Abstract

FIELD: building materials, production of decorating building pieces, tat is facing panels used for finishing works in houses, public, administration and other buildings. SUBSTANCE: to increase decorating properties of pieces and to decrease labour consumption of their production process flat surface of formation is degreased, wetted with water solution, then it is applied with dry binding substance forming decorative layer simultaneously with conglomerate inclusions of drawing texture. Then using tempered binder base layer is applied on piece and held till its solidification. Then formation is taken away and piece is covered with adhesive substance. EFFECT: increased decorating properties and decreased labour consumption of their production. 3 cl

Description

Изобретение относится к производству декоративных строительных изделий, а именно облицовочных панелей, применяемых для отделки помещений, общественных, административных и других зданий. The invention relates to the production of decorative building products, namely facing panels used for decoration of premises, public, administrative and other buildings.

Известны способы изготовления декоративных изделий, включающие нанесение декоративного, пигментированного слоя, покрытие его слоем основы, содержащим вяжущее с последующей выдержкой и расформовкой изделий (авт.св. 627102, М кл. C 04 B 27/04, 1976 г. авт.св. 1549791, М кл. B 32 B 13/00, 1987 г.). Known methods for the manufacture of decorative products, including applying a decorative, pigmented layer, coating it with a base layer containing a binder, followed by exposure and stripping of the products (ed. St. 627102, M class. C 04 B 27/04, 1976, ed. 1549791, M CL B 32 B 13/00, 1987).

Однако известные способы трудоемки, непроизводительны, а изделия имеют низкую декоративность, т. к. способ не позволяет регламентировать текстуру имитируемого рисунка камня и расширить диапазон имитируемых пород естественного камня. However, the known methods are time-consuming, unproductive, and the products have low decorativeness, because the method does not allow to regulate the texture of the simulated stone pattern and expand the range of simulated rocks of natural stone.

Наиболее близким по технической сущности является способ изготовления плит искусственного мрамора, заключающийся в нанесении на гладкую поверхность формы по заданному рисунку текстуры камня смеси сухого вяжущего с пигментом, нанесении сухого слоя вяжущего основы, выравнивании, затворении вяжущего в форме клеевой водой с последующими выдержкой до полного отверждения, расформовкой, шлифовкой и полировкой изделия. (УДК 666, П.С. Симановский, "Искусственный мрамор", М. Госиздат по архитектуре и строительству, 1950, с. 80 8, 57 63). The closest in technical essence is a method of manufacturing artificial marble slabs, which consists in applying a mixture of a dry binder with a pigment on a smooth surface of a mold according to a given pattern of stone texture, applying a dry layer of a binder base, leveling, mixing the binder in the form of adhesive water, followed by exposure to complete curing , decorating, grinding and polishing the product. (UDC 666, PS Simanovsky, “Artificial Marble”, M. State Publishing House on Architecture and Construction, 1950, p. 80 8, 57 63).

Недостатком известного способа является наличие трудоемких подготовительных операций при воссоздании заданной текстуры рисунка, требующих определенных художественных и профессиональных навыков у исполнителей, сложная и трудоемкая добавка лицевой поверхности изделия. The disadvantage of this method is the presence of time-consuming preparatory operations when reconstructing a given texture of the pattern, requiring certain artistic and professional skills of the performers, a complex and time-consuming addition of the front surface of the product.

В изделиях, получаемых известным способом, трудно получить плавные переходы цветов рисунка имитируемого камня, т.к. вяжущее различных цветов насыпается раздельно, а конгламератные включения однообразны ввиду того, что это достигается укладкой большей порции вяжущего определенного цвета и навыком исполнителя. Качество лицевой поверхности плиты требует добавки, т.к. способ не исключает возможности появления раковин на участках нижних слоев, где не затворилось вяжущее, что затруднительно проверить при изготовлении изделий "лицом вниз". Все это усложняет известный способ, снижает декоративность и качество изделий. In products obtained in a known manner, it is difficult to obtain smooth transitions of colors of the pattern of the simulated stone, because a binder of various colors is poured separately, and the conglomerate inclusions are uniform in view of the fact that this is achieved by laying a larger portion of a binder of a certain color and the skill of the performer. The quality of the front surface of the plate requires additives, as the method does not exclude the possibility of the appearance of shells in areas of the lower layers where the binder is not shut, which is difficult to verify in the manufacture of products "face down". All this complicates the known method, reduces the decorativeness and quality of products.

