Способ получения кольцеобразных сплошных катализаторов Download PDFInfo
- Publication number
- RU2006113641A RU2006113641A RU2006113641/04A RU2006113641A RU2006113641A RU 2006113641 A RU2006113641 A RU 2006113641A RU 2006113641/04 A RU2006113641/04 A RU 2006113641/04A RU 2006113641 A RU2006113641 A RU 2006113641A RU 2006113641 A RU2006113641 A RU 2006113641A
- Authority
- RU
- Russia
- Prior art keywords
- diameter
- elements
- ring
- annular
- antimony
- Prior art date
Links
- 238000000034 method Methods 0.000 title claims 22
- 239000003054 catalyst Substances 0.000 title claims 18
- 239000000203 mixture Substances 0.000 claims 15
- 239000011148 porous material Substances 0.000 claims 15
- XEEYBQQBJWHFJM-UHFFFAOYSA-N Iron Chemical compound [Fe] XEEYBQQBJWHFJM-UHFFFAOYSA-N 0.000 claims 12
- PXHVJJICTQNCMI-UHFFFAOYSA-N Nickel Chemical compound [Ni] PXHVJJICTQNCMI-UHFFFAOYSA-N 0.000 claims 12
- ATJFFYVFTNAWJD-UHFFFAOYSA-N Tin Chemical compound [Sn] ATJFFYVFTNAWJD-UHFFFAOYSA-N 0.000 claims 9
- 229910052787 antimony Inorganic materials 0.000 claims 9
- WATWJIUSRGPENY-UHFFFAOYSA-N antimony atom Chemical compound [Sb] WATWJIUSRGPENY-UHFFFAOYSA-N 0.000 claims 9
- 239000011135 tin Substances 0.000 claims 9
- 229910052718 tin Inorganic materials 0.000 claims 9
- 239000011701 zinc Substances 0.000 claims 7
- ZOXJGFHDIHLPTG-UHFFFAOYSA-N Boron Chemical compound [B] ZOXJGFHDIHLPTG-UHFFFAOYSA-N 0.000 claims 6
- 229910052684 Cerium Inorganic materials 0.000 claims 6
- RYGMFSIKBFXOCR-UHFFFAOYSA-N Copper Chemical compound [Cu] RYGMFSIKBFXOCR-UHFFFAOYSA-N 0.000 claims 6
- ZOKXTWBITQBERF-UHFFFAOYSA-N Molybdenum Chemical compound [Mo] ZOKXTWBITQBERF-UHFFFAOYSA-N 0.000 claims 6
- OAICVXFJPJFONN-UHFFFAOYSA-N Phosphorus Chemical compound [P] OAICVXFJPJFONN-UHFFFAOYSA-N 0.000 claims 6
- XUIMIQQOPSSXEZ-UHFFFAOYSA-N Silicon Chemical compound [Si] XUIMIQQOPSSXEZ-UHFFFAOYSA-N 0.000 claims 6
- RTAQQCXQSZGOHL-UHFFFAOYSA-N Titanium Chemical compound [Ti] RTAQQCXQSZGOHL-UHFFFAOYSA-N 0.000 claims 6
- HCHKCACWOHOZIP-UHFFFAOYSA-N Zinc Chemical compound [Zn] HCHKCACWOHOZIP-UHFFFAOYSA-N 0.000 claims 6
- QCWXUUIWCKQGHC-UHFFFAOYSA-N Zirconium Chemical compound [Zr] QCWXUUIWCKQGHC-UHFFFAOYSA-N 0.000 claims 6
- 229910052783 alkali metal Inorganic materials 0.000 claims 6
- 150000001340 alkali metals Chemical class 0.000 claims 6
- 229910052784 alkaline earth metal Inorganic materials 0.000 claims 6
- 150000001342 alkaline earth metals Chemical class 0.000 claims 6
- 229910052782 aluminium Inorganic materials 0.000 claims 6
- XAGFODPZIPBFFR-UHFFFAOYSA-N aluminium Chemical compound [Al] XAGFODPZIPBFFR-UHFFFAOYSA-N 0.000 claims 6
- 229910052785 arsenic Inorganic materials 0.000 claims 6
- RQNWIZPPADIBDY-UHFFFAOYSA-N arsenic atom Chemical compound [As] RQNWIZPPADIBDY-UHFFFAOYSA-N 0.000 claims 6
- QVGXLLKOCUKJST-UHFFFAOYSA-N atomic oxygen Chemical compound [O] QVGXLLKOCUKJST-UHFFFAOYSA-N 0.000 claims 6
- 229910052797 bismuth Inorganic materials 0.000 claims 6
- JCXGWMGPZLAOME-UHFFFAOYSA-N bismuth atom Chemical compound [Bi] JCXGWMGPZLAOME-UHFFFAOYSA-N 0.000 claims 6
- 229910052796 boron Inorganic materials 0.000 claims 6
- GWXLDORMOJMVQZ-UHFFFAOYSA-N cerium Chemical compound [Ce] GWXLDORMOJMVQZ-UHFFFAOYSA-N 0.000 claims 6
- 239000010941 cobalt Substances 0.000 claims 6
- 229910017052 cobalt Inorganic materials 0.000 claims 6
- GUTLYIVDDKVIGB-UHFFFAOYSA-N cobalt atom Chemical compound [Co] GUTLYIVDDKVIGB-UHFFFAOYSA-N 0.000 claims 6
- 229910052802 copper Inorganic materials 0.000 claims 6
- 239000010949 copper Substances 0.000 claims 6
- 229910052742 iron Inorganic materials 0.000 claims 6
- 229910052750 molybdenum Inorganic materials 0.000 claims 6
- 239000011733 molybdenum Substances 0.000 claims 6
- 229910052759 nickel Inorganic materials 0.000 claims 6
