RU2508264C1 - Wood concrete mixture - Google Patents

Wood concrete mixture Download PDF

Info

Publication number
RU2508264C1
RU2508264C1 RU2012145509/03A RU2012145509A RU2508264C1 RU 2508264 C1 RU2508264 C1 RU 2508264C1 RU 2012145509/03 A RU2012145509/03 A RU 2012145509/03A RU 2012145509 A RU2012145509 A RU 2012145509A RU 2508264 C1 RU2508264 C1 RU 2508264C1
Authority
RU
Russia
Prior art keywords
water
concrete mixture
gypsum
portland cement
wood concrete
Prior art date
Application number
RU2012145509/03A
Other languages
Russian (ru)
Inventor
Юлия Алексеевна Щепочкина
Original Assignee
Юлия Алексеевна Щепочкина
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Юлия Алексеевна Щепочкина filed Critical Юлия Алексеевна Щепочкина
Priority to RU2012145509/03A priority Critical patent/RU2508264C1/en
Application granted granted Critical
Publication of RU2508264C1 publication Critical patent/RU2508264C1/en

Abstract

FIELD: chemistry.
SUBSTANCE: wood concrete mixture contains, wt %: portland cement 41.5-45; hogged chips 27.2-29.2; gypsum 0.5-1; ethylhydrosiloxane polymer 0.3-0.5; capron fibre cut to 3-30 mm pieces 0.3-0.5; water 26-28.
EFFECT: high frost resistance of articles made from the wood concrete mixture.
1 tbl

Description

Изобретение относится к промышленности строительных материалов, в частности к производству изделий (блоков) из древесно-цементных композиций, используемых преимущественно в сельском строительстве.The invention relates to the building materials industry, in particular to the production of products (blocks) from wood-cement compositions used mainly in rural construction.

Известна арболитовая смесь, содержащая, мас.%: цемент (портландцемент) 47-52; древесную дробленку 30-33; гипс 1-3; известь 9-15; хлорид кальция 2-6,5 [1].Known arbolite mixture containing, wt.%: Cement (Portland cement) 47-52; wood chips 30-33; gypsum 1-3; lime 9-15; calcium chloride 2-6.5 [1].

Задача изобретения состоит в повышении морозостойкости изделий из арболитовой смеси.The objective of the invention is to increase the frost resistance of articles made of arbolite mixture.

Технический результат достигается тем, что арболитовая смесь, содержащая портландцемент, древесную дробленку, гипс, воду, дополнительно содержит полимер этилгидросилоксана и нарезанное на отрезки 3-30 мм капроновое волокно, при следующем соотношении компонентов, мас.%: портландцемент 41,5-45; древесная дробленка 27,2-29,2; гипс 0,5-1; полимер этилгидросилоксана 0,3-0,5; нарезанное на отрезки 3-30 мм капроновое волокно 0,3-0,5; вода 26-28.The technical result is achieved by the fact that the arbolite mixture containing Portland cement, wood chips, gypsum, water, additionally contains a polymer of ethylhydrosiloxane and nylon fiber cut into segments of 3-30 mm, in the following ratio, wt.%: Portland cement 41.5-45; wood chips 27.2-29.2; gypsum 0.5-1; ethyl hydrosiloxane polymer 0.3-0.5; cut into segments of 3-30 mm nylon fiber 0.3-0.5; water 26-28.

Составы арболитовой смеси приведены в таблице.The compositions of the arbolite mixture are shown in the table.

КомпонентыComponents Содержание, мас.%:Content, wt.%: состав №1composition No. 1 состав №2composition No. 2 ПортландцементPortland cement 41,541.5 4545 Древесная дробленкаWood chippings 29,229.2 27,227,2 ГипсGypsum 0,50.5 1one Полимер этилгидросилоксанаEthyl Hydrosiloxane Polymer 0,30.3 0,50.5 Нарезанное на отрезки 3-30 мм капроновое волокно3–30 mm nylon fiber cut into pieces 0,50.5 0,30.3 ВодаWater 2828 2626 Морозостойкость, циклыFrost resistance cycles ~25~ 25 ~25~ 25

Арболитовую смесь приготовляют следующим образом.Arbolite mixture is prepared as follows.

Проводят дозированне компонентов смеси. Древесную дробленку замачивают в водопроводной воде на 1-2 сут. Портландцемент смешивают с гипсом, нарезанным на отрезки 3-30 мм капроновым волокном, добавляют воду, полимер этилгидросилоксана, а затем древесную дробленку. При расчете количества добавляемой в смесь воды учитывается влага, содержащаяся в древесной дробленке. В случае необходимости в смесь добавляют воду или, наоборот, замоченную древесную дробленку отжимают для достижения требуемого водоцементного отношения. Полученную арболитовую смесь укладывают в форму, уплотняют и оставляют до затвердевания. Извлеченное из формы изделие выдерживают при комнатной температуре не менее 28 сут. Прочность полученных изделий при сжатии составляет не менее 5 МПа.Spend dosage components of the mixture. Wood chips are soaked in tap water for 1-2 days. Portland cement is mixed with gypsum, cut into segments of 3-30 mm nylon fiber, water, ethylhydrosiloxane polymer, and then wood chips are added. When calculating the amount of water added to the mixture, the moisture contained in the wood chips is taken into account. If necessary, water is added to the mixture, or, conversely, the soaked wood chips are pressed to achieve the desired water-cement ratio. The resulting arbolite mixture is laid in a mold, compacted and left to solidify. The product removed from the mold is kept at room temperature for at least 28 days. The compressive strength of the obtained products is not less than 5 MPa.

Источник информацииThe source of information

1. Патент №2058967 РФ, 2005.1. Patent No. 2059567 of the Russian Federation, 2005.

Claims (1)

Арболитовая смесь, содержащая портландцемент, древесную дробленку, гипс, воду, отличающаяся тем, что дополнительно содержит полимер этилгидросилоксана и нарезанное на отрезки 3-30 мм капроновое волокло, при следующем соотношении компонентов, мас.%: портландцемент 41,5-45; древесная дробленка 27,2-29,2; гипс 0,5-1; полимер этилгидросилоксана 0,3-0,5; нарезанное на отрезки 3-30 мм капроновое волокно 0,3-0,5; вода 26-28. Arbolite mixture containing Portland cement, wood chips, gypsum, water, characterized in that it further comprises a polymer of ethylhydrosiloxane and a capron fiber cut into sections of 3-30 mm, in the following ratio, wt.%: Portland cement 41.5-45; wood chips 27.2-29.2; gypsum 0.5-1; ethyl hydrosiloxane polymer 0.3-0.5; cut into segments of 3-30 mm nylon fiber 0.3-0.5; water 26-28.
RU2012145509/03A 2012-10-25 2012-10-25 Wood concrete mixture RU2508264C1 (en)