Для снижения трудоемкости изготовления изделия и повышения его декоративности в способе изготовления декоративного изделия из минерального вяжущего вещества, включающем затворение на гладкой поверхности формования сухого вяжущего вещества декоративного пигментированного слоя, в том числе с текстурой рисунка, имеющий конгламератные включения, нанесение слоя основы, выдержку до полного отверждения и расформировку изделия, поверхность формования обезжиривают, вяжущее пигментированного слоя наносят на предварительно смоченную поверхность формования до исчезновения текстуры рисунка, слой основы формируют раствором затворенного вяжущего, а декоративную поверхность расформованного изделия покрывают адгезизом. To reduce the complexity of manufacturing the product and increase its decorativeness in the method of manufacturing a decorative product from a mineral binder, including mixing a decorative pigmented layer on a smooth molding surface of a dry binder, including with a pattern texture, having conglomerate inclusions, applying a base layer, exposure to full curing and deformation of the product, the molding surface is degreased, the binder of the pigmented layer is applied to a previously wetted surface the formation of the mold until the texture disappears, the base layer is formed with a solution of the closed binder, and the decorative surface of the deformed product is coated with adhesion.

В случае необходимости изготовления изделий, имеющих текстуру рисунка с конгламератными включениями, эти места после обезжиривания смазывают жировым раствором или после смачивания поверхности формования в этих местах наносят спирт каплями. If it is necessary to manufacture products having the texture of a pattern with conglomerate inclusions, these areas after degreasing are greased with a fat solution or after wetting the molding surface in these places, alcohol is applied in drops.

Способ изготовления декоративного изделия реализуют следующим способом. A method of manufacturing a decorative product is implemented as follows.

Изделие изготавливается "лицом книзу". Гладкую, горизонтально расположенную поверхность формования обезжиривают уайт-спиртом или другим известным обезжиривающим средством и покрывают душирующим потоком воды, содержащим упрочняющие и гидрофобные добавки из расчета 0,5 3% от массы воды, необходимой для затворения вяжущего декоративного слоя толщиной 1 2 мм. В зависимости от породы имитируемого камня, текстуры рисунка, цвета основного фона, разводов, прожилок, конгламератных включений на смоченную поверхность наносят раствор красителей, составляющих 0,5 5% от массы вяжущего, а для темного основного фона до 17 20% Затем ровным слоем произвольно наносят вяжущее до исчезновения свободной жидкости. The product is made "face down". The smooth, horizontally located molding surface is degreased with white alcohol or another known degreasing agent and coated with a fragrant water stream containing hardening and hydrophobic additives at the rate of 0.5–3% of the mass of water necessary for mixing the cementitious decorative layer with a thickness of 1 2 mm. Depending on the breed of the simulated stone, the texture of the pattern, the color of the main background, stains, veins, and conglomerate inclusions, a solution of dyes is applied to the wetted surface, constituting 0.5 to 5% by weight of the binder, and for a dark main background to 17 to 20% Then, with an even layer randomly apply an astringent until the disappearance of free fluid.

В качестве вяжущего используют гипс, фосфогипс, портланд-цемент, магнезит, известь. As a binder, gypsum, phosphogypsum, Portland cement, magnesite, lime are used.

В качестве упрочняющей и гидрофобной добавки используют карбамидную смолу, латекс, известково-канифольную эмульсию, добавки на основе полисилоксанов и др. As a hardening and hydrophobic additive, urea resin, latex, a calc-rosin emulsion, additives based on polysiloxanes and others are used.

Краситель можно также в сухом виде добавлять в вяжущее, а форму в этом случае смачивают только водой с добавками. The dye can also be added in a dry form to the binder, and in this case the form is moistened only with water with additives.

В случае наличия конгламератных включений в текстуре рисунка декоративного слоя в местах их расположения обезжиренную поверхность формования смазывают жировым раствором, например керосином, а затем покрывают водным раствором с добавками, раствором красителей. В этом случае на жировых пятнах поверхности водный раствор не растекается, а собирается каплями различной величины. При нанесении вяжущего последнее как бы стекает по краям этих капель, образуя контрастные очертания на их краях. Форма включений зависит от формы жирового пятна и образовавшихся капель жидкости и др. In the case of the presence of conglomerate inclusions in the texture pattern of the decorative layer at their locations, the defatted molding surface is greased with a fat solution, for example kerosene, and then coated with an aqueous solution with additives, a dye solution. In this case, the aqueous solution does not spread on the grease spots on the surface, but is collected in drops of various sizes. When applying a binder, the latter, as it were, drains along the edges of these drops, forming contrasting outlines on their edges. The form of inclusions depends on the shape of the grease stain and the resulting drops of liquid, etc.