- 229910052760 oxygen Inorganic materials 0.000 claims 6
- 239000001301 oxygen Substances 0.000 claims 6
- 229910052698 phosphorus Inorganic materials 0.000 claims 6
- 239000011574 phosphorus Substances 0.000 claims 6
- 229910052710 silicon Inorganic materials 0.000 claims 6
- 239000010703 silicon Substances 0.000 claims 6
- 229910052716 thallium Inorganic materials 0.000 claims 6
- BKVIYDNLLOSFOA-UHFFFAOYSA-N thallium Chemical compound [Tl] BKVIYDNLLOSFOA-UHFFFAOYSA-N 0.000 claims 6
- 229910052719 titanium Inorganic materials 0.000 claims 6
- 239000010936 titanium Substances 0.000 claims 6
- WFKWXMTUELFFGS-UHFFFAOYSA-N tungsten Chemical compound [W] WFKWXMTUELFFGS-UHFFFAOYSA-N 0.000 claims 6
- 229910052721 tungsten Inorganic materials 0.000 claims 6
- 239000010937 tungsten Substances 0.000 claims 6
- 229910052725 zinc Inorganic materials 0.000 claims 6
- 229910052726 zirconium Inorganic materials 0.000 claims 6
- 230000006835 compression Effects 0.000 claims 5
- 238000007906 compression Methods 0.000 claims 5
- 238000010438 heat treatment Methods 0.000 claims 4
- ZSLUVFAKFWKJRC-IGMARMGPSA-N 232Th Chemical compound [232Th] ZSLUVFAKFWKJRC-IGMARMGPSA-N 0.000 claims 3
- VYZAMTAEIAYCRO-UHFFFAOYSA-N Chromium Chemical compound [Cr] VYZAMTAEIAYCRO-UHFFFAOYSA-N 0.000 claims 3
- GYHNNYVSQQEPJS-UHFFFAOYSA-N Gallium Chemical compound [Ga] GYHNNYVSQQEPJS-UHFFFAOYSA-N 0.000 claims 3
- KJTLSVCANCCWHF-UHFFFAOYSA-N Ruthenium Chemical compound [Ru] KJTLSVCANCCWHF-UHFFFAOYSA-N 0.000 claims 3
- 229910052772 Samarium Inorganic materials 0.000 claims 3
- BQCADISMDOOEFD-UHFFFAOYSA-N Silver Chemical compound [Ag] BQCADISMDOOEFD-UHFFFAOYSA-N 0.000 claims 3
- 229910052776 Thorium Inorganic materials 0.000 claims 3
- 229910052770 Uranium Inorganic materials 0.000 claims 3
- 229910052793 cadmium Inorganic materials 0.000 claims 3
- BDOSMKKIYDKNTQ-UHFFFAOYSA-N cadmium atom Chemical compound [Cd] BDOSMKKIYDKNTQ-UHFFFAOYSA-N 0.000 claims 3
- CWJSHJJYOPWUGX-UHFFFAOYSA-N chlorpropham Chemical compound CC(C)OC(=O)NC1=CC=CC(Cl)=C1 CWJSHJJYOPWUGX-UHFFFAOYSA-N 0.000 claims 3
- 229910052804 chromium Inorganic materials 0.000 claims 3
- 239000011651 chromium Substances 0.000 claims 3
- 229910052733 gallium Inorganic materials 0.000 claims 3
- 229910052732 germanium Inorganic materials 0.000 claims 3
- GNPVGFCGXDBREM-UHFFFAOYSA-N germanium atom Chemical compound [Ge] GNPVGFCGXDBREM-UHFFFAOYSA-N 0.000 claims 3
- PCHJSUWPFVWCPO-UHFFFAOYSA-N gold Chemical compound [Au] PCHJSUWPFVWCPO-UHFFFAOYSA-N 0.000 claims 3
- 229910052737 gold Inorganic materials 0.000 claims 3
- 239000010931 gold Substances 0.000 claims 3
- 229910052738 indium Inorganic materials 0.000 claims 3
- APFVFJFRJDLVQX-UHFFFAOYSA-N indium atom Chemical compound [In] APFVFJFRJDLVQX-UHFFFAOYSA-N 0.000 claims 3
- WPBNNNQJVZRUHP-UHFFFAOYSA-L manganese(2+);methyl n-[[2-(methoxycarbonylcarbamothioylamino)phenyl]carbamothioyl]carbamate;n-[2-(sulfidocarbothioylamino)ethyl]carbamodithioate Chemical compound [Mn+2].[S-]C(=S)NCCNC([S-])=S.COC(=O)NC(=S)NC1=CC=CC=C1NC(=S)NC(=O)OC WPBNNNQJVZRUHP-UHFFFAOYSA-L 0.000 claims 3
- QSHDDOUJBYECFT-UHFFFAOYSA-N mercury Chemical compound [Hg] QSHDDOUJBYECFT-UHFFFAOYSA-N 0.000 claims 3
- 229910052753 mercury Inorganic materials 0.000 claims 3
- 229910052758 niobium Inorganic materials 0.000 claims 3
- 239000010955 niobium Substances 0.000 claims 3
- GUCVJGMIXFAOAE-UHFFFAOYSA-N niobium atom Chemical compound [Nb] GUCVJGMIXFAOAE-UHFFFAOYSA-N 0.000 claims 3
- VXPLXMJHHKHSOA-UHFFFAOYSA-N propham Chemical compound CC(C)OC(=O)NC1=CC=CC=C1 VXPLXMJHHKHSOA-UHFFFAOYSA-N 0.000 claims 3
- 229910052761 rare earth metal Inorganic materials 0.000 claims 3
- 150000002910 rare earth metals Chemical class 0.000 claims 3
- 229910052702 rhenium Inorganic materials 0.000 claims 3
- WUAPFZMCVAUBPE-UHFFFAOYSA-N rhenium atom Chemical compound [Re] WUAPFZMCVAUBPE-UHFFFAOYSA-N 0.000 claims 3
