TWI240726B - Polyurethane prepolymers comprising alkoxysilane terminal groups, a method of producing them and their use for the production of sealing materials - Google Patents
Polyurethane prepolymers comprising alkoxysilane terminal groups, a method of producing them and their use for the production of sealing materials Download PDFInfo
- Publication number
- TWI240726B TWI240726B TW088118634A TW88118634A TWI240726B TW I240726 B TWI240726 B TW I240726B TW 088118634 A TW088118634 A TW 088118634A TW 88118634 A TW88118634 A TW 88118634A TW I240726 B TWI240726 B TW I240726B
- Authority
- TW
- Taiwan
- Prior art keywords
- polyurethane prepolymer
- patent application
- scope
- alkoxysilane
- molecular weight
- Prior art date
Description
1240726 經濟部智慧財產局員工消費合作社印梦 A7 五、發明說明(丨) · 本發明關於含有烧氧基石夕貌末端基並且以特殊、 常高之聚胺基甲酸酷預聚物為基料之聚胺基甲:聚 物,關於其生產方法及關於農用七 、 黏合劑的用途。 用方;作為低模數密封材料之 經由一種石夕烧縮合聚合反應進行交聯之院氧基石夕垸官以 之聚胺基甲酸醋已被知道久了。例如,在"黏合劑時二 4/1995,30 和其後數頁(作者:Ta-Mln Feng,B a Waldmann)可發現此議題之回顧性文章。 . j建築工業和汽車1業上逐漸增加使用此類烧氧基石夕烧末 端基、水分熟化、單成份聚胺基甲酸醋作為挽曲塗層、穷 =黏合劑組合物。在如這些的應用中,對有延伸“: ^以及對纽速度有相#的要求。㈣是以先前技術系 統無法完全達到建築部門所需的性質程度。
EP A 59636Q描途烧氧基㈣官能基之聚胺基甲酸醋預 其係適合作為密封材料之黏合劑。但是明確描述於I 的產物不適合用於生產撓曲、低模數密封材
枓如這些建築部門中所用的Q 建築邛門所用之密封材料的性質輪廓被詳細列於DIN IS0 η^〇〇。相同的觀察結果也可應用在關於ep-A 596360接下 來最近所發表的專利申請案,即Ερ_Α Μ〗】⑽和Εκα 297公釐) (請先間讀背面之注意事項再填寫本頁) -..-------訂---------線秦 1240726 發明說明(2 ) 807649中。在户此土 a κ 於制、生古二先則技術專利中所描述的產物是適合用 用二::二^、封材料如這些工程領域所用的,但不適合 用表衣仏建柴用低模數密封材料。 明目的是提供含有烷氧基矽烷末端基並且適合用 ^作^生產低模數密封材料之黏合劑的聚胺基甲酸醋預聚 &匕1曰口有^几氧基石夕燒末端基和 '細節描述於下之聚胺基曱 酸酷預聚物之準備證明可能達成此目的,其中這些聚胺基 :@义S日預χκ物疋以特殊、分子量非常高之聚胺基甲酸醋預 聚物為基料。 