TW202315546A - 用於化妝墊壓塊的非織造材料 - Google Patents
用於化妝墊壓塊的非織造材料 Download PDFInfo
- Publication number
- TW202315546A TW202315546A TW111128647A TW111128647A TW202315546A TW 202315546 A TW202315546 A TW 202315546A TW 111128647 A TW111128647 A TW 111128647A TW 111128647 A TW111128647 A TW 111128647A TW 202315546 A TW202315546 A TW 202315546A
- Authority
- TW
- Taiwan
- Prior art keywords
- cosmetic
- pad
- pet
- composition
- nonwoven material
- Prior art date
Abstract
由雙組分纖維形成的非織造材料可以用作化妝墊,以將化妝品組合物(例如液體粉底)保持在外殼中,供消費者與施用器一起使用。雙組分纖維的使用可以允許將各種天然或合成材料用於芯和殼,可以調節所述芯和殼以獲得與化妝品組合物的最大相容性。形成非織造材料的雙組分纖維可以是聚對苯二甲酸乙二醇酯(PET)芯/聚乙烯(PE)殼組合物。該PET/PE組合物可以允許與侵蝕性化學成分組合的最大穩定性和耐化學性。使用這些非織造材料的化妝墊可以使消費者感覺到在感覺上愉悅並且在產品的整個壽命期間以最佳品質表現。當填充或浸透產品時,化妝墊也可以看上去美觀。
Description
本公開一般性涉及非織造材料,並且更具體地涉及用於化妝墊壓塊的非織造材料。
化妝品粉底通常包含在具有基材的壓塊內,其通常為可以保持液體化妝品組合物的墊。基材由聚乙烯泡沫、聚氨酯泡沫、丁腈或海綿橡膠或泡沫形成。然而,這些基材可能遭受各種缺點。例如,聚氨酯泡沫限於具有相當窄的黏度特性的化妝品組合物。太稀的產品不能被泡沫保持,而太稠的產品可能不能有效地注入泡沫。在另一個實例中,某些配方可能不能被注入聚氨酯泡沫、丁腈橡膠和類似材料中,因為它們與它們(例如含有有機防曬活性劑的配方)不相容。它們可能吸收紫外活性物質,導致產品在使用時不能表現出足夠的防曬因數(SPF)。已經採用替代材料(例如合成的非織造纖維)作為化妝品纖維的基材。然而,這些類型的非織造纖維不太能夠吸收、保持和均勻地分配化妝品組合物。
本公開的實施方案可以提供用於保持化妝品組合物的化妝墊,所述墊包含:由雙組分纖維形成的非織造材料,所述雙組分纖維的纖維直徑範圍為5-40 μm,優選18-30 μm,其中與由非微纖維形成的墊相比,所述化妝品組合物在由所述非織造材料形成的所述化妝墊上的分佈在整個使用期間保持更穩定。所述雙組分纖維可以選自但不限於:聚對苯二甲酸乙二醇酯(PET)芯/聚乙烯(PE)殼組合物、聚丙烯(PP)/聚丙烯(PP)組合物、聚丙烯(PP)/聚乙烯(PE)組合物、聚對苯二甲酸乙二醇酯(PET)/聚丙烯(PP)組合物及其共混物。所述非織造材料可以至少部分地由來自原生樹脂或再生樹脂的纖維形成。所述墊的厚度可以是約2 mm至20 mm,優選5 mm至15 mm,並且直徑為約20-100 mm。所述墊可以包括加入到所述非織造材料中的一種或多種黏結劑纖維。
所述非織造材料可以由雙組分纖維形成,所述雙組分纖維可以包含聚對苯二甲酸乙二醇酯(PET)芯/聚乙烯(PE)殼組合物。所述非織造材料的密度可以是20-35 kg⁄m
3。所述非織造材料的密度和纖維直徑可以低於由非微纖維形成的化妝墊。所述非織造材料的密度可以高於由聚氨酯形成的化妝墊。所述非織造材料的吸附性可以是0.0900 g/m
