibers are microfibers, which may be continuous or discontinuous, are generally smaller than 10 microns in average diameter, and are generally tacky when deposited onto a forming surface. [0045]
  • As used herein “multilayer laminate” means a laminate including two or more layers of material laminated into a finished structure. For example, one or more of the layers may be a spunbond layer and/or some of the layers may be a meltblown layer. One specific example of a multilayer laminate is a spunbond/meltblown/spunbond (SMS) laminate. Other multilayer laminates are disclosed in U.S. Pat. No. 4,041,203 to Brock et al., U.S. Pat. No. 5,169,706 to Collier, et al, U.S. Pat. No. 5,145,727 to Polls et al., U.S. Pat. No. 5,178,931 to Perkins et al. and U.S. Pat. No. 5,188,885 to Timmons et al. A multilayer laminate may be made by sequentially depositing onto a moving forming belt first a spunbond fabric layer, then a meltblown fabric layer and last another spunbond layer and then bonding the laminate in a manner described below. Alternatively, the fabric layers may be made individually, collected in rolls, and combined in a separate bonding step. Such fabrics usually have a basis weight of from about 0.1 to 12 ounces per square yard (osy) [3 to 400 grams per square meter (gsm)], or more particularly from about 0.75 osy to about 3 osy (25-102 grams per square meter). Multi-layer laminates may also have various numbers of meltblown layers or multiple spunbond layers in many different configurations and may include other materials like films (F) or coform materials, e.g. SMMS, SM, SFS, and so forth. [0046]
  • As used herein the terms “nonwoven” and “nonwoven fabric or web” mean a web having a structure of individual fibers, filaments or threads which are interlaid, but not in an identifiable manner as in a knitted fabric. Nonwoven fabrics or webs have been formed from many processes such as for example, meltblowing processes, spunbonding processes, and bonded carded web processes. The basis weight of nonwoven fabrics is usually expressed in ounces of material per square yard (osy) or grams per square meter (gsm) and the fiber diameters useful are usually expressed in microns. (Note that to convert from osy to gsm, multiply osy by 33.91). [0047]
  • As used herein, the term “solid” does not completely exclude the presence of voids or cavities in the interior of the projections. On the contrary, as will be apparent to those skilled in the art, the forming the projections may well leave voids or cavities in the projections due to variabilities in processing. The term “solid” as used herein, therefore, means that the interior of a given projection is not substantially free from fibers or filaments or other solid when compared with the base material. [0048]
  • As used herein the term “spunbonded webs” refers to webs comprising small diameter fibers which are formed by extruding molten thermoplastic material as filaments from a plurality of fine, usually circular capillaries of a spinneret with the diameter of the extruded filaments then being rapidly reduced as by, for example, in U.S. Pat. No. 4,340,563 to Appel et al., and U.S. Pat. No. 3,692,618 to Dorschner et al., U.S. Pat. No. 3,802,817 to Matsuki et al., U.S. Pat. Nos. 3,338,992 and 3,341,394 to Kinney, U.S. Pat. No.3,502,763 to Hartman, and U.S. Pat. No. 3,542,615 to Dobo et al. Spunbond fibers are generally not tacky when they are deposited onto a forming surface. Spunbond fibers are generally continuous and have average diameters (from a sample of at least 10) larger than 7 microns, more often, between about 10 and 20 microns. [0049]
  • These terms may be defined with additional language in the remaining portions of the specification. [0050]
  • DETAILED DESCRIPTION
  • As discussed above, the present invention provides three-dimensional nonwoven fabrics having one or more macroscopic surface features. It is desirable that the surface features are macroscopic in size and provide separation between the majority of the nonwoven fabric surface and a body part that is in contact with the nonwoven fabric. Such a nonwoven fabric is particularly useful as a body side liner in a personal care article, such as a diaper, pantiliner and so forth. Nonwoven fabrics of the present invention may further indude apertures and non-macroscopic projections as well as the macroscopic features. Nonwoven fabrics of the present invention are also useful for making garments, medical products, cleaning products, packaging materials, construction materials such as sound proofing and insulation, and so forth. [0051]
  • Exemplary nonwoven webs of the present invention are illustrated in FIGS. 1A, 1B and [0052] 1C; FIGS. 5A, 5B and 5C; and FIG. 8. The present invention will be described with reference to the exemplary nonwoven web illustrated in FIGS. 1A, 1B and 1C. The nonwoven web is a three-dimensional nonwoven web 100 that includes a top-side base surface 104 that defines an x,y-plane and at least one macroscopic surface feature 120 extending out of the x,y-plane wherein a macroscopic surface feature 120 is characterized as a feature having an apex 106 that extends at least about 1 millimeter above the x,y-plane of the top-side base surface 106. The nonwoven web illustrated in FIGS. 1A, 1B and 1C and described in greater detail in Example 1 includes macroscopic features having apexes 106 that extend at least about 2 millimeters above the x,y-plane of the top-side base surface 106. The nonwoven web illustrated in FIGS. 5A, 5B and 5C and described in greater detail in Example 5 includes macroscopic features having apexes 106 that extend at least about 3 millimeters above the x,y-plane of the top-side base surface 106. In certain embodiments, the macroscopic features have an apex that extends at least about 1, 1.5, 3, 5 or even about 6 millimeters above the x,y-plane. It is desirable that the macroscopic features 120 have increased height to provide increased separation. Increased height of the macroscopic features increases the bulk thickness T of the web and thus decreases the bulk density of the nonwoven web. For example, the regional bulk density of a nonwoven web of the present invention may be less than 0.04 grams per cubic centimeter, less than 0.03 grams per cubic centimeter or even less than 0.02 grams per cubic centimeter.
  • It is also desirable that the macroscopic features [0053] 120 maintain a height of at least 1 millimeter above the x,y-plane of the top-side base surface 104 under a particular load, for example under a 1.2 kPa load (Pf), to minimize contact when pressure is applied to the nonwoven web 100. In certain embodiments, the macroscopic features maintain a height h of at least about 1, 1.5, 3, 5 or even 6 millimeters above the x,y-plane of the top-side base surface 104 under load. A substantially planar article resting on the nonwoven web of FIGS. 1A, 1B and 1C is illustrated in FIGS. 2A, 2B and 2C to demonstrate some of the features of the nonwoven webs of the present invention. The contact area of an object P with a nonwoven sheet 100 is the sum of the area(s) 106 of the nonwoven sheet that directly contact the object P resting on the nonwoven sheet, more particularly the macroscopic features 120. For example, the contact area of an object P supported by surface features 120 of a nonwoven 100 is the sum of the areas of all of the features and any other parts of the nonwoven web, if any, that directly contact the object P resting on the features 120. In FIG. 2A, the contact area of object P with the nonwoven 100 is the sum of the cross-hatched areas shown in FIGS. 2A and 2C. The percent contact area that an object P has with a nonwoven web supporting P with features 120, is measured by dividing the contact area described above by the flat contiguous area that connects all of the points of the sheet that directly contact the article. For example, if an object is supported by sixteen macroscopic features 100, then the area of the nonwoven web that includes the features supporting the object P is the contiguous “bulk area” (Lp×Wp) measured in a plane parallel to the nonwoven base plane that connects all of the sixteen features or the parts of the sixteen features that support the object. Therefore the percent contact area would be the contact area divided by the bulk area (Lp×Wp). In FIG. 2C, the pressure that an object P supported by the nonwoven transmits to the sheet Pw is measured by dividing the weight of the supported object P by the flat contiguous area (Lp×Wp) beneath the object. The average pressure observed by the surface feature Pf is determined by correcting for the actual area in contact with the load. The average pressure observed by the surface feature Pf can be determined by dividing Pw by the percent contact area.