- 229910052703 rhodium Inorganic materials 0.000 claims 3
- 239000010948 rhodium Substances 0.000 claims 3
- MHOVAHRLVXNVSD-UHFFFAOYSA-N rhodium atom Chemical compound [Rh] MHOVAHRLVXNVSD-UHFFFAOYSA-N 0.000 claims 3
- 229910052707 ruthenium Inorganic materials 0.000 claims 3
- KZUNJOHGWZRPMI-UHFFFAOYSA-N samarium atom Chemical compound [Sm] KZUNJOHGWZRPMI-UHFFFAOYSA-N 0.000 claims 3
- 229910052709 silver Inorganic materials 0.000 claims 3
- 239000004332 silver Substances 0.000 claims 3
- 239000011949 solid catalyst Substances 0.000 claims 3
- 229910052715 tantalum Inorganic materials 0.000 claims 3
- GUVRBAGPIYLISA-UHFFFAOYSA-N tantalum atom Chemical compound [Ta] GUVRBAGPIYLISA-UHFFFAOYSA-N 0.000 claims 3
- 229910052714 tellurium Inorganic materials 0.000 claims 3
- PORWMNRCUJJQNO-UHFFFAOYSA-N tellurium atom Chemical compound [Te] PORWMNRCUJJQNO-UHFFFAOYSA-N 0.000 claims 3
- JFALSRSLKYAFGM-UHFFFAOYSA-N uranium(0) Chemical compound [U] JFALSRSLKYAFGM-UHFFFAOYSA-N 0.000 claims 3
- 229910052720 vanadium Inorganic materials 0.000 claims 3
- LEONUFNNVUYDNQ-UHFFFAOYSA-N vanadium atom Chemical compound [V] LEONUFNNVUYDNQ-UHFFFAOYSA-N 0.000 claims 3
- HGINCPLSRVDWNT-UHFFFAOYSA-N Acrolein Chemical compound C=CC=O HGINCPLSRVDWNT-UHFFFAOYSA-N 0.000 claims 2
- VQTUBCCKSQIDNK-UHFFFAOYSA-N Isobutene Chemical compound CC(C)=C VQTUBCCKSQIDNK-UHFFFAOYSA-N 0.000 claims 2
- QQONPFPTGQHPMA-UHFFFAOYSA-N Propene Chemical compound CC=C QQONPFPTGQHPMA-UHFFFAOYSA-N 0.000 claims 2
- DKGAVHZHDRPRBM-UHFFFAOYSA-N Tert-Butanol Chemical compound CC(C)(C)O DKGAVHZHDRPRBM-UHFFFAOYSA-N 0.000 claims 2
- 239000000470 constituent Substances 0.000 claims 2
- 239000007789 gas Substances 0.000 claims 2
- 238000000465 moulding Methods 0.000 claims 2
- 230000003647 oxidation Effects 0.000 claims 2
- 238000007254 oxidation reaction Methods 0.000 claims 2
- 239000012779 reinforcing material Substances 0.000 claims 2
- STNJBCKSHOAVAJ-UHFFFAOYSA-N Methacrolein Chemical compound CC(=C)C=O STNJBCKSHOAVAJ-UHFFFAOYSA-N 0.000 claims 1
- 229910052792 caesium Inorganic materials 0.000 claims 1
- 230000003197 catalytic effect Effects 0.000 claims 1
- 229910052700 potassium Inorganic materials 0.000 claims 1
- 239000000126 substance Substances 0.000 claims 1
Classifications
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
-
- C—CHEMISTRY; METALLURGY
- C07—ORGANIC CHEMISTRY
- C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
- C07C51/00—Preparation of carboxylic acids or their salts, halides or anhydrides
- C07C51/16—Preparation of carboxylic acids or their salts, halides or anhydrides by oxidation
- C07C51/21—Preparation of carboxylic acids or their salts, halides or anhydrides by oxidation with molecular oxygen
- C07C51/25—Preparation of carboxylic acids or their salts, halides or anhydrides by oxidation with molecular oxygen of unsaturated compounds containing no six-membered aromatic ring
- C07C51/252—Preparation of carboxylic acids or their salts, halides or anhydrides by oxidation with molecular oxygen of unsaturated compounds containing no six-membered aromatic ring of propene, butenes, acrolein or methacrolein
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
- B01J23/002—Mixed oxides other than spinels, e.g. perovskite
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
- B01J23/70—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper
- B01J23/76—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
- B01J23/70—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper
- B01J23/76—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36
- B01J23/84—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36 with arsenic, antimony, bismuth, vanadium, niobium, tantalum, polonium, chromium, molybdenum, tungsten, manganese, technetium or rhenium