本I明關方;含有烧氧基石夕院末端基之聚胺基甲酸醋預聚 物,其可藉 、 A)線性聚胺基甲酸酯預聚物,其係由下列化合物反應所製 得的 n ϋ»— n .1.» ·ϋ ϋ ϋ I I β ϋ I ·ϋ I n iai 心華OJ* I ϋ n ϋ I (請先閱讀背面之注意事項再填寫本頁) 1) 經濟部智慧財產局員工消費合作社印製 π) 一種NC〇含量為20。/。至6〇%之芳族、脂族或環脂 知-一兴氣酸S旨成份與 一種多元醇成份,其包含一種聚氧基伸烷基二醇卷 作其主成份而且其分子量為3000至2〇,〇〇〇,與田 Β)含烷氧基矽烷和胺基之式(I)化合物 -4 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 五、發明說明( 其中 R和R,
:表相同或不同的烷基,其係包含 ,較佳係1至4個碳原子, 至8個碳原 和 代表相同或不同的CVCVP其十、^ 係白人1 兀基或〇1-〇8烷氧基,^ '、έ 1至4個碳原子,條件兔1 1木仵為至少一個基團代』 ^•。烷氧基, 子其特徵在於聚胺基甲酸嶋
广〇。至5。,_’較佳係從2。 〇J 如由其NC0含量和NC〇官能 式⑴中的X、γ和z彼此獨立,較佳係代表甲氧基或乙氧 本發明也關於一種生產含有烷氧基矽烷末端基之聚胺基甲 酸酯預聚物的方法,其係藉 1240726 A7 B7 五、發明說明(4 A)平均分子量為從丨5,〇〇〇至5〇,〇〇〇之線性聚胺基曱酸酯 預聚物,該平均分子量係從其NCO含量和NC〇官能 度所算得, 與 B)含烷氧基矽烷和胺基之式⑴化合物 ?H2 9h-N—(CH2)5—S*r~*Y i〇〇R CO〇Rf z (I), 其中 I麵 Itr、
R和R5代表相同或不同的烷基,其係包含丨至8個 碳原子,較佳係1至4個碳原子, 和 ---.--1·--------------訂---------· (請先閱讀背面之注意事項再填寫本頁) 經濟部智慧財產局員工消費合作社印製 X、γ、z代表相同或不同的烷基或烷氧基,其係包含 1至4個碳原子,條件為至少一個基團代表 烷氧基, 反應,其特徵在於聚胺基甲酸酯預聚物A)的平均分子 !24〇726 Α7 五、發明說明(5 ) 如由其NCO含量和NCO官 量是從15,000至5〇 〇〇〇 能度所算得。 本發明是基於令人驚訝的觀臾社 基而且分子量—果’ έ有烧氧基錢末端 r - 41 - 门4寸殊聚胺基曱酸酯預聚物熟化可_ 仔!剝洛的產物,不管苴小旦 …、儿j擭 形成密封材料,储料曰自、-Γ聯位置而且其可經加工 α哀材枓頒不出極佳的彈力性質。 的異氛酸醋預聚“)是依聚胺”酸醋化 =彳ζ:;藉二異氰酸醋成份0與多元醇成“) ‘所衣仔的,其特徵在於下面細節中。 減本發明使用異氰酸醋含量為20至60重量%之任何先前 ㈣脂族、環脂族或芳族二異氰酸自旨作為聚異氰酸醋成份 =入角牛’芳族”和"環脂族"二異氰酸醋等項是指每個分子 U至少—個芳族或環脂族環的二異氛酸醋,其中較佳但 it須^少兩個異氮酸醋基中的—個是直接連接在芳族 ,二知私%上。作為成份G或成份G的一部份之合適或較佳 :質為分子量範圍170 i 300《芳族或環脂族二異氰酸 S曰,如4,4’-二苯基甲烷二異氰酸酯,視情況為與2,4,-二苯 土甲、兀一兴氱酸酯的摻混物、2,4-二異氰酸酯基曱苯和其最 好$有相對於該混合物高達35重 量〇/❹之2,6-二異氰酸酯基 曱笨的工業混合物、1-異氰酸酯基-3,3,5 —三甲基異氰酸 酯基曱基環己烷(IPDI)、雙-(4-異氰酸酯基環己基)曱烷、卜 1240726 經濟部智慧財產局員工消費合作社印製 A7 B7 五、發明說明(6 ) 異氰酸酯基甲基-4(3)-異氰酸酯基-甲基-環己烷和1,3-二異氰酸酯基-6-甲基-環己烷,視情況為與1,3-二異氰酸酯 基-2-甲基環己烷的摻混物。當然也可使用上述異氰酸酯之 混合物。 