  • Desirably, the macroscopic feature(s) [0054] 120 minimize contact of an object resting on the feature(s) such that the area of contact of the nonwoven web with an article resting on the macroscopic surface feature at given load is less than 50 percent of the bulk area of the nonwoven web (Lp×Wp) supporting the article. More desirably, the area of contact of the nonwoven web with an article resting on the macroscopic surface feature at a given load of article to contact area of nonwoven web may be less than 40, 30 and even less than 25 percent of the bulk area of the nonwoven web supporting the article. Thus, it is desirable that the nonwoven web and the macroscopic features of the nonwoven web do not compress completely under a given load so that the features minimize contact area and provide separation under a given load. It is also desirable that the features are resilient and return to some measurable height h, desirably greater than 1 mm, after a 3.45 kPa load is applied to the web so that the features provide separation after a 3.45 kPa is applied to the web and is then removed.
  • The nonwoven may include a plurality of macroscopic features to provide separation over a larger area or to provide increased support. The frequency of macroscopic features may vary greatly. For example, it is envisioned that nonwoven webs of the present invention may include as few as 1 macroscopic surface feature per 1, 10, 50 or even 100 square centimeters of nonwoven web in the in the x,y-plane. It is desirable to decrease the number of macroscopic features per unit area of web to decrease contact area. The frequency of the macroscopic features in Examples 1-3 below was about 2 features per square centimeter and about 1 feature per square centimeter in Examples 4 and 5. The frequency of the macroscopic feature illustrated in FIG. 8 may be one feature per 500 square centimeters. [0055]
  • As illustrated in FIG. 8, it is not necessary to provide macroscopic features [0056] 120 over the entire surface 104 of the web 100. For example, one or more macroscopic feature may be provided in a particular location, for example the target zone of a diaper liner, to provide separation in that location as illustrated in FIG. 8. FIG. 8 illustrates a nonwoven web 100 that includes only one macroscopic surface feature 120 measuring about 10 centimeters by 10 centimeters along the exterior widths and an interior opening dimension of about 9 centimeters by 9 centimeters. The macroscopic feature 120 has a height of about 4 millimeters. The single macroscopic features 120 desirably should be located in the target zone of a diaper liner to provide separation between a baby's bottom and the diaper liner surface and any absorbent material located beneath the liner in the target zone.
  • In one particular embodiment, the macroscopic features maintain a height of at least 1 millimeter above the x,y-plane of the top-side base surface under a 1.2 kPa load (P[0057] f). In another embodiment, the macroscopic features maintain a height of at least 1.5 millimeters above the x,y-plane of the top-side base surface under a 1.2 kPa load (Pf). In yet other embodiments, the macroscopic features maintain a height of at least 3, 5 and even 6 millimeters above the x,y-plane of the top-side base surface under a 1.2 kPa load (Pf). In another particular embodiment, the macroscopic feature maintains a height of at least 1 millimeter above the x,y-plane of the top-side base surface under a 1.8 kPa load (Pf). In other embodiments, the macroscopic feature maintains a height of at least 1.5, 3 and even 6 millimeters above the x,y-plane of the top-side base surface under a 1.8 kPa load (Pf). In yet another particular embodiment, the macroscopic feature maintains a height of at least 1 millimeter above the x,y-plane of the top-side base surface under a 10 kPa load. In other embodiments, the macroscopic feature maintains a height of at least 1.5, 3 and even 6 millimeters above the x,y-plane of the top-side base surface under a 10 kPa load. The nonwoven webs of the present invention may include macroscopic features that provide at least 0.08, 0.09 and even greater than 0.10 cubic centimeters per square centimeter of air space between the top surface of the nonwoven web and an article resting on the macroscopic surface feature at a 0.3450 kPa load on the web (Pw).
  • In the exemplary embodiments, the nonwoven web is illustrated as a single layer web that has a uniform composition in the x, y and z directions. However, nonwoven webs of the present invention may be laminates having a uniform composition in the in both the x and the y directions. In the exemplary embodiments, the nonwoven webs of the present invention are also bicomponent spunbond nonwoven webs. However, nonwoven webs of the present invention can be made by methods other than spunbond methods and may include single component and/or multicomponent fibers, filaments and layers. [0058]
  • Spunbond nonwoven webs are formed by depositing melt spun, continuous multicomponent polymeric fibers onto a forming surface. Bicomponent fibers and melt spinning are known and are described in U.S. Pat. Nos. 5,575,874 and 5,643,653 issued to Griesbach et al. which are herein incorporated by reference in their entirety. Multicomponent meltspun nonwoven fabrics and methods of making multicomponent meltspun nonwoven fabrics are also known and are described in U.S. Pat. No. 5,382,400 issued to Pike et al. which is also herein incorporated by reference in its entirety. Methods for extruding multicomponent polymeric filaments are also known. Suitable materials for preparing the bicomponent filaments of the nonwoven fabrics of the present invention include PD-3155 polypropylene available from Exxon Mobil of Houston, Tex.; a linear low density polyethylene (LLDPE) available under the designation ASPUN 6811A, 2553 LLDPE and 61800 polyethylene available from Dow Chemical Company of Midland, Mich.; and 25355 and 12350 HDPEs available from Dow Chemical Company. When a polypropylene is component A and a polyethylene is component B, the bicomponent filaments may comprise from about 20 to about 80 percent by weight of a polypropylene and from about 80 to about 20 percent polyethylene. More desirably, the filaments may comprise from about 40 to about 60 percent by weight polypropylene and from about 60 to about 40 percent by weight polyethylene. [0059]
  • It is desirable that the filaments of the nonwoven web are crimped to provide a lofty nonwoven. Although the illustrated method of carrying out the present invention includes multicomponent filaments that are crimped, the present invention encompasses uncrimped fibers as well as fibers that are crimped by other methods, for example mechanically crimping fibers. Crimped fibers and methods of crimping fibers are known in the art. The present invention also contemplates use of nonwoven webs made by other methods for example, bonded carded webs, meltblown webs and webs made from uncrimped filaments and/or single component filaments. When the spunbond filaments are crimped, the fabric of the present invention advantageously results in a relatively high loft material that is also relatively resilient. The crimp of the filaments creates an open web structure with substantial void portions between filaments and the filaments are bonded at points of contact of the filaments. Again, although the nonwoven fabric described above is made with spunbond bicomponent filaments, it should be understood that nonwoven fabrics of the present invention may be made with single component spunbond filaments, meltblown filaments, bonded carded webs, air laid webs and so forth. For example, single component spunbond filaments can be made in the same manner as described in the Examples except that the spinneret will be adapted to make single component filaments. See, for example, the patents previously identified with respect to spunbond processes. Furthermore, the fibers may be bonded by adding an adhesive polymeric component in another manner. [0060]
  • A spunbond/meltblown/spunbond (SMS) laminate nonwoven fabric can be made to include macroscopic surface features. Meltblown processes of making nonwoven fabrics and SMS nonwoven fabrics are known. Suitable meltblowing techniques and SMS fabrics are disclosed in U.S. Pat. No. 4,041,203, the disclosure of which is incorporated herein by reference. U.S. Pat. No. 4,041,203 references the following publications on meltblowing techniques which are also incorporated herein by reference: an article entitled “Superfine Thermoplastic Fibers” appearing in Industrial Engineering Chemistry, Volume 48, Number 8, ppgs. 1342-1346 which describes work done at the U.S. Naval Research Laboratories in Washington, D.C.; Naval Research Laboratory Report 111437, dated Apr. 15, 1954; U.S. Pat. Nos. 3,715,251; 3,704,198; 3,676,242; and 3,595,245; and British Specification No.1,217,892. [0061]
