US20010024851A1 - Method of manufacturing insulating-gate semiconductor device - Google Patents
Method of manufacturing insulating-gate semiconductor device Download PDFInfo
- Publication number
- US20010024851A1 US20010024851A1 US09/817,118 US81711801A US2001024851A1 US 20010024851 A1 US20010024851 A1 US 20010024851A1 US 81711801 A US81711801 A US 81711801A US 2001024851 A1 US2001024851 A1 US 2001024851A1
- Authority
- US
- United States
- Prior art keywords
- trench
- forming
- film
- insulating
- semiconductor device
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The cell density of power MOSFET used as a switch is determined by the width of the trench formed in the device, the processing limit of which is limited by the spatial resolution of the exposure apparatus used in the photolithographic process. This invention provides a method of manufacturing such devices which overcomes the processing limitation imposed by the exposure apparatus, and doubles the cell density and reduces the input capacitance for further reducing the on-state resistance and improving the switching speed. By forming a second CVD oxide film over a first oxide film defining the opening for forming a trench and subsequent anisotropic RIE etching of the second film, a side-wall film is added to the mask pattern, which promotes a further reduction of the width of the trench by more than one half.
Description
- This invention relates to a method of manufacturing insulating-gate semiconductor device, more specifically to a method of manufacturing insulating-gate semiconductor device in which a fine trench structure is created based on trench width reduction using a self-aligned formation of an overlapping masking layer.
- Recently, with the growth of the mobile computing/communication terminal market there has been an increasing demand for lithium-ion batteries which are smaller in size and yet larger in capacity. The protecting circuit board for the management of charging and discharging the lithium-ion battery has to be small in order to meet the need for total weight reduction of the mobile computing/communication terminal and in order to withstand short circuits due to excessive loads. In this application, it was required that the protecting circuit boards be small, as the boards were housed inside the container of the lithium-ion battery. This size reduction has been accomplished by the use of COB (Chip on Board) technology using multiple chip components. On the other hand, as the switching devices on the board such as power MOSFET are connected to the lithium-ion battery in series, there is also a need for reducing the on-state resistance of the switching devices. This is an indispensable ingredient in mobile telephone applications for extending the calling period and the stand-by period.
- For achieving a low on-state resistance, developments have been made for increasing the cell density by applying micro-fabrication technology to the chip manufacturing process. As a result, in a typical planar structure where the channel was formed on the surface of the semiconductor substrate, the cell density was 7.4 million per square inch. Further, in the first-generation trench structure where the channel was formed along the side of the trench, the cell density was 25 million per square inch. Improvements were made in the second-generation trench structure so that the cell density reached 72 million per square inch.
- As described above, the cell density has been increased by the adoption of the trench structure for forming the cells, and the on-state resistance has decreased accordingly. However, at this point, there is no room for manipulating the current micro-fabrication process for further reducing the size of the trench structure. The only way to achieve the reduction is to introduce a new exposure apparatus with a higher spatial resolution in the micro-fabrication process, if such an apparatus is available.
- This invention involves a micro-fabrication process in which the process limitations due to the spatial resolution of the exposure apparatus used in the photolithographic process can be overcome by modifying the process for forming the masking layer for the trench, this overcomes the problems described above.
- The invention provides method of manufacturing an insulating-gate semiconductor device that includes forming a channel layer on a drain region of a semiconductor substrate, forming an opening for forming a trench in a first insulating film formed on the surface of the semiconductor substrate, forming a side-wall film around a side wall of the opening for forming a trench by anisotropic etching of a second insulating film formed over the first insulating film, forming a trench piercing through the channel layer by etching using the first insulating film and the side-wall film as a mask, forming a gate insulating film on an inside wall of the trench, forming a gate electrode by filling the trench with a semiconductor material, and forming a source region adjacent to the trench in the surface region of the channel region.
- In the manufacturing method described above, the side-wall film is formed based on a self-aligned formation of the second insulating film over the first insulating film. Thus, the side-wall film further reduces the width of the opening for forming a trench in the mask pattern, the processing limit of which is determined by the spatial resolution of the exposure apparatus used for creating the photoresist mask pattern. As a result, it is possible to create a trench structure of a size which is smaller than the spatial resolution of the exposure apparatus.
