TW528579B - Method for producing insole plate for shoes - Google Patents
Method for producing insole plate for shoes Download PDFInfo
- Publication number
- TW528579B TW528579B TW91110301A TW91110301A TW528579B TW 528579 B TW528579 B TW 528579B TW 91110301 A TW91110301 A TW 91110301A TW 91110301 A TW91110301 A TW 91110301A TW 528579 B TW528579 B TW 528579B
- Authority
- TW
- Taiwan
- Prior art keywords
- density
- rubber sheet
- woven fabric
- rolled
- double
- Prior art date
Abstract
Description
528579 ---案號 91110301 五、發明說明(1) 9a L 30528579 --- Case number 91110301 V. Description of the invention (1) 9a L 30
t,明是有關一種鞋之中底板製造方法,特別地H 關該南密度熱可塑性材料、低密度熱町塑性材料、塑= 泡絨布和不織布等四種材料,係同時熱壓成雙密度複H 板’而能具有降低鞋之中底板製造成本、及增強鞋二, 結合強度的產業利用價值者。 &板 查,第八七--二六八0號「鞋中底板之製造方法t, Ming is a method for manufacturing a shoe midsole, especially H. The four materials of the South Density Thermoplastic Material, Low Density Thermoplastic Material, Plastic = Foam Cloth and Non-Woven Cloth are simultaneously hot pressed into a double density compound H-boards can reduce the manufacturing cost of midsole shoes, and enhance the industrial use value of the second combination of strength. & Board check, No. 87-No. 2680 "Manufacturing method of sole plate in shoes
發明專利案,係本案發明人所發明申請的,請參閱第— 至第三圖所示,其係將高密度熱可塑性材料(A )及低漆圖 熱可塑性材料(B )分別經由二送料筒以螺旋輸送至加二度 押出機内,而該呈熔融狀之高、低密度熱可塑性材^ ^八之 (B )於輪送押出至該押出機之模頭(3)時,則會相互熱壓-溶接為一層次分明之長扁狀雙密度膠板(丨〇 )結構,且^ ^ 扁狀雙密度膠板(1 〇 )續經由輾壓機滾筒以輾壓製成適合^ 中底板之厚度,繼而,於該長扁狀雙密度膠板(i 0)底面黏 固有不織布層(2 0 )後’其再經由輾壓機滾筒以輾壓整平 該長扁狀雙密度膠板(1 〇 )結構,隨之,利用裁切機將該長 扁狀雙密度膠板(1 0)裁切成數片具雙密度之鞋型中底板粗 胚(3 0 ),而該中底板粗胚(3 〇 )則再藉由成型模具以熱壓成 ,一具有足跟部位及足掌部位之鞋中底板(4〇 )成品;其缺點 ,乃該案需在長扁狀雙密度膠板(丨〇)底面另外背膠貼合一不 織布層(2 0 ),再利用輾壓機予以輾壓整平,不但費時耗事 ,亦需購置另一台輾壓機,故而其投資費用及加工成本已 不符合時代之需求,且不具競爭力,實乃業者極欲突破者The invention patent case is an application filed by the inventor of this case, please refer to the first to third figures, which are the high-density thermoplastic material (A) and the low-painted thermoplastic material (B) respectively through two feeding barrels Spiral conveying into the second-degree extruder, and the molten high and low-density thermoplastic (^) Eight (B) will be heated to each other when they are extruded to the die head (3) of the extruder. The compression-melting is a long-layered flat double-density rubber sheet (丨 〇) structure, and ^ ^ the flat double-density rubber sheet (1 〇) is continuously rolled by a roller of a roller to make it suitable for the thickness of the middle floor. Then, after the inherently non-woven layer (20) is adhered to the bottom surface of the long flat double-density rubber sheet (i 0), it is then rolled and flattened by the roller of the rolling machine (1 0). ) Structure, and then using a cutting machine to cut the long flat double-density rubber sheet (1 0) into several pieces of double-density shoe-shaped midsole rough embryo (30), and the mid-sole rough embryo ( 3 〇) and then hot forming by a molding mold, a shoe sole plate (4) finished product with heel and foot parts; In this case, a non-woven layer (20) was laminated on the bottom surface of the long flat double-density rubber sheet (丨 〇), and then rolled and leveled by a rolling machine, which was not only time-consuming and time-consuming, but also needed to be purchased Another rolling machine, so its investment and processing costs no longer meet the needs of the times, and it is not competitive.