- B01J23/85—Chromium, molybdenum or tungsten
- B01J23/88—Molybdenum
- B01J23/887—Molybdenum containing in addition other metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
- B01J23/70—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper
- B01J23/76—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36
- B01J23/84—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36 with arsenic, antimony, bismuth, vanadium, niobium, tantalum, polonium, chromium, molybdenum, tungsten, manganese, technetium or rhenium
- B01J23/85—Chromium, molybdenum or tungsten
- B01J23/88—Molybdenum
- B01J23/887—Molybdenum containing in addition other metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36
- B01J23/8876—Arsenic, antimony or bismuth
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
- B01J23/70—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper
- B01J23/76—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36
- B01J23/84—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36 with arsenic, antimony, bismuth, vanadium, niobium, tantalum, polonium, chromium, molybdenum, tungsten, manganese, technetium or rhenium
- B01J23/85—Chromium, molybdenum or tungsten
- B01J23/888—Tungsten
- B01J23/8885—Tungsten containing also molybdenum
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J35/00—Catalysts, in general, characterised by their form or physical properties
- B01J35/19—Catalysts containing parts with different compositions
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J35/00—Catalysts, in general, characterised by their form or physical properties
- B01J35/30—Catalysts, in general, characterised by their form or physical properties characterised by their physical properties
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J35/00—Catalysts, in general, characterised by their form or physical properties
- B01J35/50—Catalysts, in general, characterised by their form or physical properties characterised by their shape or configuration
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J35/00—Catalysts, in general, characterised by their form or physical properties
- B01J35/60—Catalysts, in general, characterised by their form or physical properties characterised by their surface properties or porosity
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
- B01J37/0009—Use of binding agents; Moulding; Pressing; Powdering; Granulating; Addition of materials ameliorating the mechanical properties of the product catalyst
- B01J37/0018—Addition of a binding agent or of material, later completely removed among others as result of heat treatment, leaching or washing,(e.g. forming of pores; protective layer, desintegrating by heat)
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
- B01J37/08—Heat treatment
-
- C—CHEMISTRY; METALLURGY
- C07—ORGANIC CHEMISTRY
- C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
- C07C45/00—Preparation of compounds having >C = O groups bound only to carbon or hydrogen atoms; Preparation of chelates of such compounds
-
- C—CHEMISTRY; METALLURGY
- C07—ORGANIC CHEMISTRY
- C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
- C07C45/00—Preparation of compounds having >C = O groups bound only to carbon or hydrogen atoms; Preparation of chelates of such compounds
- C07C45/27—Preparation of compounds having >C = O groups bound only to carbon or hydrogen atoms; Preparation of chelates of such compounds by oxidation
- C07C45/32—Preparation of compounds having >C = O groups bound only to carbon or hydrogen atoms; Preparation of chelates of such compounds by oxidation with molecular oxygen
- C07C45/33—Preparation of compounds having >C = O groups bound only to carbon or hydrogen atoms; Preparation of chelates of such compounds by oxidation with molecular oxygen of CHx-moieties