- Based on this manufacturing method, it is possible to use current manufacturing facilities, especially the exposure apparatus, for manufacturing devices having finer trench structures than the current device without requiring advanced manufacturing facilities. For example, in a conventional process, the opening for forming a trench was 1.0 μm, and accordingly the width of the trench was 1.0 μm. When the manufacturing method of the invention was applied using the same manufacturing facilities, the opening for forming the trench was the same, but the width of the trench was reduced, by more than one half, to 0.4 μm.
- The manufacturing method of the invention increases the cell density by about two times while keeping the same operational surface area as the conventional device. Thus, the on-state resistance increases accordingly, and the properties of the switching device are improved.
- Furthermore, it is another advantage of this invention that the smaller width of the trench allows the reduction of the cross-sectional area of the trench, resulting in a smaller capacitance between the gate and the source of the trench as well as a smaller capacitance between the gate and the drain of the trench. This type of capacitance has a significant influence on the cut-off frequency as input capacitance and feedback capacitance, the reduction of which improves the switching speed.
- The invention may be better understood, and its objectives, features, and advantages made apparent to those skilled in the art, by referring to the accompanying drawings.
- FIG. 1 is a cross-sectional view of a semiconductor device intermediate at a step of the method of manufacturing an insulating-gate semiconductor device of this invention.
- FIG. 2 is a cross-sectional view of a semiconductor device intermediate at a step of the method of manufacturing an insulating-gate semiconductor device of this invention following FIG. 1.
- FIG. 3 is a cross-sectional view of a semiconductor device intermediate at a step of the method of manufacturing an insulating-gate semiconductor device of this invention.
- FIG. 4 is a cross-sectional view of a semiconductor device intermediate at a step of the method of manufacturing an insulating-gate semiconductor device of this invention following FIG. 3.
- FIG. 5 is a cross-sectional view of a semiconductor device intermediate at a step of the method of manufacturing an insulating-gate semiconductor device of this invention.
- FIG. 6 is a cross-sectional view of a semiconductor device intermediate at a step of the method of manufacturing an insulating-gate semiconductor device of this invention following FIG. 5.
- FIG. 7 is a cross-sectional view of a semiconductor device intermediate at a step of the method of manufacturing an insulating-gate semiconductor device of this invention following FIG. 6.
- FIG. 8 is a cross-sectional view of a semiconductor device intermediate at a step of the method of manufacturing an insulating-gate semiconductor device of this invention following FIG. 7.
- FIG. 9 is a cross-sectional view of a semiconductor device intermediate at a step of the method of manufacturing an insulating-gate semiconductor device of this invention following FIG. 8.
- FIG. 10 is a cross-sectional view of a semiconductor device intermediate at a step of the method of manufacturing an insulating-gate semiconductor device of this invention following FIG. 9.
- FIG. 11 is a cross-sectional view of a semiconductor device intermediate at a step of a conventional method of manufacturing an insulating-gate semiconductor device.
- FIG. 12 is a cross-sectional view of a semiconductor device intermediate at a further of a conventional method of manufacturing an insulating-gate semiconductor device.
- FIG. 13 is a cross-sectional view of a semiconductor device intermediate at a further step of a conventional method of manufacturing an insulating-gate semiconductor device.
- FIG. 14 is a cross-sectional view of a semiconductor device intermediate at a further step of a conventional method of manufacturing an insulating-gate semiconductor device.
- FIG. 15 is a cross-sectional view of a semiconductor device intermediate at a further step of a conventional method of manufacturing an insulating-gate semiconductor device.
- FIG. 16 is a cross-sectional view of a semiconductor device intermediate at a further step of a conventional method of manufacturing an insulating-gate semiconductor device.
- FIG. 17 is a cross-sectional view of a semiconductor device intermediate at a further step of a conventional method of manufacturing an insulating-gate semiconductor device.
- FIG. 18 is a cross-sectional view of a semiconductor device intermediate at a further step of a conventional method of manufacturing an insulating-gate semiconductor device.
- FIG. 19 is a cross-sectional view of a semiconductor device intermediate at a further step of a conventional method of manufacturing an insulating-gate semiconductor device.
- FIG. 20 is a cross-sectional view of a semiconductor device intermediate at a further step of a conventional method of manufacturing an insulating-gate semiconductor device.
- The manufacturing method of the invention will be described hereinafter, taking an N-channel device as an example, by referring to FIG. 1 through FIG. 10.