較佳係使用1-異氰酸酯基-3,3,5-三甲基-5-異氰酸酯基甲基 環己烷(IPDI)和/或2,4-二異氰酸酯基甲苯和其最好具有相 對於該混合物高達35重量%之2,6-二異氰酸酯基曱苯的工 業混合物作為成份1)。 為了生產聚胺基甲酸酯預聚物A),二異氰酸酯成份〇與多 元醇成份ii)反應。多元醇成份ii)包含一種作為其主要成份 之分子量為從3000至20,000(相當於〇H數目為從37 3至 5.6),較佳係4000至1 5,000(相當於OH數目為從28至7 5) 的聚氧基伸烷基二醇。根據本發明偏好使用之聚氧基伸院 基一醇為這些從聚胺基甲酸醋化學技術上已知種類的聚氧 基伸烷基二醇,如這些藉適合起始物分子之乙氧基化和/或 丙氧基化所製成的。適合的起始物分子實例包括二醇類如 乙二醇、丙二醇、1,3-丁二醇、1,4-丁二醇、丨56己二醇、 2-乙基己二醇_1,3以及包括一級單胺類如脂族胺類,如乙基 胺或丁基胺。偏好使用之聚氧基伸烷基二醇具有從3〇〇〇 2 2〇,000,較佳係4000至15,000之從其〇H含量和官能度所 算得的平均分子量以及相對於聚氧基伸烷基二醇總量,其 最大環氧乙烷含量為20%。 〃 本紙張尺度適用$國國家標準(CNS)A4規格(210 X 297公釐^ .--ί---------------^---------線^^ . (請先閱讀背面之注意事項再填寫本頁) 1240726 A7 B7 五、發明說明(7 ) (請先閱讀背面之注意事項再填寫本頁) 作為成份11)之即特佳物質為最大總不飽和度為0.04毫當量 /克和從其〇H含量和官能度所算得的平均分子量為8000至 12,000之聚環氧丙烷聚醚。 根據本發明最偏好使用之低不飽和度聚醚多元醇基本上是 已知的而且描述於,例如EP-A 283 148、US-A 3278457、US_A 3427256、US-A 3829505、US-A 4472560、US-A 3278458、 US-A 3427334 、 US-A 3941849 、 US-A 4721818 、 US-A 3278459、US-A 3427335 和 US-A 4355188 ° 根據本發明可使用之聚醚多元醇具低不飽和度而且最好是 利用金屬氰化物當作觸媒所製成的,若說出最偏好使用之 低飽和度聚醚多元醇可用於生產撓曲、低模數密封材料是 特別有利的事實必定讓人極為驚訝,因為根據先前技術較 硬和模數較高的聚胺基甲酸酯是利用此類多元醇所製得 的。 經濟部智慧財產局員工消費合作社印製 在生產NCO預聚物A)的過程中,視情況可同時使用輔助量 之分子量為32至500的低分子量二羥基和三羥基醇。適合 的實例包括乙二醇、U3-丁二醇、1,4-丁二醇、1,6-己二醇、 甘油或三羥甲基丙烷。但是不偏好同時使用低分子量醇 類。 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 1240726 A7 五、發明說明(8 ) 但是,在生產NCO預聚物A)的過程中,也可同時使用輔助 里之先别技術多g此基聚酸多元醇,雖這也是不偏好的。 根據本發明可用作成份A)之聚胺基甲酸酯預聚物的製造可 藉一異氰酸酯成份i)與二醇成份ii)在從40至12〇,較作 係在50至1〇〇。〇的溫度範圍内,但維持NC〇/〇H當量比在 從1.2 : i至1.8 : 較佳係從K3 : i至]6 :〗下反應而達 成。在生產這些聚胺基曱酸酯預聚物的過程中,視情況可 同時使用從聚胺基甲酸酯化學技術已知的胺或有機金 媒。 ^旬 根據本發明可使用之聚胺基甲酸酯預聚物八)的Ν(:〇含量曰 從0.21至0.56%,較佳係從〇.28至〇 42%,相當於平二= 子量是從1 5,000至50,00〇,較佳係從2〇,〇〇()至4〇,〇⑽—。刀 在根據本發明方法的第二個階段中,根據本發明可使 聚胺基甲酸酯預聚物A)與式⑴化合物反應, 之 CH;-CH-9 ;〇OR i〇OR,