Конгламератные включения в текстуре рисунка декоративного слоя можно получить также путем нанесения на обезжиренную и смоченную поверхность формования спирта каплями, а затем наносят вяжущее, как описано выше. Падающие капли спирта разбивают слой жидкости на поверхности формования, разгоняют ее в стороны, оставляя место падения свободным от жидкости а в декоративном слое образуются пятна с контрастными очертания контура. Формула включений зависит от величины капли спирта, высоты ее падения и др. The conglomerate inclusions in the texture of the pattern of the decorative layer can also be obtained by applying drops to a defatted and moistened surface of molding alcohol, and then a binder is applied, as described above. Drop drops of alcohol break the liquid layer on the molding surface, disperse it to the sides, leaving the place of falling free of liquid and spots form with a contrasting outline in the decorative layer. The inclusion formula depends on the size of a drop of alcohol, the height of its drop, etc.

После формирования декоративного слоя его покрывают слоем основы из затворенного вяжущего с заполнителями (для прочности) или без них. В этом случае возможна установка армирующих элементов или закладных деталей. After the formation of the decorative layer, it is covered with a base layer of a closed binder with aggregates (for strength) or without them. In this case, it is possible to install reinforcing elements or embedded parts.

Затем изделие выдерживают в форме до окончательного отверждения и расформовывают. Лицевую декоративную поверхность готового изделия покрывают адгезивом. Then the product is kept in shape until the final cure and unformed. The front decorative surface of the finished product is coated with adhesive.

В качестве адгезива используют лака, клеи, эпоксидные, кремнийорганические смолы и др. в зависимости от назначения изделий, среды. As an adhesive, varnish, glues, epoxy, organosilicon resins, etc. are used, depending on the purpose of the products and the environment.

Полученные изделия имеют на лицевой стороне изделия глянцевую поверхность с многоцветным насыщенным рисунком, имеющим прожилки, разводы с плавными или резкими переходами цветов, конгламератные включения с широким диапазоном получаемых текстур рисунка. Адгезив, применяемый для покрытия декоративной поверхности, а также гидрофобные добавки, введенные при нанесении декоративного слоя, придают изделию блеск полированного изделия и устойчивость к воздействиям окружающей среды. The resulting products have a glossy surface with a multicolored saturated pattern on the front side of the product, with streaks, stains with smooth or sharp transitions of colors, conglomerate inclusions with a wide range of texture patterns. The adhesive used to cover the decorative surface, as well as the hydrophobic additives introduced during the application of the decorative layer, give the product a gloss of the polished product and resistance to environmental influences.

Предлагаемым способом можно получить изделия с заранее подобранной текстурой рисунка по цвету и фактуре, имитирующей такие естественные камни, как мрамор всех пород и оттенков, яшму, мраморизованный брекчевидный известняк и др. при значительном снижении трудоемкости изготовления изделий. The proposed method allows you to get products with a pre-selected texture of the picture in color and texture, imitating such natural stones as marble of all breeds and shades, jasper, marbled brexevic limestone, etc. with a significant reduction in the complexity of manufacturing products.

Claims

1. A method of manufacturing a decorative product from a mineral binder, comprising mixing a decorative, pigmented layer, for example, with a texture of a pattern having conglomerate inclusions, applying a base layer, holding until completely cured, followed by unfolding of the product, characterized in that that the smooth molding surface is degreased, the binder of the pigmented layer is applied to the previously wetted molding surface arbitrarily, until it disappears The development of free fluid, simultaneously forming conglomerate inclusions of the texture of the pattern, the base layer is formed with a solution of the closed binder, and the decorated surface of the deformed product is coated with adhesive.

2. The method according to claim 1, characterized in that in places of conglomerate inclusions of the texture of the pattern, the surface of the molding is lubricated with a fat solution before wetting.

3. The method according to claim 1, characterized in that in the places of conglomerate inclusions of the texture of the pattern, drops of alcohol are applied to the wetted molding surface.