- FIG. 1 shows a process for forming
channel layer 4. First, an epitaxial N− silicon layer is grown on an N+silicon semiconductor substrate 1 to form adrain region 2. Then,oxide film 3 is formed on the surface of theepitaxial layer 2 and a portion ofoxide film 3 corresponding tochannel layer 4 is removed by etching. Using theoxide film 3 as a mask, boron dopants with a dose of about 1.0×1013 cm−2 are injected through the mask into thedrain region 2, and thermally diffused for forming P-type channel 4. - FIG. 2 follows FIG. 1 and shows a process for creating an opening for forming a trench6. A first insulating film, an
oxide film 5 formed by CVD (chemical vapor deposition) in this embodiment, is formed on the entire top surface of the device intermediate. Thefirst oxide film 5 is made of NSG (non-doped silicate glass) and has a thickness of 3000 angstrom. Then, a photoresist film is formed on theCVD oxide film 5 and lithographically patterned to create a masking pattern for forming the opening for forming a trench 6. TheCVD oxide film 5 is dry-etched through the photoresist mask and the opening for forming a trench 6 is created in the area where the trench is to be formed. The width of the opening is about 1.0 μm and thechannel layer 4 is exposed through the opening. Though a CVD process is used to form thefirst oxide film 5 in this embodiment, a thermal oxidation process can be used instead. Furthermore, theCVD oxide film 5 can be replaced by a nitride film, which is capable of preventing contamination from the outside environment, or a multi-layer film in which the nitride film is formed on the oxide film. - A process for forming a side-
wall film 8, which is unique in the present invention, is now described by referring to FIG. 3 and FIG. 4. - FIG. 3 shows a process for forming a second insulating film on the first insulating film. A
second oxide film 7 is formed on the entire surface of the firstCVD oxide film 5, including the inside wall of the opening for forming a trench 6, using a LP-CVD process or LP-TEOS. The deposition on the inside wall of the opening forms the side-wall film. The thickness of the second oxide film is about 5000 angstrom. In this configuration, theCVD oxide film 7 can be replaced by a nitride film, which is capable of preventing contamination from the outside environment, or by a multi-layer film made of the nitride film and the oxide film. - FIG. 4 shows a process for anisotropically etching the second
CVD oxide film 7. In this process, an anisotropic RIE (reactive ion etching) is used for removing the secondCVD oxide film 7 without a mask since the anisotropic RIE has much higher etching rate in the vertical direction than in the horizontal direction. As a result, when thesecond oxide film 7 is removed from the surface of thefirst oxide film 5, the side-wall film 8 emerges as a self-aligned oxide layer covering the inside wall of the opening for forming a trench 6. Since the firstCVD oxide film 5 has a thickness of about 3000 angstrom, the side-wall film 5 has a thickness of about 3000 angstrom at both sides of the trench, resulting in a reduction of the width of the trench from 1.0 μm, which is the width of the original opening for forming a trench 6, to about 0.4 μm. - FIG. 5 shows a process for forming the
trench 9. The silicon semiconductor substrate is etched using a CF-based or HBr-based etching gas with theCVD oxide film 5 and the side-wall film 8 being used as a mask for forming atrench 9 piercing through thechannel layer 4 and reaching thedrain region 2. The depth of the trench is about 2.0 μm and its width is about 0.4 μm, as the side-wall portion 8 of the mask protects the extra region which is not covered by the firstCVD oxide film 5. - FIG. 6 shows a process for forming a gate insulating film, which is
oxide film 11 in this embodiment. First, an oxide film, which is not shown in the figure, is formed on the inside wall of the trench and the surface of thechannel layer 4 in a dummy oxidation (sacrificed oxidation) process, which is required to cure the damage caused by the previous dry etching process. Then, the oxide film and the firstCVD oxide film 5 are removed by another etching, and the device intermediate is heated above 1000° C. for oxidizing the silicon until agate oxide film 11 of a thickness of about 700 angstrom is formed on the top surface of the device intermediate. - FIG. 7 follows FIG. 6 and shows a process for forming
gate electrode 13. First, apolysilicon layer 12 without dopants is deposited on the entire top surface of the device intermediate with a thickness larger than one half of the width of the opening for forming a trench 6, which is about 5000 angstrom in this embodiment. Phosphorus dopants are injected into the polysilicon at a high dose and diffused for making the polysilicon highly conductive. Thepolysilicon layer 12 is then removed from the top surface of the device intermediate by another etching without a mask, leaving thegate electrode 13 buried in thetrench 9. - FIG. 8 follows the process of FIG. 7 and shows a process for forming a
body region 14. First, a photoresist film PR is formed on the top surface of the device intermediate of FIG. 7 except a region betweentrenches 9, and boron dopants are injected into the portion ofchannel layer 4 exposed through the opening with a dose of 5.0×1014 cm−2 for makingbody region 14 of P+ type. Then, the photoresist film PR is removed from the top surface.Body region 14 is required for the voltage stabilization of a substrate including thedrain region 2 and thechannel layer 4. - FIG. 9 shows a process for forming a