- C07C45/34—Preparation of compounds having >C = O groups bound only to carbon or hydrogen atoms; Preparation of chelates of such compounds by oxidation with molecular oxygen of CHx-moieties in unsaturated compounds
- C07C45/35—Preparation of compounds having >C = O groups bound only to carbon or hydrogen atoms; Preparation of chelates of such compounds by oxidation with molecular oxygen of CHx-moieties in unsaturated compounds in propene or isobutene
-
- C—CHEMISTRY; METALLURGY
- C07—ORGANIC CHEMISTRY
- C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
- C07C45/00—Preparation of compounds having >C = O groups bound only to carbon or hydrogen atoms; Preparation of chelates of such compounds
- C07C45/27—Preparation of compounds having >C = O groups bound only to carbon or hydrogen atoms; Preparation of chelates of such compounds by oxidation
- C07C45/32—Preparation of compounds having >C = O groups bound only to carbon or hydrogen atoms; Preparation of chelates of such compounds by oxidation with molecular oxygen
- C07C45/37—Preparation of compounds having >C = O groups bound only to carbon or hydrogen atoms; Preparation of chelates of such compounds by oxidation with molecular oxygen of >C—O—functional groups to >C=O groups
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
- B01J23/70—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper
- B01J23/76—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36
- B01J23/84—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36 with arsenic, antimony, bismuth, vanadium, niobium, tantalum, polonium, chromium, molybdenum, tungsten, manganese, technetium or rhenium
- B01J23/85—Chromium, molybdenum or tungsten
- B01J23/88—Molybdenum
- B01J23/887—Molybdenum containing in addition other metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36
- B01J23/8877—Vanadium, tantalum, niobium or polonium
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J2523/00—Constitutive chemical elements of heterogeneous catalysts
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J35/00—Catalysts, in general, characterised by their form or physical properties
- B01J35/60—Catalysts, in general, characterised by their form or physical properties characterised by their surface properties or porosity
- B01J35/61—Surface area
- B01J35/612—Surface area less than 10 m2/g
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J35/00—Catalysts, in general, characterised by their form or physical properties
- B01J35/60—Catalysts, in general, characterised by their form or physical properties characterised by their surface properties or porosity
- B01J35/61—Surface area
- B01J35/613—10-100 m2/g
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J35/00—Catalysts, in general, characterised by their form or physical properties
- B01J35/60—Catalysts, in general, characterised by their form or physical properties characterised by their surface properties or porosity
- B01J35/63—Pore volume
- B01J35/633—Pore volume less than 0.5 ml/g
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J35/00—Catalysts, in general, characterised by their form or physical properties
- B01J35/60—Catalysts, in general, characterised by their form or physical properties characterised by their surface properties or porosity
- B01J35/66—Pore distribution
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
- B01J37/0009—Use of binding agents; Moulding; Pressing; Powdering; Granulating; Addition of materials ameliorating the mechanical properties of the product catalyst
- B01J37/0063—Granulating
Landscapes
- Chemical & Material Sciences (AREA)
- Organic Chemistry (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Oil, Petroleum & Natural Gas (AREA)
- Physics & Mathematics (AREA)
- Thermal Sciences (AREA)
- Catalysts (AREA)