I 丨一(CH2)^—Si—-Y 2 I餘 (I), (請先閱讀背面之注意事項再填寫本頁) ..-------訂---------線隊 經濟部智慧財產局員工消費合作社印製 其中 R和R,代表相同或不同的烷基,其係包含1至 子,較佳係1至4個碳原子,最佳係〗至 低1碳原 個碳原 -10 本紙張尺度適用中國國家標準(CN^TT見格(210 x 297公楚 1240726
子 X Y Z代表相同或不同的烷基或烷氧基,其係包含1至4 個石反原子’條科為至少一個基圑代表和較佳係三個 全部代表Ci-Cs烷氧基, 根據本I明可使用之含有烷氧基矽烷和胺基 之化合物的產 生如EP-A 596360所描述可藉式(π)胺基烷基烷氧基矽烷 X Η2Ν—(CH2)j—Si—Y ' I z其中X、Y、Z具有式⑴所定之意義, (II), (請先閱讀背面之注意事項再填寫本頁)
..-------訂---------線 I 經濟部智慧財產局員工消費合作社印製 代表相同或不同的烧基或烧氧基,其係包含1至4 與式(III)之順式丁烯二酸和/或反式丁烯二酸的酯類反應而達成ROOC CH_—CH COOR1 (H1), i'kr ,' 、DJ、. -11 -
本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 1240726 經濟部智慧財產局員工消費合作社印製 A7 五、發明說明(10) 其中 R和R,彼此獨立,代表Cl_c8烷基。 適合的式(II)胺基烷基號氧基矽烷實例包括3_胺基丙基三甲 氧基矽Ί、3-胺基丙基三乙氧基矽院和3_胺基丙基-甲基- 一乙氧基矽烷;特佳係3_胺基丙基三甲氧基矽烷和3_胺基 丙基三乙氧基石夕、j:完。 在根據本發明方法中,NC〇預聚物與含有烷氧基矽烷和胺 基之式(I)化合物的反應是在從0至15〇艺,較佳係 的/m度範圍内進行,其中定量比例一般是經過選擇以使每 莫耳所用的NCO基最好使用0.95至1.1莫耳胺基矽烷基化 :物每莫耳所用白勺Nc〇基最好使们莫耳胺基石夕烧基化 s物使用較尚的反應溫度時,根據Ep_a 807649的教導可 能發生環縮合反應。但是,這絕不是麻煩,甚至時常是有 利的。 本發明另外關於含有绽氧基料末端基之根據本發明聚胺 基甲酸酯預聚物用於作為生產不含異氰酸酯、低模數聚胺 基曱酸s旨密封材料’較佳係建築部門所用密封材料之黏合 劑的用途。這些密封材料在大氣中水分的作用下經由一種 石夕丈元縮合聚合反應進行交聯。 -12 - 本紙張尺度適用中國國家標準(CNS)A4規格(21〇 X 297公爱) 丨 |*丨丨—·--------------訂--------- (請先閱讀背面之注意事項再填寫本頁) 1240726
經濟部智慧財產局員工消費合作社印製 些ΐί物之密封材料,根據產生密封材料-彳,3有纟兀氧基矽烷末端基之根據本發 酸醋預聚物也可與慣用塑 =錢基f ,, y 填枓、色素、乾燥劑、添 ::先安定劑、抗氧化劑、觸變劑、觸媒或鍵結劑和祝 N况舁其他輔助物質和添加劑一起調配。 適口的填料貝例包括碳黑、煙霧狀水合石夕石、礦物礦物白 ,和煙霧狀白細[適合的塑化劑實例包括苯二, 酸酯、己二酸酯、酚的烷基磺酸酯或磷酸酯。 觸變劑的實例包括熱解水合矽石、聚醯胺、衍生自氫化蓖 麻油之產物以及聚氯化乙烯。 可引用有機錫化合物和胺觸媒作為適合熟化反應的觸媒。 有機錫化合物的實例包括··二丁基錫二醋酸鹽、二丁基錫 一月桂酸鹽、二丁基錫雙-乙醯基丙酮酸鹽和羧酸錫,例如 辛‘錫。上述錫觸媒視情況可與胺觸媒如胺基碎坑或二氮 雜二環辛烷合併使用。 