1363a.ptc 第4頁 528579 dz i, ao1363a.ptc Page 4 528579 dz i, ao
好梦有鐘於此’本案發明人本著乾石乞探究、精勤修習之求 動^珅,配合多年來從事鞋底、鞋墊、鞋中底、釘鞋、運 者=及其相關零配件之製造設計所累積之專業知識及開發 具各經驗’潛心鑽研並歷經實際試作,而提供出一種「^ 之中底板製造方法」,以改進習之缺失。 、告即,本發明之主要目的,係在提供一種鞋之中底板製 2 t法’其高密度熱可塑性材料、低密度熱可塑性材料和 膠發泡絨布、不織布等材料,係同時熱壓成雙密度複合 二板,確可縮減許多製造過程,降低人工成本,並節省投 貧设備,極具產業利用價值者。 本發明之次要目的,係在提供一種鞋之中底板製造^ f ’乃藉由該高密度熱可塑性材料和低密度熱可塑性材米 二炫貼合塑膠發泡絨布層與不織布層,據此增進其間之矣 石強度,進而提昇鞋中底板之品質者。 、 為使貴審查委員對本發明之製造方法、特徵及功岁There is a good dream here "The inventor of this case is based on dry stone begging and diligent practice ^ 珅, cooperate with the manufacturing design of soles, insoles, midsoles, spikes, transporters = and their related parts for many years The accumulated professional knowledge and development have various experiences' with intensive research and practical trials, and provide a "^ middle floor manufacturing method" to improve the lack of learning. That is to say, the main purpose of the present invention is to provide a 2 t method for making sole plates in shoes. Its high-density thermoplastic material, low-density thermoplastic material, rubber foamed flannel, non-woven fabric and other materials are simultaneously hot-pressed into The double-density composite second board can indeed reduce many manufacturing processes, reduce labor costs, and save poor investment equipment, which has great industrial use value. A secondary object of the present invention is to provide a shoe midsole manufacturing ^ f 'by using the high-density thermoplastic material and the low-density thermoplastic material Mi Erxuan to fit the plastic foamed fleece layer and the non-woven fabric layer, and accordingly, Those who increase the strength of vermiculite in the meantime, and then improve the quality of the sole plate in the shoe. In order to make your review committee understand the manufacturing methods, features and functions of the present invention
,點,能獲致更進一步之瞭解,兹舉數較佳實 配合圖式說明于后: J 圖示簡單說明: 程圖 第一圖係第八七一 八〇遽專利案實施例製造流 第二圖係第八七--二六八〇f声直4丨丨安认施You can get a better understanding. The following is a better description of the figures and the description of the diagrams: J The diagram is briefly explained: The first diagram of the process diagram is the second embodiment of the manufacturing flow of the patent of 8778. The picture is the 87th-2680f sound straight 4 丨 丨
材料膠板上裁切鞋型中底板粗胚物料示音圖。 又A 、υ 5虎專利案之鞋中麻拓忐 品立體圖。 释丫展柢成 第三圖係第八七一一二六八〇缺奎也Material rubber board cut the shoe shape mid-sole rough material material audio chart. Also, A, υ 5 Tiger patent case shoes in the case of Ma Tuo products perspective. Shi Ya Zhan Chengcheng The third picture is the 8171, 2680
528579 案號 91110301 92. 年 ai 月 曰 修正528579 Case No. 91110301 Amendment
五、發明說明(3) 第四圖係本發明之 第五圖係本發明藉 板之結構立體示意圖。 第六圖係本發明藉 板之結構側面示意圖。 第七圖係本發明於 胚物料示意圖。 第八圖係本發明所 示意圖。 第九圖係本發明之 第十圖係本發明之 第十一圖係本發明 第十二圖係本發明 第十三圖係本發明 圖號部份: (51)高密度熱可塑 (5 2 )低密度熱可塑 ^ (53)塑膠發泡絨布 (54) 不織布 (55) (55A)(55B)雙 (5 6 )鞋型中底板粗 (5 7 )鞋中底板 (6 0 )押出機 (61)送料筒A 第一較佳實施例 由押出機以熱壓 製造流程圖。 熔合雙密度複合膠 由押出機以熱壓熔合雙密度複合膠 雙密度複合膠板裁切鞋型中底板粗 製成雙密度複合鞋中底板成品結構 第二較佳實施例 第三較佳實施例 之第四較佳實施 之第五較佳實施 之第六較佳實施 性材料 性材料 密度複合膠板 胚V. Description of the invention (3) The fourth figure is a perspective view of the structure of the borrowing plate of the present invention. The sixth figure is a schematic side view of the structure of the borrow board of the present invention. The seventh diagram is a schematic diagram of the present invention on the embryo material. The eighth diagram is a schematic diagram of the present invention. The ninth figure is the tenth figure of the present