2t
5。所述非織造材料的吸附性可以高於由非微纖維形成的化妝墊。所述墊可以通過施加6N的力而具有壓縮距離,其對於乾燥墊與填充有所述化妝品組合物的墊大致相同。
本公開的其它實施方案可以提供用於保持化妝品組合物的化妝墊,所述墊包含:由雙組分纖維形成的非織造材料,所述雙組分纖維具有纖維直徑範圍為5-40 μm,優選18-30 μm的聚對苯二甲酸乙二醇酯(PET)芯/聚乙烯(PE)殼組合物。在100-200次按壓由所述非織造材料形成的墊之間,所述化妝品組合物的分佈可以保持穩定。這反映了與由非微纖維形成的墊相比,所述化妝品組合物在根據本公開的實施方案由所述非織造材料形成的所述化妝墊上的分佈在整個使用期間保持更穩定。所述非織造材料的密度和纖維直徑可以低於由非微纖維形成的化妝墊。所述非織造材料的密度可以高於由聚氨酯形成的化妝墊。所述非織造材料的吸附性可以高於由非微纖維形成的化妝墊。
本公開的進一步的實施方案可以提供用於保持化妝品組合物的化妝墊,所述墊包含:由雙組分纖維形成的非織造材料,所述雙組分纖維選自但不限於:聚對苯二甲酸乙二醇酯(PET)芯/聚乙烯(PE)殼組合物、聚丙烯(PP)/聚丙烯(PP)組合物、聚丙烯(PP)/聚乙烯(PE)組合物、聚對苯二甲酸乙二醇酯(PET)/聚丙烯(PP)組合物及其共混物,其中所述化妝墊可以通過施加6N的力而具有壓縮距離,其對於乾燥墊與填充有所述化妝品組合物的墊大致相同。所述非織造材料的密度和纖維直徑可以低於由非微纖維形成的化妝墊,並且所述非織造材料的吸附性可以高於由非微纖維形成的化妝墊。
從以下附圖、描述和請求項中,其它技術特徵對於本領域技術人員來說可以是顯而易見的。
本公開的實施方案可以提供由雙組分纖維形成的非織造材料,所述非織造材料可以用作化妝墊,以將化妝品組合物(例如液體粉底)保持在外殼中,供消費者與施用器一起使用。根據本公開的實施方案的非織造材料可以優化材料結構和美觀性以用於多種組合物。使用根據本公開的實施方案的非織造材料的化妝墊可以使消費者感覺到在感覺上愉悅並且在產品的整個壽命期間以最佳品質表現。當填充或浸透產品時,化妝墊也可以看上去美觀。
非織造材料是各種纖維類型的無規纏結,例如通過梳理、交叉鋪網和/或黏合方法形成的雙組分纖維,所述方法包括但不限於熱黏合、針刺和/或水刺。在本公開的實施方案中使用雙組分纖維可以允許將各種天然或合成材料用於芯和殼,其可被調節以與化妝品組合物具有最大相容性。根據本公開的實施方案形成非織造材料的雙組分纖維可以包括聚對苯二甲酸乙二醇酯(PET)芯/聚乙烯(PE)殼組合物。該PET/PE組合物可以允許與侵蝕性化學成分組合的最大穩定性和耐化學性,如本文更詳細地討論的。雖然在本公開的實施方案中描述了具有PET/PE組合物的非織造材料,但是在不偏離本公開的情況下可以使用材料的其它組合,包括但不限於聚丙烯(PP)/聚丙烯(PP)、聚丙烯(PP)/聚乙烯(PE)、聚對苯二甲酸乙二醇酯(PET)/聚丙烯(PP)及其共混物。應當理解,在不偏離本公開的情況下,可以加入在較高或較低溫度下熔融的黏結劑纖維以改變結構。
如所反映的,例如,通過本文所述的分析,消費者可以在美學和感官上優選由非織造微纖維(例如PET/PE材料)形成的化妝墊。根據本公開的實施方案用於化妝墊的微纖維沖切材料可以保持最好具有200-400 gsm基重和250-400 cfm透氣率的配方。根據本公開的實施方案的化妝墊材料的厚度可以是約2 mm至20 mm,優選5 mm至15 mm,並且直徑為約20-100 mm。應當理解,根據本公開的實施方案形成化妝墊的材料可以是圓形的;然而,在不偏離本公開的情況下,材料或墊本身可以假定其它形狀。還應當理解,根據本公開的實施方案的非織造材料可以由來自原生樹脂或再生樹脂的纖維製成,以便更具可持續性。