  • Spunbond meltblown integrated composite (SMIC) materials are described and illustrated in the previously mentioned U.S. Pat. Nos. 5,575,874 and 5,643,653 issued to Griesbach et al. Generally, an SMIC material can be produced by meltblowing material on each side of a spunbond filament curtain. Meltblowing dies can be positioned on each side of the spunbond filament curtain in a symmetric fashion to produce a SMIC fabric. The process is described in more detail in U.S. Pat. Nos. 5,575,874 and 5,643,653 issued to Griesbach et al. which are incorporated by reference herein. The SMIC fabric that is formed can be positioned on a surface that includes topographical features and bonded with hot air to provide a SMIC fabric that includes surface features. [0062]
  • When used to make liquid absorbent articles, a nonwoven fabric of the present invention may be treated with conventional surface treatments or contain conventional polymer additives to enhance the wettability of the fabric. For example, the nonwoven fabric may be treated with polyalkylene-oxide modified siloxanes and silanes such as polyalkylene-oxide modified polydimethyl-siloxane as disclosed in U.S. Pat. No. 5,057,361. Such a surface treatment enhances the wettability of the fabric. The nonwoven web may be treated before it is incorporated into a product. [0063]
  • Nonwoven fabrics of the present invention may include nonwoven fabrics having zones of different liquid handling properties. More specifically, a nonwoven fabric of the present invention may include a fabric that directs flow along all three dimensions of the fabric: along the length of the fabric coplanar with the land areas, along the width of the fabric coplanar with the land areas, and through the thickness or depth of the fabric. These zones of different liquid handling ability are created by areas of topographical surface definition. These topographical regions can vary in basis weight, density and/or filament orientation. In addition, the topographical features can have phobicity differences, which further enhance fluid handling. [0064]
  • As previously stated, nonwoven fabrics of the present invention can be used as separation layers or body side liner materials and may include materials having one large projection or a relatively small number of spaced projections. The present invention includes a nonwoven structure having macroscopic surface features that can be used to separate one surface from another surface, for example, a baby's bottom from an absorbent layer of a diaper. In several desirable embodiments, the structure has physical, aesthetic, and functional attributes that are particularly desirable for use as a body-side liner; a surge material or a liner/surge combination in disposable absorbent products such as: diapers; training pants; incontinent pads; feminine hygiene products such as feminine pads, sanitary napkins, and pantiliners; and so forth. [0065]
  • The discussion that follows is primarily directed to the use of the invention as a unique moisture-pervious top-sheet structure [0066] 100 embodied in a disposable diaper 400 as illustrate in FIGS. 7 and 8. While this is contemplated as being one desirable use, it should be understood that the present invention also has utility in a wide variety of absorptive devices, both disposable and reusable, such as sanitary napkins, catamenial tampons, incontinent pads, and so forth and in non-absorptive devices, such as industrial materials, sound proofing, insulation, packaging and so forth. The detailed description of the top-sheet structure 700 and its use in a disposable diaper 400 will allow those skilled in the art to readily adapt the invention to other devices.
  • As previously stated, it is desirable that the surface features of a web of the present invention are resistant to compression so that the web can be used as a body-side liner in a diaper or other absorbent product to separate the absorbent portion of the absorbent product from the wearer's skin. A view of a disposable absorbent product, for example a diaper [0067] 400, is provided in FIG. 6. Various layers have been cut away to more clearly show the structural details of this particular embodiment. A novel topsheet or body-side liner of the present invention is shown at 700. The other two major components of the disposable diaper 400 are an absorbent element or pad 410 and a backsheet 430. The drawing of diaper 400 in FIG. 6 is a simplified representation of a disposable diaper. A more detailed description of a disposable diaper is contained in U.S. Pat. No. 5,827,259 issued to Laux et al. and is hereby incorporated herein by reference.
  • FIG. 7 illustrates a cross-sectional view taken through line [0068] 7-7 of FIG. 6. The surface features 720 separate a wearer's skin 450 from absorbent material 410 located beneath the liner 700. The liner 420 rests on the absorbent material 410 at base areas 702. Desirably, the contact area of the surface features is less than the contact area of the base areas. Specifically, it is desirable that the nonwoven web 700 is oriented with the macroscopic surface features 720 that provide the least contact area under load are pointing toward the wearer 450. It is also desirable that the contact area of a wearer with the liner is less than 50 percent of the surface area or footprint of wearer on the liner, more desirably the contact area is less than 40 percent, 30 percent and even more desirably the contact area is less than 25 percent. It is believed that reduction in contact between the wearer's skin and wet or damp portions of a diaper improves the skin health of the wearer. It is also believed that separation will improve fluid handling of an absorbent article.
  • It is not necessary that the surface features are completely resistant to compression. [0069]
  • The surface features may compress when a compressive force is applied to the topography. For example, when a baby sits down a majority of the baby's weight is transmitted to the surface features and the liner surface and the features may substantially compress providing little separation between the liner surface and the wearer's skin. However, it is desirable that the topography is not completely compressed during normal use and that some degree of separation is provided by the topography. It is also desirable that the surface features are resilient and are not permanently deformed by forces likely to be transmitted to the surface features during normal use. Specifically, it is desirable that deformation is within the elastic limits of the surface features and the accompanying structure. Thus, a wearer's skin is separated from a substantial portion of the liner surface by the surface features during use. The surface features should provide some degree of separation when a baby is at rest, crawling or walking and desirably even when a majority of the baby's weight is transmitted to the surface features or to the liner. [0070]
  • Although the nonwoven fabric webs of the exemplary embodiments were made by embossing spunbond webs, nonwoven webs of the present invention can be made through the use of other methods. Those of skill in the art will appreciate that a nonwoven web of the present invention can be made via other methods of making webs other than spunbond methods and by methods other than embossing. For example, a nonwoven web having surface macroscopic surface features can be made by the methods described in U.S. patent application Ser. No.__/______, entitled “METHODS FOR MAKING NONWOVEN MATERIALS ON A SURFACE HAVING SURFACE FEATURES AND [0071]
  • NONWOVEN MATERIALS HAVING SURFACE FEATURES” filed by Express Mail Procedure EL471213680 US contemporaneously herewith and which is hereby incorporated by reference herein. Again, other processes of making nonwoven webs can be adapted to make webs that include surface features within the present invention. For example the nonwoven web may be a bonded-carded web (BCW), a coform web, an airlaid web, a spunbond/meltblown/spunbond (SMS) web and so forth. Additionally, the webs can be formed from or include a variety of materials, cellulose, pulp fibers, bicomponent fibers, and so forth. Other modifications and treatments known to those of skill in the art may be used with the present invention. [0072]
  • Nonwoven fabrics having stabilized three-dimensional, macroscopic topographical features can be produced by thermoforming flat non-woven base sheets. The nonwoven base sheet may be a bonded-carded web (BCW), a coform web, an airlaid web, a spunbond/meltblown/spunbond (SMS) web and so forth. Desirably, the webs are thermoformed to have surface features over less than 50 percent of the area of the web, more desirably, less than 40 percent, still more desirably less than 30 percent and most desirably less than 25 percent. It is also desirable that the material and basis weight of the web and the pattern that is thermoformed are selected so that the features do not completely compress and provide separation at a pressure on the feature (P[0073] f) of 1.2 kPa, more desirably do not completely compress and provide separation at 1.8 kPa and even at 10 kPa. It is also desirable that the surface features that are thermoformed are at least 1 mm in height to provide increase separation and air circulation between the majority of the nonwoven material surface and a body that is in contact with the nonwoven material surface. It may be further desirable to provide surface features that are at least 1.5 mm, 3 mm, 5 mm, and even 6 mm in height.