特別適合的乾燥劑包括烷氧基矽烷基化合物如乙烯基三甲 氧基矽烷、甲基三甲氧基矽烷、異丁基三甲氧基矽烷和十 六燒基三甲氧基矽烷。 -13 - 本紙張尺度_中國國家標準(CN_S)A4規格⑽χ 297公楚) I. -------^-------- (請先閲讀背面之注意事項涛填寫本買) •線; 1240726 A7 B7 五、發明說明(〗2 可使用已知官能基矽烷作為此鍵結劑,例如上述類型之胺 基矽烷以及胺基乙基-3-胺基丙基三甲氧基-和/或队胺基乙 基胺基丙基-甲基-二甲氧基矽烷、環氧基矽烷和/或氫硫 基石夕焼。 忒已父聯聚合物是以其傑出的延伸度以及同時以其低模數 為特色。制是以低總不飽和度之聚氧基丙二醇為基料的 產物是以其低模數、極佳的機械性f和以其低表面剝落程 度為特色’其中聚氧基丙三醇最好用於作為三醇成份⑴。 — — — — — — — — — « — — — — — II ^ I I I I---I · C請先閱讀背面之注意事項再填寫本頁) 經濟部智慧財產局員工消費合作社印製 -14 - 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 1240726 A7 B7 五、發明說明(I3) 實例 實例1 在100 C下’ 166.5克異佛爾酮二異氰酸酯與4000克之〇H 數目為14和不飽和度為〇 〇〇5毫當量/克的聚丙二醇 (Acclaim 8200 ; Aco所製造的)預聚合直到理論NC〇含量達 到0.5%。所獲得的聚胺基甲酸酯預聚物之算得的平均分子 量為16,600。將該批次物冷卻至6(rc後,逐滴迅速加入 175.5克N-(3-三甲氧基矽烷基丙基)門冬氨酸二乙基酯(根 據EP-A 596360之實例5所製成的)於其中,並且攪拌該混 合物直到IR光譜圖上不再出現異氰酸酯帶。所獲得的含有 烷氧基矽烷末端基之聚胺基甲酸酯預聚物的黏度為26,〇〇〇 毫帕(23°C )。 ’ 利用二丁基錫二醋酸鹽作為觸媒將澆鑄在玻璃板上之薄膜 隔夜熟化以形成一種蕭氏(Shore)A硬度為13之透明且撓曲 性高的塑膠。 & 經濟部智慧財產局員工消費合作社印製 11[------Φ-1Ι (請先閱讀背面之注音3事項再填寫本頁) 線· 實例2 在8(TCf ’ 104.4克曱苯2,4_二異氰酸醋與2〇〇〇克⑽數 目為28的聚醚二醇預聚合直到理論NC〇含量達到〇 6%, 其中聚醚二醇是藉丙二醇之丙氧基化和接著丙氧基化產物
1240726 經濟部智慧財產局員工消費合作社印製 A7 五、發明說明(l4 ) ^乙乳基化所製成的(P0/E〇比例·· 80 ·· 20)。所獲得的聚胺 土甲fee S曰預I物之算得的平均分子量為21。將該批次 勿7 W7至6〇c後’逐滴迅速加入64 6克N_(3_三甲氧基石夕 =基丙基)門冬氨酸二甲基醋(根據EP-A 596360之實例4所 乂 ^的)方、其中,直到IR光譜圖上不再出現異氰酸酯帶。所 &付的3有'J:元氧基矽烷末端基之聚胺基甲酸酯預聚物的黏 度為96,0〇〇毫帕(23。匸)。 利==丁基錫二醋酸鹽作為觸媒將澆鑄在玻璃板上之薄膜 仪;^化㈣成—種蕭氏(ShGre)A硬度為9之透明且棱曲 性高的塑膠。 實例3 在、〇下克兴佛爾酮二異氰酸S旨與4000克之〇h 數目為14和不飽和度為〇〇〇5毫當量/克的聚丙二醇 (Acdaim 8200 ; Aco所製造的)預聚合直到理論nc〇含量達 到0.4%。所獲得的聚胺基甲酸酯預聚物之算得的平均分子 量為21,000。將該批次物冷卻至6〇。〇後,逐滴迅速加入 140.4克N-(3-三甲氧基矽烷基丙基)門冬氨酸二乙基醋(根 據EP-A 596360之實例5所製成的)於其中,並且攪拌該混 合物直到IR光譜圖上不再出現異氰酸醋帶。所獲得的含有 烷氧基矽烷末端基之聚胺基曱酸酯預聚物的黏度為Μ 〇〇〇 毫帕(23°C)。 ’ -16 - 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公楚) I- ---------訂---------線赢 (請先閱讀背面之注意事項再填寫本頁) 1240726 五、發明說明(I5 ) 利用;7 丁基锡二醋酸鹽作為觸媒將堯鑄在玻璃板上之薄膜 隔夜熟化以形成—種蕭氏de)A硬度為15之透明且撓曲 性高的塑膠。 i d钪曲 實例4 在C下I47.9克商業用混合物與5300克之〇η數目為 ㈣和不飽和度為0.005毫#量/克的聚丙二醇(Acciaim 12200,Aco所製造的)預聚合直到理論Nc〇含量達到 0.54%’其中商業用混合物包含8〇重量%曱苯2,4_二显氰酸 醋和20重量%甲苯认二異氰酸醋。所獲得的聚胺基;酸 酯預聚物之算得的平均分子量為丨5,5〇〇。將該批次物冷卻 至60C後,逐滴迅速加入226」克N-(3_三甲氧基矽烷基丙 基)門冬氨酸二甲基酯(根據Ep_A 59636〇之實例4所製成的) 方、其中,並且攪拌該混合物直到IR光譜圖上不再出現異氰 酸知帶。所獲得的含有烷氧基矽烷末端基之聚胺基甲酸酯 預聚物的黏度為25,000毫帕(23°C )。 利用二丁基錫二醋酸鹽作為觸媒,將澆鑄在玻璃板上之薄 膜隔夜熟化以形成一種蕭氏(shore)A硬度為u之透明且撓 曲性局的塑膠。 -17 - 本紙張尺度·中國國家標準(CNS)A4規格(210 X 297公爱) (請先閱讀背面之注意事項再填寫本頁) .. 線- 經濟部智慧財產局員工消費合作社印製 1240726 A7 五、發明說明(丨6) 在100C下,166.5克異佛爾酮二異氰酸酯與53〇〇克之〇H 數目為10.6和不飽和度為〇〇〇5毫當量/克的聚丙二醇 (ACClaim 12200 ; A⑶所製造的)預聚合直到理論NC〇含量 達到0.38%。所獲得的聚胺基甲酸醋預聚物之算得的平均分 子量為22,_。將該批次物冷卻至6代後,逐滴迅速加入 Π5.5克N-(3-三甲氧基矽烷基丙基)門冬氨酸二乙基酯消 據EP-A S96360之實例5所製成的)於其中,並且攪拌該混 物直到汛光譜圖上不再出現異氰酸醋帶。所獲得的 烷虱基矽烷末端基之聚胺基甲酸酯預聚物的黏度為 毫帕(23°C )。 ’ 訂 利用二丁基錫二醋酸鹽作為觸媒,將澆鑄在破璃板上之薄 膜隔仪熟化以形成一種蕭氏(Sh〇re)A硬度為12之透明且撓 曲性高的塑膠。 ① 實例6 之聚胺基甲酸酯密封材料:— 在商業上可取得之行星式混合器中操作下列成份以產生立 即可用的密封材料: 41.6份重 之實例3的預聚物 18 - ί紙張斤"適用(cns)a7^格⑵0 χ 297^) 1240726 A7 五、發明說明(17) 14.6份重 二異十—烷基苯二甲酸酯(塑化劑) 0.20伤重 二丁基錫雙-乙酸基丙酮酸鹽 (在溶劑石腦油1〇〇所形成的1〇%溶液) 1.50份重 乙烯基三甲氧基矽烷 41.6份重 煙霧狀白堊(種類:Socal U1S2) 在1 〇〇笔巴的壓力下,以丨〇分鐘分散該混合物,因此將内 部溫度提高至60°C。接著加入 0.5伤重 N-胺基乙基_3_胺基丙基-曱基二甲氧基矽烷 並在1〇〇毫巴的壓力下攪拌10分鐘以將其摻入。 因此所製得的密封材料·表現出極佳安定性,可黏至近戶 基材上並且經約1.5小時之外皮形成時間熟化。 (請先閱讀背面之注意事項再填寫本頁} 心01— — — — — — — — — 線 經濟部智慧財產局員工消費合作社印製 9 11 本紙張尺度適用中國國家標準(CNS)A4規格(210 χ 297公釐)
Claims (1)