進行各種實驗分析以評價根據本公開的實施方案的PET/PE非織造材料的彈性和吸收性。這些分析通過調節纖維材料、直徑、橫截面形狀、剛性以及纖維黏合、基重和製造中使用的其它方法參數來進行。PET/PE非織造材料允許來自PET的剛性和來自PE的柔性的平衡,導致在整個使用期間更一致的結構。另外,選擇小的纖維直徑(例如微纖維)以產生更大的孔並增加孔隙率和吸附性。將PET/PE分析與現有聚氨酯(PU)泡沫和現有化妝品材料(ECM) (即,非微纖維)進行比較。各種化妝墊材料的表徵包括評價纖維直徑(如果適用)、密度以及吸附性。PET/PE、PU和ECM的材料規格在表1中闡述。
使用掃描電子顯微鏡(SEM)評價各種材料的纖維直徑。圖1描述根據本公開的實施方案,具有SEM圖像的填充的化妝墊的美學外觀。PET/PE材料具有18-30 μm的纖維直徑範圍,20-35 kg⁄m
3密度,如上表1中所反映的。如在表1中所反映的,根據本公開的實施方案的PET/PE材料具有比PU泡沫更大的密度和比ECM更大的吸附性,允許材料保持較高黏度的產品。類似地,PET/PE微纖維材料的吸附性或材料通過毛細作用吸收水的能力大於ECM,並且更像PU。
為了評價各種化妝墊材料的彈性,還評價了壓縮和恢復。通過在沖切材料的整個表面區域上施加6N的力,評價壓縮距離,比較PU、ECM和PET/PE的乾燥材料相對於填充的/浸透的材料。圖2描述根據本公開的實施方案,通過施加6N的力,對於乾燥材料相對於填充的/浸透的材料,壓縮距離的圖形比較。如在圖2中反映的,與PU (0.90 mm相對於5.67 mm)和ECM (2.57 mm相對於5.12 mm)相比,對於乾燥材料和填充的/浸透的PET/PE材料,壓縮距離(以毫米計)彼此最相似(4.57 mm相對於4.45 mm)。考慮到PET/ PE材料的壓縮距離的相似性,與由PU材料或ECM形成的墊相比,消費者可以在整個產品壽命週期(即,隨著墊被抽空)體驗根據本公開的實施方案由PET/PE材料形成的墊的更一致的性能。
中心位置測試和模擬消費者評審證實,與PU材料或ECM相比,根據本公開的實施方案,PET/PE材料在每次按壓時獲得或負載的產品的量的一致性表現更好。在100-200次按壓由PET/PE材料形成的墊之間,粉底分佈保持穩定。因此,與由非微纖維形成的墊相比,化妝品組合物在由PET/PE材料形成的化妝墊上的分佈在整個使用期間保持更穩定。測試反映PET/PE材料在每次按壓所獲得的產品的量上具有較小的變化,指示當與PU材料或ECM相比時,在所獲得的量的一致性上具有更好的性能。
使用Thwing-Albert壓縮/柔性儀器測量PU和PET/PE材料的恢復或返回到其初始厚度的化妝墊的記憶。壓縮和恢復可以以滯後的形式記錄。圖3描述根據本公開的實施方案,PU和PET/PE材料的化妝品材料滯後曲線。如本文所述,該曲線開始於測量當施加壓力(1.5 psi/17.5N力)時材料的厚度(以毫米測量)變化。當壓力釋放時,可以繼續測量厚度變化,並且由材料形成的墊返回到其初始厚度。在圖3中描述的曲線反映了PU材料在壓縮和恢復之間具有較大的面積,表示“柔軟”的感覺和逐漸的恢復時間。相反,PET/PE的滯後表示壓縮的立即和相同的恢復(即,PET/PE比PU材料更一致)。
圖4描述根據本公開的實施方案,化妝墊相容性特徵。更具體地,圖4描述可以在墊內評價化妝品的彙集的情況。在本公開的實施方案中,厚度和彈性(springiness)/彈性(resilience)也可以與表面光滑度和美觀、化學相容性和/或填充容易度/不均勻填充一起測量。例如,通過條件處理材料總共四周來評價浸透防曬成分的化妝墊的行為。將每種類型的樣品在50℃下條件處理以與室溫樣品比較。所有這三種材料(PU、PET/PE和ECM)保留材料記憶和吸收性。一些不相容的特性將是硬度或顯著的壓縮和產品在表面上彙集。