  • A nonwoven base sheet may be thermoformed to include macroscopic features on a heated surface, for example mating plates having surface features on a heated press, having macroscopic features. Heated presses are well known in the art and are readily available. The press should be set at a temperature high enough that to allow the nonwoven web to be permanently deformed but not so high so as to destroy the desirable properties of the nonwoven, for example breathability. Forming plates may have any of a variety of features to impart surface features to the nonwoven. A first pattern of surface features is illustrated in FIGS. 3A, 3B, and [0074] 3C and a second pattern of surface features is illustrated in FIGS. 4A and 4B. Each set of plates includes a first plate and a second plate having an array of surface features, for example squares or triangles, respectively. A variety of other patterns are possible, for example hexagons and diamonds, provided that one or more of the features are macroscopic. Two basic plate designs may be used for forming these plates, standard male and female plates or interdigitated plates. In the examples described herein interdigitating plates were used to provide repeating patterns of squares and triangles. The nonwoven base sheet is placed between the plates and heat and pressure are applied to thermoform the nonwoven base sheet. Three-dimensional nonwoven sheets having stabilized macroscopic topography were produced in the Examples. Although the illustrated nonwoven fabrics include surface features that are uniformly distributed in both the x-direction and the y-direction, nonwoven fabrics of the invention may include features that are uniformly distributed in only one direction. Furthermore, nonwoven fabrics of the invention may include features that are not uniformly provided or distributed on the fabric surface and can be provided and distributed in any pattern.
  • Nonwoven webs of the present invention that include macroscopic surface features may be treated with optional treatments and/or additives to modify one or more properties of the web. For example, non-raised areas of the webs may be treated with a hydrophilic treatment to increase fluid intake. The resulting non-treated raised areas, i.e. the surface features, will be more hydrophobic relative to the treated non-raised areas. Thus, this web provides drier, raised surface contact areas and improving overall skin dryness. The surface features can run the entire length or width of a structure. The surface features can vary in rigidity to increase or decrease the weight-bearing capacity of the features and the nonwoven web. [0075]
  • In order to provide a better understanding of some features of nonwoven webs of the present invention, and not by way of limitation, the following examples and data are provided. [0076]
  • COMPARATIVE EXAMPLE A
  • A diaper liner material was used as a comparative example, Comparative Example A. Comparative Example A was a 0.5 osy nonwoven synthetic fabric web formed 98 percent by weight of 3155 polypropylene from Exxon of Houston, Tex. and 2 percent by weight of titanium dioxide. The 0.5 osy nonwoven synthetic fabric web was formed by a spunbonded process. Fibers having a round cross section were used to form the web and had an average diameter of the approximately 22 microns (3 dpf). The web was formed by randomly laying continuous filaments and then thermal point bonding the randomly laid filaments. The thermal point bonding of the web was accomplished with a pattern having a bond area of 14-21 percent and a pin density of 460 pins/in[0077] 2. The pin geometry was a diamond geometry. Additional details of the liner material can be found in U.S. Pat. No. 6,152,904 hereby incorporated by reference herein.
  • EXAMPLE 1
  • A nonwoven synthetic fabric web having macroscopic surface features was prepared by first forming an underbonded, bicomponent spunbond web and then embossing macroscopic features into the underbonded web. The macroscopic surface features were embossed into the web using heat and pressure applied by heated plates, with one of the plates having at least one macroscopic feature, to impart permanently deformed macroscopic projections into the web. [0078]
  • The underbonded, bicomponent spunbond nonwoven fabric web was formed from continuous bicomponent filaments. Continuous bicomponent filaments were made from approximately equal amounts of two polymer components in a side-by-side configuration. The composition of the first polymer component was 98 percent by weight of 3155 polypropylene from Exxon of Houston, Tex. and 2 percent by weight of titanium dioxide. The composition of second component was 100 percent by weight of 61800 polyethylene from Dow Chemical Company of Midland, Mich. The spin hole geometry of the spin pack was 0.6 mm diameter with a length to diameter (L/D) ratio of 4:1 and the spinneret had 50 holes per inch (19.685 holes per cm) in the cross direction. The melt temperature in the spin pack was 410° F. (210 C) and the throughput was 0.6 grams/hole/minute (ghm). The forming height was 12 inches (30.5 cm). The quench air flow rate of the air quencher was 32 standard cubic feet per minute (scfm) and the temperature was 50° F. aspirator temperature was ambient, approximately 75° F. (23.9° C.), and the aspirator pressure was 3.5 pounds per square inch (psi) (24.31 kPa). An under wire vacuum at 7 inches water (17,440 dynes/cm[0079] 2) was used to collect the filaments onto a forming wire. A hot air knife (HAK) at 270° F. (132.2° C.) inlet air with an exit air temperature of 180° F. (82.2° C.), pressure was 0.8 psi (5.52 kPa) and the height of the HAK above the wire was 1.5 inches (3.8 cm) was used to help integrate the filaments into an underbonded web. The unbonded nonwoven was then directed to a Through Air Bonder (TAB). The TAB was set at an air temperature of approximately 270° F. (132.2° C.) and 0.5 psi (34,470 dynes/cm2) of air pressure and exhaust to form the fibers into an underbonded but integrated web. The line speed was adjusted to approximately 290 ft/min. (88.5 m/min.) to produce a 0.5 ounces per yard (osy) [17 grams per square meter (gsm)] nonwoven material.
  • This underbonded web was then thermoformed into a three-dimensional nonwoven sheet having stabilized macroscopic topography by embossing a three-dimensional “squares” pattern into the web using heat and pressure applied by the heated interdigitating plates [0080] 300 and 350 illustrated in FIGS. 3A and 3B. Each interdigitating plate included a pattern of projections that intemeshed with a similar pattern of projections on the opposing plate. The first plate 300 included a checkerboard pattern of square projections as shown in FIG. 3A. Each projection 310 on the first plate was approximately 3 millimeters in height and measured approximately 5 millimeters by 5 millimeters at the base and terminated in a square distal top surface 320 that measured slightly greater than 3 millimeters by 3 millimeters (approximately 3.5 mm×3.5 mm). The projections were spaced apart approximately 9.5 millimeters from center to center in both x and y directions. The second plate 350 illustrated in FIG. 3B included a similar pattern of alternating square projections 310 of approximately 4 millimeters in height, with each projection 310 measuring approximately 4 millimeters by 4 millimeters at the base and terminating in square distal top surface 320 that measured slightly less than 3 millimeters by 3 millimeters (approximately 2.9 mm×2.9 mm).