invention is the eleventh figure of the present invention is the twelfth figure of the present invention is the thirteenth figure of the present invention is the number part of the present invention: (51) High density thermoplastic (5 2 ) Low-density Thermoplastic ^ (53) Plastic Foam Flannel (54) Non-Woven Fabric (55) (55A) (55B) Double (5 6) Shoe Type Midsole Thick (5 7) Shoe Midsole (6 0) Extruder ( 61) The first preferred embodiment of the feeding barrel A is a flow chart of hot pressing by an extruder. Fused double-density composite rubber is cut out of the shoe-shaped midsole by hot extrusion fusion double-density composite glue and double-density composite rubber sheet. The finished structure of the double-density composite shoe mid-sole is the second preferred embodiment and the third preferred embodiment. Fourth preferred implementationFifth preferred implementationFifth preferred implementationSixth preferred implementation
製造流程圖。 製造流程圖。 例製造流程圖 例製造流程圖 例製造流程圖 1363a.ptc 第6頁 528579Manufacturing flowchart. Manufacturing flowchart. Example manufacturing flowchart Example manufacturing flowchart Example manufacturing flowchart 1363a.ptc Page 6 528579
(6 2 )送料筒b (6 3 )模頭 (70)輾壓機 (7 1 )滾筒 (82)(82A)(82B)單密度複合膠板 (8 3 )鞋型中底板粗胚 (8 4 )鞋中底板 凊參閱第四圖至第八圖所示,本發明係一種鞋之中 板製造方法,係將高密度熱可塑性材料(51)及低密度執可 ,性材料(52)各別利用押出機(6〇)之送料筒a (61)及;^料 同^ (62)以螺旋輸送至加熱之模頭(63)内,以使該熔融狀 =同、低始、度熱可塑性材料(5丨)(5 2 )經過輾壓機(7 〇 )之滾 筒(7 1 )輾壓互熱熔接為一層次分明之長扁狀雙密度膠板择 構,其中; " 該高密度熱可塑性材料(51)、低密度熱可塑性材料(5 2)經過輾壓機(70)之滾筒(71)輾壓時,其上、下二面即同 時輸送塑膠發泡絨布(53)與不織布(54)一併輾壓,以令該 塑膠發泡絨布(53)和不織布(54)之間熱熔貼一層雙密度膠 -板’而形成一次成型之雙密度複合膠板(5 5 )的製造方法, 繼而利用裁切機將該雙密度複合膠板(55)裁切成數片鞋型 :底板粗胚(56),而該鞋型中底板粗胚(56)則再藉由成型 模,以熱壓成一具有足跟部位及足掌部位之鞋中底板(5 7) f =、’如此’不但可節省大量的生產設備之投資成本,並 能縮減製造工時’相對降低鞋之中底板(5 7 )元件售價者。(6 2) Feeding cylinder b (6 3) Die head (70) Rolling machine (7 1) Roller (82) (82A) (82B) Single-density composite rubber sheet (8 3) Shoe type middle floor rough embryo (8 4) Shoe midsole: Refer to the fourth to eighth figures. The present invention relates to a method for manufacturing a midsole of a shoe. A high-density thermoplastic material (51) and a low-density material (52) are used. Do not use the feeding barrel a (61) and extruder (60) of the extruder (60); ^ material is the same as ^ (62) spirally conveyed into the heated die (63), so that the molten state = same, low start, warm The plastic material (5 丨) (5 2) is passed through the roller (7 1) of the rolling machine (70) to be welded to each other to form a layered long flat double-density rubber sheet. Among them, " 该 高When the density thermoplastic material (51) and low density thermoplastic material (5 2) are rolled by the roller (71) of the rolling machine (70), the upper and lower sides of the material are simultaneously conveyed with the plastic foamed flannel (53) and The non-woven fabric (54) is rolled together, so that a layer of double-density rubber-sheet is hot-melted between the plastic foamed fleece (53) and the non-woven fabric (54) to form a single-molded double-density composite rubber sheet (5 5) Manufacturing method, following Use a cutting machine to cut the double-density composite rubber sheet (55) into several shoe shapes: the bottom plate rough embryo (56), and the shoe bottom plate rough embryo (56) is then hot-pressed by a forming die. Forming a shoe midsole with heel and sole (5 7) f =, 'So' can not only save a lot of investment costs in production equipment, but also reduce manufacturing man-hours. 'Relatively lower midsole (5 7 ) Component seller.