對於在條件處理後用6 N施加力進行壓縮,測試每種材料的相容性樣品。將這些結果與初始壓縮結果進行比較。圖5描述根據本公開的實施方案,使用6 N施加力的相容性壓縮的比較。更具體地說,從樣品(PU、ECM、PET/PE)被填充的時間、在室溫下填充後4周和在50℃下4周,比較樣品(PU、ECM、PET/PE)的壓縮距離(mm)。如在圖5中所反映的,當與PU材料和ECM相比時,PET/PE材料從初始填充到在室溫和50℃兩者下4周的百分比變化較小。因此,這些結果反映PET/PE材料可以在整個產品壽命期間表現一致。
填充效率對於用選擇的化妝墊的生產是重要的。在填充材料時觀察到的客觀機器參數包括但不限於活塞速度、按壓時間和上升延遲。表2顯示根據本公開的實施方案,PU材料相對於PET/PE材料,這些參數如何增加/減小。如在表2中所反映的,PET/PE材料增加活塞填充速度和上升延遲,並減少按壓時間;這些參數反映根據本公開的實施方案的PET/PE材料比PU材料更快填充。
通過模擬消費者使用化妝墊來評價通過施加力以及使用前後材料比較的產品擠出。從由PU材料以及ECM (非微纖維材料)和PET/PE材料形成的墊材料中抽空產品。表3反映用過的材料和填充的、未用過的材料(新的)之間的差異。
如在表3中描述的,PU材料厚度保持相當,而ECM從使用時變得略微壓縮並且從未完全恢復。隨著消費者的使用,用於將產品從墊材料中抽空的力增加,因為較少的產品保留在基材中。平均而言,施加到ECM的力大於PU材料,具有較少的產品擠出。然而,在第一次施用和100/200/300次按壓後通過中心位置測試,ECM和PET/PE材料的質地和外觀之間沒有顯著差異。
圖6描述根據本公開的實施方案,通過粉撲施加力(N),對於PU材料、PET/PE材料和ECM的產品擠出(g)。如在圖6中所反映的,PET/PE材料在整個使用期間具有一致的產品負載,而PU材料具有較大的變化。
圖7描述根據本公開的實施方案,通過中心位置測試,關於每次按壓所獲得的量,ECM與PET/PE材料的圖形比較。如本文所反映的,在整個使用期間,當與ECM (200-250次按壓期間,63%變化)相比時,PET/PE材料的產品獲得更一致(200-250次按壓期間,47%變化)。這與模擬消費者使用測試結果一致。因此,與PU材料或ECM相比,消費者將感覺到在整個產品壽命週期內由根據本公開的實施方案的PET/PE材料形成的墊具有一致的性能。
進一步的測試證實,與由ECM形成的墊相比,根據本公開的實施方案由PET/PE材料形成的墊在限定區域(Sa)內的每個點處表現出更大的平均高度值(圖8)(圖9) (174.32 µm 相對於116.69 µm)。峰和穀更佔優勢,觀察到降低產物負載。這種測試通過消費者使用研究進一步證實。
儘管已經詳細描述了本公開及其優點,應當理解,在不偏離由所附請求項限定的本公開的精神和範圍的情況下,可以對本文進行各種改變、替換和變更。此外,本申請的範圍不旨在限於說明書中描述的過程、機器、製造、物質組成、裝置、方法和步驟的特定實施方案。如本領域普通技術人員將從本公開容易理解的,根據本公開,可以利用目前存在的或以後開發的執行與本文描述的相應的實施方案基本相同功能或實現基本相同結果的過程、機器、製造、物質組成、裝置、方法或步驟。因此,所附請求項旨在將這樣的過程、機器、製造、物質組成、裝置、方法或步驟包括在其範圍內。
為了更完整地理解本公開,現在結合附圖參考以下描述,在附圖中:
[圖1]描述根據本公開的實施方案,具有掃描電子顯微鏡(SEM)圖像的填充的化妝墊的美學外觀;