  • The patterned plates were heated to a temperature of about 275° F. (135° C.) and the underbonded web was placed on one of the heated plated. The opposing heated plate was then placed on over the web so that the projections on the second plate intermeshed with the projections on the first plate as illustrated in FIG. 3C. Embossing pressure of approximately 115 psi (793 kPa) was then applied to the plates for approximately 35 seconds. After sufficient heat and pressure were applied to deform the web, the plates were separated and the web was removed from the between plates. The resulting three-dimensional material having macroscopic features is illustrated in FIGS. 1A, 1B and [0081] 1C and had an effective bulk thickness of 76 mils (1.93 mm). The method of determining the effective bulk thickness employed a STARRET®-type bulk tester and a pressure (Pw) of 0.05 pounds per square inch (3,450 dynes/cm2).
  • EXAMPLE 2
  • Example 1 was repeated except the line speed of the forming wire and TAB was adjusted to approximately 120 ft/min. (36.6 m/min.) to produce a 1.2 ounces per yard (osy) [40.7 grams per square meter (gsm)] material. The 1.2 osy underbonded material of Example 2 was thermoformed using the squares pattern as described in Example 1. The resulting three-dimensional material having macroscopic features is illustrated in FIGS. 1A, 1B and [0082] 1C and had an effective bulk thickness of 80 mils (2.0 mm).
  • EXAMPLE 3
  • Example 1 was repeated except the line speed of the forming wire and TAB was adjusted to approximately 58 ft/min. (17.7 m/min.) to produce a 2.5 ounces per yard (osy) [85 grams per square meter (gsm)] material. The 2.5 osy underbonded material of Example 3 was thermoformed using the squares pattern as described in Example 1. The resulting three-dimensional material having macroscopic features is illustrated in FIGS. 1A, 1B and [0083] 1C and had an effective bulk thickness of 98 mils (2.5 mm).
  • EXAMPLE 4
  • Example 2 was repeated except that a 1.2 osy underbonded web was thermoformed into a three-dimensional nonwoven sheet having stabilized macroscopic topography by embossing a three-dimensional “triangles” pattern into the web using heat and pressure applied by the heated interdigitating plates [0084] 400 and 450 illustrated in FIGS. 4A and 4B.
  • The 1.2 osy (40.7 gsm) underbonded web was thermoformed into a three-dimensional nonwoven sheet having stabilized macroscopic topography by embossing a three-dimensional “triangles” pattern into the web using heat and pressure applied by the heated interdigitating plates [0085] 400 and 450 illustrated in FIGS. 4A and 4B. Each interdigitating plate included a pattern of triangular projections that intermeshed with a similar pattern of triangular projections on the opposing plate. The first plate 400 included a pattern of triangular tooth-like projections as shown in FIG. 4A. Each triangular projection 410 on the first plate was approximately 3 millimeters in height and had an equilateral triangular base that measured approximately 8 millimeters along any one side and terminated in a equilateral triangular distal top surface 420 that measured approximately 5 millimeters along any one side. The projections were spaced apart approximately 9 millimeters from center to center in both x and y directions. The second plate 450 illustrated in FIG. 4B included a similar pattern of alternating triangular projections 410 of approximately 4 millimeters in height, with each projection 410 having an equilateral triangular base measuring approximately 8.5 millimeters along any one side and terminating in equilateral triangular distal top surface 420 that measured approximately 5 millimeters along any one side.
  • The resulting three-dimensional material having macroscopic features is illustrated in FIGS. 5A, 5B and [0086] 5C and had an effective bulk thickness of 120 mils (3.05 mm).
  • EXAMPLE 5
  • Example 3 was repeated except that a 2.5 osy (85 gsm) underbonded web was thermoformed into a three-dimensional nonwoven sheet having stabilized macroscopic topography by embossing a three-dimensional “triangles” pattern into the web using heat and pressure applied by the heated interdigitating plates [0087] 400 and 450 illustrated in FIGS. 4A and 4B. The resulting three-dimensional material having macroscopic features is illustrated in FIGS. 5A, 5B and 5C and had an effective bulk thickness of 133 mils (3.38 mm).
  • Test Methods [0088]
  • Basis Weight [0089]
  • Basis weights of the examples were determined by measuring and cutting 3 inch (7.6 cm) diameter circular samples from each sample of material. Each three-inch sample was weighed using a balance. The weight of a sample was recorded in grams and then divided by the sample area to provide the basis weight of the sample. Five samples of each example of material were measured and weighed using this procedure to provide an averaged basis weight for each example of nonwoven material. [0090]
  • Caliper [0091]
  • Material caliper or thickness of the examples was also measured. The caliper of an example material was determined by measuring the thickness of the example material (web) under a 0.05 psi (3,450 dynes/cm[0092] 2) load (Pw) using a STARRET®-type bulk tester. The thicknesses were measured and recorded in units of millimeters. Samples of material were cut into 4 inch by 4 inch (10.2 cm by 10.2 cm) squares. Five samples were cut and measured under using the above-described procedure and averaged to provide a mean thickness for each example.
  • Bulk Density [0093]
  • The bulk densities of the nonwoven materials of the Examples were calculated by dividing the weight per unit area of a sample of the nonwoven material in grams per square meter (gsm) by the caliper of the sample of material in millimeters (mm). The web caliper was measured at 0.05 psi (3,450 dynes/cm[0094] 2) as described in determining caliper. The result was multiplied by 0.001 to convert the value to grams per cubic centimeter (g/cc). A total of five samples of each Example was evaluated and averaged to provide the density value.