- Organic Low-Molecular-Weight Compounds And Preparation Thereof (AREA)
- Low-Molecular Organic Synthesis Reactions Using Catalysts (AREA)
Claims (28)
1. Способ получения кольцеобразных сплошных катализаторов, имеющих изогнутую и/или неизогнутую торцевую поверхность колец, активная масса которых имеет стехиометрический состав общей формулы I
в которой X1 означает никель и/или кобальт,
X2 означает таллий, щелочной металл и/или щелочно-земельный металл,
X3 означает цинк, фосфор, мышьяк, бор, сурьму, олово, церий, свинец и/или вольфрам,
X4 означает кремний, алюминий, титан и/или цирконий,
а означает от 0,2 до 5,
b означает от 0,01 до 5,
с означает от 0 до 10,
d означает от 0 до 2,
е означает от 0 до 8,
f означает от 0 до 10 и
n означает число, которое определяется валентностью и количеством отличных от кислорода элементов в I,
или стехиометрический состав общей формулы II
в которой Y1 означает только висмут или висмут и, по меньшей мере, один из таких элементов, как теллур, сурьма, олово и медь,
Y2 означает молибден или молибден и вольфрам,
Y3 означает щелочной металл, таллий и/или самарий,
Y4 означает щелочно-земельный металл, никель, кобальт, медь, марганец, цинк, олово, кадмий и/или ртуть,
Y5 означает железо или железо и, по меньшей мере, один из таких элементов, как ванадий, хром и церий,
Y6 означает фосфор, мышьяк, бор и/или сурьму,
Y7 означает редкоземельный металл, титан, цирконий, ниобий, тантал, рений, рутений, родий, серебро, золото, алюминий, галлий, индий, кремний, германий, свинец, торий и/или уран,
а′ означает от 0,01 до 8,
b′ означает от 0,1 до 30,
с′ означает от 0 до 4,
d′ означает от 0 до 20
е′ >0-20,
f′ означает от 0 до 6,
g′ означает от 0 до 15,
h′ означает от 8 до 16,
х′, у′ означают числа, которые определяются валентностью и количеством отличных от кислорода элементов в II и
р, q означают числа, отношение p/q которых составляет от 0,1 до 10, и кольцеобразная форма которых, не учитывая, в случае необходимости, существующую кривизну торцевой поверхности, имеет длину L от 2 до 11 мм, наружный диаметр А от 2 до 11 мм и толщину стенки W от 0,75 до 1,75 мм,
согласно которому из источников элементарных составляющих активной массы получают тонкодисперсную пластичную смесь, а из этой смеси, в случае необходимости, при добавлении вспомогательных средств для формования и/или вспомогательных армирующих материалов формуют кольцеобразные формованные изделия, предшествующие сплошным катализаторам, торцевая поверхность которых является изогнутой и/или неизогнутой, после чего термической обработкой при повышенной температуре их переводят в кольцеобразные сплошные катализаторы, отличающийся тем, что прочность при боковом сжатии кольцеобразных формованных изделий, предшествующих сплошным катализаторам, ≥12 Н и ≤23 Н.
2. Способ по п.1, отличающийся тем, что прочность при боковом сжатии кольцеобразных формованных изделий, предшествующих сплошным катализаторам, ≥13 H и ≤22 H.
3. Способ по п.1, отличающийся тем, что прочность при боковом сжатии кольцеобразных формованных изделий, предшествующих сплошным катализаторам ≥15 Н и ≤20 Н.
4. Способ по п.1, отличающийся тем, что размеры колец дополнительно соответствуют условию: L/А = 0,3 - 0,7.
5. Способ по п.1, отличающийся тем, что размеры колец дополнительно соответствуют условию: L/А = 0,4 - 0,6.
6. Способ по п.1, отличающийся тем, что размеры колец дополнительно соответствуют отношению внутреннего диаметра I к наружному диаметру А = 0,5 - 0,8.
7. Способ по п.1, отличающийся тем, что размеры колец дополнительно соответствуют отношению внутреннего диаметра I к наружному диаметру А = 0,6 - 0,7.
8. Способ по п.1, отличающийся тем, что L = 2 - 6 мм.
9. Способ по п.1, отличающийся тем, что L = 2 - 4 мм.
10. Способ по п.1, отличающийся тем, что L = 4 - 8 мм.
11. Способ по п.1, отличающийся тем, что L = 5 - 7 мм.
