RU2316489C1 - Стекло - Google Patents
Стекло Download PDFInfo
- Publication number
- RU2316489C1 RU2316489C1 RU2006130072/03A RU2006130072A RU2316489C1 RU 2316489 C1 RU2316489 C1 RU 2316489C1 RU 2006130072/03 A RU2006130072/03 A RU 2006130072/03A RU 2006130072 A RU2006130072 A RU 2006130072A RU 2316489 C1 RU2316489 C1 RU 2316489C1
- Authority
- RU
- Russia
- Prior art keywords
- glass
- tio
- cao
- mgo
- sio
- Prior art date
Abstract
Изобретение относится к области технологии силикатов, в частности к составам стекла, которое может быть использовано в производстве изделий хозяйственно-бытового назначения, посуды. Технический результат - повышение термостойкости стекла. Стекло содержит, мас.%: SiO2 50,0-55,0; Al2О3 8,0-12,0; TiO2 1,0-2,0; CaO 8,0-12,0; MgO 3,0-7,0; К2О 4,0-6,0; В2О3 16,0-17,0. 1 табл.
Description
Изобретение относится к области технологии силикатов, в частности к составам стекла, которое может быть использовано в производстве изделий хозяйственно-бытового назначения, посуды.
Известно стекло, включающее SiO2, Al2O3, TiO2, CaO, MgO, K2O, B2O3 и другие компоненты /1/.
Известно стекло, содержащее, мас.%: SiO2 54,4-61,2; Al2O3 12,0-17,2; Fe2O3 0,3-3,4; TiO2 0,01-0,6; CaO 7,07-8,6; MgO 0,12-1,5; K2O 2,5-3,2; Na2O 10,2-13,0; F' 1,4-3,1 /2/.
Цель изобретения состоит в повышении термостойкости стекла.
Цель достигается тем, что стекло дополнительно содержит B2O3, при следующем соотношении компонентов, мас.%: SiO2 50,0-55,0; Al2O3 8,0-12,0; TiO2 1,0-2,0; CaO 8,0-12,0; MgO 3,0-7,0; K2O 4,0-6,0; B2O3 16,0-17,0.
В таблице приведены составы стекла.
Таблица | ||||||||
Состав | Компоненты, мас.%: | Термостойкость, | ||||||
SiO2 | Al2O3 | TiO2 | CaO | MgO | K2O | B2O3 | °C | |
1 | 50,0 | 12,0 | 2,0 | 12,0 | 3,0 | 4,0 | 17,0 | 200-220 |
2 | 52,5 | 10,0 | 1,5 | 10,0 | 5,0 | 5,0 | 16,0 | 200-220 |
3 | 55,0 | 8,0 | 1,0 | 8,0 | 6,0 | 6,0 | 16,0 | 200-220 |
Источники информации
1. Патент Великобритании №1454335, С1М, 1976.
2. Авторское свидетельство СССР №1477701, С03С 3/087, 3/112 1989.
Claims (1)
- Стекло, содержащее SiO2, Al2О3, TiO2, CaO, MgO, K2O, отличающееся тем, что дополнительно содержит В2О3 при следующем соотношении компонентов, мас.%:
SiO2 50,0-55,0 Al2O3 8,0-12,0 TiO2 1,0-2,0 CaO 8,0-12,0 MgO 3,0-7,0 K2O 4,0-6,0 В2О3 16,0-17,0