1363a.ptc 第7頁 528579 案號 91110301 五、發明說明(5) 如第九圖所示,係為本發明鞋之中底板製造方法之第 實施例,該高密度熱可塑性材料(51 )與低密度熱可塑性 |材料(52)乃利用押出機(60)之模頭(63)輪送,經過轆麼機 (7 0 )之滾筒(71 )轆Μ時’其上、下二面即同時輸送不織布 (5 4 )—併輾壓,以令該上、下二層不織布(5 4 )之間埶熔貼 一層雙密度膠板,而形成一次成型之雙密度複合膠板(55α )的製造方法者。 請再參看第十圖所示,係為本發明鞋之中底板製造方 法之第三較佳實施例,該高密度熱可塑性材料及低密 度熱可塑性材料(52)利用押出機(60)之模頭(63)輸送,ς Ϊ過J壓:^之滾筒(71)振壓時,其下面同時輸送不織 :俾使該不織布(54)上面熱溶貼設-層雙 而形 次成型之雙密度複合膠板(55Β)之製 再如第十一圖所示,係為本發明鞋之中 之弟四實施例,係將單密度熱可塑性 -丨製4方法 (60)之一送料筒以螺旋輸送至加埶之=^用押出機 熔融狀之單密产埶w输 ^、 、頭(6 3)内,而使該 |(⑴輾膠板結經過輾壓機(7〇)之滾筒 (71)轆壓^度;:塑二:料(81)於經過輾壓機(70)之滾筒 |與不織布(54)一併输—=即同時輸送塑膠發泡絨布(53) (54)之間熱溶貼—層^板:布(53)和不織布 膠板(82)的製造方法, ^成次成型之單密度複合 方法再利用裁切機將該單密度複合膠板 1363a.ptc 第8頁 5285791363a.ptc Page 7 528579 Case No. 91110301 V. Description of the invention (5) As shown in the ninth figure, this is the first embodiment of the method for manufacturing sole plates in shoes according to the present invention. The high-density thermoplastic material (51) and low Density Thermoplastic | Material (52) is conveyed by the die head (63) of the extruder (60) and passed through the roller (71) of the machine (70). The upper and lower sides are conveyed simultaneously. Non-woven fabric (5 4) —rolling to make a layer of double-density rubber sheet fused between the upper and lower two layers of non-woven fabric (5 4) to form a single-molded double-density composite rubber sheet (55α) By. Please refer to FIG. 10 again, which is a third preferred embodiment of a method for manufacturing a sole plate in a shoe of the present invention. The high-density thermoplastic material and the low-density thermoplastic material (52) use a mold of an extruder (60). The head (63) is conveyed. When the roller (71) is vibrated and pressed by J, the non-woven fabric is conveyed at the same time: The non-woven fabric (54) is hot-melted and placed on top of it. The manufacturing of the density composite rubber sheet (55B) is shown in the eleventh figure, which is the fourth embodiment of the shoe of the present invention. It uses the single-density thermoplastic-one of the four methods (60) to make the feeding barrel to Spiral conveying into the single-density product 熔融, 头, and head (6 3) melted by the extruder, so that the ((rolling rubber sheet knot passes through the roller of the rolling machine (70)) (71) Pressing degree ;: Plastic II: Material (81) is passed through the roller of the rolling machine (70) | and the non-woven fabric (54) is input together-= that the plastic foamed flannel (53) (54) is simultaneously conveyed Hot-melt paste between the layers-the sheet: the manufacturing method of the cloth (53) and the non-woven rubber sheet (82), the single-density composite method of forming a single sheet, and then using a cutting machine to cut the single-density composite rubber sheet 1363a.ptc 8 528 579