[圖2]描述根據本公開的實施方案,對於乾燥材料相對於填充的/浸透的材料,通過施加6N的力而具有的壓縮距離的圖形比較;
[圖3]描述根據本公開的實施方案,化妝品材料滯後曲線;
[圖4]描述根據本公開的實施方案,化妝墊相容性特徵;
[圖5]描述根據本公開的實施方案,具有6 N施加力的相容性壓縮;
[圖6]描述根據本公開的實施方案,通過粉撲施加力的產品擠出(payoff);
[圖7]描述根據本公開的實施方案,通過中心位置測試的每次按壓所獲得的量的圖形比較;
[圖8]描述對於ECM的Sa測試;和
[圖9]描述根據本公開的實施方案的PET/PE材料的Sa測試。
Claims (20)
- 一種用於保持化妝品組合物的化妝墊,所述墊包含: 由雙組分纖維形成的非織造材料,所述雙組分纖維的纖維直徑範圍為18-30 μm, 其中與由非微纖維形成的墊相比,所述化妝品組合物在由所述非織造材料形成的所述化妝墊上的分佈在整個使用期間保持更穩定。
- 如請求項1所述的化妝墊,所述雙組分纖維選自: 聚對苯二甲酸乙二醇酯(PET)芯/聚乙烯(PE)殼組合物、聚丙烯(PP)/聚丙烯(PP)組合物、聚丙烯(PP)/聚乙烯(PE)組合物、聚對苯二甲酸乙二醇酯(PET)/聚丙烯(PP)組合物及其共混物。
- 如請求項1所述的化妝墊,所述雙組分纖維包含: 聚對苯二甲酸乙二醇酯(PET)芯/聚乙烯(PE)殼組合物。
- 如請求項1所述的化妝墊,所述非織造材料至少部分地由來自原生樹脂或再生樹脂的纖維形成。
- 如請求項1所述的化妝墊,其厚度為約2 mm至20 mm。
- 如請求項1所述的化妝墊,其直徑為約20-100 mm。
- 如請求項3所述的化妝墊,所述非織造材料的密度為20-35 kg⁄m 3。
- 如請求項7所述的化妝墊,其中所述非織造材料的密度和纖維直徑低於由非微纖維形成的化妝墊。
- 如請求項7所述的化妝墊,其中所述非織造材料的密度高於由聚氨酯形成的化妝墊。
- 如請求項3所述的化妝墊,所述非織造材料的吸附性為0.0900 g/m 2t 5。
- 如請求項9所述的化妝墊,其中所述非織造材料的吸附性高於由非微纖維形成的化妝墊。
- 如請求項1所述的化妝墊,進一步包含: 加入到所述非織造材料中的一種或多種黏結劑纖維。
- 如請求項3所述的化妝墊,通過施加6N的力而具有壓縮距離,其對於乾燥墊與填充有所述化妝品組合物的墊大致相同。
- 一種用於保持化妝品組合物的化妝墊,所述墊包含: 由雙組分纖維形成的非織造材料,所述雙組分纖維具有纖維直徑範圍為18-30 μm的聚對苯二甲酸乙二醇酯(PET)芯/聚乙烯(PE)殼組合物。
- 如請求項14所述的化妝墊,其中與由非微纖維形成的墊相比,所述化妝品組合物在由所述非織造材料形成的所述化妝墊上的分佈在整個使用期間保持更穩定。
- 如請求項14所述的化妝墊,其中所述非織造材料的密度和纖維直徑低於由非微纖維形成的化妝墊。
- 如請求項14所述的化妝墊,其中所述非織造材料的密度高於由聚氨酯形成的化妝墊。
- 如請求項14所述的化妝墊,其中所述非織造材料的吸附性高於由非微纖維形成的化妝墊。
- 一種用於保持化妝品組合物的化妝墊,所述墊包含: 由雙組分纖維形成的非織造材料,所述雙組分纖維選自: 聚對苯二甲酸乙二醇酯(PET)芯/聚乙烯(PE)殼組合物、聚丙烯(PP)/聚丙烯(PP)組合物、聚丙烯(PP)/聚乙烯(PE)組合物、聚對苯二甲酸乙二醇酯(PET)/聚丙烯(PP)組合物及其共混物, 其中所述化妝墊通過施加6N的力而具有壓縮距離,其對於乾燥墊與填充有所述化妝品組合物的墊大致相同。
- 如請求項19所述的化妝墊,其中所述非織造材料的密度和纖維直徑低於由非微纖維形成的化妝墊,和 其中所述非織造材料的吸附性高於由非微纖維形成的化妝墊。