12. Способ по п.1, отличающийся тем, что толщина стенки колец составляет от 1 до 1,5 мм.
13. Способ по п.1, отличающийся тем, что размеры колец, выраженные А×L×I, представляют собой размеры из группы, включающей
а) 5 мм × 3 мм × 2 мм,
b) 5 мм × 3 мм × 3 мм,
c) 5,5 мм × 3 мм × 3,5 мм,
d) 6 мм × 3 мм × 4 мм,
e) 6,5 мм × 3 мм × 4,5 мм и
f) 7 мм × 3 мм × 5 мм.
14. Способ по п.1, отличающийся тем, что активная масса имеет стехиометрический состав общей формулы I, причем
а означает от 0,4 до 2;
b означает от 2 до 4;
с означает от 3 до 10;
d означает от 0,02 до 2;
е означает от 0 до 5 и
f означает от 0,5 до 10.
15. Способ по п.1, отличающийся тем, что активная масса имеет стехиометрический состав общей формулы I, причем
X1 означает Со;
X2 означает К, Cs и/или Sr;
X3 означает Zn и/или Р и
X4 означает Si.
16. Способ по п.1, отличающийся тем, что активная масса имеет стехиометрический состав II и содержит трехмерно распространенные, отграниченные от окружения вследствие отличного от окружения состава области химического состава Y1 a′Y2 b′Ox′, самый большой диаметр которых составляет от 1 нм до 100 мкм.
17. Способ по п.1, отличающийся тем, что Y1 означает Bi.
18. Способ по п.1, отличающийся тем, что термическую обработку кольцеобразного формованного изделия, предшествующего сплошному катализатору, осуществляют при температурах, которые превышают 350°С, но не превышают 650°С.
19. Способ по одному из пп.1-18, отличающийся тем, что термическую обработку осуществляют в ленточном обжиговом устройстве.
20. Кольцеобразный сплошной катализатор с изогнутой и/или неизогнутой торцевой поверхностью кольца, активная масса которого имеет стехиометрический состав общей формулы I
в которой X1 означает никель и/или кобальт,
X2 означает таллий, щелочной металл и/или щелочно-земельный металл,
X3 означает цинк, фосфор, мышьяк, бор, сурьму, олово, церий, свинец и/или вольфрам,
X4 означает кремний, алюминий, титан и/или цирконий,
а означает от 0,2 до 5,
b означает от 0,01 до 5,
с означает от 0 до 10,
d означает от 0 до 2,
е означает от 0 до 8,
f означает от 0 до 10 и
n означает число, которое определяется валентностью и количеством отличных от кислорода элементов в I,
или стехиометрический состав общей формулы II
в которой Y1 означает только висмут или висмут и, по меньшей мере, один из таких элементов, как теллур, сурьма, олово и медь,
Y2 означает молибден или молибден и вольфрам,
Y3 означает щелочной металл, таллий и/или самарий,
Y4 означает щелочно-земельный металл, никель, кобальт, медь, марганец, цинк, олово, кадмий и/или ртуть,
Y5 означает железо или железо и, по меньшей мере, один из таких элементов, как ванадий, хром и церий,
Y6 означает фосфор, мышьяк, бор и/или сурьму,
Y7 означает редкоземельный металл, титан, цирконий, ниобий, тантал, рений, рутений, родий, серебро, золото, алюминий, галлий, индий, кремний, германий, свинец, торий и/или уран,
а′ означает от 0,01 до 8,
b′ означает от 0,1 до 30,
с′ означает от 0 до 4,
d′ означает от 0 до 20,
е′ >0-20,
f′ означает от 0 до 6,
g′ означает от 0 до 15,
h′ означает от 8 до 16,
х′, у′ означают числа, которые определяются валентностью и количеством отличных от кислорода элементов в II и
р, q означают числа, отношение p/q которых составляет от 0,1 до 10, кольцеобразная форма которых, не учитывая, в случае необходимости, существующую кривизну торцевой поверхности, имеет длину L от 2 до 11 мм, наружный диаметр А от 2 до 11 мм и толщину стенки W от 0,75 до 1,75 мм,
и отличающийся тем, что его специфическая площадь поверхности О составляет от 5 до 20 м2/г, а общий объем пор от 0,1 до 1 см3/г, причем различные диаметры пор вносят свою часть в общий объем пор V:
поры диаметром <0,03 мкм: ≤5 об. %;
поры диаметром от ≥0,03 до ≤0,1 мкм: ≤25 об. %;
поры диаметром от >0,1 до <1 мкм: ≥70 об. %; и
поры диаметром от ≥1 до ≤10 мкм: ≤10 об. %.