1240726 A8 B8 C8 D8 六、申請專利範圍 專利申請案第88118634號 ROC Patent Appln. No.88118634 修正後無劃線之申請專利範圍中文本-附件(一) Amended Claims in Chinese - EncUIII) 5 ^(民國94年7月丨曰送呈) (Submitted on July 丨,200$) 1. 一種含有烷氧基矽烷末端基之聚胺基甲酸酯預聚 物,其可藉下列化合物反應製得的 10 A) 線性聚胺基甲酸酯預聚物,其係由下列化合 物反應所製得的 i) 一種NCO含量為20%至60%之芳族、 脂族或環脂族二異氰酸酯成份與 ii) 一種多元醇成份,其包含一種聚氧基伸 15 烷基二醇當作其主成份而且其分子量為 3000 至 20,000,與 B) 含烷氧基矽烷和胺基之式(I)化合物 ,ΐ CH;——CH——9—(CH2)—Sp-Y ⑴’ 20 io〇R 000R1 Z 經濟部智慧財產局員工消費合作社印製
其中 R和R’ 代表相同或不同的烷基,其係包 含1至8個碳原子, 25 和 X、Y、Z代表相同或不同的烷基或烷氧基, 其係包含1至4個碳原子,條件 為至少一個基團代表烷氧基, -20 - 88365B-接 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 1240726 A8 B8 C8 D8 六、申請專利範圍 特徵在於聚胺基甲酸酯預聚物A)的平均分子 量是從15,000至50,000,如由其NCO含量 和NCO官能度所算得。 2. 根據申請專利範圍第1項之含有烷氧基矽烷末端 5 基之聚胺基甲酸酯預聚物,其特徵在於聚胺基甲 酸酯預聚物A)的平均分子量是從20,000至 40,000,如由其NCO含量和NCO官能度所算得。 3. 根據申請專利範圍第1項之含有烷氧基矽烷末端 基之聚胺基曱酸酯預聚物,其特徵在於最大總不 10 飽和度為0.04毫當量/克和從其OH含量和官能度 所算得的平均分子量為8000至20,000之聚環氧丙 烷聚醚用於生產聚胺基曱酸酯預聚物A)。 4. 根據申請專利範圍第1項之含有烷氧基矽烷末端 基之聚胺基甲酸酯預聚物,其特徵在於彼此獨立 15 的X、Y和Z代表甲氧基或乙氧基。 經濟部智慧財產局員工消費合作社印製 5. 根據申請專利範圍第1項之含有烷氧基矽烷末端 基之聚胺基甲酸酯預聚物,其中式(I)化合物中之R 及R’代表包含1至4個碳原子之相同或不同的烷 基 20 6. —種產生根據申請專利範圍第1至5項中任一項 之含有烷氧基矽烷末端基之聚胺基甲酸酯預聚物 的方法,其藉 A) 如從其NCO含量和NCO官能度所算得之平 均分子量為從15,000至50,000的線性聚胺 -21 - 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 1240726 Α8 Β8 C8 D8 六、申請專利範圍 基甲酸酯預聚物 與 B) 含烷氧基矽烷和胺基之式(I)化合物 CHj-CH-H—(CH2)5 COOR COOR (I), 10 其中 R和R, 和 代表相同或不同的烷基,其係包 含1至8個碳原子, 15 經濟部智慧財產局員工消費合作社印製 20 8. X、Y、Z代表相同或不同的烷基或烷氧 基,其係包含1至4個碳原子, 條件為至少一個基團代表烷氧 基, 反應,特徵在於聚胺基甲酸酯預聚物Α)的平 均分子量是從15,000至50,000,如由其 NCO含量和NCO官能度所算得。 根據申請專利範圍第6項之方法,其中式(I)化合 物中之R及R’代表包含1至4個碳原子之相同或 不同的烷基。 根據申請專利範圍第1項之含有烷氧基矽烷末端 基之聚胺基甲酸酯預聚物,其係用於生產低模數 密封材料。 -22 -
本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐)