RU2010139887A - METHOD FOR PRODUCING DECORATIVE PRODUCTS WITH A FILLER FROM AMBER AND / OR WASTE OF ITS PROCESSING (OPTIONS) - Google Patents

Abstract

 1. A method of manufacturing decorative products with a filler from amber and / or waste from its processing, including preparing a molding composition consisting of caustic magnesite, a solution of magnesium chloride, a filler, a filler (silica sand), followed by molding, compaction by vibration, curing, drying, characterized in that amber and / or its waste are used as a filler, molding material with a ratio of components, wt.%: caustic magnesite 20-25 filler, amber 10-15 magnesium chloride solution 20-25 fill eh, quartz sand the rest! it is poured into the mold of the required size, compacted with vibration for 0.5-1 min, dried at a temperature of 13-30 ° C for 1-3 days, then removed from the mold, sanded, polished, final polishing is performed, for example, with a mixture of paraffin and wax for fixing or, if necessary, varnish. ! 2. A method of manufacturing decorative products with amber filler and / or waste from its processing includes preparing a molding composition consisting of caustic magnesite, a solution of magnesium chloride, filler, aggregate (silica sand), followed by molding, vibration compaction, curing, drying, characterized the fact that amber and / or its wastes are used as a filler, the manufacturing method includes two stages, at the first stage all stages are performed according to the first embodiment until drying is completed at a ratio of components in the molding composition, wt.%: caustic magnesite 20-25 filler, amber 10-15 solution of magnesium chloride 20-25 filler, quartz sand the rest! at the second stage, the molding material is prepared with the same

Claims (3)

1. A method of manufacturing decorative products with a filler from amber and / or waste from its processing, including preparing a molding composition consisting of caustic magnesite, a solution of magnesium chloride, a filler, a filler (silica sand), followed by molding, compaction by vibration, curing, drying, characterized in that the filler used amber and / or its waste, molding material with a ratio of components, wt.%: caustic magnesite 20-25 amber filler 10-15 magnesium chloride solution 20-25 silica sand aggregate rest, it is poured into the mold of the required size, compacted with vibration for 0.5-1 min, dried at a temperature of 13-30 ° C for 1-3 days, then removed from the mold, sanded, polished, final polishing is performed, for example, with a mixture of paraffin and wax for fixing or, if necessary, varnish. 2. A method of manufacturing decorative products with amber filler and / or waste from its processing includes preparing a molding composition consisting of caustic magnesite, a solution of magnesium chloride, filler, aggregate (silica sand), followed by molding, compaction by vibration, curing, drying, characterized the fact that amber and / or its wastes are used as a filler, the manufacturing method includes two stages, at the first stage all stages are performed according to the first embodiment until drying is completed at a ratio of components in the molding composition, wt.%: caustic magnesite 20-25 amber filler 10-15 magnesium chloride solution 20-25 silica sand aggregate rest at the second stage, the molding material is prepared with the same ratio of components, using amber and / or its waste instead of filler, wood filler, then the molding material is poured onto the first layer to the height of the desired product size, compacted with vibration for 1-2 minutes, performed drying in a drying chamber at a temperature of at least 16 ° C for at least two days, after which the product is removed from the mold, ground, polished, final polished, for example, with a mixture of paraffin and wax for fixing or, if necessary, awns are varnished. 3. A method of manufacturing decorative products with amber filler and / or waste from its processing includes preparing a molding composition consisting of caustic magnesite, a solution of magnesium chloride, filler, aggregate (silica sand), followed by molding, compaction by vibration, curing, drying, characterized the fact that amber and / or waste from its production is used as a filler, which is laid out according to a predetermined pattern, for example, in the form of a mosaic, poured with a composition including caustic magnesite and astvor magnesium chloride in the ratio, in weight.%: 60-70 and 40-30 to completely cover the pattern of the filler and allowed to stand for 5-6 hours, then the molding material in a ratio, wt.%: caustic magnesite 20-25 filler, sawdust 10-15 magnesium chloride solution 20-25 silica sand aggregate rest pour on the first layer to the height of the desired size of the product, compact it with vibration for 1-2 minutes, perform drying in a drying chamber at a temperature of at least 16 ° C for at least two days, after which the product is removed from the mold, ground, ground, for example, diamond abrasives, until the appearance on the surface of the picture is a mosaic of amber, which is polished with polishing skins.