21. Кольцеобразный сплошной катализатор по п.20, в котором О = от 5 до 10 м2/г.
22. Кольцеобразный сплошной катализатор по п.20, в котором V = от 0,2 до 0,4 см3/г.
23. Кольцеобразный сплошной катализатор по п.20, причем различные диаметры пор вносят свою часть в общий объем пор V:
поры диаметром <0,03 мкм: ≥0 и ≤5 об. %;
поры диаметром от ≥0,03 до ≤0,1 мкм: ≥3 и ≤20 об. %;
поры диаметром от >0,1 до <1 мкм: ≥75 и ≤95 об. %;
поры диаметром от ≥1 до ≤10 мкм: ≥0 и ≤5 об. %.
24. Кольцеобразный сплошной катализатор по п.20, причем диаметр пор dмакс от 0,3 до 0,8 мкм вносит самую большую часть в общий объем пор V.
25. Кольцеобразный сплошной катализатор по п.20, причем прочность при боковом сжатии составляет от 5 до 13 Н.
26. Кольцеобразный сплошной катализатор по одному из пп.20-25, в котором отношение мнимой плотности массы к подлинной >0,55.
27. Кольцеобразное формованное изделие, предшествующее сплошному катализатору, формуемое термической обработкой при повышенной температуре до получения кольцеобразного сплошного катализатора с изогнутой и/или неизогнутой торцевой поверхностью кольца, активная масса которого имеет стехиометрический состав общей формулы I
в которой X1 означает никель и/или кобальт,
X2 означает таллий, щелочной металл и/или щелочно-земельный металл,
X3 означает цинк, фосфор, мышьяк, бор, сурьму, олово, церий, свинец и/или вольфрам,
X4 означает кремний, алюминий, титан и/или цирконий,
а означает от 0,2 до 5,
b означает от 0,01 до 5,
с означает от 0 до 10,
d означает от 0 до 2,
е означает от 0 до 8,
f означает от 0 до 10 и
n означает число, которое определяется валентностью и количеством отличных от кислорода элементов в I,
или стехиометрический состав общей формулы II
в которой Y1 означает только висмут или висмут и, по меньшей мере, один из таких элементов, как теллур, сурьма, олово и медь,
Y2 означает молибден или молибден и вольфрам,
Y3 означает щелочной металл, таллий и/или самарий,
Y4 означает щелочно-земельный металл, никель, кобальт, медь, марганец, цинк, олово, кадмий и/или ртуть,
Y5 означает железо или железо и, по меньшей мере, один из таких элементов, как ванадий, хром и церий,
Y6 означает фосфор, мышьяк, бор и/или сурьму,
Y7 означает редкоземельный металл, титан, цирконий, ниобий, тантал, рений, рутений, родий, серебро, золото, алюминий, галлий, индий, кремний, германий, свинец, торий и/или уран,
а′ означает от 0,01 до 8,
b′ означает от 0,1 до 30,
с′ означает от 0 до 4,
d′ означает от 0 до 20,
е′ >0-20,
f′ означает от 0 до 6,
g′ означает от 0 до 15,
h′ означает от 8 до 16,
х′, y′ означают числа, которые определяются валентностью и количеством отличных от кислорода элементов в II и
р, q означают числа, отношение p/q которых составляет от 0,1 до 10, кольцеобразная форма которых, не учитывая, в случае необходимости, существующую кривизну торцевой поверхности, имеет длину L от 2 до 11 мм, наружный диаметр А от 2 до 11 мм и толщину стенки W от 0,75 до 1,75 мм,
получаемый следующим образом: из источников элементарных составляющих активной массы получают тонкодисперсную пластичную смесь, и из этой смеси, в случае необходимости, при добавлении вспомогательных средств для формования и/или вспомогательных армирующих материалов, формуют кольцеобразные формованные изделия, предшествующие сплошным катализаторам, торцевая поверхность которых является изогнутой и/или неизогнутой, а их прочность при боковом сжатии ≥12 Н и ≤23 H.
28. Способ получения акролеина и/или метакролеина путем гетерогенного каталитического частичного окисления в газовой фазу пропена, изобутена и/или трет-бутанола, отличающийся тем, что катализатор для окисления в газовой фазе представляет собой кольцеобразный сплошной катализатор по одному из пп.20-26 или кольцеобразный сплошной катализатор, получаемый способом по одному из пп.1-19.