  • Contact Area [0095]
  • The contact surface areas of the nonwoven materials of the Examples were also measured. The test equipment included: a 3″×4″ (7.6 cm×10.2 cm) sample stage with minimum thickness of ¼″ inch (6.35 mm), a 12.25″×5″×{fraction (3/16)}″ (31 cm×12.7 cm×0.48 cm) piece of LUCITE®, a sample of each material cut into 3″×4″ (7.6 cm×10.2 cm) rectangle, a bulk compressometer, a thermometer, a fine pen, transparency paper cut to a 3″×4″ (7.6 cm×10.2 cm) rectangle, and an rH gauge (hygrometer). All contact areas that were measured using this procedure are nominal contact areas. That is the contact areas are defined by the contact that the surface features have with a flat surface resting on the features. This is not the sum of the individual fiber areas that are technically in contact with the flat surface over the projected area of the sample but include the areas between the individual fibers. [0096]
  • Initial Measurement and Setup [0097]
  • 1) Perform test in a controlled environment of 74±4° F. (23.3±2.2° C.) and 50±10% rH. [0098]
  • 2) Samples shall be prepared from materials that are representative of materials produced as they are removed from the forming line and before they are wound or packaged. [0099]
  • 3) Samples are to be cut from sections of the web that are uniform and representative of the parent material. [0100]
  • 4) Three 3″×4″ (7.6 cm×10.2 cm) rectangular samples are cut from the parent material of each Example. [0101]
  • 5) The initial bulk of each sample is measured using a bulk compressometer. [0102]
  • 6) A load is applied and when the reading is stable for 4 seconds the value is recorded. The sample is immediately removed from the load after the value is recorded. [0103]
  • Initial Contact Surface/Area [0104]
  • 7) The 3″×4″ (7.6 cm×10.2 cm) sample stage is placed on top of a flat, level surface. [0105]
  • 8) The 3″×4″ (7.6 cm×10.2 cm) sample is then lined with the stage and placed on top. [0106]
  • 9) An initial surface contact area is taken by placing a flat, clear surface over the top of the sample. A piece of transparency paper was used for this method. [0107]
  • 10) The material provides a load of less than 0.003 psi on the material for the initial reading. [0108]
  • 11) From the perspective directly above each contacting topographic surface feature, the perimeter of surface contact is recorded for the materials by tracing the perimeter with a fine pen. [0109]
  • 12) The area of the material contacting the flat surface is then recorded as the initial contact area. This area is determined from the tracing performed in step 11. [0110]
  • 13) This initial contact area is divided by the projected area of the sample (i.e. 12 square inches) to give a percentage of contact surface/area for the sample. [0111]
  • Contact Surface Under Increased Load [0112]
  • 14) For additional contact area measurements under heavier loads, a flat rectangular piece of Lucite® material is placed over the sample material. [0113]
  • 15) The center of the rectangular piece of Lucite® material is measured. [0114]
  • 16) A 3″×4″ (7.6 cm×10.2 cm) rectangle has been centered on the rectangular piece of Lucite® material and traced. The edges of the traced perimeter are parallel to the edges of the Lucite® material rectangle. [0115]
  • 17) The Lucite® material is 12.25″×5″×{fraction (3/16)}″ (31 cm×12.7 cm×0.48 cm) in dimension and weighs 0.6 lbs (273 grams). [0116]
  • 18) A piece of transparency paper is placed over the Lucite material so that the perimeter of the features may be recorded on the paper. [0117]
  • 19) From the perspective directly above each contacting topographic surface feature, the perimeter of surface contact is recorded using a fine pen for the materials. [0118]
  • 20) The area of the material contacting the flat surface is then recorded for the material and the load condition is also recorded. [0119]
  • 21)This contact area under load is divided by the projected area of the sample (i.e. 12 inch[0120] 2 or77.4 cm2) to give a percentage of contact surface/area for the sample.
  • 22) The average true load that the surface features experience is determined by dividing the weight the plate exerts on the sample by the area of the sample in contact with the flat load. E.g. 0.6 lbs on a 12 inch[0121] 2 sample that has 20% contact area would show a 20% contact area at a pressure of 0.25 psi [0.6 lbs/(12 inch2×20%)].
  • Additional contact area measurements were made using two different weights, 1.2 lbs and 6 lbs (0.545 and 2.73 kg). The contact area is measured until the weight equaled 6 lbs or the contact area is greater than 90 percent. [0122]
  • 23) A flat rectangular piece of Lucite® material is placed over the sample material. [0123]
  • 24) The center of the rectangular piece of Lucite® material is measured determined. [0124]
  • 25) A 3″×4″ (7.6 cm×10.2 cm) rectangle has been centered on the rectangular piece of Lucite® and traced. The edges of the traced perimeter are parallel to the edges of the Lucite® rectangle. [0125]
  • 26) The Lucite® is 12.25″×5″×{fraction (3/16)}″ (31 cm×12.7 cm ×0.48 cm) in dimension and weighs 0.6 lbs (273 grams). [0126]
  • 27) On the edges of the Lucite® material 0.3 lbs (136.35 grams) of weight are added on each end to provide a total weight of 1.2 lbs of force being placed on the 12 inch[0127] 2 web.
  • 28) A piece of transparency paper is placed over the Lucite material so that the perimeter of the features may be recorded on the paper. [0128]
  • 29) From the perspective directly above each contacting topographic surface feature, the perimeter of surface contact is recorded using a fine pen for the materials. [0129]
  • 30) The area of the material contacting the flat surface is then recorded for the material and the load condition is also recorded. [0130]
  • 31) This contact area under load is divided by the projected area of the sample (i.e. 12 inch[0131] 2) to give a percentage of contact surface/area for the sample.
  • 32) The average true load that the surface features experience is determined by dividing the weight the plate exerts on the sample by the area of the sample in contact with the flat load. E.g. 6 lbs on a 12 inch[0132] 2 sample that has 20% contact area would show a 20% contact area at a pressure of 2.5 psi [0.6 lbs/(12 inch2×20%)].
  • 33) Repeat steps 22-30 where step 26 is modified to provide a weight of 2.7 lbs (1227 grams) on each side for a total load of 6 lbs (2.72 kg). [0133]
  • 34) Perform experiment until either the total load on the sample equals 6 lbs or the nominal contact area that the sample has with the flat material is greater than 90 percent. [0134]
  • 35) Take and record the material's (web's) bulk at most 5 minutes after step 29. [0135]
  • Pressure Applied to Web (P[0136] w)
  • Referring to FIG. 2A, the contact area of object P with the nonwoven [0137] 100 is the sum of the cross-hatched areas shown in FIGS. 2A and 2C. The pressure that an object P supported by features 120 transmits to a nonwoven web 100 is measured by dividing the weight of the supported object P by the flat contiguous area that connects all of the points of the sheet that directly contact the article. For example, if an object is supported by sixteen macroscopic features 100, then the area of the nonwoven web supporting the object P is the contiguous area (Wp×Lp) measured in a plane parallel to the nonwoven base plane that connects all of the sixteen features or the parts of the sixteen features that support the object. In FIG. 2C, the pressure that an object P supported by the nonwoven transmits to the sheet is measured by dividing the weight of the supported object P by the flat contiguous area Lp by Wp beneath the object.
  • Average Pressure Observed by Surface Features (P[0138] f)
  • The average true load that the surface features experience is determined by dividing the weight the plate exerts on the sample by the area of the sample in contact with the flat load. The average pressure observed by the surface feature P[0139] f is determined by correcting for the actual area in contact with the load Pw. This is done by dividing Pw by the percent contact area.
  • Web Volume Measurement Method [0140]
  • The nonwoven web volume is determined from a measurement of the void volume inside the web and the volume occupied by the fibers. Fiber volume is calculated from the weight of the web divided by fiber density. For webs that possess a high degree of topography, the internal void volume is measured from a liquid saturation experiment wherein liquid that is not contained in internal pores is excluded from the measurement. [0141]
  • This can be determined using an apparatus based on the porous plate method reported by Burgeni and Kapur in the [0142] Textile Research Journal, Volume 37, pp. 356-366 (1967), the disclosure of which is incorporated by reference. The apparatus includes a movable stage interfaced with a programmable stepper motor, and an electronic balance controlled by a computer. A control program automatically moves the stage to a desired height, collects data at a specified sampling rate until equilibrium is reached, and then moves the stage to the next calculated height. Controllable parameters include sampling rates, criteria for equilibrium and the number of absorption/desorption cycles.