(8 2 )裁切成數 9Z L 30 年 月—日 (8 3 )則再藉 位鞋之中底 另請配合 ,該單密度熱 3 )輸送,於經 二面便同時輸 之間熱熔貼設 板(82A)的製 再者,如 方法之第六實 出機(60)之模 輾壓時,其下 不織布(5 4 )上 密度複合膠板 前述為本 做任何形式上 作有關本發明 圖保護之範疇 綜上所述 到降低製造成 用價值與進步 開使用,實已 合理之審查, 胚 部 片鞋型中 由成型模 板(8 4 )成 參閱第十 可塑性材 過輾壓機 送不織布 一層膠板 造方法者 第十三圖 施例,該 頭(6 3 )輸 面便同時 面熱炼貼 (82B)的 發明之較 之限制, 之任何修 底板粗胚 具以熱壓 品者。 -—圖所不 料(81)係 (7 0 )之滾 (5 4 )—併,而形成 〇 所示,係 單密度熱 送,於經 輸送不織 設一層膠 製造方法 佳實施例 是以,凡 倚或變更 (83),而該鞋型中底板粗 成一具有足跟部位及足掌 ’為本發明之第五實施例 利用押出機(60)之模頭(6 筒(Π )輾壓時,其上、下 輾壓,以使該不織布(54) 一次成型之單密度複合膠 為本發明鞋之中底板製造 可塑性材料(8 1)係利用押 過轆壓機(7 〇 )之滾筒(7 1) 布(5 4 )—併輾壓,而使該 板’即形成一次成型之單 者。 ’並非企圖據以對本發明 有在相同之發明精神下所 ’皆仍應包括在本發明意 ’本發明鞋之中底;^ >r原板I艳方法,確實能夠達 :料間之結合強度,極具產業上利 二丄:查申請前並未見於諸刊物,亦未曾公::务明專利之規定,謹請鈞局詳予公平 並早日賜准專利為禱。(8 2) Cut into the number 9Z L 30 months-days (8 3) Then borrow the midsole of the shoes. Please also cooperate with the single density heat 3) Conveying, hot melting between the two sides and then simultaneously feeding For the manufacture of the mounting board (82A), such as when the die of the sixth machine (60) of the method is rolled, the density composite rubber board on the non-woven fabric (5 4) below is made in any form as described above. The scope of protection of the invention map. In summary, it has been reasonably reviewed to reduce the value of manufacturing and use in advance. The shape of the shoe of the embryo part is formed by the molding template (84). Refer to the tenth plastic material. The example of the thirteenth figure of the method of making a layer of non-woven rubber sheet, the head (6 3) loses the surface and simultaneously faces the invention of the hot-rolled paste (82B). . -—Unexpected (81) is (7 0) roll (5 4) —and formed as shown in 0, is a single-density hot-sending, and a layer of glue manufacturing method is the best embodiment, Where it is leaned or changed (83), and the sole plate of the shoe shape is roughened to have a heel part and a sole of the foot, this is the fifth embodiment of the present invention when using the die (6 cylinder (Π) of the extruder (60) when rolling The single-density composite rubber formed by one-time molding of the non-woven fabric (54) as the plastic material (81) of the sole plate of the shoe of the present invention is a roller (pressed by a press machine (70)). 7 1) Cloth (5 4) —and rolled, so that the plate 'forms a one-time-formed order.' It is not an attempt to have the present invention in the same spirit of the invention 'should still be included in the intention of the present invention. 'The midsole of the shoes of the present invention; ^ > r original plate I Yan method, it can indeed achieve: the strength of the combination of materials, which is very industrially advantageous: before the application has not been seen in the publications, nor has it been public :: service To clarify the provisions of patents, I would like to ask the Bureau to give details and to grant patents as soon as possible.
Claims (1)