source region 15. First, another photoresist film PR is formed on the top surface of the device intermediate except for thetrench 9 and the region of thechannel layer 4 adjacent to thetrench 9, and arsenic dopants are injected into the portion of thechannel layer 4 exposed through the opening with a dose of 5.0×1015 cm−2 for making asource region 15 of N+ type. Then, the photoresist film PR is removed from the top surface. As a result, a channel, not shown in the figure, is formed along the side of thetrench 9 between thedrain region 2 and thesource region 15. - FIG. 10 shows a process for forming a
source electrode 17. First, aninterlayer insulating film 16 made of BPSG (boron phosphorus silicate glass) or the like is deposited on the entire top surface of the device intermediate using a CVD process or the like. The BPSG film is removed by etching, except a few regions including the regions above thegate electrode 13, using a photoresist film patterned accordingly as a mask. Finally, asource electrode 17 made of aluminum or aluminum alloy is formed on the top surface of the device intermediate by a sputtering process for making contact with thebody region 14 and thesource region 15. - For further understanding the advantages of the manufacturing method of the present invention, the conventional manufacturing method of the similar device will be described hereinafter by referring to FIG. 11 through FIG. 20. A comparison between the two manufacturing methods will clarify the significant step taken in the present invention.
- FIG. 11 shows a process for forming a
channel layer 24. First, an epitaxial N− silicon is grown on an N+ siliconlayer semiconductor substrate 21 to form adrain region 22. Then, anoxide film 23 is formed on the surface of the epitaxial layer and a portion of theoxide film 23 corresponding to thechannel layer 24 is removed by etching. Using theoxide film 23 as a mask, boron dopants with a dose of 1.0×1013 cm−2 are injected through the mask into thedrain region 22, and are thermally diffused for forming a P-type channel 24. - The process for forming the trench will be now described by referring to FIG. 12 through FIG. 15.
- FIG. 12 shows a CVD process for depositing
oxide film 25, which is made of NSG and has a thickness of 3000 angstrom. Though a CVD process is used to form theoxide film 25, a thermal oxidation process can be used instead. - FIG. 13 shows a process for forming a masking pattern made of
oxide film 25. First, a photoresist film is formed on theCVD oxide film 25 and lithographically patterned to create a masking pattern for forming the opening for formingtrench 26. TheCVD oxide film 25 is then dry-etched through the photoresist mask, and the opening for forming atrench 26 is created in the area where the trench is to be formed. The width of the opening is about 1.0 μm and thechannel layer 24 is exposed through the opening. - FIG. 14 shows a process for forming
trench 27. The silicon semiconductor substrate is etched using a CF based or HBr based etching gas with theCVD oxide film 25 being used as a mask for forming atrench 27 piercing through thechannel layer 24 and reaching thedrain region 22. The depth of the trench is about 2.0 μm and its width is about 1.0 μm, as the width of the opening for forming atrench 26 dictates the width of thetrench 27. - FIG. 15 shows a process for removing the
CVD oxide film 25. First, an oxide film, which is not shown in the figure, is formed on the inside wall of thetrench 27 and the surface of thechannel layer 24 in a dummy oxidation process, which is required to cure the damage caused by the previous dry etching process. Then, the oxide film and theCVD oxide film 25 are removed by another etching. - FIG. 16 shows a process for forming
gate insulating film 31. In this process, the device intermediate is heated above 1000° C. for oxidizing the silicon until agate oxide film 31 of a thickness of about 700 angstrom is formed on the top surface of the device intermediate. - FIG. 17 shows a process for forming a
gate electrode 33 buried in thetrench 27. First, apolysilicon layer 32 without dopants is deposited on the entire top surface of the device intermediate. Then, phosphorus dopants are injected into the polysilicon layer at a high dose and diffused for making the polysilicon highly conductive. Thepolysilicon layer 32 is then removed from the top surface of the device intermediate by another etching without a mask, leavinggate electrode 33 buried in thetrench 27. - FIG. 18 shows a process for forming a
body region 34. First, a photoresist film PR is formed on the top surface of the device intermediate except the region between thetrenches 27, and boron dopants are injected into the portion of thechannel layer 24 exposed through the opening with a dose of 5.0×1014 cm−2 for making abody region 34 of P+ type. Then, the photoresist film PR is removed from the top surface. - FIG. 19 shows a process for forming a
source region 35. First, another photoresist film PR is formed on the top surface of the device intermediate except thesource region 35 and thegate electrode 33, and arsenic dopants are injected into thechannel layer 24 using the photoresist film as a mask with a dose of 5.0×1015 cm−2 for making asource region 35 of N+ type. Then, the photoresist film PR is removed from the top surface. - FIG. 20 shows a process for forming a
source electrode 37. First, aninterlayer insulating film 36 made of BPSG or the like is deposited on the entire top surface of the device intermediate using a CVD process or the like. The BPSG film is removed by etching, except for a few regions including the ones above thegate electrode 13, using a photoresist film patterned accordingly as a mask. Finally, asource electrode 37 made of aluminum or aluminum alloy is formed on the top surface of the device intermediate by a sputtering process for making a contact to thebody region 34 and thesource region 35. - By comparing the method of manufacturing insulating-gate semiconductor device of this invention to that of the conventional art, it is obvious to those skilled in the art that the manufacturing method of this invention has a significant advantage over the conventional method by adding only a few process steps to those of the conventional art. This addition includes the formation of the second insulating film over the first insulating film, as shown in FIG. 3, and the anisotropic etching by RIE of the second insulating film, as shown in FIG. 4. These two processes are compatible with other processes in the manufacturing method, and are easily to be incorporated. Yet, the improvement produced by the added steps is significant enough to reduce the width of the trench to about one half of the width of the trench manufactured by the conventional method. In the conventional method described above, the opening for forming a trench is 1.0 μm, and accordingly the width of the trench is 1.0 μm. In the method of the embodiment of the present invention described above, the opening for forming a trench was the same, but the width of the trench reduced, by more than one half, to 0.4 μm.
- The key in achieving the above improvement is the formation of the side-wall film, which is formed based on a self-aligned formation of the second insulating film over the first insulating film. This side-wall film further reduces the width of the opening for forming a trench in the mask pattern, the processing limit of which is determined by the spatial resolution of the exposure apparatus used for creating the photoresist mask pattern. As a result, it is possible to create a trench structure, the size of which is smaller than the spatial resolution of the exposure apparatus.
- In the aforementioned embodiment, a manufacturing method for an N-channel device is described. However, it is also possible that a P-channel device may be fabricated based on the method of the present invention. This is one of many modifications of this invention within the scope of the claims of the application.
- While the invention has been described and illustrated with respect to a particular embodiment, it will be understood by those skilled in the art that various other changes and modifications may be made without departing from the spirit and scope of the invention. All such modifications are intended for inclusion within the scope of the following claims.
Claims (6)
1. A method of manufacturing an insulating-gate semiconductor device, comprising:
forming a channel layer of a conduction type on a surface region of a semiconductor substrate, said surface region having an opposite conduction type to the channel layer and being formed into a drain region;
forming an opening for forming a trench in a first insulating film formed on the surface of the semiconductor substrate;
forming a side-wall film around a side wall of the opening for forming a trench by anisotropic etching of a second insulating film formed over the first insulating film;
forming a trench piercing through the channel layer by etching, said first insulating film and said side-wall film being used as a mask;
forming a gate insulating film on an inside wall of the trench;
forming a gate electrode by filling the trench with a semiconductor material; and
forming a source region adjacent to the trench in the surface region of the channel region, the conduction type of said source region is the same as the conduction type of the drain region.
2. A method of manufacturing insulating-gate semiconductor device according to , wherein the width of the trench is smaller than about one half of the width of the opening for forming a trench.
claim 1
3. A method of manufacturing insulating-gate semiconductor device according to , wherein the first insulating film is an oxide film formed by a chemical vapor deposition process or an oxide film formed by thermal oxidation process.
claim 1
4. A method of manufacturing insulating-gate semiconductor device according to , wherein the first insulating film is a nitride film or a multi-layer film made of a nitride film and an oxide film.
claim 1
5. A method of manufacturing insulating-gate semiconductor device according to , wherein the second insulating film is an oxide film formed by a chemical vapor deposition process.
claim 1
6. A method of manufacturing insulating-gate semiconductor device according to , wherein the second insulating film is a nitride film or a multi-layer film made of a nitride film and an oxide film.
claim 1