  • Data for this analysis was collected using a liquid containing a surfactant to render the nonwoven web totally wettable and the measurement was done in desorption mode. That is, the material was saturated at zero height and the porous plate (and the effective capillary tension on the sample) was progressively raised in discrete steps corresponding to the desired capillary radius or capillary tension. At zero height, a certain amount of liquid trapped in the interface between the web and the plate exists, due to the topography of the nonwoven web. As the plate is raised, the amount of liquid pulled out from the sample was monitored. Readings at each height were taken every fifteen seconds and equilibrium was assumed to be reached when the average change of four consecutive readings was less than 0.005 g. The interfacial liquid (at the interface between the saturated nonwoven web sample and the porous plate) is typically removed by raising the plate slightly (0.5-0.7 cm). The internal void volume is expressed as cc/gram. [0143]
  • The nonwoven web volume is the sum of the internal void volume measurement described above and the fiber volume. [0144]
  • V nw=Web volume(cc/g)=Internal void volume+(1/fiber density)
  • Volume of Space Between Liner and a Flat Surface as Measured Using a Bulk Compressometer [0145]
  • A circular sample of each Example was taken and the volume the sample created by separating its top and bottom planes was determined by multiplying the area of the circle (3″) and the sample's caliper t (t was determined using a STARRET®-type bulk tester). This volume will be specified V[0146] p to represent the volume of space separating the top and bottom planes of the shaped material.
  • V p(cc)=t(cm)×area of circle(cm 2)
  • The nonwoven web volume (V[0147] nw) that was determined using the method described above was then be subtracted from volume of space separating the two planes (Vp) to yield the volume of space not occupied by the web between the two planes (Vs).
  • V s(cc)=V p(cc)−V nw(cc)
  • Because V[0148] nw and V p were determined using the same circular sample area, the volume of space not occupied by the web between the two planes (Vs) can be divided by the area to determine volume (cc)/area(cm2) or Vsa.
  • V sa(cc/cm 2)=Vs(cc)/area(cm 2)
  • The materials used in the examples were generally symmetric. Therefore, the volume of space per unit area between the top surface of the liner and the skin V[0149] ls was determined by dividing Vsa by 2.
  • V ls(cc/cm 2)=V sa(cc)/2
  • This assumption is safe for the patterns used in the Examples because the surface that faces toward the body side provides the least amount of contact with the body. Therefore, assuming the sides are symmetric estimates the true volume above the web. [0150]
  • Percent Recovery [0151]
  • The method of determining bulk recovery uses P[0152] w or the load that is observed by the web. The samples are cut into 3″ circles, and the caliper or thickness of the samples is measured. The caliper of an example material is determined by measuring the thickness of the example material (web) under a 0.05 psi (3,450 dynes/cm2) load (Pw) using a STARRET®-type bulk tester. The thickness is measured in units of thousandths of an inch. The recorded data provides an initial Bulk thickness (Bulk0) for the material.
  • The sample is then removed and placed under a load P[0153] w of 3.45 kPa. The load is applied for 5 minutes then removed. The material is allowed to recovery at ambient conditions for 5 minutes. The caliper of the material is then measured once more using the bulk tester under the 0.05 psi (3,450 dynes/cm2) load (Pw) to provide a final thickness (Bulkf).
  • The final thickness is divided by the initial thickness to provide a percent recovery of the bulk. [0154]
  • % Recovery=Bulkf/Bulk0
  • Test Results [0155]
  • Test results of the tests on the Examples are provided in Table A below. Failure of rial to provide separation is indicated by the symbol“--” in Table A. [0156]
    Topographic Liner Properties
    Bulk Bulko Bulkf
    Density % CONTACT AREA UNDER Vls % Recovery (mils/ (mils/ t (mils/
    Example Pattern (g/cc) SPECIFIED LOAD (cc/cm2) bulkf/bulko microns) microns) microns)
    A Flat 0.067 0.000 100%  8/200  8/200  8/200
    1 0.5 osy 0.012 25% 0.086  80%  76/1930  61/1550 10/250
    (17 gsm) @0.2 psi
    Squares (1.4 kPa)
    2 1.2 osy 0.018 30.2% 37% 0.087  95%  80/2030  76/1930 16/405
    (41 gsm) @0.17 psi @0.27 psi
    Squares (1.2 kPa) (1.9 kPa)
    3 2.5 osy 0.036 26% 27% 27% 0.096  98%  98/2490  96/2440 20/510
    (85 gsm) @0.19 psi @.37 psi @1.86 psi
    Squares (1.3 kPa) (2.55 kPa) (12.8 kPa)
    4 1.2 osy 0.014 23% 37% 0.120  94% 120/3050 113/2870 16/405
    (41 gsm) @0.22 psi @0.27 psi
    Triangles (1.5 kPa) (1.9 kPa)
    5 2.5 osy 0.025 20% 20% 26% 0.138  96% 133/3380 128/3250 20/510
    (85 gsm) @0.25 psi @0.51 psi @1.91 psi
    Triangles (1.7 kPa) (3.5 Kpa) (13.2 kPa)
  • Thus, it is apparent that there has been provided, in accordance with the invention, a nonwoven fabric having macroscopic surface features. While the invention has been described in conjunction with specific embodiments thereof, it is evident that many alternatives, modifications, and variations will be apparent to those skilled in the art in light of the foregoing description. Accordingly, it is intended to embrace all such alternatives, modifications, and variations as fall within the spirit and broad scope of the appended claims. [0157]

Claims (37)

    We claim:
  1. 1. A three-dimensional nonwoven web having a regional, bulk density of less than 0.04 grams per cubic centimeter and comprising
    a top-side base surface that defines an x,y-plane and
    at least one macroscopic surface feature extending out of the x,y-plane wherein a macroscopic surface feature is characterized as a feature having an apex that extends at least about 1 millimeters above the x,y-plane of the top-side base surface and the maintains a height of at least 1 millimeter above the x,y-plane of the top-side base surface under a 1.2 kPa load (Pf)
    wherein the at least one macroscopic feature results in contact of an object resting on the macroscopic feature such that the percent contact area of the nonwoven web with an article resting on the macroscopic surface feature at a 1.2 kPa load (Pf) is less than 50 percent of the bulk area of the nonwoven web supporting the article.
  2. 2. The nonwoven web of claim 1, wherein a macroscopic feature is characterized as a feature having an apex that extends at least 1.5 millimeters above the x,y-plane.
  3. 3. The nonwoven web of claim 1, wherein a macroscopic feature is characterized as a feature having an apex that extends at least 3 millimeters above the x,y-plane.
  4. 4. The nonwoven web of claim 1, wherein a macroscopic feature is characterized as a feature having an apex that extends at least 5 millimeters above the x,y-plane.
  5. 5. The nonwoven web of claim 1, wherein a macroscopic feature is characterized as a feature having an apex that extends at least about 6 millimeters above the x,y-plane.
  6. 6. The nonwoven web of claim 1, wherein the percent contact area of the nonwoven web with an article resting on the macroscopic surface feature at a 1.2 kPa load (Pf) is less than 40 percent of the bulk area of the nonwoven web supporting the article.
  7. 7. The nonwoven web of claim 1, wherein the percent contact area of the nonwoven web with an article resting on the macroscopic surface feature at a 1.2 kPa load (Pf) is less than 30 percent of the bulk area of the nonwoven web supporting the article.
  8. 8. The nonwoven web of claim 1, wherein the percent contact area of the nonwoven web with an article resting on the macroscopic surface feature at a 1.2 kPa load (Pf) is less than 25 percent of the bulk area of the nonwoven web supporting the article.
  9. 9. The nonwoven web of claim 1, wherein the nonwoven web comprises a plurality of macroscopic features and the frequency of macroscopic features is at least 1 macroscopic surface feature per 100 square centimeters of nonwoven web in the in the x,y-plane.
  10. 10. The nonwoven web of claim 1, wherein the nonwoven web comprises a plurality of macroscopic features and the frequency of macroscopic features is at least 1 macroscopic surface feature per 50 square centimeters of nonwoven web in the in the x,y-plane.
  11. 11. The nonwoven web of claim 1, wherein the nonwoven web comprises a plurality of macroscopic features and the frequency of macroscopic features is at least 1 macroscopic surface feature per 10 square centimeters of nonwoven web in the in the x,y-plane.
  12. 12. The nonwoven web of claim 1, wherein the nonwoven web comprises a plurality of macroscopic features and the frequency of macroscopic features is at least 1 macroscopic surface feature per 1 square centimeter of nonwoven web in the in the x,y-plane.
  13. 13. The nonwoven web of claim 1, wherein the regional bulk density of the nonwoven web is less than 0.03 grams per cubic centimeter.
  14. 14. The nonwoven web of claim 1, wherein the e regional bulk density of the nonwoven web is less than 0.02 grams per cubic centimeter.
  15. 15. The nonwoven web of claim 9, wherein the macroscopic features maintain a height of at least 1.5 millimeters above the x,y-plane of the top-side base surface under a 1.2 kPa load (Pf).
  16. 16. The nonwoven web of claim 9, wherein the macroscopic features maintain a height of at least 3 millimeters above the x,y-plane of the top-side base surface under a 1.2 kPa load (Pf).
  17. 17. The nonwoven web of claim 9, wherein the macroscopic features maintain a height of at least 6 millimeters above the x,y-plane of the top-side base surface under a 1.2 kPa load (Pf).
  18. 18. The nonwoven web of claim 1, wherein the macroscopic feature maintains a height of at least 1 millimeter above the x,y-plane of the top-side base surface under a 1.8 kPa load (Pf).
  19. 19. The nonwoven web of claim 1, wherein the macroscopic feature maintains a height of at least 1.5 millimeters above the x,y-plane of the top-side base surface under a 1.8 kPa load (Pf).
  20. 20. The nonwoven web of claim 1, wherein the macroscopic feature maintains a height of at least 3 millimeters above the x,y-plane of the top-side base surface under a 1.8 kPa load (Pf).
  21. 21. The nonwoven web of claim 1, wherein the macroscopic feature maintains a height of at least 6 millimeters above the x,y-plane of the top-side base surface under a 1.8 kPa load (Pf).
  22. 22. The nonwoven web of claim 1, wherein the macroscopic feature maintains a height of at least 1 millimeter above the x,y-plane of the top-side base surface under a 10 kPa load (Pf).
  23. 23. The nonwoven web of claim 1, wherein the macroscopic feature maintains a height of at least 1.5 millimeters above the x,y-plane of the top-side base surface under a 10 kPa load (Pf).
  24. 24. The nonwoven web of claim 1, wherein the macroscopic feature maintains a height of at least 3 millimeters above the x,y-plane of the top-side base surface under a 10 kPa load (Pf).
  25. 25. The nonwoven web of claim 1, wherein the macroscopic feature maintains a height of at least 6 millimeters above the x,y-plane of the top-side base surface under a 10 kPa load (Pf).
  26. 26. The nonwoven web of claim 9, wherein the macroscopic features provide at least 0.08 cubic centimeters of air space between the top surface of the nonwoven web and an article resting on the macroscopic surface feature at a 1.2 kPa load (Pf) of article to contact area of nonwoven web per 1.0 square centimeter of nonwoven web.
  27. 27. The nonwoven web of claim 9, wherein the macroscopic features provide at least 0.09 cubic centimeters of air space between the top surface of the nonwoven web and an article resting on the macroscopic surface feature at a 1.2 kPa load (Pf) of article to contact area of nonwoven web per 1.0 square centimeter of nonwoven web.
  28. 28. The nonwoven web of claim 9, wherein the macroscopic features provide at least 0.10 cubic centimeters of air space between the top surface of the nonwoven web and an article resting on the macroscopic surface feature at a 1.2 kPa load (Pf) of article to contact area of nonwoven web per 1.0 square centimeter of nonwoven web.
  29. 29. The nonwoven web of claim 1, wherein the nonwoven web has a uniform composition in the x and y directions.
  30. 30. The nonwoven web of claim 1, wherein the nonwoven web comprises a laminate.
  31. 31. The nonwoven web of claim 1, wherein the nonwoven web comprises bicomponent fibers.
  32. 32. A three-dimensional, nonwoven web having a regional, bulk density of less than 0.03 grams per cubic centimeter and comprising
    a top-side base surface that defines an x,y-plane and
    a plurality of macroscopic surface features extending out of the x,y-plane at a frequency of at least one macroscopic feature per 100 square centimeter of nonwoven web wherein a macroscopic surface feature is characterized as a feature having an apex that extends at least about 3 millimeters above the x,y-plane of the top-side base surface and the maintains a height of at least 3 millimeters above the x,y-plane of the top-side base surface under a 1.2 kPa load (Pf) p2 wherein the macroscopic features results in contact of an object resting on the macroscopic feature such that the percent contact area of the nonwoven web with an article resting on the macroscopic surface features at a 1.2 kPa load (Pf) less than 40 percent of the bulk area of the nonwoven web supporting the article.
  33. 33. The nonwoven web of claim 32, wherein a macroscopic feature is characterized as a feature having an apex that extends at least 5 millimeters above the x,y-plane.
  34. 34. The nonwoven web of claim 32, wherein a macroscopic feature is characterized as a feature having an apex that extends at least about 6 millimeters above the x,y-plane.
  35. 35. The nonwoven web of claim 32, wherein the percent contact area of the nonwoven web with an article resting on the macroscopic surface feature at a 1.2 kPa load (Pf) is less than 30 percent of the bulk area of the nonwoven web supporting the article.
  36. 36. The nonwoven web of claim 32, wherein the percent contact area of the nonwoven web with an article resting on the macroscopic surface feature at a 1.2 kPa load (Pf) is less than 25 percent of the bulk area of the nonwoven web supporting the article.
  37. 37. A three-dimensional, embossed nonwoven web having a regional, bulk density of less than 0.03 grams per cubic centimeter and comprising
    a top-side base surface that defines an x,y-plane and
    a plurality of macroscopic surface features extending out of the x,y-plane at a frequency of at least one macroscopic feature per 1 square centimeter of nonwoven web wherein a macroscopic surface feature is characterized as a feature having an apex that extends at least about 5 millimeters above the x,y-plane of the top-side base surface and the maintains a height of at least 3 millimeters above the x,y-plane of the top-side base surface under a 1.8 kPa load (Pf)
    wherein the macroscopic features results in contact of an object resting on the macroscopic feature such that the percent contact area of the nonwoven web with an article resting on the macroscopic surface features at a 1.8 kPa load (Pf) is less than 40 percent of the bulk area of the nonwoven web supporting the article.
US10136805 2002-04-30 2002-04-30 Nonwoven materials having surface features Abandoned US20030203691A1 (en)